• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.05a
• /
• pp.33-36
• /
• 2011

Recently, It has increased to use ultra high strength concrete. It is effective to mix organic fibers for preventing spalling. But if fiber mixed, flowability of concrete is decreases. The aim of this study is to evaluation of fire resistance performance for fiber-mixed ultra high strength concrete on field application. As a result, flowability of nylon fiber mixed concrete is better than polyethylene fiber mixed. In non-fiber and polyethylene fiber mixed concrete, spalling occurred. And strain converged at 0.004. Also, residual strength could not evaluate. Nylon fiber mixed concrete is effective to prevent spalling. And it remians 50% residual strength compare with compressive strength at room temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.11a
• /
• pp.51-54
• /
• 2009

In this study, the fire resistance test was carried out with a parameter such as fiber(PP+NY) mixed ratio on high strength concrete with 80MPa, and the spalling resistance property was evaluated. Concrete material test was carried out with a parameter such as fiber(PP+NY) mixed ratio(0%, 0.05%, 0.1%, 0.2%) of high strength concrete with 80MPa. Although the flowability and the strength capacity were delicately decreased with a increase of fiber mixed ratio, they satisfied the target limits. As the spalling resistance property after the fire resistance test of 3 hours, the spalling was partly shown on the high strength concrete with fiber(PP+NY) mixed ratio of 0% but, wasn't shown on the high strength concrete with fiber(PP+NY) mixed ratio of 0.05% ~ 0.2%.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.204-205
• /
• 2017

In this study, flowability and strength on ultra high performance concrete(UHPC) pre-mixed binders with fiber was investigated. The flow of UHPC with pre-mixed binders was higher than that of seperate mixing conditions. The UHPC using PVA fiber with high specific surface area showed a low flow compared to steel fiber. An pre-mixing method led to improved strength of UHPC and low deviation of specimens due to dispersion effect of each materials.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.05a
• /
• pp.87-91
• /
• 2008

The study examined fire resistance of concrete followed by change of mixed rate in PP and NY composite fiber and the results were as follows. In the event of fluidity in concrete not set, plane satisfied 600±100, its target slump flow, and fluidity was reduced as organic fiber's mixed rate was increased. Air amount satisfied 3.0±1.0, its target air amount, and didn't have distinct differences in reduction and increase according to organic fiber's kind and change of its mixed rate. However, it had a tendency that fluidity was reduced as the mixed rate was increased. In characteristics of hardening concrete, the 28th day compressive strength followed by organic fiber's kind and change of its mixed rate didn't have a lot of differences and satisfied high strength scope as about 70MPa. In spalling characteristics after fire resistance test, spalling was happened in non-mixture, plane combination, and P1N0. In other combinations, spalling resistance was happened. The relic compressive strength rate was 56%, the best condition, in P3N1(PP0.03%, NY0.01% compositeness) mixing PP fiber with NY fiber at once.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.491-496
• /
• 2001

In recent years, the research and development about the new material proceed rapidly and actively in the building industry. As building structures become bigger, higher and more specialized, so does the demand for material with higher strength. In the future, we will need to research repair and rehabilitation to make high strength concrete mixed steel fibrous building safe. The carbon fiber reinforced plastic bonding method is widely used in reinforcing the existing concrete structure among the various methods. The repair of initiate loaded reinforced high-strength concrete beams mixed steel fibrous with epoxy bonded Carbon Fiber Sheets(CFS) was investigated experimentally. The CFS thickness and length were varied to assess the peel failure at the curtailment of CFS, The behaviour of the repaired beams was represented by load-longitudinal steel strain relation and failure modes were discussed. The test results indicate that CFS is very effective for strengthening the demand beams and controlling deflections of reinforced high strength concrete beams mixed steel fibrous happen diagonal crack, the increase in the number of CFS layers over two layers didn't effect the increase in the strength of beams.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.11a
• /
• pp.81-85
• /
• 2009

In the recent years, the high strength concrete has increasingly been used according to extending market of tall buildings. However, Ministry of Land, transport and Maritime Affairs was established by law with an alternative plan after June 2008 because of the weakness of high strength concrete accompanied spalling phenomena in fire. The mix design of concrete has to properly meet standards which are the spalling resistance of concrete and limited temperature of steel reinforcement. The fire proof concrete mixed fiber has widely been used to meet spalling safety on the many construction sites, the most researches about the fire proof concrete mixed fiber had being carried out focused on fire resistance, compressive strength and cast in place of concrete. But the most important thing is column shortening used the fire proof concrete within the vertical members. In this paper, the fire proof concrete filled spalling safety standards was experimented by required material when the column shortening is revised between normal concrete and fire proof concrete mixed fiber and then the results have done a comparative analysis. Also, The paper aimed to indicate a basic data for revision of column shortening of fire proof concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.5-6
• /
• 2017

Ultra high-strength concrete can prevent spalling by mixed ratio of PP and NY fiber. However, there is a lack of research on the deterioration of strength due to changes in mechanical properties after spalling prevention. In this study, the effect of high temperature on the mechanical properties of 150MPa concrete mixed with PP and NY fiber was evaluated. As a result, mixing PP and NY fiber is judge to be little effect on the mechanical properties of the 150MPa concrete at high temperature.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.44 no.1
• /
• pp.93-102
• /
• 2002

Steel fiber and polymer are used widely for reinforcement material of RC structures because of its excellences of the durability, serviceability as well as mechanical properties. The purpose of this study is to investigate the shear behavior of polymer cement high strength concrete beams mixed with steel fiber. The compressive strength of concrete was based on the 100$\times$200 mm cylinder specimens. The compressive strength of concrete are 320$kgf/cm^2$, 436 $kgf/cm^2$ and 520 $kgf/cm^2$ in the 28 days. The static test was carried out to measure the ultimate load, the initial load of flexural and diagonal cracking, crack patterns and fracture modes. Also, load-strain and load-deflection examined. During the test cracks were sketched against the load values according to the growth of crack. result are as follows; (1) The failure modes of the specimens are increased in rigidity and durability with mixing steel fiber and polymer. (2) The load of initial crack was similar a theory of shear-crack strength. (3) The deflection and strain at failure load of Polymer-steel fiber high strength concrete beams were increased, improving the brittleness of the high strength concrete.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.11 no.1
• /
• pp.1-6
• /
• 2011

To improve fire-resistance of a high strength concrete against explosive spalling under elevated temperature, fibers can be mixed with concrete to provide flow paths of evaporated water within concrete to the free surface. The fiber-mix concrete approach is effective against explosive spalling when the flow path generated from melting fibers at the elevated temperature is interconnected to transport high pressurized evaporated water from the inside concrete to the free surface. The percolation theory can identify the connectivity of the fibers and provide an estimate of the fire-resistance of concrete by investigating layout of fibers. In this study, the correlation between percolation theory and explosive spalling of fiber-mixed high strength concrete is analyzed and the connectivity of the fiber in concrete is stereologically investigated by using virtual specimens of fiber-mixed high strength concrete.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.11 no.2
• /
• pp.45-52
• /
• 2011

To improve fire-resistance of a high strength concrete against spalling under elevated temperature, fibers can be mixed to provide flow paths of evaporated water to the surface of concrete when heated. In this study, the experiment of a column under fire and mechanical loads is conducted and the material model for predicting temperature of reinforcement steel bar and mechanical behavior of fiber-mixed high strength concrete is suggested. The material model in previous studies is modified by incorporating physical behavior of internal concrete and thermal characteristics of concrete at the elevated temperature. Thermo-mechanical analysis of the fiber-mixed high strength concrete column is conducted using the calibrated material model. The performance of the proposed material model is confirmed by comparing thermo-mechanical analysis results with the experiment of a column under fire and mechanical loads.