• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.146-152
• /
• 1996

Polypropylene fiber reinforced mortar and concrete as civil material or architectural material have been used in America and British etc, and have been researched. Polypropylene fibers have many advantages in many points ; in economical costs, chemical stability and durability. It has been reported that polypropylene fiber can control restrained tensile stresses and cracks and increase toughness, resistance to impact, corrosion, fatigue and durability. This study has been performed to obtain the properties of polypropylene fiber reinforced concrete such as compressive strength, flexural strength, toughness, slump, drying shrinkage crack and drying shrinkage characteristics. The test variables are fiber contents, fiber length, fiber types, and so on. From the results of this study, we can expect the effects of the admixtures of polypropylene fiber about strength and drying shrinkage properties in concrete and mortar.

• Journal of the Korean Ceramic Society
• /
• v.32 no.8
• /
• pp.865-872
• /
• 1995

Ultra-fine $\beta$-SiC powders were fabricated by self-propagating high temperature synthesis process (SHS) using microwave oven. The flexural strength, fracture toughness, and hardness of hot pressed sample at 200$0^{\circ}C$ for 60 min using synthesized SiC powders, which had 2 wt% of Al2O3 and 2.5 wt% of B4C content, showed 438 MPa, 4.15MPa.m1/2 and 28 GPa, respectively. The highest strength, fracture toughness, and hardness of composites containing 4wt% of Al2O3, which had highest relative density of 99.9%, showed 458 MPa, 4.6MPa.m1/2 and 36.2 GPa, respectively.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.333-336
• /
• 2005

This paper presents a comparative evaluation of eight different types of steel fibers used as reinforcing material in concrete beams. The fibers which used ultra-strength steel fiber reinforced concrete were fiber length of 30 to 60mm, aspect ratio of 43 to 86, W/B ratio 0.16 to 0.30, fiber types of both ends hooked and straight shape and fiber volume fraction of 1 to 5$\%$. As for the test results, it estimated the influence of fiber volume, length and aspect ratio on the mechanical properties of high toughness concrete, the mechanical properties improved according to increase fiber volume, to increase aspect ratio and to long fiber length. And the resonable fiber volume in high toughness concrete was analyzed 2$\%$ based on the results of mechanical properties.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.221-243
• /
• 1997

The objective of this study was to characterize the mechanical properties of $Y_{2}O_{3}$-containing glass infiltrated ceramic core material, which was made by pressureless powder packing method. A pure alumina powder with a grain size of about $4{\mu}m$ was packed without pressure is silicon mold to form a bar shaped sample, and applied PVA solution as a binder. Samples were sinterd at $1350^{\circ}C$ for 1 hour. After cooling, $Y_{2}O_{3}$-containing glass($SiO_{2},\;Y_{2}O_{3},\;B_{2}O_{3},\;Al_{2}O_{3}$, ect) was infiltrated to the sinterd samples at $1300^{\circ}C$ for 2 hours and cooled. Six different proportions $Y_{2}O_{3}$ of were used to know the effect of the mismatch of the thermal expansion coefficient between alumina powder and glass. The samples were ground to $3{\times}3{\times}30$ mm size and polished with $1{\mu}m$ diamond paste. Flexural strength, fracture toughness, hardness and other physical properties were obtained, and the fractured surface was examined with SEM and EPMA. Ten samples of each group were tested and compared with In-Ceram(tm) core materials of same size made in dental laboratory. The results were as follows : 1. The flexural strengths of group 1 and 3 were significantly not different with that of In-Ceram, but other experimental groups were lower than In-Ceram. 2. The shrinkage rate of samples was 0.42% after first firing, and 0.45% after glass infiltration. Total shrinkage rate was 0.87%. 3. After first firing, porosity rate of experimental groups was 50%, compared with 22.25% of In-Ceram. After glass infiltration, porosity rate of experimental groups was 2%, and 1% in In-Ceram. 4. There was no statistical difference in hardness between two materials tested, but in fracture toughness, group 2 and 3 were higher than In-Ceram. 5. The thermal expansion coefficients of experimental groups were varied to $4.51-5.35{\times}10^{-6}/^{\circ}C$ according to glass composition, also the flexural strengths of samples were varied. 6. In a view of SEM, many microparticles about $0.5{\mu}m$ diameter and $4{\mu}m$ diameter were observed in In-Ceram. But in experimental group, the size of most particles was about $4{\mu}m$, and a little microparticles was observed. The results obtained in this study showed that the mismatch of the thermal expansion coefficients between alumina powder and infiltrated glass affect the flexural strength of alumin/glass composite. The $Y_{2}O_{3}$-containing glass infiltrated ceramic core made by powder packing method will takes less time and cost with sufficient flexural strength similar to all ceramic crown made with slip casting technique.

• Journal of the Korea Institute of Building Construction
• /
• v.22 no.6
• /
• pp.553-564
• /
• 2022

Concrete is a representative composite material that shows excellent performance in the construction field. However, it is a brittle and nonhomogeneous material and exhibits weak behavior against bending and tensile forces. To compensate for such weakens, fiber reinforcement has been utilized, and steel fiber has been recognized as one of the best material for such purpose. However, steel fiber can seriously affect the durability of concrete exposed to the marine environment due to the corrosion caused by chlorine ions. This study intended to evaluate the mechanical performance of steel fiber reinforce concrete during and after repeated wet/dry cycles in salt solution. According to the experimental results, there was no reduction in the relative dynamic modulus of concrete during the repeated wet/dry cycles in salt solution for 37 weeks. Flexural strength was not decreased after completion of repeated wet/dry cycles in salt solution. There was no sign of corrosion in steel fibers after visual observation of fractured surface. However, the flexural toughness was decreased, and this is because about half of the concrete specimen showed failure before reaching the maximum displacement of 3 mm. Although repeated wet/dry cycles in salt solution did not cause cracks in concrete through corrosion of steel fibers, specific attention is required because it can reduce flexural toughness of steel fiber reinforced concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1992.10a
• /
• pp.202-207
• /
• 1992

The objective of this study is to develop analytical techniques of polymer impregnated concrete flexural members for its proper applications. crystalline methylmethacrylate(MMA) is chosen as a monomer of polymer impregnants, On the basis of members. fracture toughness, fracture energy , critical crack width, and tension softening relations near crack tip are formulated in terms of member depth, initial notch length and the flexural strength of normal concrete. The structural analysis rocedure and the finite element computer program developed in the study are applicable to evaluate elastic behavior, ultimate strength, and tension softening behavior of MMA type PIC structural members subject to various loading conditions. It is concluded that the developed structural analysis procedure and the finite element computer program are applicable to analysis and design of in-situ and precast PIC structural members.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.04a
• /
• pp.93-98
• /
• 1993

In order to discuss the mechanical properties of fiber reinforced composites with fly ash, lime, gypsum and polymer emulsion-Stylene Butadiene Rubber Latex (SBR) , experimental studies on FRC were carried out. The kinds of fiber used in FRC are PAN-dervied and Pitch-derived carbon fiver, alkali-resistance glass fiber. As a test results, the flexural strength and tougthness of fiber reinforced fly ash. lime.gypsum cement composites are remarkably increased by fiber contents ,but compressive strength of the composites are influenced by kinds of fiber more than by fiber contents. Also, addition of a polymer emulsion (SBR) to the composites decreased the bulk specific gravity, but compressive and flexural strengths, toughness of the composites are not influenced by it, are considerably improved by increasing fiber contents.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.327-332
• /
• 2001

It is generally observed that steel fiber reinforced concrete with traditional straight steel fibers overcomes brittle nature of plain concrete by failure mechanisms by fiber pull-out rather than fiber rupture resulting from fiber yielding or concrete fracture at failured surface. Ring type steel fibers in concrete which is confined in concrete matrix and has better orientation, thus, lead to fiber yielding and concrete fracture as well as increase of flexural behavior of concrete more efficiently, Comparative experimental study is performed in order to measure the relative efficiencies of steel fiber reinforced concrete reinforced with two different fibers. It is found that better toughness is obtained from the ring type steel fiber reinforced concrete than from straight steel fiber reinforced concrete under flexural loading.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.47 no.2
• /
• pp.63-72
• /
• 2005

In this study, the physical and mechanical properties of steel fiber reinforced lightweight polymer concrete were investigated experimentally with various steel fiber contents. All tests were performed at room temperature, and stress-strain curve and load-deflection curve were plotted up to failure. The unit weight of steel fiber reinforced lightweight polymer concrete was in the range of $1,020{\sim}1,160\;kg/m^3$, which was approximately $50\%$ of that of the ordinary polymer concrete, The compressive strength, splitting tensile strength, flexural toughness and flexural load-deflection curves after maximum load were shown with increase of steel fiber content. The stress-strain curves of steel fiber reinforced lightweight polymer concrete were bilinear in nature with a small transition zone, Based on these results, steel fiber reinforced lightweight polymer concrete can be widely applied to the polymer composite products.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.377-380
• /
• 2006

HPFRCCs(High performance fiber reinforced cementitious composites) is a class of FRCCs(Fiber reinforced cementitious composites) exhibit multiple crack. Multiple crack lead to improvement in ductility, toughness, and deformation capacity under compressive and tensile stress. These properties of HPFRCCs are affected by type of fiber, water cement ratio, type of admixture and rate of substitution. Furthermore these influence dispersion of fiber, mixing performance and fluidity of mixture. In this paper, HPFRCCs made of steel cord and carbon fiber were tested with water cement ratio, type of admixture and rate of substitution to evaluate characteristics of mixing and flexural strength.