• The Korean Journal of Ceramics
• /
• v.6 no.1
• /
• pp.58-63
• /
• 2000

The preparation of Y-doped $SrZrO_3$powder by ultrasonic spray pyrolysis was investigated as a representative system, in order to produce fine, single phase multicomponent oxide powders. A precursor solution containing metal nitrates, citric acid and ethylene glycol was atomized glycol was atomized with an ultrasonic spray nozzle. Gel particles formed by organic functional groups were pyrolyzed and subsequently calcined at $800^{\circ}C$ to obtain well-crystallized, single perovskite phase. Most of large particles exhibited macroscopic pores and weak agglomeration between primary particles. However, strong agglomeration was observed in the surfaces of large particles. The effect of the microstructures of these particles on size reduction to submicron particles was described.

• Proceedings of the KIEE Conference
• /
• 1993.11a
• /
• pp.222-224
• /
• 1993

In this paper, The optimum oxidation conditions for the formation of Cu-Zn ferrite were investigated using precipitates obtained by the mixture of $CuCl_2{\cdot}2H_2O$, $ ZnCl_2$, $FeCl_3{\cdot}6H_2O$ and NaOH. The precipitates were prepared by coprecipitation method on various temperatures and oxidation conditions. The oxidation products were examined by SEM, XRD, and VSM. The particles obtained at 70($^{\circ}C$) were more spherical and fine than that of prepared at 25($^{\circ}C$), 50($^{\circ}C$), 60($^{\circ}C$), respectively. By $H_2O_2$ oxidation, the saturation magnetization of the powders was little influenced, But, by air oxidation the saturation magnetization of the powders was influenced intricately. According to our experimental data, the saturation magnetization of the powders increased with reaction time and was saturated at 9 hours.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.10a
• /
• pp.167-172
• /
• 1993

In domestic, there are not adequate admixtures for concrete now, so the study on that is required deeply, Accordingly the purpose of this study is to analyze the application possibilities of Natural Zeolite and Mud Stone as admixtures for concrete through comparing the compressive strength prorerties of mortar mixed with imported Silica Fume those mixed with domestic Zeolite and Mud Stone. As the results from this study, the optimum displacement rate of Silica Fume, Zeolite and Mud Stone is 15%, 5~10%, 15% respectively. In Zeolite and Mud Stone, the compressive strength is higher in proportion as the powder is fine. Consequentely, the application possibility the application possibility of Zeolite and Mud Stone is very sufficient as admixtures for concrete.

• Journal of Advanced Marine Engineering and Technology
• /
• v.32 no.6
• /
• pp.862-868
• /
• 2008

Many studies have been conducted to increase heat transfer in fluid. One of the various heat transfer enhancement techniques is suspending fine metallic or nonmetallic solid powder in traditional fluid. Nanofluid is defined as a new kind of heat transfer fluid containing a very small quantity of nanometer particles that are uniformly and stably suspended in a liquid. This study investigates the effect of nanofluid containing diamond, CuNi and CuAg nanometer particles, and proposes the heat transport mechanism of nanofluid. The test result shows that the thermal conductivity of nanofluid is much higher than that of traditional fluid, and the increasing rate of the conductivity is dependent on the conductivity of the solid metal.

• Journal of Korea Foundry Society
• /
• v.10 no.2
• /
• pp.162-170
• /
• 1990

The major effects of RSP sre 1) extension of solid solubilities, 2) formation of metastable phaeses, 3) microstructural refinement 4) segregationless. The main trust of this study was to investigate the effects of superimposing RSP on the structure and properties of HSLA steels. Powder was made by NGA (Nitrogen Gas Atomization) process, and consolidated by HIP. The high grain-coarsening resistance of NGA-HIP steels was attributed to a fine dispersion of oxide precipitates. The average grain size for the NGA-HIP steels was somewhat finer than that for the conventional HSLA steels, The impact properteis of NGA-HIP steels were improved over those of the conventional HSLA steels.

• Ocean and Polar Research
• /
• v.26 no.3
• /
• pp.515-521
• /
• 2004

The processes of formation and dissociation of gas hydrates were investigated by monitoring pressure and temperature variations in a pressure cell in order to understand the kinetic behavior of gas hydrate and the controlling factors fur the phase transition of gas hydrate below freezing. Gas hydrates were made kom guest gases ($CH_4,\;CO_2$, and their mixed-gas) and fine ice powder. We found that formation and dissociation speeds of gas hydrates were not controlled by temperature and pressure conditions alone. The results of this study suggested that pressure levels at the formation of mixed-gas hydrate determine the transient equilibrium pressure itself.

• The Korean Journal of Rheology
• /
• v.2 no.1
• /
• pp.67-78
• /
• 1990

세라믹 분말의 사출성형성을 평가하기 위하여 다양한 혼합체 시스템에 대한 혼합도 와 유변학적 성질을 질화규소 미세분말의 부피비를 변화시키면서 조사하였다. 열가소성 결 합체 시스템은 폴리에틸린 폴리에틸렌 왁스 그리고 미소량의 첨가제를 혼합하여 사용하였 다. 혼합성능을 평가하기 위하여 비분산혼합에서는 총접촉면적비를 그리고 분산혼합에서는 총파괴표면적비를 혼합척도로서 사용하여 정성적으로 모형화하였다. 사용된 혼합기내의 유 동장을 해석하기 위하여 뉴우톤유체를 가정하여 유동해석을 수행하였다. 혼합물의 혼합도는 각각 5분 30분 동안 혼합된 시편을 주사전자현미경 사진에 의해 관찰하여 평가하였다. 또한 혼합물의 사출성형성 그리고 혼합질 점도 토우크 곡선 사이의 관계를 규명하기 위하여 전단 변형를 속도를 따른 점도를 모세관 점도계를 사용하여 측정하였으며 질화규소의 부피비가 60%일 때까지는 만족할 만한 성형성과 혼합질을 가짐을 알 수 있었다.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.10a
• /
• pp.59-65
• /
• 1997

The calibration of O.M.D is carried out experimentally and is analysed theoretically. O.M.D experimentally measures the change in optical density of artificially contaminated oil which contains Fe powder of 5, 10, 20, 30, 40, 50, 70, 100, 200 ppm. The change in optical density, D$_1$ means the logarithmic transmittance of I$_0$ over $I_1 D_2$ denotes the logarithmic transmittance I$_2$ over I$_1$ on electromagnetic force which arranges the ferrous particles along the line of magnetic force. The theoretical D$_1$ which increases linearly as increasing Fe concentrations, is analysed by light attenuation theory. The difference between theoretical D$_1$ and experimental D$_1$ is due to the attenuation of micro bubbles and the agglomeration of fine particles in the sample oil. The calibrated O.M.D is applied to the sample oil from the high-powered diesel engine. Also the results are compared with those out of the off-line techniques such as JOAP and ICP.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.31 no.2
• /
• pp.86-91
• /
• 1999

A new test method has been developed for a quantitative evaluation of macro-stickies in recycled pulps. The method uses a fine slot screen to separate a sticky particles form fiber in the pulp samples. The obtained sticky particles were spread on filter paper and covered with silicon carbide powder in order to make the stickies area with sufficient contrast between stickies and background. The stickies are then counted by a scanner-based image analysis system. The validity of this evaluation method of stickies of KOCC, ONP and white ledger wastepaper recycling plants respectively. It is shown that this method can be applied for a quantitative determination of stickies content in various recycled pulp samples. With this testing method, reproducible and reliable data were obtained for the actual mill pulp samples.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.339-344
• /
• 1997

During recent years the durability of concrete structures has attracted considerable interest in concrete practice, material research and long-term deformation. To preserve the brittleness of concrete as well as energy absorption and impact resistance, amount of fiber usage has greatly increased year to year in the field of public works. When fly ash, fine powder, mixed into concrete, it condensed the void of concrete structure. Expecially, there's a great effect for strength improvement of concrete by initial pozzolanic reactions. Pozzolan reaction, between cement particle and fly ash, can elaborate the micro structure of matrix. So it was able to improve the effect of fiber reinforced by increased adhesion between cement paste and steel fiber. And so, in this paper, we dealt SFRC for the purpose of efficiently using of industrial by-products and its economical manufacturing. Also we performed the test for durability such as chemical resistance, freeze-thaw resistance and accelerated carbonation of SFRC using fly ash.