• 한국재료학회지
• /
• 제15권3호
• /
• pp.155-160
• /
• 2005

The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is very corrosive fir typical structural materials. So, it is essential to choose the optimum material f3r the process equipment handling molten salt. In this study, the corrosion behavior of Al-Y coated Haynes 263 in a molten salt of $LiCl-Li_2O$ under oxidation atmosphere was investigated at $650^{\circ}C$ for $72\~168$ hours. The corrosion rate of Al-Y coated Haynes 263 was low while that of bare Haynes 263 was high in a molten salt of $LiCl-Li_2O$. Al-Y coated Haynes 263 improved the corrosion resistance better than bare Haynes 263 alloy. An Al oxide layer acts as a protective film which Prohibits Penetration of oxygen. Corrosion Products were formed $Li(Ni,Co)O_2$ and $LiTiO_2$ on bare Haynes 263, but $LiAlO_2,\;Li_5Fe_5O_8\;and\;LiTiO_2$ on Al-Y coated Haynes 263.

• 한국수소및신에너지학회논문집
• /
• 제31권5호
• /
• pp.419-428
• /
• 2020

The kinetics of direct methanation over activated charcoal-supported molybdenum catalyst at 30 bar was studied in a cylindrical fixed-bed reactor. When the temperature was not higher than 400℃, the CO conversion increased with increasing temperature according to the Arrhenius law of reaction kinetics. While XRD and Raman analysis showed that Mo was present as Mo oxides after reduction or methanation, TEM and XPS analysis showed that Mo₂C was formed after methanation depending on the loading of Mo precursor. When the temperature was as high as 500℃, the CO conversion was dependent not only on the Arrhenius law but also on the catalyzed reaction by nanoparticles, which came off from the reactor and thermocouple by metal dusting. These nanoparticles were made of Ni, Fe, Cr and alloy, and attributed to the formation of carbon deposit on the wall of the reactor and on the surface of the thermocouple. The carbon deposit consisted of amorphous and disordered carbon filaments.

• 한국전기전자재료학회논문지
• /
• 제22권4호
• /
• pp.342-349
• /
• 2009

This study investigated the growth characteristics of carbon nanotubes (CNTs) by changing a period of annealing time and a $C_{2}H_{2}/H_2$ flow ratio at temperature as low as $450^{\circ}C$ with inductively coupled plasma chemical vapor deposition. The 1-nm-thick Fe-Ni-Co alloy thin film served as a catalyst layer for the growth of CNTs, which was thermally evaporated on the 15-nm-thick Al underlayer deposited on the 50-nm-thick Ti diffusion barrier. The annealing at low temperature of $450^{\circ}C$ brought about almost no granulation of the catalyst layer, and the CNT growth was not affected by a period of annealing time. A study of changing the flow rate of $C_{2}H_{2}$ and $H_2$ showed that as the ratio of the $C_{2}H_{2}$ flow rate to the $H_2$ flow rate was lowered, the CNTs were grown to be longer With further decreasing the flow ratio, the length of CNTs reached the maximum and then became shorter. Under the optimized gas flow rates, we successfully synthesized CNTs with a uniform length over a 4-inch Si wafer at $450^{\circ}C$.

• 전자공학회논문지
• /
• 제54권3호
• /
• pp.131-137
• /
• 2017

네트워크 기반의 휴대용 전자 제품의 시장 성장으로 전기기기들은 더욱 소형화 되고 있는 추세이고 내부 부품간의 거리가 가까워져 회로 단락의 위험이 높아지고 있다. 회로의 단락 상황에서 유입되는 높은 과전류로 부터 폭발이나 화재 없이 전자기기를 안전하게 보호하기 위해서는 차단용량이 높은 밀폐형 카트리지 퓨즈를 적용해야 하지만 제품의 소형화 추세에 따른 공간의 문제로 해당 퓨즈의 적용이 불가능한 실정이다. 이를 해결하기 위해서 화학적 결합으로 퓨즈 가용체를 보호하는 밀폐형 퓨즈보다 공기의 유입이 자유로울 뿐만 아니라 물리적 결합으로 퓨즈링크를 보호하는 반밀폐형 초소형 퓨즈가 적용되는 것이 적합하지만 높은 차단용량 특성을 구현하는데 한계가 있다. 이에 본 논문에서는 상대적으로 공간을 적게 차지하면서 높은 차단용량을 갖는 반밀폐형 초소형 퓨즈를 위한 퓨즈 가용체 합금과 퓨즈링크의 설계 기술을 통하여 회로의 단락 상황에서 안전성을 확보하였다.

• 대한기계학회논문집
• /
• 제12권5호
• /
• pp.1083-1091
• /
• 1988

본 연구에서는 위의 두번째 연구동향과 맥락을 같이하는 것으로서 스테인리스 강(SUS304)에 대한 진공브레이징 연구 및 탄소강의 진공 브레이징에 대한 연구결과들 을 토대로 하여 SUS304와 탄소강과의 진공브레이징 현상을 연구하였는데 특히 모재의 탄소함유량, 브레이징시간 및 접합부 틈새(joint clearance)등에 따라 접합부에 나타 나는 여러 금속학적 현상의 규명 및 접합강도(joint strength)에 대해 변수들이 미치 는 영향을 연구 하였다.

• 한국표면공학회지
• /
• 제55권6호
• /
• pp.448-459
• /
• 2022

Generally, steel is the most commonly used in the industry because of good strength, processability and cost-effectiveness. Steel can be surface-treated such as coating or used as an alloy by adding elements such as Cr, Ni, Zr, and Al to increase corrosion resistance. However, even if steel is used in same environment corrosion resistance is sharply lowered when it is exposed to a high temperature for a fixed or extended period of time due to an overload or other factors. In particular, the use of hot-dip aluminized plated steel, which is used in high-temperature atmospheres, is increasing due to the surface Al₂O₃ oxide film. This steel necessitates an urgent solution as issues of corrosion resistance limitations often appear. It is an important issue that not only cause analysis but also the research for the surface treatment method that can be solved. Thus, in this study, Cr in which it is expected to be effective in corrosion resistance and heat resistance attempted to deposit on hot dip aluminized plated steel with PVD sputtering. And it was possible to present the surface treatment application of various types of industrial equipment exposed to high temperature and basic design guidelines for use by confirming the corrosion resistance of hot dip Al-Si plated steel with Cr film deposited at high temperature.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2002년도 제3회 최신 분말제품 응용기술 Workshop
• /
• pp.25-37
• /
• 2002

The most important industrial application of gamma radiation in characterizing green compacts is the determination of the density. Examples are given where this method is applied in manufacturing technical components in powder metallurgy. The requirements imposed by modern quality management systems and operation by the workforce in industrial production are described. The accuracy of measurement achieved with this method is demonstrated and a comparison is given with other test methods to measure the density. The advantages and limitations of gamma ray densitometry are outlined. The gamma ray densitometer measures the attenuation of gamma radiation penetrating the test parts (Fig. 1). As the capability of compacts to absorb this type of radiation depends on their density, the attenuation of gamma radiation can serve as a measure of the density. The volume of the part being tested is defined by the size of the aperture screeniing out the radiation. It is a channel with the cross section of the aperture whose length is the height of the test part. The intensity of the radiation identified by the detector is the quantity used to determine the material density. Gamma ray densitometry can equally be performed on green compacts as well as on sintered components. Neither special preparation of test parts nor skilled personnel is required to perform the measurement; neither liquids nor other harmful substances are involved. When parts are exhibiting local density variations, which is normally the case in powder compaction, sectional densities can be determined in different parts of the sample without cutting it into pieces. The test is non-destructive, i.e. the parts can still be used after the measurement and do not have to be scrapped. The measurement is controlled by a special PC based software. All results are available for further processing by in-house quality documentation and supervision of measurements. Tool setting for multi-level components can be much improved by using this test method. When a densitometer is installed on the press shop floor, it can be operated by the tool setter himself. Then he can return to the press and immediately implement the corrections. Transfer of sample parts to the lab for density testing can be eliminated and results for the correction of tool settings are more readily available. This helps to reduce the time required for tool setting and clearly improves the productivity of powder presses. The range of materials where this method can be successfully applied covers almost the entire periodic system of the elements. It reaches from the light elements such as graphite via light metals (AI, Mg, Li, Ti) and their alloys, ceramics ($AI_20_3$, SiC, Si_3N_4, $Zr0_2$, ...), magnetic materials (hard and soft ferrites, AlNiCo, Nd-Fe-B, ...), metals including iron and alloy steels, Cu, Ni and Co based alloys to refractory and heavy metals (W, Mo, ...) as well as hardmetals. The gamma radiation required for the measurement is generated by radioactive sources which are produced by nuclear technology. These nuclear materials are safely encapsulated in stainless steel capsules so that no radioactive material can escape from the protective shielding container. The gamma ray densitometer is subject to the strict regulations for the use of radioactive materials. The radiation shield is so effective that there is no elevation of the natural radiation level outside the instrument. Personal dosimetry by the operating personnel is not required. Even in case of malfunction, loss of power and incorrect operation, the escape of gamma radiation from the instrument is positively prevented.

• 청정기술
• /
• 제25권1호
• /
• pp.14-18
• /
• 2019

여러 금속 부품을 가공하기 위하여 사용된 염화제이철 에칭 폐액은 유가금속인 니켈 등을 함유하고 있다. 본 연구에서는 식각공정을 완료한 에칭폐액을 재생하고 부산물로 나온 니켈 함유 폐액으로부터 정제하여 니켈 금속분말로 제조하는 공정을 개발하였다. 부산물인 니켈함유용액을 철 등의 불순물을 침전 제거하기 위하여 수산화나트륨 수용액을 실험을 통하여 가수분해 중화제로서 선정하였고, 이를 통하여 철 등의 불순물을 pH = 4 조건하에 침전 제거하였다. 그 후, 불순물로 잔류하는 망간 및 아연과 같은 금속이온들을 D2EHPA (Di-(2-ethylhexyl) phosphoric acid)를 사용하여 용매추출 하였다. 정제된 염화니켈은 99% 이상의 순도를 가지고 있으며, 그 후 환원제로 하이드라진을 이용하여 99% 이상의 순도와 약 150 nm의 크기를 가지는 니켈 금속분말로 제조하였다. 염화니켈 및 니켈 금속분말의 성분은 EDTA 적정법과 유도결합 플라즈마 방출분광법(inductively coupled plasma optical emission spectrometer, ICP-OES)을 이용하여 확인하였으며, 전계방사 주사전자현미경(field emission scanning electron microscope, FE-SEM), X-선 회절분석기(X-ray diffraction, XRD) 및 투과전자현미경(transmission electron microscopy, TEM)을 통하여 금속분말의 형태, 입자 크기 및 결정성과 같은 물리적 특성을 확인하였다.

• 마이크로전자및패키징학회지
• /
• 제18권4호
• /
• pp.39-42
• /
• 2011

복합전기도금은 도금 중 반응성이 없는 물질을 첨가하여 도금층 내부에 함께 존재하도록 함으로써 이루어진다. 퍼멀로이는 철과 니켈의 합금을 말하는 것으로써 마모 특성과 내부식성이 우수하고 복합도금을 함으로써 도금층의 잔류응력 완화와 경도증가, 높은 투자율를 나타내기 때문에 산업 여러 분야에 응용된다. 복합도금을 통해 제품의 미세경도를 향상시킬 수 있으며 이는 제품의 수명과 연관된다. 하지만 실리카 나노분말 표면의 수산화기는 표면을 수분에 취약하게 만들고 이는 나노분말의 응집을 발생시켜 균일한 도금층의 형성을 어렵게 하는 요인이 된다. 본 연구에서는 실리카 나노분말의 zeta potential의 측정과 실리카 나노분말의 응집을 줄이기 위하여 전류밀도의 변화, 첨가제의 변화를 살펴보았다. 표면은 전류밀도 20 $mA/cm^2$에서 가장 효과적이었으며 이 때 실리카의 함량은 $50^{\circ}C$에서 9%로 확인되었다. 첨가제에 따라 표면 형상과 공석되는 실리카 나노입자의 함량 차이가 나타났다. 염기성 도금용액에서 sodium lauryl sulfate를 사용하였을 경우 표면이 매끄럽고 공석되는 실리카 나노분말의 양도 높았다.

• 한국주조공학회지
• /
• 제11권6호
• /
• pp.475-481
• /
• 1991

In this study the fabrication technology and mechanical properties of AC8A/$Al_2O_3$ Composites by squeeze casting process were investigated to develope for application as the piston materials that require good friction, wear resistance, and thermal stability. AC8A/$Al_2O_3$ composistes without a porosity and the break of preform were fabricated at the melt temperature of $740^{\circ}C$, the preform temperature of $500^{\circ}C$, and mold temperature of $400^{\circ}C$ under the applied pressure of $1200kg/cm^2$ as the results of the observation of microstructures. As the results of this study, the tensile strength of AC8A/$Al_2O_3$ composites was not increased linearly with $Al_2O_3$ volume fraction and so it seemed not to agree with the rule of mixture, which had been used often in metal matrix composite. Also the tensile strength after thermal fatigue test was little different from that before the test. Consequently it was thought that AC8A/$Al_2O_3$ composites fabricated under our experimental conditions had a good thermal stability and subsequently a good interface bonding. Wear rate(i.e., volume loss per unit sliding distance) of AC8A/$Al_2O_3$ composites was decreased with $Al_2O_3$ volume fraction and the sliding speed at both room temperature and $250^{\circ}C$ and so there was a good correlation between wear rate and hardness. Also the wear rate of AC/8A20% $Al_2O_3$ composities was obtained the value of $1.65cm^3/cm$ at sliding speed of 1.14m/sec as compared with about $3.0\;{\times}10^{-8}cm^3/cm$ hyereutectie Al-Si alloy(Al-16%Si-2%Cu-1%Fe-1%Ni), which applied presently for piston materials. The wear behavior of $Al_2O_3$ composites was observed to a type of abrasive wear by the SEM view of wear surface.