• Journal of Welding and Joining
• /
• v.21 no.2
• /
• pp.97-101
• /
• 2003

The change of microstructures in the base metal during transient liquid phase bonding process of directionally Ni base superalloy, GID-111 was investigated. Bonds were fabricated using a series of holding times(0~7.2ks) at three different temperatures. The flip chip bonding utilizing self-aligning characteristic of solder becomes mandatory to meet tolerances for the optical device. In this paper, a parametric study of aging condition and pad size of samples was evaluated. A TiW/Cu/electroplated Cu UBM structure was selected and the samples were aging treated to analyze the effect of intermetallic compounds with the time variations. An FIB technique was applied to the preparation of samples for TEM observations. An FIB technique is very useful to prepare TEM thin foil specimens from the solder joint interface. After aging treatment, the tendency to decrease in shear strength was measured and the structure of the solder and the UBM was observed by using SEM, TEM and EDS. As a result, the shear strength was decreased of about 21% in the 100${\mu}{\textrm}{m}$ sample at 17$0^{\circ}C$ aging compared with the maximum shear strength of the sample with the same pad size. In the case of the 12$0^{\circ}C$ aging treatment, 18% of decrease in shear strength was measured at the 100${\mu}{\textrm}{m}$ pad size sample. An intermetallic compound of Cu6Sn5 and Cu3Sn were also observed through the TEM measurement by using.

• Journal of Welding and Joining
• /
• v.23 no.6
• /
• pp.99-105
• /
• 2005

The mixing ratio effect of the GTD-111(base metal) powder and the GNI-3 (Ni-l4Cr-9.5Co-3.5Al-2.5B) powder on TLP(Transient Liquid Phase) bonding phenomena and mechanism was investigated. At the mixing ratio of the base metal powder under $50wt\%$, the base metal powders fully melted at the initial time and a large amount of the base metal near the bonded interlayer was dissolved by liquid inter metal. Liquid insert metal was eliminated by isothermal solidification which was controlled by the diffusion of B into the base metal. The solid phases in the bonded interlayer grew epitaxially from the base metal near the bonded interlayer inward the insert metal during the isothermal solidification. The number of grain boundaries farmed at the bonded interlayer corresponded with those of base metal. At the mixing ratio above $60wt\%$, the base metal powder melted only at the surface of the powder and the amount of the base metal dissolution was also less at the initial time. Nuclear of solids firmed not only from the base metal near the bonded interlayer but also from the remained base metal powder in the bonded interlayer. Finally, the polycrystal in the bonded interlayer was formed when the isothermal solidification finished. When the isothermal solidification was finished, the contents of the elements in the boned interlayer were approximately equal to those of the base metal. Cr-W borides and Cr-W-Ta-Ti borides formed in the base metal near the bonded interlayer. And these borides decreased with the increasing of holding time.

• Journal of Magnetics
• /
• v.9 no.2
• /
• pp.52-59
• /
• 2004

As deposited and annealed MTJs with the structure of $Ta(5 nm)/Cu(10 nm)/Ta(5 nm)/Ni_{80}Fe_{20}(2 nm)/Cu(5 nm)/ Ir_{25}Mn_{75}(10 nm)/Co_{70}Fe_{30}(2.5 nm)/Al-O/Co_{70}Fe_{30}(2.5nm)/Ni_{80}Fe_{20}(t)/Ta(5nm)/Ni_{80}Fe_{20}(t)/Ta(5 nm)$, where t=10, 30, 60 and 100 nm were characterized by XRD and magnetic hysteresis loops measurements. The XRD measurements were done in grazing incidence $(GID scan-2{\theta})$ and ${\theta}-2{\theta}$ geometry, by rocking curve $(scan-{\omega})$ and pole figures in order to establish correlation between texture and crystallites size and magnetic parameters of exchange biased and interlayer coupling. The variations of shifting and coercivity field of free and pinned layers after annealing in $300^{\circ}C$ correlate with the improvement of ［111］ texture and grains size of $Ni_{80}Fe_{20}$ and $Ir_{25}Mn_{75}$ respectively. The exchange biased and the coercivity fields of the pinned layer linearly increased with increasing grain size of $Ir_{25}Mn_{75}$, The reciprocal proportionality between interlayer coupling and coercivity fields of the free layer and grain size of $Ni_{80}Fe_{20}$ was found. The enhancement of interlayer coupling between pinned and free layers, after annealing treatment, indicates on the correlated in-phase roughness of dipolar interacting interfaces due to increase of crystallites size of $Ni_{80}Fe_{20}$.