• Transactions of the Korean hydrogen and new energy society
• /
• v.16 no.4
• /
• pp.343-349
• /
• 2005

In this study, We had surface-treated single-walled carbon nanotubes (SWNTs) for improving hydrogen storage capacity. The SWNTs were treated by heat treatment, acid treatment and fluorinated at various temperatures. The SWNTs were characterized by Raman spectroscopy and TEM and estimated hydrogen storage capacities at 303K. As shown Raman spectra and TEM images, the structure of fluorinated SWNTs were stable at 423K but changed to the MWNTs-like structure or onion structure over 523K. Hydrogen storage capacity of SWNTs fluorinated at 423K was remarkably increased 2.6 times than that of pristine SWNTs. For SWNTs fluorinated at 573K, the amount of hydrogen adsorbed wasn't increased compared with SWNTs fluorinated at 423K. Therefore, high hydrogen storage capacity of SWNTs could be archived by fluorinated condition at 423K, which was not changed SWNT structure.

• Journal of the Semiconductor & Display Technology
• /
• v.4 no.3 s.12
• /
• pp.5-9
• /
• 2005

The bonding structure of organic materials such as fluorinated amorphous carbon films was classified into two types due to the chemical shifts. The electrical properties of fluorinated amorphous carbon films also showed very different effect of two types notwithstanding a very little difference. Fluorinated amorphous carbon films with the cross-link break-age structure existed large leakage current resulting from effect of the electron tunneling. Increasing the cation due to the electron-deficient group increased the barrier height of the films with the cross-link amorphous structure, therefore the electric characteristic of the final materials with low dielectric constant was also improved. The lowest dielectric constant is 2.3 at the sample with the cross-link amorphous structure.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.6
• /
• pp.1337-1340
• /
• 2009

Electrical properties of a fluorinated carbon black (CB)-filled high-density polyethylene (HDPE) polymeric switch were investigated as a function of fluorination pressure at 0.1 ~ 0.4 MPa. From the FT-IR results, the absorption spectra of the fluorinated CB show an absorption band at 1400 ~ 1000 $cm^{-1}\;for\;{\nu}_{C-F}$ and the peak intensity increased with increasing fluorination pressure. Also, the analysis of XPS spectra of the fluorinated CB indicated that fluorine content increased with increasing fluorination pressure. Meanwhile, the surface free energy of the fluorinated CB decreased with increasing fluorination pressure. Consequently, the increase of fluorine contents of CB made a disappearance of negative temperature coefficient (NTC) behavior of the polymeric switch, which was probably due to the reduction of CB reaggregation after melting point of the HDPE, resulted from the decreasing of London dispersive component of the surface free energy for CB particles.

• Carbon letters
• /
• v.26
• /
• pp.25-30
• /
• 2018

The dielectric medium used in electrophoretic displays (EPDs) is required to be an environmentally friendly solvent with high density, low viscosity, and a large electric constant. Hydrofluoroether, a highly fluorinated solvent with eco-friendly characteristics, is regarded as a viable alternative medium for EPDs, owing to the similarity of its physical properties to those of the conventional EPD medium. Surface modification of particles is required, however, in order for it to disperse in the charged solvent. Also, positive/negative charges should be present on the particle surface to enable electrophoretic behavior. In this study, carbon black particles wrapped with positively charged nitrogen (N-CBs) were fabricated by a simple hydrothermal process using a poly(diallyldimethylammonium chloride) solution as a black coloring agent for the EPD. The dispersion behavior of N-CBs was investigated in various solvents.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.386-390
• /
• 2016

The surface of carbon nanotubes (CNTs) was modified by fluorination and applied to conductive materials to improve the energy efficiency of a capacitive desalination (CDI) electrode. CNTs were fluorinated at room temperature with a mixed gas of fluorine and nitrogen, and activated carbon based CDI electrodes were then prepared by adding 0-0.5 wt% of untreated CNTs or fluorinated CNTs with respect to the activated carbon. Fluorinated CNTs showed improved dispersibility in the electrode and also slurry as compared to untreated CNTs, which was confirmed by the zeta potential and scanning electron microscopy. Fluorinated CNTs added electrodes showed higher desalination efficiency but lower energy consumption than those of using untreated CNTs added electrodes. This was attributed to the decrease in the resistance of CDI electrodes due to the improved dispersibility of CNTs by fluorination.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2005.05a
• /
• pp.67-72
• /
• 2005

The bonding structure of organic materials such as fluorinated amorphous carbon films was classified into two types due to the chemical shifts. The electrical properties of fluorinated amorphous carbon films also showed very different effect of two types notwithstanding a very little difference. Fluorinated amorphous carbon films with the cross-link breakage structure existed large leakage current resulting from effect of the electron tunneling. Increasing the cation due to the electron-deficient group increased the barrier height of the films with the cross-link amorphous structure, therefore the electric characteristic of the final materials with low dielectric constant was also improved. The lowest dielectric constant is 2.3 at the sample with the cross-link amorphous structure.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.68.1-68.1
• /
• 2007

• Bulletin of the Korean Chemical Society
• /
• v.30 no.9
• /
• pp.2071-2076
• /
• 2009

The single-walled carbon nanotubes (SWCNTs) produced by chemical vapor deposition (CVD) were directly fluorinated with fluorine ($F_2$) gas in a temperature range 20 ~ 400 ${^{\circ}C}$. The surface properties and morphology of the SWCNTs were investigated in terms of fluorination temperature. As a result, Raman spectra showed a pair of bands at 1340 and 1590 $cm^{-1}$ peculiar to disordered $sp^2$-carbons. These results indicated that C-F bonds were formed on the rear surfaces of the nanotubes by fluorination, while the external surfaces as well as the layers between the internal and external surfaces retained their $sp^2$-hybridization. XPS analysis exhibited that fluorine atoms were bonded to carbon atoms on internal surfaces (rear surfaces) of the nanotubes and the amount of fluorine attached on the nanotubes was increased with increasing the fluorination temperature. Consequently, the direct fluorination of carbon nanotubes led to functionalization and modification of pristine nanotubes with respect to surface and morphological properties.

• Carbon letters
• /
• v.26
• /
• pp.112-116
• /
• 2018

• Carbon letters
• /
• v.20
• /
• pp.81-85
• /
• 2016