• Journal of Advanced Marine Engineering and Technology
• /
• 제23권6호
• /
• pp.806-813
• /
• 1999

The effect of Post-Weld Heat Treatment(PWHT) of SS400 Steel was investigated with parameters such as micro vickers hardness corrosion potential polarization behaviors galvanic current Al anode generating current Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM)by PWHT is lower than that of each parts by Non Post-Weld Heat Treatment(NPWHT) However hardness of WM of HAZ part was the highest among those three parts and HAZ area were also acted as cathode without any case of heat treatment. Potential difference between each three parts by PWHT was also smaller compared to NPWHT. Therefore it is suggested that Corrosion resistance property is increased by PWHT. However both Al anode generating current and anode weight loss was also decreased by PWHT compared to NPWHT when SS400 steel is cathodically protected by Al anode.

• 한국군사과학기술학회지
• /
• 제11권2호
• /
• pp.43-52
• /
• 2008

The galvanic corrosion of a vessel, or systems fitted to minimize the ship's corrosion such as ICCP (Impressed Current Cathodic Protection) system and sacrificial anodes, can lead to significant electrical current flow in the sea. The presence of vessel's current sources associated with corrosion will give rise to detectable electric field surrounding the vessel and can put it at risk from mine threats. For this reason, it is necessary to design corrosion protection systems so that they don't only prevent a hull corrosion but also minimize the electric field signature. In this paper, we describe theoretical backgrounds of underwater electric field signature due to corrosion and corrosion protection system on naval vessels and analysis results of the electric field according to the ship's hull and it's propeller coating damage and ICCP anode displacement.

• Corrosion Science and Technology
• /
• 제7권3호
• /
• pp.168-172
• /
• 2008

A new type of electrochemical random signal (electrochemical noise) analysis technique was applied to localized corrosion of anodic oxide film formed 1100 aluminum alloy in $0.5kmol/m^3$ $H_3BO_4/0.05kmol/m^3$ $Na_2B_4O_7$ with $0.01kmol/m^3$ NaCl. The effect of anodic oxide film structure, barrier type, porous type, and composite type on galvanic corrosion resistance was also examined. Before localized corrosion started, incubation period for pitting corrosion, both current and potential slightly change as initial value with time. The incubation period of porous type anodic oxide specimens are longer than that of barrier type anodic oxide specimens. While pitting corrosion, the current and potential were changed with fluctuations and the potential and the current fluctuations show a good correlation. The records of the current and potential were processed by calculating the power spectrum density (PSD) by the Fast Fourier Transform (FFT) method. The potential and current PSD decrease with increasing frequency, and the slopes are steeper than or equal to minus one (-1). This technique allows observation of electrochemical impedance changes during localized corrosion.

• 한국표면공학회지
• /
• 제36권4호
• /
• pp.301-306
• /
• 2003

Multilayered WC-Ti/suv $1-x/Al_{x}$ N coatings were deposited on AISI D2 steel using cathodic arc deposition (CAD) method. These coatings contain structural defects such as pores or droplets. Thus, the substrate is not completely isolated from the corrosive environment. The growth defects (pores, pinholes) in the coatings are detrimental to corrosion resistance of the coatings used in severe corrosion environments. The localized corrosion behavior of the coatings was studied in deaerated 3.5 wt.% NaCl solution using electrochemical techniques (potentiodynamic polarization test) and surface analyses (GDOES, SEM, AES, TEM). The porosity was calculated from the result of potentiodynamic polarization test of the uncoated and coated specimens. The calculated porosity is higher in the $WC-Ti_{0.6}$ $Al_{0.4}$ N than others, which is closely related to the packing factor. The positive effects of greater packing factor act on inhibiting the passage of the corrosive electrolyte to the substrate and lowering the localized corrosion kinetics. From the electrochemical tests and surface analyses, the major corrosion mechanisms can be classified into two basic categories: localized corrosion and galvanic corrosion.

• 대한치과보철학회지
• /
• 제38권1호
• /
• pp.85-97
• /
• 2000

The purpose of this study was to compare the corrosion characteristics between implant fixture and two types of abutment screw ; gold screw, titanium screw. The anodic polarization behavior, the galvanic corrosion behavior, and the crevice corrosion behavior of prepared samples were investigated using potentiostat and scanning electron microscope. The results were as follows: 1. Anodic polarization behavior of samples; The primary passivation potential of implant fixture was -420mV, implant abutment was -560mV. titanium screw was -370mV and gold screw was -230mV. All samples were shown to have a high corrosion potential and good formation of passive film. The critical passive current density of gold screw was higher than that of other samples and the sample of gold screw showed a unstable passive film formation at passive region. 2. Galvanic corrosion behavior of samples; Contact current density between implant fixture and titanium screw showed $8.023{\times}10^{-5}C/cm^2$. Contact current density between implant fixture and gold screw showed $5.142{\times}10^{-5}C/cm^2$. 3. Crevice corrosion behavior of samples; The crevice corrosion resistance of sample using titanium screw was higher than that of sample using gold screw, and a severe corrosion morphologies were observed at the fixture-screw interface by the scanning electron microscope.

• Journal of Advanced Marine Engineering and Technology
• /
• 제24권4호
• /
• pp.460-469
• /
• 2000

A study on the corrosion behavior of RE36 steel for marine structure was investigated with parameters such as micro-Vickers hardness, corrosion potential and corrosion current density measurement of weld metal(WM), base metal (BM) and heat affected zone(HAZ), Al anode generating current and Al anode weight loss quantity in case of cathodic protection. And we carried out slow strain rate test(SSRT) in order to research mechanical properties such as stress at maximum load, percent strain, time to fracture and strain to failure ratio etc and to find out limiting cathodic polarization potential for hydrogen embrittlement with applied cathodic polarization potential. Hardness of HAZ part was the highest among those three parts and also galvanic corrosion susceptibility was the highest in HAZ part among those three parts due to the lowest corrosion potential than other parts. However corrosion current density was the highest in WM part among those three parts. And the optimum cathodic polarization potential showing the best mechanical properties obtained by SSRT method with applied constant cathodic potential was from - 770mV to - 875mV(SCE). However it is suggested that limiting cathodic polarization potential indicating hydrogen embrittlement on the mechanical properties was under - 900mV(SCE).

• 한국산학기술학회논문지
• /
• 제20권5호
• /
• pp.559-568
• /
• 2019

최근 해양환경의 대형 SOC구조물 증가에 따른 구조물 내구성 증진에 관심이 증가되고 있다. 내구성 증진을 위해 개발된 FRP Hybrid Bar의 구조적 성능은 검증 되었으나 부식에 대한 저항성을 평가한 연구는 미흡하여 본 연구를 수행 하였다. 본 연구에서는 콘크리트 중의 철근 종류에 따른 철근부식 저항성을 평가하였다. 평가를 위하여 철근은 일반철근과 FRP hybrid Bar을 사용하였다. 시험방법은 갈바닉전류(Galvanic)와 반전지법(Half-Cell)을 사용하였으며, 철근부식 촉진을 위하여 콘크리트 내부에 염분을 0%, 1.5%, 3%, 6% 첨가하였다. 그 결과 갈바닉전류측정에서 FRP Hybrid Bar는 부식전류가 측정되지 않았다. 반면 일반철근에서는 시험 직후 부식이 발생하는 결과를 나타내었다. Half-Cell측정 결과에서도 4단계의 염분 함유량의 차이와 광물질혼화재료를 사용한 콘크리트와 일반콘크리트에 관계없이 FRP Hybrid Bar의 부식 저항성이 우수하게 나타났다. 따라서 FRP Hybrid Bar는 해양환경 및 철근부식이 예측되는 구조물용 대체 철근으로 사용이 가능하나 부착성능, 탄성계수, 절곡부의 강선 노출에 대한 처리 방법 등이 개선되면 염해로부터 철근부식 저항성 확보를 요구하는 구조물에 사용 할 수 있는 우수한 소재로 판단된다.

• 마이크로전자및패키징학회지
• /
• 제25권3호
• /
• pp.31-36
• /
• 2018

본 연구에서는 DRAM 소자의 Pressure Cooker Test (PCT) 신뢰성 평가 후 발생한 불량 원인에 대한 연구를 진행하였다. 불량 시료의 물리적 관측 결과 변색, Al의 부식 및 손실, 그리고 금속 간 중간 절연막 박리 등이 관측되었다. 추가 물리적 화학적 분석 결과 비정상적인 물질인 $Al_XO_Y$ 층을 발견하였다. 불량 원인을 파악 하기 위해 package ball 크기 실험 및 보호막 pin hole 등의 연관성 실험을 진행하였으나 원인으로 판명되지 않았다. 또한 EMC 물질에 포함되어 있는 Cl에 의한 Al 할로겐화 평가를 진행하였다. 진행 결과 약간의 개선 효과를 보였지만 완벽한 문제 해결을 이루어 내지 못했다. Galvanic corrosion 가능성 가설을 세웠고, 면밀한 분석 결과 pad open 지역에서 Ti 잔존물을 발견할 수 있었다. 검증 실험으로 repair 식각 분리 실험을 진행하여 개선 효과를 보았다. 개선 된 조건에서 PCT 신뢰성 기준치를 만족 하는 결과를 얻었다. 금번 PCT 불량 메카니즘은 다음과 같이 설명할 수 있다. 공정 repair etch시 Ti 잔류물이 남아 Galvanic 메커니즘에 의해 Al이 이온화 된다. 이온화 된 Al이 후속 PCT 신뢰성 측정 시 $H_2O$와 반응하여 비 정상 물질인 $Al_XO_Y$를 생성하였다.

• 분석과학
• /
• 제5권1호
• /
• pp.97-101
• /
• 1992

순수한 니켈과 티타늄이 같은 양 함유되어 있는 NiTi 금속간 화합물의 인공 생리식염수에서의 부식 특성을 순수한 니켈 및 티타늄과 함께 연구하였다. Tafel 외삽법과 선형 분극법 공히 유사한 결과를 보였으며, 부식 전류 Icorr와 부식 속도는 다음과 같은 순서로 증가하였다. NiTi

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2005년도 후기학술대회논문집
• /
• pp.232-233
• /
• 2005

Stainless steel has been stably used closed by passivity oxidation films($Cr_2O_3$) is made by neutral atmospheric environment. However, passivity oxidation films of the surface of stainless steel occasionally comes to be destroyed in seawater which is influenced by an environment having halogen ion like $Cl^-$, then, localization corrosion comes to occur. Stainless steel 304 for shaft system material of the small-size FRP fishing boat on seawater environments made an experiment on simulation of sacrifical anode(Al, Zn). Through these experiment and study, following results have been obtained ; According to the field inspection and corrosion simulation, the corrosion on the 2nd class stainless steel shaft(STS 304) in FRP fishing boat has been verified to occur by crevice corrosion and galvanic corrosion etc.. According to the comparison and analysis of Stainless steel 304 shaft materials after simulation leaving unprotected and applying cathodic protection, unprotected shaft specimen of stainless steel 304 was severely corroded, but, protected shaft specimen was not totally corroded. This result is assumed to be made by the facts that anodic reaction, $Fe{\rightarrow}Fe^{2+}$ + $2e^-$, has been restricted by the cathodic protection current of sacrificial anode material.