• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.311-320
• /
• 2011

Fly ash (FA), byproduct from power plant has been actively used as mineral admixture for concrete. However, since bottom ash (BA) is usually used for land reclaim or subbase material, more active reuse plan is needed. Pond ash (PA) obtained from reclaimed land is mixed with both FA and BA. In this study, 6 PA from different domestic power plant are prepared and 5 different replacement ratios (10%, 20%, 30%, 50%, and 70%) for fine aggregate substitutes are considered to evaluate engineering properties of PA as fine aggregate and durability performance of PA concrete. Tests for fine aggregate of PA for fineness modulus, density and absorption, soundness, chloride and toxicity content, and alkali aggregate reaction are performed. For PA concrete, durability tests for compressive strength, drying shrinkage, chloride penetration/diffusion, accelerated carbonation, and freezing/thawing are performed. Also, basic tests for fresh concrete like slump and air content are performed. Although PA has lower density and higher absorption, its potential as a replacement material for fine aggregate is promising. PA concrete shows a reasonable durability performance with higher strength with higher replacement ratio. Finally, best PA among 6 samples is selected through quantitative classification, and limitation of PA concrete application is understood based on the test results. Various tests for engineering properties of PA and PA concrete are discussed in this paper to evaluate its application to concrete structure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.2
• /
• pp.623-631
• /
• 2018

In this study, the degree of deterioration of concrete was investigated in the laboratory under conditions of carbonation and freeze-thaw cycling, which are the major causes of the deterioration of its performance. In this test, the carbonated concrete was subjected to combined freeze-thaw deterioration tests for up to 300 cycles, and its dynamic elastic modulus and compressive strength were measured. The evaluation of the effect of the water-binder ratio on normal concrete subjected to combined carbonization and freezing-thawing showed that its resistibility against such combined deterioration decreased more rapidly in the concrete with a water-binder ratio of 55 % compared with that having a water-binder ratio of 35 %. In the case where the concrete was blended with a mineral admixture consisting of fly ash and blast furnace slag at the same water-binder ratio, it showed an increase of its resistibility against combined deterioration.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.45-52
• /
• 2017

This study evaluated the durability of nuclear power plant concrete. The main parameters were the water-to-binder ratio and admixture type. The results revealed that high-volume ground granulated blast-furnace slag(GGBS) concrete had lower initial strength, while the strength reached higher after 28 days. On the other hand, the initial strength of fly ash blended concrete was high, but the long-term strength of the robbery was low. The measured durability of GGBS blended concrete was found to be better than that of the existing concrete mix for use in the construction of nuclear power plants. Especially, the GGBS blended concrete was more durable than the fly ash blended concrete in terms of chloride attack, carbonation resistivity and freezing-thawing durability in low compressive strength. The effects of concrete compressive strength according to gamma rays were minor.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.6
• /
• pp.29-36
• /
• 2015

In this study, to examine the use of sulfur polymer as a coating agent for concrete, durability and hazard evaluations were performed. The result of the evaluation indicated that the chemical resistance of the coating agent for concrete was outstanding against acidic, base, and alkaline solutions. The evaluation of the bond strength after an accelerated weathering test depending on the mixing condition indicated that the most outstanding strength characteristic was obtained when silica powder and fly ash were mixed at the same time. The bond strength exceeded 1 MPa in every mixing condition even after the repeated hot and cold treatment of the coating agent specimen for concrete, and the SFS mix proportion showed the highest bond strength. The examination of the accelerated carbonation and chloride ion penetration resistance of the concrete coated with the coating agent indicated that the specimen coated with the coating agent using silica powder as a filler showed the most outstanding durability. When a fish toxicity test was performed to examine the hazard of the use of the functional polymer as a coating agent for concrete, the functional polymer was found to have no effect on the organisms. When the chemical resistance, freezing and thawing resistance, carbonation, and chloride ion penetration resistance of the coating agent were considered, substituting silica powder and fly ash as the fillers of the functional polymer by 20%, respectively, was the optimal level in the range of this study.

• Journal of Soil and Groundwater Environment
• /
• v.18 no.1
• /
• pp.102-111
• /
• 2013

A novel MgO-based binder was developed and applied to treat the anoxic sediment that was collected from Seonakdong river, Korea and was contaminated with heavy metals. The treated sediment was evaluated by measuring compressive strength, expansion, leaching of heavy metals and storage characteristics for $CO_2$. Initially, an optimal blending ratio of lime (L)/fly ash (FA)/blast furnace slag (BFS) that was to be mixed with MgO was screened to be $L_{0.3}-FA_{0.1}-BFS_{0.6}$. Long-term strengths of the sediments that were treated by various mixtures of MgO and $L_{0.3}-FA_{0.1}-BFS_{0.6}$ were then evaluated and the blending ratios between 4 : 6 and 6 : 4 were found optimal, which yielded a compressive strength of 4.09 MPa. On this basis, the optimal MgO-based binder was selected to be a 5 : 5 mixture of MgO and $L_{0.3}-FA_{0.1}-BFS_{0.6}$. The good performance of the MgO-based binder was believed to be due to the formation of Mg $(OH)_2$, which filled the micropores and also increased the density of the solidified matrices. The MgO-based binder exhibited an average stabilizing capacities for heavy metals of 92.9%, which was similar to or higher than that of Portland cement. It was found that 69.1 kg of carbon dioxide could be sequestrated after 365 days of curing when treating a ton of anoxic sediments.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.3
• /
• pp.173-180
• /
• 2013

This paper is to investigate an effect of waste cooking oil(WCO) on the engineering properties and durability of high volume admixture concrete. Fly ash with 30% and blast furnace slag with 60% were incorporated in OPC to fabricate high volume admixture concrete with 0.5 of W/B. Emulsified refining cooking oil(ERCO) was made by mixing WCO and emulsifying agent to improve fluidity. ERCO was replaced by cement from 0.25 to 1.0%. As results, the increase of ERCO resulted in decrease of slump and air contents. For compressive strength, the use of ERCO led to decrease the compressive strength at 28 days, while it had similar strength or much higher strength than plain concrete at 180 days. Resistance to carbonation and chloride penetration was improved with the increase of ERCO contents due to decreased pore distribution by saponification between ERCO and concrete, while freeze-thaw resistance was degraded due to air loss.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.48-55
• /
• 2022

This study uses the recovered water as mixing water and artificial lightweight aggregate pre-wetting water as part of a study to increase the recycling rate and reduce greenhouse gas of the ready-mixed concrete recovered during the concrete transport process, and cement fine powder of blast furnace slag(BFS) and fly ash(FA). The engineering characteristics of the three-component lightweight aggregate mortar used as a substitute were reviewed. For this purpose, the flow, dry unit mass, compressive strength, drying shrinkage, neutralization depth, and chloride ion penetration resistance of the three-component lightweight aggregate mortar were measured. When used together with the formulation, when 15 % of BFS and 5 % of FA were used, it was found to be positive in improving the compressive strength and durability of the mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.287-294
• /
• 2019

GGBFS(Ground Granulated Blast Furnace Slag) has been widely used in concrete for its excellent resistance chloride and chemical attack, however cracks due to hydration heat and dry shrinkage are reported. In many International Standards, GGBFS with low fineness of 3,000 grade is classified for wide commercialization and crack control. In this paper, the mechanical and durability performance of concrete were investigated through two mix proportions; One (BS) has 50% of w/b(water to binder) ratio and 60% replacement ratio with low-fineness GGBFS, and the other (TS) has 50% of w/b and 60% replacement ratio with 4000 grade and FA (Fly Ash). The strength difference between TS and BS concrete was not great from 3 day to 91 day of age, and BS showed excellent performance for chloride diffusion and carbonation resistance. Two mixtures also indicate a high durability index (more than 90.0) for freezing-thawing since they contain sufficient air content. Through improvement of strength in low fineness GGBFS concrete at early age, mass concrete with low hydration heat and high durability can be manufactured.

• The Journal of Engineering Geology
• /
• v.26 no.1
• /
• pp.117-128
• /
• 2016

Chemical reaction tests were performed to assess the properties of hardened specimens of cement pastes (KS-1 Portland and Class G) exposed to supercritical CO₂ for 1, 10, and 100 days. After exposure, the samples' measured permeability and strength were compared with values measured for pristine samples. The pristine cements had permeabilities of 0.009~0.025 mD, which increased by one order of magnitude after 100 days of exposure (to 0.11~0.29 mD). The enhancement of permeability is attributed to the stress release experienced by the samples after removal from the pressure vessel after exposure. Despite its enhancement, the measured permeability mostly remained lower than the API (American Petroleum Institute) recommended maximum value of 0.2 mD. The degradation of the cement samples due to exposure to supercritical CO₂ led to a layer of altered material advancing inwards from the sample edges. The Vickers hardness in the altered zone was much higher than that in the unaltered zone, possibly owing to the increase in density and the decrease in porosity due to the carbonation that occurred in the altered zone. Hardness close to the edge within the altered zone was found to have decreased significantly, which is attributed to the conversion of C-S-H into less-strong amorphous silica.