• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Korean Journal of Crystallography
• /
• v.11 no.2
• /
• pp.95-101
• /
• 2000

Ferroelectric SrBi2Ta2O9 (SBT) thin films of Pt/Ti/SiO2 electrode were fabricated using a sintered SBT target with various Bi2O3 content by rf magnetron sputtering. Good hysteresis loop characteristics were observed in the SBT thin films deposited with 50mol% excess Bi target. SBT thin films crystallized from 650℃ however, good hysteresis loop can be obtained in the film annealed above 700℃. pt/TiO2/SiO2 and Pt/SiO2 electrodes were also used to investigate the Pt electrode dependence of SBT thin films. SBT thin films showed random oriented polycrystalline structure and similar morphology regardless of electrodes with quite different surface morphology. A 0.2㎛ thick SBT film annealed at 750℃ exhibited the remanent polarization (2Pr) of μC/㎠ and coercive voltage(Vc) of 1V at an applied voltage of 5V.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.501-504
• /
• 2003

In this paper, for enhancement of property on a-Si:H TFTs We measure interface characteristics of ferroelectrics thin film and a-Si:H thin film. First, SrTiO$_3$ thin film is deposited bye-beam evaporation. Deposited films are annealed for 1 hour in N2 ambient at 150$^{\circ}C$ ∼ 600$^{\circ}C$. Dielectric characteristics of deposited SrTiO$_3$ films are very good because dielectric constant shows 50∼100 and breakdown electric field are 1∼1.5MV/cm. a-SiN:H,a-Si:H(n-type a-Si:H) are deposited onto SrTiO$_3$ film to make MFNS(Metal/ferroelectric/a-SiN:H/a-Si:H) by PECVD. After the C-V measurement for interface characteristics, MFNS structure shows no difference with MNS(Metal/a-SiN:H/a-Si:H) structure in C-V characteristics but the insulator capacitance value of MFNS structure is much higher than the MNS because of high dielectric constant of ferroelectrics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.723-727
• /
• 2003

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in $Ar/O_2$ atmosphere. SBN30 thin film of $1000{\AA}$ was pre-deposited as a seed layer on $Pt(100)/TiO_2/SiO_2/Si$ substrate followed by SBN60 deposition up to $3000{\AA}$ in thickness. As-deposited SBN60/SBN30 layer was heat-treated at different temperatures of 650, 700, 750, and $800^{\circ}C$ in air, respectively The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. There was no difference in the crystal structure with heat-treatment temperature, but the electric properties depended on the heating temperature and was the best at $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was $15{\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1075, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.85-88
• /
• 2003

$Sr_xBa_{1-x}Nb_2O_6$(SBN, $025{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in Ar/$O_2$ atmosphere. SBN30 thin film of 500 ${\AA}$ was pre-deposited as a seed layer on Pt(l00)/$TiO_2$/$SiO_2$/Si substrate followed by SBN60 deposition up to 4500 ${\AA}$ in thickness. SBN60/SBN30 layer was deposited at different Oxygen amount of 0, 8.1, 17, and 31.8 sccm, respectively. The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. The crystal structure and the electric properties depended on the Oxygen amount, heating temperature and was the best at O2 = 8.1 seem, $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was 13 ${\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1492, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.7
• /
• pp.611-615
• /
• 2003

Eu-doped lead zirconate titanate(Pb$\sub$1.1/(Zr$\sub$0.6/Ti$\sub$0.4/)O$_3$; PZT) thin films on the Pt/Ti/SiO$_2$/Si substrates prepared by a sol-gel method. The effect on structural and electrical properties of PZT thin films measured according to the Eu content. Eu-doping altered significantly dielectric and ferroelectric properties. The remanent polarization and the coercive field decreased with the increasing Eu content. The dielectric constant and the dielectric loss of PZT thin films decreased with the increasing Eu content. The 0.5 mol% of Eu-doped PZT thin film showed improved fatigue characteristic comparing to the undoped PZT thin film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.486-491
• /
• 2002

We have fabricated $Bi_{3.25}La_{0.75}Ti_3O_12$ (BLT) thin films on the Pt/Ti/$SiO_2$/Si substrates using a metalorganic decomposition (MOD) method with annealing temperature from $550^{\circ}C$ to $750^{\circ}C$. The structural properties of BLT films examined by x-ray diffraction (XRD). From XRD analysis. BLT thin films show polycrystalline structure. The layered-perovskite phase was obtained by spin-on films at above $600^{\circ}C$ for 1h. Scanning electron microscopy (SEM) showed uniform surface composed of rodlike grains. The grain size of BLT films increased with increasing annealing temperature. The BLT film annealed at $650^{\circ}C$ was measured to have a dielectric constant of 279, dielectric loss of 1.85(%), remanent polarization of $25.66\mu C/\textrm{cm}^2$, and coercive field of 84.75 kV/cm. The BLT thin films showed little polarization fatigue test up to $3.5{\times}10^9$ bipolar cycling at 5 V and 100 kHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.202-203
• /
• 2007

Ferroelectric SBT($SrBi_2Ta_2O_9$) thin films were deposited on Pt/Ti/$SiO_2$/Si substrate using R.F. magnetron sputtering method. The ferroelectric and electric characteristics were investigated with various post-annealing of Pt at $200{\sim}600^{\circ}C$. Compared with SBT thin film which had not post-annealed, the electrical properties and crystallizations of the SBT thin films were relatively improved by the post-annealing of Pt bottom electrode. The crystallization were characterized by X-ray diffraction (XRD). The electrical properties characteristics were observed by HP 4192A and precision LC.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.66-66
• /
• 2007

Lead zirconate titanate (PZT) is one of the most attractive perovskite-type materials for ferroelectric random access memory (FRAM) due to its higher remanant polarization and the ability to withstand higher coercive fields. We first applied the damascene process using chemical mechanical polishing (CMP) to fabricate the PZT thin film capacitor to solve the problems of plasma etching including low etching profile and ion charging. The $0.8{\times}0.8\;{\mu}m$ square patterns of silicon dioxide on Pt/Ti/$SiO_2$/Si substrate were coated by sol-gel method with the precursor solution of PZT. Damascene process by CMP was performed to pattern the PZT thin film with the vertical sidewall and no plasma damage. The polarization-voltage (P-V) characteristics of PZT capacitors and the current-voltage characteristics (I-V) were examined by change of process parameters. To examine the CMP induced damage to PZT capacitor, the domain structure of the polished PZT thin film was also investigated by piezoresponse force microscopy (PFM).

• Bulletin of the Korean Chemical Society
• /
• v.18 no.1
• /
• pp.56-61
• /
• 1997

Lead zirconate titanate (PZT) thin fills were deposited onto the Pt/Ti/SiO2/Si substrate by the pulsed laser deposition with the second harmonic wavelength (532 nm) of Nd:YAG laser. In order to determine the optimum conditions for the film deposition, the phase of the films were investigated as functions of ambient oxygen pressure, substrate temperature, and laser fluence. Also the chemical composition analysis was conducted for the PZT films deposited under various ambient oxygen pressure. When the distance between substrate and bulk PZT target is set to 20 mm, the optimum conditions have been determined to be 3 torr of oxygen pressure, 1.5 J/cm2 of laser fluence, and 823-848(±10) K range of substrate temperature. At these conditions, perovskite phase PZT films were obtained on platinized silicon. The chemical composition of the films is very similar to that of PZT bulk target. The physical structure of the deposited films analyzed by scanning electron microscopy shows a columnar morphology perpendicular to the substrate surface. Capacitance-Voltage hysteresis loop measurements show also a typical characteristics of ferroelectric thin film. The dielectric constant is found to be 528 for the 0.48 μm thickness of PZT thin film.