• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.676-680
• /
• 2010

Most TCOs such as ITO, AZO(Al-doped ZnO), FTO(F-doped $SnO_2$) etc., which have been widely used in LCD, touch panel, solar cell, and organic LEDs etc. as transparent electrode material reveal n-type conductivity. But in order to realize transparent circuit, transparent p-n junction, and introduction of transparent p-type materials are prerequisite. Additional prerequisite condition is optical transparency in visible spectral region. Oxide based materials usually have a wide optical bandgap more than ~3.0 eV. In this study, single-phase transparent semiconductor of $SrCu_2O_2$, which shows p-type conductivity, have been synthesized by 2-step solid state reaction at $950^{\circ}C$ under $N_2$ atmosphere, and single-phase $SrCu_2O_2$ thin films of p-type TCOs have been deposited by RF magnetron sputtering on alkali-free glass substrate from single-phase target at $500^{\circ}C$, 1% $H_2$/(Ar + $H_2$) atmosphere. 3% $H_2$/(Ar + $H_2$) resulted in formation of second phases. Hall measurements confirmed the p-type nature of the fabricated $SrCu_2O_2$ thin films. The electrical conductivity, mobility of carrier and carrier density $5.27{\times}10^{-2}S/cm$, $2.2cm^2$/Vs, $1.53{\times}10^{17}/cm^3$ a room temperature, respectively. Transmittance and optical band-gap of the $SrCu_2O_2$ thin films revealed 62% at 550 nm and 3.28 eV. The electrical and optical properties of the obtained $SrCu_2O_2$ thin films deposited by RF magnetron sputtering were compared with those deposited by PLD and e-beam.

• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.290-293
• /
• 2001

The SrBi$_2$Nb$_2$O$_{9}$ (SBN) thin films were deposited on p-type(100) Si substrates by rf magnetron sputtering to confirm the Possibility of Pt/SBN/Si structure for the application of nondestructive read out ferroelectric random access memory (NDRO- FRAM). The SBN thin films were deposited by co-sputtering method with Sr$_2$Nb$_2$O$_{7}$ (SNO) and Bi$_2$O$_3$ ceramic targets. The SBN thin films deposited at room temperature were annealed at $700^{\circ}C$ for 1hr in $O_2$ ambient. The structural and electrical properties of SBN with different power ratios of targets were measured by x-ray diffraction(XRD), scanning electron microscopy(SEM), capacitance-voltage(C-V), and current-voltage(I-V). The C-V curves of the SBN films showed hysteresis curves of a clockwise rotation showing ferroelectricity. When the Power ratio of the SNO/Bi$_2$O$_3$ targets was 120 W/100 W, the SBN thin films had excellent electrical properties. The memory window of SBN thin film was 1.8 V-6.3 V at applied voltage of 3 V-9 V and the leakage current density was 1.5 $\times$ 10$^{-7}$ A/$\textrm{cm}^2$ at applied voltage of 5 V The composition of SBN thin films was analysed by electron probe X-ray micro analyzer(EPMA) and the atomic ratio of Sr:Bi:Nb with pawer ratio of 120 W/100 W was 1:3:2.

• Korean Journal of Materials Research
• /
• v.12 no.12
• /
• pp.962-966
• /
• 2002

The $SrBi_2$$Nb_2$$O_{9}$ (SBN) thin films were deposited with $SrNb_2$$O_{6}$ / (SNO) and $Bi_2$$O_3$ targets by co-sputtering method. For the growth of SBN thin films, we adopted the various power ratios of two targets; the power ratios of the SNO target to $Bi_2$$O_3$ target were 100 W : 20 W, 100 W : 25 W, and 100 W : 30 W during sputtering the SBN films. We found that the electrical properties of SBN films were greatly dependent on Bi content in films. The $Bi_2$Pt and $Bi_2$$O_3$ phase as second phases occurred at the films with excess Bi content greater than 2.4, resulting in poor ferroelectric properties. The best growth condition of the SBN films was obtained at the power ratio of 100 W : 25 W for the two targets. At this condition, the crystallinity and electrical properties of the films were improved at even low annealing temperature as $700^{\circ}C$ for 1h in oxygen ambient and the Sr, Bi and Nb component in the SBN films were about 0.9, 2.4, and 1.8 respectively. From the P-E and I-V curves for the specimen, the remnant polarization value ($2P_{r}$) of the SBN films was obtained about 6 $\mu$C/c $m^2$ at 250 kV/cm and the leakage current density of this thin film was $2.45$\times$10^{-7}$ $A/cm^2$ at an applied voltage of 3 V.V.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.2
• /
• pp.58-65
• /
• 2016

This study was a preparatory experiment aimed the development of membrane scaffolds for tissue engineering. A PCL composite solution contained sodium chloride(NaCl). PCL porous membrane scaffolds were formed on a glass casting plate using a film applicator and immersed in distilled water to remove the NaCl reaching after drying. NaCl was used as a pore former for a 3 dimensional pore net-work. The dry condition parameters were $4^{\circ}C$, room temperature (RT) and $40^{\circ}C$ for each different temperatures in the drying experiment. SEM revealed the morphology of the pores in the membrane after drying and evaluated the in vitro cytotoxicity for basic bio-compatibility. The macro and micro pores existed together in the scaffold and showed a 3-dimensional pore net-working morphology at RT. The in vitro cytotoxicity test result was "grade 2" in accordance with the criterion for cytotoxicity by ISO 10993-5. The dry condition affected the formation of a 3 dimensional pore network and micro and macro pores. Therefore, these results are expected provide the basic process for the development of porous membrane scaffolds to control degradation and allow drug delivery.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.77-77
• /
• 2017

Titanium and its alloys offer attractive properties in a variety of applications. These are widely used for the field of biomedical implants because of its good biocompatibility and high corrosion resistance. Titanium anodizing is often used in the metal finishing of products, especially those can be used in the medical devices with dense oxide surface. Based on SAE/AMS (Society of Automotive Engineers/Aerospace Material Specification) 2488D, it has the specification for industrial titanium anodizing that have three different types of titanium anodization as following: Type I is used as a coating for elevated temperature forming; Type II is used as an anti-galling coating without additional lubrication or as a pre-treatment for improving adherence of film lubricants; Type III is used as a treatment to produce a spectrum of surface colours on titanium. In this study, we have focused on Type II anodization for the medical (dental and orthopedic) application, the anodized surface was modified with gray color under alkaline electrolyte. The surface characteristics were analyzed with Focused Ion Beam (FIB), Scanning Electron Microscopy (SEM), surface roughness, Vickers hardness, three point bending test, biocompatibility, and corrosion (potentiodynamic) test. The Ti-6Al-4V alloy was used for specimen, the anodizing procedure was conducted in alkaline solution (NaOH based, pH>13). Applied voltage was range between 20 V to 40 V until the ampere to be zero. As results, the surface characteristics of anodic oxide layer were analyzed with SEM, the dissecting layer was fabricated with FIB method prior to analyze surface. The surface roughness was measured by arithmetic mean deviation of the roughness profile (Ra). The Vickers hardness was obtained with Vickers hardness tester, indentation was repeated for 5 times on each sample, and the three point bending property was verified by yield load values. In order to determine the corrosion resistance for the corrosion rate, the potentiodynamic test was performed for each specimen. The biological safety assessment was analyzed by cytotoxic and pyrogen test. Through FIB feature of anodic surfaces, the thickness of oxide layer was 1.1 um. The surface roughness, Vickers hardness, bending yield, and corrosion resistance of the anodized specimen were shown higher value than those of non-treated specimen. Also we could verify that there was no significant issues from cytotoxicity and pyrogen test.

• Korean Journal of Organic Agriculture
• /
• v.20 no.4
• /
• pp.655-668
• /
• 2012

Foliar diseases are major constraints to profitable organic tomato production. Especially, powdery mildew, leaf mold and gray mold of tomato occur severely on organic cultured tomatoes in Korea. This study was conducted to develop organic tomato cultivation technology using environmental-friendly disease control methods (resistance cultivar planting, air circulation fan installation, oil-egg yolk mixtures, and microbial agents). When tomatoes were cultivated in plastic film house installed with air circulation fan, daily range of temperature was decreased by $2{\sim}7^{\circ}C$, average relative humidity was decreased by 1~5% compared to those in plastic house without air circulation fan. Consequently, incidence of tomato leaf mold and tomato gray mold was reduced by 55.0% and 24.4%, respectively. Control effect of microbial agents and oil-egg yolk mixtures against major tomato diseases was examined in plastic house. As a result, the control value of microbial agents against tomato gray mold and tomato leaf mold showed at the range of 49.0~55.9 %(gray mold) and 39.2~58.2%(leaf mold), respectively. The control value of oilegg yolk mixtures against tomato powdery mildew showed 97.6%. Fifteen tomato cultivars were evaluated for disease resistance against leaf mold and powdery mildew in organically cultivated tomato field. Among 15 tomato cultivars, seven cultivars including 'Super-top' were found to be high resistant to tomato leaf mold. Also 'Powerking', one of fifteen tomato cultivars, showed to be high resistant to tomato powdery mildew.

• Journal of the Korean Vacuum Society
• /
• v.11 no.3
• /
• pp.176-182
• /
• 2002

Amorphous $TiO_2$ thin films were deposited on glass substrates by ion beam sputtering in which the ratio of $O_2$/Ar gas used as discharged gas was varied from 0 to 2. After optical and microstructure properties and chemical composition of thin films was analyzed, antireflection coating layers were fabricated with $SiO_2$/$TiO_2$ multi-layers. Thin films deposition was performed at room temperature and ion beam voltage and ion current density for sputtering of target were fixed at 1.2 kV and 200 $\mu\textrm{A}/\textrm{cm}^2$, respectively. Refractive indexs of the deposited $TiO_2$films were 2.40-2.45 at a wavelength of 633 nm. $TiO_2$films had high transmission and stoichiometry when ratio of $O_2$/Ar was 1. Rms roughness of deposited $TiO_2$ film was below 7 $\AA$. In excessive $O_2$ environments, however Rms roughness increased over 50 $\AA$. Transmittance decreased by scattering of rough surface. Reflectance of $SiO_2$/$TiO_2$multi-layers was below 1% in visible light.

• Journal of Mushroom
• /
• v.18 no.1
• /
• pp.115-119
• /
• 2020

This study was conducted to investigate the effect of post-harvest CO₂ treatment on the quality of the 'Gonji-7ho' oyster mushroom. The harvested mushrooms were pre-cooled at 3℃ for 1 day and placed in a gas-tight chamber with 0%, 30%, or 50% of CO₂ concentration for 3 hours at 3℃. Next, 400 g of the oyster mushroom sample was packaged into 20-㎛ thick oriented polypropylene (OPP) film bags and stored at 4℃ for 21 days. Treatment with 30% of CO₂ treatment maintained the highest stipe firmness of the oyster mushrooms during storage. The stipe lightness (CIE L^⁎) was the highest at 14 and 21 days, while the stipe yellowness (CIE b^⁎) was the lowest at 2 and 7 days of storage. Therefore, we concluded that the 30% CO₂ treatment maintained the overall visual quality of the 'Gonji-7ho' oyster mushroom until 17 days of storage at 3℃. Our results suggest that the shelf life of 'Gonji-7ho' oyster mushroom could be extended by the postharvest application of 30% CO₂ for 3 hours during low temperature storage.

• The Korean Journal of Food And Nutrition
• /
• v.26 no.3
• /
• pp.339-344
• /
• 2013

This study is conducted to investigate the shelf life of pork rectum stored at refrigerated temperatures (1, 5 and $10^{\circ}C$). The pH of the boiled pork rectum ($7.1{\pm}0.1$) was slightly higher than that of the raw pork rectum ($6.7{\pm}0.1$). TBA value of the boiled pork rectum was higher than that of raw pork rectum. The TBA values of the raw and boiled pork rectum stored at $10^{\circ}C$ was rapidly increased at 4 days after beginning of preservation. The TBA values of raw and boiled pork rectum stored at $5^{\circ}C$ rapidly increased after 8 and 6 days after beginning of preservation, respectively. VBN values of both raw and boiled rectum preserved at $10^{\circ}C$ were maintained below 20 mg% for 8 days since the beginning of storage. Furthermore, it is preferred that the pork rectum was boiled for 20 minutes at $100^{\circ}C$ to restrain mesophiles, psychrophiles, and coliform bacteria effectively. Thus, the most desirable condition was when the pork rectum was consumed within 6 days and stored at $10^{\circ}C$.

• Food Science of Animal Resources
• /
• v.33 no.3
• /
• pp.390-394
• /
• 2013

The aim of this study was to determine the optimal storage condition of pre-packed Hanwoo beef without freezing. Hanwoo loin was purchased from a local distributor at 48 h after slaughter, then sliced in $1.5{\pm}0.5$ cm thickness, and packed in a polyethylene (PE) tray covered with linear low-density polyethylene (LLDPE) film. The studied factors to set the optimal storage condition were chamber temperature (5, 2.5 and $-1^{\circ}C$ for 14 d), cooling method (direct and indirect cooling system), and ultraviolet (UV) light irradiation for beef surface sterilization (0, 30, 60, and 120 min). The changes of pH, thiobarbituric acid reactive substances (TBARS) and number of aerobic bacteria were measured during storage. Beef samples stored in $-1^{\circ}C$ showed the minimal increasing rate in TBARS and microbial growth. After 15 d of storage, there was no significant difference in pH and TBARS values. However, the microbial population of beef stored in direct type cooling chamber ($4.25{\pm}0.66$ Log CFU/g) was significantly lower than that of beef stored in indirect type chamber ($6.47{\pm}0.08$ Log CFU/g) (p<0.05). After 4 d of storage, 60 or 120 min UV light irradiated beef samples showed significantly lower microbial population, and at 14 d of storage, 60 min UV irradiated beef sample showed significantly lower microbial population ($3.14{\pm}0.43$ Log CFU/g) than control ($4.46{\pm}0.13$ Log CFU/g) (p<0.05). However, TBARS values of 60 or 120 min UV light irradiated beef samples were significantly higher than non-irradiated beef sample after 4 d of storage (p<0.05).