• Journal of the Korean Chemical Society
• /
• v.63 no.6
• /
• pp.453-458
• /
• 2019

Synthesis of ZnCo₂O₃ oxide is performed by sol-gel method via nitrate-citrate route. Powder X-ray diffraction (XRD) study shows monoclinic unit cell having lattice parameters: a = 5.721(1) Å, b = 8.073(2) Å, c = 5.670(1) Å, β = 93.221(8)°, space group P_2/m and Z = 4. Average crystallite sizes determined by Scherrer equation are the range ~14-32 nm, whereas SEM micrographs show nano-micro meter size particles formed in ZnCo₂O₃. Endothermic peak at ~798 K in the Differential scanning calorimetric (DSC) trace without weight loss could be due to structural transformation and the endothermic peak ~1143 K with weight loss is due to reversible loss of O₂ in air atmosphere. Energy Dispersive X-ray (EDX) analysis profile shows the presence of elements Zn, Co and O which indicates the purity of the sample. Magnetic measurements in the range of +12 kOe to -12 kOe at 10 K, 77 K, 120 K and at 300 K by PPMS-II Physical Property Measurement System (PPMS) shows hysteresis loops having very low values of the coercivity and retentivity which indicates the weakly ferromagnetic nature of the oxide. Observed X-band EPR isotropic lineshapes at 300 K and 77 K show positive g-shift at g_iso ~2.230 and g_iso ~2.217, respectively which is in agreement with the presence of paramagnetic site Co²⁺(3d⁷) in the oxide. DC conductivity value of 2.875 ×10^-8 S/cm indicates very weakly semiconducting nature of ZnCo₂O₃ at 300 K. DRS absorption bands ~357 nm, ~572 nm, ~619 nm and ~654 nm are due to the d-d transitions ⁴T_1g(⁴F)→²E_g(²G), ⁴T_1g(⁴F)→⁴T_1g(⁴P), ⁴T_1g(⁴F)→⁴A_2g(⁴F), ⁴T_1g(⁴F)→⁴T_2g(⁴F), respectively in octahedral ligand field around Co²⁺ ions. Direct band gap energy, E_g~ 1.5 eV in the oxide is obtained by extrapolating the linear part of the Tauc plot to the energy axis indicates fairly strong semiconducting nature of ZnCo₂O₃.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.220-224
• /
• 2000

Ultra-fine $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$ferrite powders have been prepared by the sol-gel method. The crystallographic and magnetic properties of the sample have been investigated by means of x-ray diffraction, Mossbauer spetroscopy and vibrating sample magnetometry. The formation of nano crystallized particles is confirmed. The x-ray diffractions of all samples with various compositions clearly indicate the presence of spinel structure. The Mossbauer spectra could be fitted as the superposition of two sextets due to F $e^{3+}$ A-site and B-site. The IS and QS values nearly constant with substituted Co-Ti contents, whereas $H_{hf}$ of B-site decreases with increasing Co-Ti substitution in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$. The magnetic behaviour of powders shows that the saturation magnetization and the coercivity decrease with increasing x in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$.$.X>.

• The Korean Journal of Mycology
• /
• v.10 no.2
• /
• pp.67-73
• /
• 1982

The $(NH_4)_2\;SO_4$ (70%) treated crude enzymes from the culture filtrates of the$C-7^{+t}$ strain of Pyricularia oryzae which was grown on 2% CMC (carboxymethyl cellulose) for 8 days at $28^{\circ}C$ were chromatographied on Sephadex G-150 and DEAE-Sephadex A-25 columns. From the chromatography, three fractions of CMCase$(C_x)$ was examined using Na-CMC as substrate. The $C_x$ enzyme activity was optimal at pH 6.0 and $40^{\circ}C$, stable up to $40^{\circ}C$. The values of Km and Vmax of the enzyme were $2.8{\times}10\;mM$ and 5.9m moles/hour, respectively. The molecular weight determined by Sephadex G-150 column chromatography was around 80,000. Approximately sevenfold purified $C_x$ enzyme gave a single protein band on the polyacrylamide gel electrophoresis.

• BMB Reports
• /
• v.34 no.4
• /
• pp.371-378
• /
• 2001

The Glycoprotein D (gD) gene of the HSV-1 strain F was cloned, sequenced, recombinated into the HcNPV (Hyphantria cunea nuclear polyhedrosis virus) expression vector and expressed in insect cells. The gD gene was located in the 6.43 kb BamHI fragment of the strainF. The open reading frame (ORF) of the gD gene was 1,185 by and codes 394 amino acid residues. Recombinant baculoviruses, GD-HcNPVs, expressing the gD protein were constructed. Spodoptera frugiperda cells, infected with the recombinant virus, synthesized a matured gX-gD fusion protein with an approximate molecular weight of 54 kDa and secreted the gD proteins into the culture media by an immunoprecipitation assay The fusion gD protein was localized on the membrane of the insect cells, seen by using an immunofluorescence assay The deduced amino acid sequence presents additional characteristics compatible with the structure of a viral glycoprotein: signal peptide, putative glycosylation sites and a long C-terminal transmembrane sequence. These results indicate the utility of the HcNPV-insect cell system for producing and characterizing eukaryotic proteins.

• Journal of the Chungcheong Mathematical Society
• /
• v.16 no.1
• /
• pp.1-6
• /
• 2003

By considering a hyperspace CL(X) of a Hausdorffspace X with the Vietoris topology [6] also called the finite topology and treating X as a subspace of CL(X) with the natural embedding, it is obtained that homotopic maps f, g : $X{\rightarrow}Y$ are lifted to homotopic maps on the respective hyperspaces.

• Journal of the Korean Mathematical Society
• /
• v.56 no.6
• /
• pp.1689-1701
• /
• 2019

Let ${\star}$ be a semistar operation on the integral domain D. In this paper, we prove that D is a $G-{\tilde{\star}}-GCD$ domain if and only if D[X] is a $G-{\star}_1-GCD$ domain if and only if the Nagata ring of D with respect to the semistar operation ${\tilde{\star}}$, $Na(D,{\star}_f)$ is a G-GCD domain if and only if $Na(D,{\star}_f)$ is a GCD domain, where ${\star}_1$ is the semistar operation on D[X] introduced by G. Picozza [12].

• Journal of the Korean Chemical Society
• /
• v.16 no.6
• /
• pp.373-377
• /
• 1972

The analytical conditions for the fluorescence X-ray determination of small amount of cupper in solution were established. Copper in solution was extracted by diethyldithiocarbamate ethyl acetate and adsorbed by zinc powder. After drying, it was pressed to tablet under the pressure of $250Kg/cm^2.$$K_{\alpha}2(2{\theta}_{LiF} = 45.08^{\circ})$. The limit of detection was estimated to be about $10{\mu}g$ by the method of standard addition with an error of 10 %.

• Plant Resources
• /
• v.5 no.1
• /
• pp.1-6
• /
• 2002

Genetic improvement of the cultivated soybean [Glycine max (L.) Merr] may be possible through hybridization with its wild progenitor, G. soja Sieb. & Zucc. Interspecific cross between G. max (Hwangkeumkong) and G. soja (IT.182932) was made in the summer of 1997. In F$_2$ the percentage of plant height, nodes per plant, and pods per plant were high but gradually reduced from F$_2$ to F$_4$. In contrast pod length, seeds per pod, and 100-seeds weight were increased gradually through generations advanced. Wild variation as evident in F$_2$ in plant height, number of branches, pods per plant, and 100-seeds weight. Twenty six percent of the F$_2$, 44 % of the F$_3$ and 60% of the F$_4$ segregants showed more G. max traits. The combination of useful traits from both species is possible through interspecific hybridization. The characters that could be transferred from wild species to cultivated species are more pod number, better capacity, and resistance to disease and insects. The interspecific derivatives offer scope for selection for high grain yield. Therefore, introducing genes from G. soja to G. max could be contribute to greater genetic diversity of future cultivars. And semicultivated soybean had some desired characteristics including tolerance to adverse environments and multi-seed characters. It means the infusing of semicultivated germplasm to the cultivated soybean could increase number of seeds and pods per plant significantly, and consequently could enhance selecting potential on yield.

• Asian-Australasian Journal of Animal Sciences
• /
• v.21 no.1
• /
• pp.107-119
• /
• 2008

To determine the true digestible phosphorus (TDP) requirement of growing pigs, two experiments were designed with the experimental diets containing five true digestible P levels (0.16%, 0.20%, 0.23%, 0.26% and 0.39%) and the ratio of total calcium to true digestible P (TDP) kept at 2:1. In Experiment 1, five barrows (Duroc${\times}$Landrace${\times}$Yorkshire) with an average initial body weight of 27.9 kg were used in a $5{\times}5$ Latin-square design to evaluate the effect of different dietary P levels on the digestibility and output of P and nitrogen. In Experiment 2, sixty healthy growing pigs (Duroc${\times}$Landrace${\times}$Yorkshire) with an average body weight (BW) of 21.4 kg were assigned randomly to one of the five dietary treatments (12 pigs/diet), and were used to determine the true digestible phosphorus (TDP) requirement of growing pigs on the basis of growth performance and serum biochemical indices. The results indicated that the true digestibility of P increased (p<0.05) linearly with increasing dietary TDP level below 0.26%. The true P digestibility was highest (56.6%) when dietary TDP was 0.34%. Expressed as g/kg dry matter intake (DMI), fecal P output increased (p<0.05) linearly with increasing P input. On the basis of g/kg fecal dry matter (DM), fecal P output was lowest for Diet 4 and highest (p<0.05) for Diet 5. The apparent digestibility of crude protein (CP) did not differ (p>0.05) among the five diets, with the average nitrogen output of 12.14 g/d and nitrogen retention of 66% to 74% (p>0.05), which suggested that there was no interaction between dietary P and CP protein levels. During the 28-d experimental period of Experiment 2, the average daily gain (ADG) of pigs was affected by dietary TDP levels as described by Eq. (1): $y=-809,532x^4+788,079x^3-276,250x^2+42,114x-1,759$; ($R^2=0.99$; p<0.01; y = ADG, g/d; x = dietary TDP, %), F/G for pigs by Eq. (2): $y=3,651.1x^4-3,480.4x^3+1,183.8x^2-172.5x+10.9$ ($R^2=0.99$; p<0.01; y = F/G; x = dietary TDP, %), and Total P concentrations in serum by Eq. (3): $y=-3,311.7x^4+3,342.7x^3-1,224.6x^2+195.6x-8.7$ (R2 = 0.99; p<0.01; y = total serum P concentration and x = dietary TDP, %). The highest ADG (782 g/d), the lowest F/G (1.07) and the highest total serum P concentration (3.1 mmol/L) were obtained when dietary TDP level was 0.34%. Collectively, these results indicate that the optimal TDP requirement of growing pigs is 0.34% of the diet at a total Ca to TDP ratio of 2:1.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.5
• /
• pp.269-280
• /
• 2021

PURPOSE. The objective of this study was to evaluate the effect of thickness reduction and fatigue on the failure load of monolithic zirconia crowns. MATERIALS AND METHODS. 140 CAD-CAM fabricated crowns (3Y-TZP, inCorisTZI, Dentsply-Sirona) with different ceramic thicknesses (2.0, 1.5, 1.0, 0.8, 0.5 mm, respectively, named G2, G1.5, G1, G0.8, and G0.5) were investigated. Dies of a mandibular first molar were made of composite resin. The zirconia crowns were luted with a resin composite cement (RelyX Unicem 2 Automix, 3M ESPE). Half of the specimens (n = 14 per group) were mouth-motion-fatigued (1.2 million cycles, 1.6 Hz, 200 N/ 5 - 55℃, groups named G2-F, G1.5-F, G1-F, G0.8-F, and G0.5-F). Single-load to failure was performed using a universal testing-machine. Fracture modes were analyzed. Data were statistically analyzed using a Weibull 2-parameter distribution (90% CI) to determine the characteristic strength and Weibull modulus differences among the groups. RESULTS. Three crowns (21%) of G0.8 and five crowns (36%) of G0.5 showed cracks after fatigue. Characteristic strength was the highest for G2, followed by G1.5. Intermediate values were observed for G1 and G1-F, followed by significantly lower values for G0.8, G0.8-F, and G0.5, and the lowest for G0.5-F. Weibull modulus was the lowest for G0.8, intermediate for G0.8-F and G0.5, and significantly higher for the remaining groups. Fatigue only affected G0.5-F. CONCLUSION. Reduced crown thickness lead to reduced characteristic strength, even under failure loads that exceed physiological chewing forces. Fatigue significantly reduced the failure load of 0.5 mm monolithic 3Y-TZP crowns.