• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.280-281
• /
• 2006

Powder grades pre-alloyed with 1.5-3 wt% chromium can be successfully sintered at the conventional temperature $1120^{\circ}C$ although well-monitored sintering atmospheres are required to avoid oxidation. Mechanical properties of the Cr-alloyed PM grades are enhanced by a higher sintering temperature in the range $1120-1250^{\circ}C$, due to positive effects from pore rounding, increased density and more effective oxide reduction. Astaloy CrM (Fe-3 wt% Cr-0.5 wt% Mo) with 0.6 wt% graphite added obtains an ultimate tensile strength of 1470 MPa and an impact strength of 31 J at density $7.1\;g/cm^3$, after sintering at $1250^{\circ}C$ followed by cooling at $2.5^{\circ}C/s$ and tempering.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.561-562
• /
• 2006

The effect of chemical composition of the sintering atmosphere on density, microstructure and mechanical properties of Fe-3%Mn-(Cr)-(Mo)-0.3%C steels is described. Pre-alloyed Astaloy CrM and CrL, ferromanganese and graphite were used as the starting powders. Following pressing in a rigid die, compacts were sintered at 1120 and $1250^{\circ}C$ in atmospheres having different $H_2/N_2$ ratio and furnace cooled to room temperature. It has been found that the atmosphere composition has negligible effect on the as-sintered properties of the investigated materials.

• 대한금속재료학회지
• /
• 제50권7호
• /
• pp.487-493
• /
• 2012

To analyze the factors on stretch-flangeability for 980 MPa-grade hot-rolled steels, two types of steels (Fe-Cr and Fe-Mo) were manufactured by hot-rolling. Manufactured steels at the low coiling temperature, such as 400 and $500^{\circ}C$, had poor stretch-flangeability due to un-uniformly distributed carbides and a large deviation of interphase hardness. However, when the coiling temperature was set at $650^{\circ}C$ with Fe-Cr steel, 998 MPa of ultimate tensile strength, 19% of total elongation and 65% of the hole expanding ratio were achieved by microstructural constituents of polygonal ferrite (PF) and granular ferrite (GF) dispersed with fine carbides (<50 nm). Therefore, the material to attain 980 MPa with superior formability was the Fe-Cr steel that was precipitation-hardened in polygonal ferrite and granular ferrite at the coiling temperature $650^{\circ}C$.

• 한국재료학회지
• /
• 제9권10호
• /
• pp.1018-1024
• /
• 1999

Sn-3.5Ag 무연합금을 Cu 및 Alloy42 리드프레임에 납땜접합 (solder joint)하고 미세조직, 젖음성, 전단강도, 시효효과를 측정하여 비교하였다. Cu의 경우, 땜납의 Sn기지상안에 Ag(sub)3Sn과 Cu(sub)6Sn(sub)5상이, 그리고 땜납/리드프레임의 경계면에서는 1∼2㎛ 두께의 Cu(sub)6Sn(sub)5상이 형성되었다. Alloy42의 경우, 기지상내에 있는 낮은 밀도의 Ag(sub)3Sn상만이, 그리고 계면에는 0.5∼1.5㎛ 두께의 FeSn(sub)2이 형성되었다. 한편, Cu에 비해 Alloy42 리드프레임에서 퍼짐면적은 크고 접촉각은 작아 더 우수한 젖음성을 나타내었으나, 전단강도는 35%, 연신율은 75%로 낮았다. 180℃에서 1주일간 시효처리 후, Cu 리드프레임에는 계면에 η-Cu(sub)6Sn(sub)5 층외에 ξ-Cu(sub)3Sn층이 성장하였고, Alloy42 리드프레임에는 기지상내에 Ag(sub)3Sn이 구형으로 조대하게 성장하였고, 계면에는 FeSn(sub)2층만이 약 1.5㎛로 성장하였다.

• 소성∙가공
• /
• 제24권1호
• /
• pp.44-51
• /
• 2015

The current study seeks to examine the effects of V and C additions on the mechanical and low thermal expansion properties of a high strength invar base alloy. The base alloy (Fe-36%Ni-0.9%Co-2.75%Mo-0.7Cr-0.23Mn-0.17Si-0.3%C, wt.%) contains $Mo_2C$ carbides, which form as the main precipitate. In contrast, alloys with additions of 0.4%V+0.3%C (alloy A) or 0.4%V+0.45%C (alloy B) contain $Mo_2C$+[V, Mo]C carbides. The average thermal expansion coefficients of these high strength invar based alloys were measured in the range of $5.16{\sim}5.43{\mu}m/m{\cdot}^{\circ}C$ for temperatures of $15{\sim}230^{\circ}C$. Moreover, alloy B showed lower thermal expansion coefficient than the other alloys in this temperature range. For the mechanical properties, the [V, Mo]C improved hardness and strengths(Y.S. and T.S.) of the high strength invar base alloy. T.S.(tensile strength) and Y.S.(yield strength) of hot forged alloy B specimen were measured at 844.6MPa and 518.0MPa, respectively. The tensile fractography of alloy B exhibited a ductile transgranular fracture mode and voids were initiated between the [V, Mo]C particles and the matrix. Superior properties of high strength and low thermal expansion coefficient can be obtained by [V, Mo]C precipitation in alloy B with the addition of 0.4%V and 0.45%C.

• 대한금속재료학회지
• /
• 제48권6호
• /
• pp.523-532
• /
• 2010

Co-application of organic coating and cathodic protection has not provided enough durability to low-alloyed steels inseawater ballast tank (SBT) environments. An attempt has made to study the effect of alloy elements (Al, Cr, Cu, Mo, Ni, Si, W) on general and localized corrosion resistance of steels as basic research to develop new low-allowed steels resistive to corrosion in SBT environments. For this study, we measured the corrosion rate by the weigh loss method after periodic immersion in synthetic seawater at $60^{\circ}C$, evaluated the localized corrosion resistance by an immersion test in concentrated chloride solution with the critical pH depending on the alloy element (Fe, Cr, Al, Ni), determined the permeability of chloride ion across the rust layer by measuring the membrane potential, and finally, we analyzed the rust layer by EPMA mapping and compared the result with the E-pH diagram calculated in the study. The immersion test of up to 55 days in the synthetic seawater showed that chromium, aluminium, and nickel are beneficial but the other elements are detrimental to corrosion resistance. Among the beneficial elements, chromium and aluminium effectively decreased the corrosion rate of the steels during the initial immersion, while nickel effectively decreased the corrosion rate in a longer than 30-day immersion. The low corrosion rate of Cr- or Al-alloyed steel in the initial period was due to the formation of $Cr_2FeO_4$ or $Al_2FeO_4$, respectively -the predicted oxide in the E-pH diagram- which is known as a more protective oxide than $Fe_3O_4$. The increased corrosion rate of Cr-alloyed steels with alonger than 30-day exposure was due to low localized corrosion resistance, which is explained bythe effect of the alloying element on a critical pH. In the meantime, the low corrosion rate of Ni-alloyed steel with a longer than 30-day exposure wasdue to an Ni enriched layer containing $Fe_2NiO_4$, the predicted oxide in the E-pH diagram. Finally, the measurement of the membrane potential depending on the alloying element showed that a lower permeability of chloride ion does not always result in higher corrosion resistance in seawater.

• 한국세라믹학회지
• /
• 제25권5호
• /
• pp.443-448
• /
• 1988

Colored Cubic Zircona(CCZ) single crystals were grown by the skull melting method. The grown crystals were doped with up to 0.1wt% transition (Cu, Ni, Co, Ti, Fe, Mo, Cr, V, Mn) metal ions on ZrO2-Y2O3(9.5~10mol%) and their Optical transmission spectra(λ=300~800nm)data were obtained. Various colors were pronounced due to dopant effects in the grown Crystals.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2008년도 Asian Magnetics Conference
• /
• pp.50.2-50.2
• /
• 2008

• 분석과학
• /
• 제26권1호
• /
• pp.67-72
• /
• 2013

본 연구는 폐플라스틱 재활용 제품(재활용 고무대야)의 올바른 사용을 유도하기위한 기초자료로 활용하고자 수행하였다. 재활용 고무대야의 중금속(Cd, Cr, Cu, Fe, Hg, Pb, Zn) 함량과 용출량을 확인하고 김치제조 시나리오에 따라 배추 시료를 분석하여 재활용 고무대야에서 제조한 김치를 섭취할 경우의 노출량을 산정하였다. 분석결과 재활용 고무대야의 중금속함량은 Fe이 가장 높게 나왔으며 그 다음으로 Cu, Zn, Pb의 함량이 높았다. 16개 시료 중 1 개 시료가 식품공전 기구 및 용기포장 일반기준(Cd, $Cr^{6+}$, Pb, Hg 함량합계 100 mg/kg 이하)을 초과하였다. 용출시험에서는 Fe, Pb, Zn이 검출되었으나 식품공전 합성수지제 용출규격(Pb 1.0 mg/L 이하) 미만이었다. 재활용 고무대야에서 절인 배추시료의 중금속 함량 분석결과 Fe, Pb, Zn이 검출 되었으나 노출량을 산정한 결과 일일최대 섭취한계량 미만이었다. 재활용 고무대야의 시나리오에 따른 노출량 시험결과 유해물질의 함량은 일일 최대 섭취량 미만으로 나타났으나 함량분석결과 기준을 초과한 시료가 있었다. 또한 온도, 시간 등 조건변화에 따른 추가용출 가능성을 배제할 수 없으므로 식품 제조용기로 사용하는 것은 주의가 필요하다.

• 한국환경생태학회지
• /
• 제15권2호
• /
• pp.139-152
• /
• 2001

충남 서부 활석광산 주변의 수계에 대한 원소 함량특성에 대해 알아보고자 대흥 및 광천광산에 대해 수질 및 하상 퇴적물 시료와 함께 광산 주변 토양 및 모암 시료를 채취, 비교하였다. 대흥지역 퇴적물은 대부분 원소에서 SP가 GN에 비해 높았는데 이는 퇴적물 내 유색 및 무색광물 함량 차이로 판단된다. 절대 함량 비교에서 광물 결정구조 내 쉽게 Mg와 치환하는 원소는 낮은비율을, Fe와 치환하는 원소는 높은 비율을 보였는데 이는 퇴적물 내 주 구성광물내 원소 치환특성을 반영하기 때문으로 판단된다. 절대 함량의 감소 순서와 타원소들과 높은 상관관계(>0.85)의 빈도를 보이는 원소들 사이의 차이는 퇴적물 화학조성에 이차광물과 비정질 광물등의 조성도 반영되었음을 암시한다. 대흥지역 지표수는 대부분 원소에서 MSP가 SP와 GN의 중간값을, MSG는 LGN과 MSP의 중간값을 조여 수계의 혼합특성을반영하는 것으로 판단된다. 절대 함량관계에서는 SP는 GW1과 유사했고, GN은 LGN과 유사했으며, 절대함량은(Mg, Fe), (As, Sc), (Mo, V, Se) 순서로 낮아졌다. 광천지역은 갱내수가 천부 지하수에 비해 대부분 원소에서 높은 함량을 보였는데, 이는 갱내수가 더욱더 많은 물-암석반응을 거친 때문으로 판단된다. 절대 함량은 Mg, Br, Fe, (Sc, Cr), (An, Ni, V)순서로 감소하였다. 갱냉수의 지역간 원소 함량 차이는 사문암화가 우세한 광천지역과 활석화가 우세한 대흥지역 모암들 사이의물-암석 상화반응의 차이를 보여주는 것으로 판단된다 두 지역의 상부 토양 및 모암 조성에서 SP가 GN에 비해 높은 Mg 비, Ni, Cr, Co 등 함량을 보였는데, 이는 사문암 지역 내 Mg, Ni, Cr 등이 풍부한 광물들 탓으로 판단된다. 퇴적물과 수질 사이에서는 함량 경향을 뚜렷하지 않았고 원소에 따라 서로 다른 힘량 차이를 보였는데, 이는 퇴적물 원소 함량이 수계 조성을 반영하는 것이 아님을 나타낸다. 상부-토양-암석-수계의 조성관계에서 대흥지역 지표수 중 SP 조성이, 광천지역은 갱냉수가 지하수의 조성에 가까웠다.