• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.449-452
• /
• 2004

The lap splice lengths of deformed steel reinforcing bars and GFRP bars with two different to surface type were experimentally compared using beam specimens. The purpose was to evaluate the length required of the GFRP bar to develop strength equivalent to the conventional steel reinforcing bar. The main test variable was the lap splice length. Two different GFRP bar surfaces were tested: (1) spiral-type GFRP bars and (2) sand coated GFRP bars. For the conventional steel bars (SD400 grade), strength over 400 MPa in tension was reached using the lap splice length of $30d_b$. Splice failure was observed in the specimen with the lap splice length of $20d_b$. For the spiral-type and sand coated GFRP bars, the tensile strength developed in the GFRP bars decreased with decreasing splice lengths. Development of the cracks on beam surfaces was clearly visible for the beams reinforced with the GFRP bars. Mid-span deflections, however, were significantly smaller than the comparable beams with conventional steel bars indicating potential ductility problem.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.172-175
• /
• 2004

This study is to investigate the tensile properties of glass fiber reinforced polymer(GFRP) reinforcing bars with various kinds of anchor systems experimentally. Three types of anchor systems were examined: resin sleeve anchor adopted by CSA Standard, metal overlay anchor by ASTM Standards and wedge anchor normally used in prestressing tendons. Also, three different types of GFRP bars with different surface deformations were tested in this study. All test procedures including specimens preparation, test apparatus and measuring devices were made according to the recommendations of CSA Standard S806-02. From the test results, it was found that the highest tensile strength of GFRP bar was developed by resin sleeve anchor, and tensile strength of GFRP bar with CSA anchor system is $10\%$ higher than that with ASTM anchor system in the case of sand-coated GFRP bar.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.120-123
• /
• 2004

The lap splice lengths of deformed steel reinforcing bars and GFRP bars were experimentally compared using beam specimens. The purpose was to evaluate the length required of the GFRP bar to develop strength at least equivalent to the conventional steel reinforcing bar. The main test variable was the lap splice length: 10, 20, 30 $d_b$ for the deformed steel bars and 20, 30, 40 $d_b$ for the GFRP bars. Two different types of GFRP bars were tested: (1) one with spiral-type deformation and (2) plain round bars. Elastic modulus was about 1/5 of the steel bars while the tensile strength was about 690 MPa for the GFRP bars. Nominal diameter of the GFRP bars and steel bars was 12.7 and 13 mm, respectively. Normal strength concrete (28-day $f_{cu}$ = 30 MPa) was used. For the conventional steel bars (SD400 grade), strength over 400 MPa in tension was developed using the lap splice length of 20 and 30 $f_{cu}$. Only $87\%$ of the nominal yield strength was reached with the lap splice length of 10 $d_b$. For the spiral-type deformed GFRP bars with $40-d_b$ lap splice length, 440 MPa in tension was determined. The maximum tensile strength developed of the GFRP bars with smaller lap splice lengths decreased. The plain GFRP bar was not effective in developing the tensile strength even with $40-d_b$ lap splice length. Development of the cracks on beam surface was clearly visible for the beams reinforced with the GFRP bars. Mid-span deflections, however, were significantly smaller than the comparable beams with conventional steel bars indicating potential ductility problem.

• 대한토목학회논문집
• /
• 제35권1호
• /
• pp.77-84
• /
• 2015

고온에 노출된 GFRP 보강근의 인장실험을 수행하였다. 본 실험을 위한 고온노출조건은 $200^{\circ}C$ 이하의 온도에 3분간 노출하는 것으로 하였다. 이러한 조건은 다른 연구자들의 시험에서 적용한 고온노출조건과 비교하여 경미한 고온노출조건이다. 고온에서와 고온노출 후 GFRP 보강근의 인장강도와 탄성계수를 비교하였다. 실험결과, 고온에서 GFRP 보강근의 인장성능이 감소하는 것으로 나타났으나, 고온노출 후 보강근의 인장성능은 거의 고온노출전의 수준으로 회복되는 것으로 나타났다. 이와 같은 결과는 화재로 손상 받은 GFRP 보강 콘크리트 구조물의 평가를 위하여 중요한 자료가 된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.124-127
• /
• 2004

This study is to investigate the bond characteristics of glass fiber reinforced polymer(GFRP) reinforcing bars in concrete by pullout test experimentally. Three different types of GFRP bars with different surface deformations were considered in this study. Also, standard deformed steel reinforcing bar with or without epoxy-coating were included for the comparisons of bond strength. All test procedures including specimens preparation, test apparatus and measuring devices were made according to the recommendation of CSA(Canadian Standards Association) Standard S806-02. From the test results, it was found that small surface indentations contributed to increase the bond strength of GFRP bar significantly. Based on the limited test results till now, the bond strength of GFRP bar with sand-coated deformation commercially available in foreign market is around $80\%$ of that of steel deformed bars.

• 콘크리트학회논문집
• /
• 제25권2호
• /
• pp.187-194
• /
• 2013

섬유복합체(FRP)는 비부식성 재료라는 특징으로 인해 이상적인 철근 대체재로 주목 받고 있다. 그러나 현재 FRP 보강근은 철근과 달리 일반적으로 수용되는 고정된 형태가 존재하지 않고 다양한 재료와 성분비, 형태 등으로 제작되기 때문에 이에 대한 성능평가 데이터에 근거한 FRP 보강 콘크리트 부재의 거동특성 구명은 상당부분 제한될 수 있다. 더군다나 FRP 보강 콘크리트 부재의 휨거동에 대한 평가는 주로 단기 거동 측면에 집중되어 이루어져 왔다. 이 연구는 GFRP 보강근 및 이를 사용하여 보강된 콘크리트 부재의 장기거동을 평가하기 위한 것으로, 먼저 철근 대체용으로 개발된 GFRP 보강근에 대한 성능평가 결과를 제시하였고, 이의 크리프 거동 특성에 대한 3년간의 계측 결과를 제시하였다. 실험 결과 인장강도의 약 55% 이하의 하중이 지속적으로 재하되는 경우에는 100년 이상의 내구연한을 확보할 수 있는 것으로 나타났다. 또한 GFRP 보강 콘크리트 보의 장기거동을 약 1년간 관찰하였으며 이로부터 FRP 보강 부재의 장기처짐 계산식에 사용되는 수정계수 값 0.73을 도출하였다. 따라서 이 연구로부터 도출된 GFRP 보강근 및 이로 보강된 콘크리트 보의 단기 및 장기 거동 특성값은 FRP 보강 콘크리트 부재의 설계에 유용하게 활용될 수 있을 것으로 사료된다.

• 콘크리트학회논문집
• /
• 제25권2호
• /
• pp.137-144
• /
• 2013

철근콘크리트(reinforced concrete) 구조부재에서 철근의 부식으로 인한 문제점을 개선하고자 섬유보강 복합재료(FRP) 보강근(rebar)을 사용하는 것에 대한 연구가 꾸준히 진행되어져 오고 있다. 하지만 이러한 FRP 보강근을 사용한 콘크리트 부재의 환경에 대한 장기거동에 대한 연구가 아직도 미흡한 수준이다. 이 연구는 GFRP(glass fiber reinforced polymer) 보강근을 사용한 콘크리트 부재를 온도 약 $46^{\circ}C$와 습도가 80%인 인위적인 실험실에서 최대 300일까지 노출시킨 후의 장기 거동에 대한 실험적 연구를 제시하였다. 비교를 위하여 두가지 서로 다른 GFRP 보강근과 철근을 보강한 콘크리트 보 시험체를 제작하였다. 실험 결과, 장기 노출환경에서도 GFRP 보강근을 보강한 콘크리트 보 시험체의 파괴형태는 철근 보강 콘크리트 보시험체와 매우 유사한 파괴형태를 나타내었으며, 노출 시간에 따른 하중저항 감소값은 철근이 보강된 경우가 GFRP 보강근이 보강된 경우보다 하중저항 감소값이 크게 일어났다. 또한 GFRP 보강근 보강 콘크리트 보 시험체를 설계할 시에는 철근 보강보다 취성파괴에 대한 충분한 대비가 요구됨을 알 수 있었다. 그리고 압축파괴에 대한 변형도 계수(deformability factor)는 모든 경우에서 노출시간에 관계없이 큰 변화가 없음을 알 수 있었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.237-240
• /
• 2006

The corrosion of steel reinforcing bar has been the major cause of the reinforced concrete deterioration. GFRP(Glass Fiber-Reinforced Polymer) reinforcing bar has emerged as one of the most promising and affordable solutions to the corrosion problems of steel reinforcement in structural concrete. However, GFRP rebar is prone to deteriorate due to other degradation mechanisms than those for steel. The high alkalinity of concrete, for instance, is a possible degradation source. This paper presents the long-term deterioration of the GFRP rebar under alkali environmental condition.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2011년도 정기총회 및 추계학술대회 논문집
• /
• pp.2435-2438
• /
• 2011

Steel bar is used for as a reinforcing material in a concrete slab track. Bacuase the steel re-bar could provide passes for current transition, all the cross points of steel re-bars should be insulated by using plastic materials. This is due to the loss of signal intensity of track-circuit. In this study, GFRP bars are adopted in place of the traditional steel reinforcing bars for a concrete slab track to minimize the loss of the signal intensity. In order to evaluate the replacing effect on eletrical characteristic of slab track, measurements of surface resistivity are conducted on steel and GFRP reinforced precast slab tracks. In the results, the GFRP reinforced slab strack shows the higher resistivity than the steel reinforced slab track.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2003년도 학술발표논문집
• /
• pp.371-374
• /
• 2003

The corrosion of steel reinforcing bar(re-bar) has been the major cause of the reinforced concrete deterioration. FRP(Fiber-reinforced polymer) reinforcing bar has emerged as one of the most promising and affordable solutions to the corrosion problems of steel reinforcement in structural concrete. In this study, long-term durability performance of FRP re-bar were evaluated. The mechanical and durability properties of two type of CFRP- and GFRP re-bar were investigated; the FRP re-bars were subjected to alkaline solution, acid solution, salt solution and deionized water. The mechanical and durability properties were investigated by performing tensile and short beam tests. Experimental results confirmed the desirable resistance of FRP re-bar to aggressive chemical environment.