• 마이크로전자및패키징학회지
• /
• 제20권4호
• /
• pp.35-39
• /
• 2013

반도체센서의 응력에 따른 전기적 특성을 프로브 스테이션 위에서 측정하기 위해 소형 4점 굽힘 장치를 개발하였다. 4점 굽힘 장치는 $60{\times}83mm^2$의 면적을 갖는 소형 장치로 마이크로미터를 통해 정확한 변위를 인가함으로서 가해진 응력을 구할 수 있다. 유한요소해석법을 사용하여 기기의 오차를 예측하고 정밀도를 향상하였다. 실험적으로는 4점 굽힘 장치로 인가된 응력을 검증하기 위해 스트레인 게이지로 검증하였다.

• 한국재료학회지
• /
• 제12권6호
• /
• pp.508-512
• /
• 2002

$2000{\AA}-SiO_2/Si(100)$ and $560{\AA}-Si_3N_4/Si(100)$ wafers, which are 10 cm in diameter, were directly bonded using a rapid thermal annealing method. We fixed the anneal time of 30 second and varied the anneal temperatures from 600 to $1200^{\circ}C$. The bond strength of bonded wafer pairs at given anneal temperature were evaluated by a razor blade crack opening method and a four-point bonding method, respectively. The results clearly slow that the four-point bending method is more suitable for evaluating the small bond strength of 80~430 mJ/$\m^2$ compared to the razor blade crack opening method, which shows no anneal temperature dependence in small bond strength.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1994년도 춘계학술대회 논문집
• /
• pp.167-174
• /
• 1994

The creep behavior and creep fracture of alumina at high temperature were investigated under four point flexural test. The steady-state creep behavior was observed at low bending stress and the primary creep until fracture was observed at high bending stress. The loading history of bending stress did not affect on the steady-stated creep rate. Intergranular fracture was dominant for fracture of alumina at room and high temperature. However, transgranular fracture was dominant on creep fracture of alumina under high temperature by nuclueation and growth of microcracks due to residual flaws or cavities in the material.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.123-126
• /
• 2002

To evaluate the bending collapse behavior of an aluminum square tube, a finite element simulation for the four-point bending test was suggested. Local buckling deformation near the center of an aluminum tube specimen was induced which has been partly inserted by two steel bars. Simulation results showed good agreements with those of experiment.

• 한국세라믹학회지
• /
• 제31권5호
• /
• pp.543-551
• /
• 1994

The creep behavior and creep fracture of sintered alumina at high temperature were investigated under four point flexural test. Steady-state creep behavior was observed at low bending stress and primary creep until fracture was observed at hish bending stress. The loading history of bending stress did not affect on steady-state creep rate. Intergranular fracture was dominant for fracture of alumina at room and high temperature. However, transgranular fracture was dominant on creep of alumina under high temperature by nucleation and growth of microcracks due to residual flaws or cavities in the material.

• 한국세라믹학회지
• /
• 제34권10호
• /
• pp.1053-1059
• /
• 1997

The dynamic fatigue behavior of alumina ceramics was observed at room temperature using four point bending system. The dynamic fatigue fracture strength and the dynamic fatigue lifetime were observed as a function of crosshead speed and the notch length. The notched specimen showed the smaller deviation in dynamic fatigue fracture strength than the unnotched specimen. The crack growth exponent n and the material constant A of the notched specimen could be represented as functions of the notch length. Fracture strength of the specimen calculated from the notch length, when the notch length was regarded as the crack size, was in good agreement with the measured 4 point bending strength. Fracture surface of the specimen showed the different fracture modes according to the crosshead speed. The four point flexural strength, fracture toughness, Young's modulus and Weibull modulus of the alumina were measured as 360 MPa, 3.91 MPa.m1/2, 159GPa, 17.64, respectively.

• Computers and Concrete
• /
• 제23권3호
• /
• pp.171-188
• /
• 2019

This study proposed a new and efficient 2D damage-plasticity model within the framework of Isogeometric analysis (IGA) for the geometrically nonlinear damage analysis of concrete. Since concrete exhibits complicated material properties, two internal variables are introduced to measure the hardening/softening behavior of concrete in tension and compression, and an implicit gradient-enhanced formulation is adopted to restore the well-posedness of the boundary value problem. The numerical results calculated by the model is compared with the experimental data of three benchmark problems of plain concrete (three-point and four-point bending single-notched beams and four-point bending double-notched beam) to illustrate the geometrical flexibility, accuracy, and robustness of the proposed approach. In addition, the influence of the characteristic length on the numerical results of each problem is investigated.

• 대한토목학회논문집
• /
• 제31권5A호
• /
• pp.389-397
• /
• 2011

본 논문에서는 이방향 휨인장강도 시험 시 시험체에 작용하는 등방성 휨인장거동의 구현여부를 실험적으로 증명하기 위해 시험체의 변형률 측정 실험과, 시험체에 등방성 휨인장응력이 작용할 수 있도록 시험법 개선을 위한 연구를 수행하였다. 또한, 개선된 시험법을 적용하여 이방향 휨인장강도와 4점 휨인장강도 시험에 의한 일방향 휨인장강도를 측정하여 비교하였다. 실험 결과, 시험체에 발생하는 등방성 휨인장응력은 시험체의 표면 조건과 뒤틀림 정도에 많은 영향을 받는 것으로 나타났으나, 시험법 개선으로 인해 시험체에 등방성 휨인장응력상태를 확보할 수 있었다. 개선된 이방향 휨인장강도 시험에 의한 이방향 휨인장강도가 일방향 휨인장강도 보다 32% 더 큰 것으로 나타났으며, 분산성은 동일한 것으로 나타났다.

• Advances in concrete construction
• /
• 제2권3호
• /
• pp.229-247
• /
• 2014

A numerical study of the influence of shear-span/depth ratio on the cohesive crack fracture parameters and double - K fracture parameters of concrete is carried out in this paper. For the study the standard bending specimen geometry loaded with four point bending test is used. For four point loading, the shear - span/depth ratio is varied as 0.4, 1 and 1.75 and the ao/D ratio is varied from 0.2, 0.3 and 0.4 for laboratory specimens having size range from 100 - 500 mm. The input parameters for determining the double - K fracture parameters are taken from the developed fictitious crack model. It is found that the cohesive crack fracture parameters are independent of shear-span/depth ratio. Further, the unstable fracture toughness of double-K fracture model is independent of shear-span/depth ratio whereas, the initial cracking toughness of the material is dependent on the shear-span/depth ratio.

• Computers and Concrete
• /
• 제17권3호
• /
• pp.407-421
• /
• 2016

This paper presents numerical modeling of the structural behavior of CFRP (carbon fiber reinforced polymer) strengthened RC (reinforced concrete) beams under four-point bending. Simulation of debonding at the CFRP-concrete interface was focused, as it is the main failure mode of CFRP strengthened RC beams. Here, cohesive layer was employed to model the onset of debonding, which further helps to describe the post debonding behavior of the CFRP strengthened RC beam. In addition, the XFEM approach was applied to investigate the effects of crack localization on strain field on CFRP sheet and rebar. The strains obtained from the XFEM correlate better to the test results than that from CDP (concrete damaged plasticity) model. However, there is a large discrepancy between the experimental and simulated loaddisplacement relationships, which is due to the simplification of concrete constitutive law.