In the present study, bamboo/PLA biocomposites through injection molding process using extruded bamboo/PLA pellets with the fiber contents of 30, 40, and 50 wt% according to the presence and absence of bamboo fiber grinding, respectively, were fabricated and their mechanical, thermal, impact, and water absorption properties were explored. Compared to neat PLA, the flexural modulus, tensile modulus, storage modulus and impact strength of bamboo/PLA biocomposites were considerably increased. In particular, the moduli were further increased by introducing the ground bamboo fibers. In addition, use of the ground bamboo fibers was effective to enhance the long-term water resistance of the biocomposites. The heat treatment temperature of neat PLA was improved by 16% by incorporating the bamboo fibers and the fiber grinding effect was slight. The incorporation of the ground bamboo fibers to PLA did not influence the tensile strength and impact toughness of bamboo/PLA biocomposites.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.111-116
• /
• 1998

Silicon nitride is hard and tough ceramic material. Hereby, mechanical machinability is very poor. It has also high electrical resistance. Silicon nitride of extremely high electrical resistivity becomes conductive ceramic composite by adding 30 wt% TiN. Ceramics with high electrical conductivity can be electrical discharge machined. Using by the Electrical Discharge Machining (EDM) technique. $Si_3N_4-TiN$ ceramic composite with high electrical conductivity is utilized to make metal working tool. These tool materials have severe wear problem as well as oxidation. Post HIP processing after sintering $Si_3N_4-TiN$ ceramic composites was performed. The tribological property of $Si_3N_4-TiN$ composite as a function of content of TiN was investigated in air, at room temperature. The hardness, fracture toughness, and flexural strength were compared with the wear volume. SEM observation of wear tracks can make an explanation of wear mode of $Si_3N_4-TiN$ composite.

• Polymer(Korea)
• /
• v.27 no.3
• /
• pp.183-188
• /
• 2003

The dielectric constants of fluorine-containing epoxy resins, 2-diglycidylether of benzotrifluoride(FER)/4,4'-diamino-diphenyl methane (DDM) and diglycidylether of bisphenol-A (DGEBA)/DDM systems were evaluated by dielectric spectrometer. Glass transition temperature and thermal stability factors, including initial decomposed temperature, temperatures of maximum rate of degradation, and decomposition activation energy of the cured specimens were investigated by dynamic mechanical analysis and thermogravimetric analysis. For the mechanical properties of the casting specimens, the fracture toughness, flexural, and impact tests were performed, and their fractured surfaces were examined by scanning electron microscope. The dielectric constant of FER/DDM system was lower than that of commercial DGEBA/DDM system, and the mechanical properties of the cured specimens showed higher values than those of DGEBA/DDM system. This was probably due to the introduction of trifluoromethyl (CF$_3$) group into the side chain of the epoxy resins, resulting in improving the electric and mechanical properties of the epoxy cure system studied.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.644-647
• /
• 2004

Modulus of rupture (MOR) and flexural toughness in hybrid fiber reinforced cement pastes mixed with micro-fiber (carbon fiber) and macro-fiber (steel fiber) and replaced with silica fume according to the fixed ratio were researched. Reinforcing efficiency in specimens were estimated by two factors, such as strengthening factor $(F_s)$ and toughening factor $(F_t)$, which were calculated from the analysis of variance (ANOVA) of the response values, such as MOR and absorbtion energy $(W_0)$. According to the experimental design by the fractional orthogonal array, nine hybrid fibrous reinforced paste series and one non-reinforced control paste were manufactured. Specimens of each series were tested by the INSTRON Inc. 8502(model) equipment in three-points bending and then measured the load-deflection response relationships. Considerable strengthening of cement pastes resulted in' the case of other factors without carbon fiber and toughening of cement pastes about all factors showed high. Based on the significance of factors related to response values from ANOVA, following assessments were available; $F_s$ or MOR: silica fume $\gg$ steel fiber $\gg$ carbon fiber; $F_t\;or\;W_0$: steel fiber > carbon fiber > silica fume. Optimized composition condition was estimated by steel fiber of $1.5\%$, carbon fiber of $0.5\%$ and silica fume $7.5\%$ in side of strengthening and steel fiber of $1.5\%$, carbon fiber of $0.75\%$ and silica fume $7.5\%$ in side of toughening.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.381-384
• /
• 2001

The $\beta$-SiC+ZrB$_2$ and $\beta$-SiC+TiB$_2$ceramic electroconductive composites were pressureless-sintered and annealed by adding l2wt% A1$_2$ $O_3$+Y$_2$ $O_3$(6 : 4wt%) powder as a function of sintering temperature. The relative density showed highest value of 84.92% of the theoretical density for SiC-TiB$_2$ at 190$0^{\circ}C$ sintering temperature. The phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H), TiB$_2$, $Al_{5}$Y$_2$ $O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 230 MPa for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. The vicker's hardness increased with increasing sintering temperature and showed the highest for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. Owing to YAG, the fracture toughness showed the highest of 6.50 MPa . m$^{1}$2/ for SiC-ZrB$_2$ composites at 190$0^{\circ}C$. The electrical resistivity was measured by the Rauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).).

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.560-565
• /
• 2010

Nano laminated bulk $Ti_3SiC_2$ was synthesized by hot press process using TiCx/Si powder mixture at the temperature range of $1300^{\circ}C\sim1500^{\circ}C$. pure $Ti_3SiC_2$ was synthesized by a hot pressing above $1400^{\circ}C$, while unreacted TiCx were remained in bulk $Ti_3SiC_2$ which synthesized below $1400^{\circ}C$. The sintering density of bulk $Ti_3SiC_2$ were varied with the amount of TiCx. It was found that the mechanical properties and micro structures of bulk $Ti_3SiC_2$ were closely related to the amounts of TiCx which was controlled by the hot pressing temperature. The TiCx increase the flexural strength of bulk $Ti_3SiC_2$, while the fracture toughness and thermal shock resistance of bulk $Ti_3SiC_2$ were decreased with the content of TiCx. The plastic deformations of bulk $Ti_3SiC_2$ were appeared above $1000^{\circ}C$.

• Computers and Concrete
• /
• v.14 no.3
• /
• pp.299-313
• /
• 2014

Effects of polypropylene (PP) fibers, steel fibers (SF) and hybrid on the properties of highstrength fiber reinforced self-consolidating concrete (HSFR-SCC) under different volume contents are investigated in this study. Comprehensive laboratory tests were conducted in order to evaluate both fresh and hardened properties of HSFR-SCC. Test results indicated that the fiber types and fiber contents greatly influenced concrete workability but it is possible to achieve self consolidating properties while adding the fiber types in concrete mixtures. Compressive strength, dynamic modulus of elasticity, and rigidity of concrete were affected by the addition as well as volume fraction of PP fibers. However, the properties of concrete were improved by the incorporation of SF. Splitting tensile and flexural strengths of concrete became increasingly less influenced by the inclusion of PP fibers and increasingly more influenced by the addition of SF. Besides, the inclusion of PP fibers resulted in the better efficiency in the improvement of toughness than SF. Furthermore, the inclusion of fibers did not have significant effect on the durability of the concrete. Results of electrical resistivity, chloride ion penetration and ultrasonic pulse velocity tests confirmed that HSFR-SCC had enough endurance against deterioration, lower chloride ion penetrability and minimum reinforcement corrosion rate.

• Journal of the Korean Society of Environmental Restoration Technology
• /
• v.16 no.1
• /
• pp.17-25
• /
• 2013

The mechanical properties appeared at the concrete mixed with Polypropylene fiber($1kg/m^3$, $3kg/m^3$, $5kg/m^3$) are compared with normal concrete and wire mesh one and evaluated. Achieved slump test to search effect that PP fiber gets to workability, even if the mixing amount of fiber increases, confirmed that slump value is no change almost. The no difference can be caused by hard mixture, but because of the big softness of fiber there is no effect greatly up to PP fiber mixing amount $5kg/m^3$ even with soft mixture. Compressive strengths and flexural strengths of the concretes with PP fiber and without the fiber are appeared almost alike. If examine load resistance ability by PP fiber mixing amount increase, it could know that the increase of fiber mixing amount improves load resistance ability and the toughness index is increased. While normal concrete is broken at the same time with crack, fiber mixed concrete stand in flexure load continuously after crack occurrence. In compare with wire mesh embeded concrete, wire mesh mixed concrete stands in some degree in flexure load by wire mesh crack occurrence and the test piece was broken at the same time. But, it could know that the PP fiber mixed concrete resist continuously to flexure load in bigger displacement.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.169-172
• /
• 2006

In the present work, silicon nitride was fabricated with $Y_3Al_5O_{12}$ as sintering additive and its mechanical properties were investigated. Silicon nitride with 3, 5, 7wt% of $Y_3Al_5O_{12}$ was prepared and sintered by a Hot Pressing (HP) technique at 1750, $1800^{\circ}C$ for 2 hours. The Process was fulfilled under different process pressures of 30, 45MPa respectively. Mechanical properties (density, strength, hardness, fracture toughness) were investigated as a function of $Y_3Al_5O_{12}$ contents in $Si_3N_4$. $Si_3N_4-Y_3Al_5O_{12}$ ceramics showed similar mechanical properties compared with $Si_3N_4-Y_2O_3-Al_2O_3$ ceramics. But its high temperature strength was higher than $Si_3N_4-Y_2O_3-Al_2O_3$ceramics considerably.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.690-695
• /
• 2003

Soft-solution route employing PVA(Polyvinyl Alcohol) as a polymeric carrier in a mixed metal cation solution was used for synthesis of single-phase nickel aluminate (NiA1$_2$O$_4$) powders. The PVA ensured the homogeneous distribution of metal ions in the solution and it resulted in the decrease of crystallization temperature. The synthesized powders prepared by PVA addition were soft and ball-milled easily. The ball-milled powders of about 300 nm in size were fully densified to density of 4.35 g/㎤ at 1600$^{\circ}C$ for 1 h. The Vickers hardness, flexural strength, fracture toughness and thermal expansion coefficient of the sintered nickel aluminate were 14.2 ㎬, 304 ㎫, 4.8 ㎫$.$m$\^$1/2/ and 9.8${\times}$10$\^$-6//$^{\circ}C$, respectively.