• Nuclear Engineering and Technology
• /
• v.44 no.8
• /
• pp.953-960
• /
• 2012

This paper reports the irradiation effect on the deformation behavior and tensile fracture properties of A533B RPV steel. An inverse identification technique using iterative finite element (FE) simulation was used to determine those properties from tensile data for the A533B RPV steel irradiated at 65 to $100^{\circ}C$ and deformed at room temperature. FE simulation revealed that the plastic instability at yield followed by softening for higher doses was related to the occurrence of localized necking immediately after yielding. The strain-hardening rate in the equivalent true stress-true strain relationship was still positive during the necking deformation. The tensile fracture stress was less dependent on the irradiation dose, whereas the tensile fracture strain and fracture energy decreased with increasing dose level up to 0.1 dpa and then became saturated. However, the tensile fracture strain and fracture energy still remained high after high-dose irradiation, which is associated with a large amount of ductility during the necking deformation for irradiated A533B RPV steel.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.2
• /
• pp.134-144
• /
• 2011

In this paper, the global study trends for material behaviors are investigated regarding the static and dynamic hardenings and final fractures of marine structural steels. In particular, after reviewing all of the papers published at the 4th and 5th ICCGS (International Conference on Collision and Grounding of Ship), the used hardening and fracture properties are summarized, explicitly presenting the material properties. Although some studies have attempted to employ new plasticity and fracture models, it is obvious that most still employed an ideal hardening rule such as perfect plastic or linear hardening and a simple shear fracture criterion with an assumed value of failure strain. HSE (2001) presented pioneering study results regarding the temperature dependency of material strain hardening at various levels of temperature, but did not show strain rate hardening at intermediate or high strain rate ranges. Nemat-Nasser and Guo (2003) carried out fully coupled tests for DH-36 steel: strain hardening, strain rate hardening, and temperature hardening and softening at multiple steps of strain rates and temperatures. The main goal of this paper is to provide the theoretical background for strain and strain rate hardening. In addition, it presents the procedure and methodology needed to derive the material constants for the static hardening constitutive equations of Ludwik, Hollomon, Swift, and Ramberg-Osgood and for the dynamic hardening constitutive equations of power from Cowper-Symonds and Johnson-Cook.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.11a
• /
• pp.59-62
• /
• 2003

Kinds, shapes and fraction ratios of fibers have influence on properties of HPFRCC(High-Performance Fiver Reinforced Cementitious Concrete) like bending strength, strain capacity and fracture toughness. For example, hydrophilic fibers have different chemical bond strength from hydrophobic fibers, fiber shapes influence on fiber pull-out and rupture, and fiber volume fraction influence on bending strength. In this study, to estimate influences of kinds, shapes and fraction ratios of fibers, we make HFRCC with 3 kind of fiber in various volume fraction of fiber and compare cracking, bending strength and fracture toughness. As the results, bending strength of HPFRCC was increased as fiber volume fraction was increase and fiber tensile strength was increase, and strain capacity and fracture toughness of HFRCC was higher in fiber pull-out fracture than in fiber rupture fracture. And HFRCC showing pseudo strain hardening has higher fiber reinforce efficiency than others.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 1998.05a
• /
• pp.89-97
• /
• 1998

In this study, under large scale yielding conditions crack propagation is found to governed by parameters based on the J-integral or on the crack opening displacement. But initiation of crack propagation of ductile material seems to be controlled by just on parameter that is the strain. The relationship between the critical value of J-integral and the local fracture strain in uniaxial tensile test in the region of maximum reduction in area. Therefore, the fundamental theorectical equation by the proposed elastic-plastic fracture toughness and the local fracture strain has a merit. in comparison with the ASTM method, which can measure by using the load-displacement curve and the specimens in tenslie test.

• Journal of the Korean Society of Safety
• /
• v.13 no.4
• /
• pp.25-33
• /
• 1998

In this study, under large scale yielding conditions crack propagation is found to governed by parameters based on the J-integral or on the crack opening displacement. But initiation of crack propagation of ductile material seems to be controlled by just on parameter that is the strain. The relationship between the critical value of J-integral and the local fracture strain in uniaxial tensile test in the region of maximum reduction in area. Therefore, the fundamental theoretical equation by the proposed elastic-plastic fracture toughness and the local fracture strain has a merit, in comparison with the ASTM method, which can measure by using the load-displacement curve and the specimens in tensile test.

• Corrosion Science and Technology
• /
• v.10 no.4
• /
• pp.131-135
• /
• 2011

The demands of high-strength steel have been steadily increased to reduce the weight of vehicles. Although the TRIP steel has been the promising candidate material for the purpose, high strength hinders the application due to the susceptibility to hydrogen delayed fracture in the corrosive environment. Moreover, the testing method was not specified in the ISO standards. In this work, the test method to evaluate the susceptibility of hydrogen delayed fracture was studied by slow strain rate testing technique. The four test experimental parameters were studied : strain rate, hydrogen charging time, holding time after hydrogen charging, and holding time after cadmium plating. The steel was fractured by hydrogen in case the strain rate was in the range of $1{\times}10^{-4}{\sim}5{\times}10^{-7}/sec$. It was confirmed that the slow strain rate test is effective method to evaluate the susceptibility to hydrogen delayed fracture. The holding time over 24 hrs after hydrogen charging, nullified the hydrogen effect, that is, the specimen was no more susceptible to hydrogen after 24 hrs even though the specimen was fully hydrogen-charged. Moreover, cadmium electroplating could not prevent from diffusing out the hydrogen from the steel in the experiment. The effective experimental procedures were discussed.

• Transactions of Materials Processing
• /
• v.25 no.2
• /
• pp.91-95
• /
• 2016

This paper is concerned with modeling of a ductile fracture criterion for sheet metal considering anisotropy to predict the sudden fracture of advanced high strength steel (AHSS) sheets during complicated forming processes. The Lou−Huh ductile fracture criterion is modified using the Hill’s 48 anisotropic plastic potential instead of the von Mises isotropic plastic potential to take account of the influence of anisotropy on the equivalent plastic strain at the onset of fracture. To determine the coefficients of the model proposed, a two dimensional digital image correlation (2D-DIC) method is utilized to measure the strain histories on the surface of three different types of specimens during deformation. For the derivation of an anisotropic ductile fracture model, principal stresses (𝜎₁,𝜎₂, 𝜎₃) are expressed in terms of the stress triaxiality, the Lode parameter, and the equivalent stress (𝜂_𝐻, 𝐿,) based on the Hill’s 48 anisotropic plastic potential. The proposed anisotropic ductile fracture criterion was quantitatively evaluated according to various directions of the maximum principal stress. Fracture forming limit diagrams were also constructed to evaluate the forming limit in sheet metal forming of AHSS sheets over a wide range of loading conditions.

• Restorative Dentistry and Endodontics
• /
• v.15 no.1
• /
• pp.20-32
• /
• 1990

The plane strain fracture toughness of a material characterize the resistance to fracture in the presence of a sharp crack under severe tensile condition. Fracture toughness can be determined by indentation method. The purpose of this study was to investigate the fracture toughness of dental amalgams by measuring the plane strain fracture toughness and the fracture toughness from indentation method. Two conventional and four high copper amalgam alloys were employed for this study. The amalgams were prepared according to the A.D.A. spec. No. 1 and inserted into the specially designed mould with the single edge notch specimen to use in 3-point bending method. The specimens (20mm long, 4mm wide, 2mm thick) were stored at $37^{\circ}C$ for 1 week, and tested in 3-point bending by means of Instron at a cross-head speed of 1mm/min. In indentation method, the specimens were made in same manner as single edge notch specimens. The test was conducted with Vickers hardness tester at 10kg load. The following results were obtained. 1. The plane strain fracture toughness and the fracture toughness from indentation method were higher in the low copper amalgams than the high copper amalgams. 2. In high copper amalgams, the fracture toughness of amalgams decreases according as the copper contents increase. 3. In similar copper contents, the single composition amalgams have a higher fracture toughness than the admixed amalgams.

• Coupled systems mechanics
• /
• v.4 no.3
• /
• pp.211-235
• /
• 2015

In this work we present a one-dimensional damage model capable of representing the dynamic fracture for elastodamage bar with combined hardening in fracture process zone - FPZ and softening with embedded strong discontinuities. This model is compared with another one we recently introduced (Do et al. 2015) and it shows a good agreement between two models. Namely, it is indicated that strain-softening leads to a sensitivity of results on the mesh discretization. Strain tends to localization in a single element which is the smallest possible area in the finite element simulations. The strain-softening element in the middle of the bar undergoes intense deformation. Strain increases with increasing mesh refinement. Strain in elements outside the strain-softening element gradually decreases to zero.

• Computers and Concrete
• /
• v.7 no.4
• /
• pp.387-402
• /
• 2010

From typical stress-axial strain curve and stress-volume strain curve of a concrete under uniaxial compression, the initiation and localization of microcracks within the interior of the specimen can be identified. The occurrence of random microcrack indicates the end of the linear elasticity, and the localization of microcrack implies formation of major crack, which triggers the onset of unstable crack propagation. The interval between initiation and localization of microcracks is characterized by a stable microcrack growth. Based on fracture behavior observed from a uniaxial compressive test of a concrete cylinder, a model has been developed to extract fundamental fracture properties of a concrete, i.e. the equivalent fracture toughness and the size of fracture process zone. The introduction of cracking Poisson's ratio accounts for tensile failure characteristics of concrete even under uniaxal compression. To justify the validity of the model proposed, tests on three-point bending have been performed to obtain the fracture toughness in accordance with two parameter fracture model and double-K fracture model. Surprisingly, it yields favorably comparable results and provides an encouraging alternative approach to determine fracture properties for concretes.