Recent high efficiency electronic devices have been found to have heat emission problems. As for LEDs, an excessive increase in the device temperature causes a drop of the luminous efficiency and circuit lifetime. Therefore, heat release in the limited space of such electronic parts is very important. This is a study of the possibility of using a coating of carbon materials as a solution for the thermal emission problem of electronic devices. Powdered carbon materials, cokes, carbon blacks, amorphous graphite, and natural flakes were coated with an organic binder on an aluminum sheet and the subsequent thermal emissivity was measured with an FT-IR spectrometer and was found to be in the range of $5{\sim}20\;{\mu}m$ at $50^{\circ}C$. The emissivity of the carbon materials coated on the aluminum sheet was shown to be over 0.8 and varied according to carbon type. The maximum thermal emissivity on the carbon black coated-aluminum surface was shown to be 0.877. The emissivity of the anodized aluminum sheets that were used as heat releasing materials of the electronic parts was reported to be in the range of 0.7~0.8. Therefore, the use of a coating of carbon material can be a potential solution that facillitates heat dissipation for electronic parts.

• 한국의류학회지
• /
• 제41권1호
• /
• pp.131-140
• /
• 2017

Uniform nanofibers of polyurethane with different content of Juniperus Chinensis extracts (JCE) were successfully prepared by the electrospinning method. We investigated physiochemical properties of prepared compound nanoweb according to various concentrations of Juniperus Chinensis extracts using a Fourier transform infrared (FT-IR) spectrometer, X-ray diffractometer (XRD), thermogravimeter (TGA), and differential scanning calorimeter (DSC). The antibacterial activity of the JCE loaded PU nanofiber was conducted using the disk diffusion test against Gram-positive and Gram-negative bacteria. JCE was induced in the infrared spectra in the absorption band of PU/JCE nanowebs at $3,300cm^{-1}$, $2,960cm^{-1}$, $1,400-1,600cm^{-1}$, and $1,050cm^{-1}$. Thermal stability decreased with increasing JCE content in the PU/JCE nanowebs. The DSC curve of the PU nanoweb shows an endotherm peak at $420^{\circ}C$; in addition, the peak also became smaller and broader with increasing JCE content. The diffraction intensities of PU observed at 2 theta of $20^{\circ}$ decreased with the increasing amount of JCE in the compound nanoweb. In addition, the crystal intensities of the compound nanowebs also decreased along with the JCE content. Structural analysis indicates that JCE and PU are miscible. Juniperus Chinensis incorporated PU nanofibers demonstrated excellent antibacterial properties against both Gram-positive and Gram-negative bacteria.

• 한국결정성장학회지
• /
• 제19권4호
• /
• pp.165-171
• /
• 2009

기존의 합성방법에 사용되는 백금 도가니의 단점을 보완할 수 있는 알루미나 도가니를 사용하여 천연 및 기존의 합성루비와 유사한 적색의 투명한 결정을 성장시켰다. $PbO-B_2O_3$ 가 흔합된 플럭스를 사용하여 $915{\sim}1350^{\circ}C$의 온도에서 약 240시간 실험 후 최대 9.02 ${\times}$ 6.36 mm 투명한 적색의 결정이 성장되었다. 이 결정을 보석학적 기초검사를 통하여 굴절률, 내포물, 비중 등의 특성과 FT-IR, UV-VIS spectrometer 및 XRD 를 사용하여 기존의 합성루비 및 천연루비의 특성과 비교분석하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.254.1-254.1
• /
• 2014

Atmospheric plasma's electron temperature is less than thermal plasma, so it is useful at bio experiment. We have investigated the optical emission spectroscopy (OES) lines by spectrometer during Atmospheric plasma bombardment onto the PBS surface by using an Ar gas flow. Also we have measured the OH radical density inside the solution induced by the Atmospheric plasma bombardment. OH radical species are appeared at 308 nm and 309 nm. Densities of OH radical species has been found to be significantly decreased versus depth of the solution from 2 mm to 6 mm. OH radical density inside the PBS is measured to be about $1.87{\times}1016cm-3$ downstream at 2 mm from the surface under optimized Ar gas flow of 200 sccm in Atmospheric plasma. Also we have investigated cell viability of lung cancer and normal cell after Atmospheric plasma treatment for fixed exposure time in 60 seconds, but different depths. We used SEM, we observed change of cell morphorogy, did experiment about FDA & PI Staining method. It is found that there is selectivity between the lung cancer and lung normal cell, in which cancer cell definitely has higher cell death ratio more than normal cell. We have investigated change of bond structure in FT-IR spectroscopy, the following peaks were observed: and intense O-H peak at 3422 cm-1 and at 2925 cm-1 corresponds to C-H stretch vibrations of methylene group.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.275.2-275.2
• /
• 2014

현재 자동차 분야에서 차량 경량화의 한 수단으로 자동차용 유리를 고강도 투명 플라스틱 소재인 Polycarbonate(PC)로 대체하고자 하는 연구가 이루어지고 있다. 하지만, PC의 낮은 내마모 특성과 자외선에 의한 열화 및 변색 현상은 해결하여야 할 문제점으로 지적되고 있으며, 에너지 소비 저감을 위하여 적외선 영역 반사율(reflectance)이 높은 저방사(low emissivity) 특성이 요구되고 있다. 본 연구에서는, ICP-assisted reactive magnetron sputtering 장비를 이용하여 투과율(transmittance)이 확보되고, 고경도 특성을 갖는 Al-Si-N와 300 nm 파장 이하의 자외선 차단 특성이 있는 SiN:H 그리고 저방사 특성을 위해 Al을 증착하였고, 박막의 증착 순서는 SiN:H 박막을 가장 아래에 증착하고 그 위에 Al/Al-Si-N 박막을 다층으로 형성하였다. 박막의 chemical state와 crystallinity를 확인하기 위하여 XPS(X-ray Photoelectron Spectroscopy), XRD (X-ray Diffraction)를 이용하여 분석하였다. Knoop ${\mu}$-hardness tester와 Taber tester를 이용하여 경도 및 내마모 특성을 분석하였다. 제작된 샘플의 Al-Si-N 박막 경도는 Si 비율에 따라 다른 경도 특성을 갖는데, 실제 Si/(Al+Si) 비율이 24%에서 최대 31 GPa의 경도 값을 갖는 것을 확인하였다. UV-Vis Spectrometer를 이용하여 250 nm~700 nm 파장의 투과율을 측정하였고, 자외선 영역의 경우 SiN:H 박막에 의해 300 nm 이하의 파장에서 2% 이하의 투과율을 확인하였다. 그리고 FT-IR(Fourier Transform Infrared Spectroscopy)를 이용하여 $2.5{\mu}m{\sim}15{\mu}m$ 파장의 반사율을 이용하여 방사율을 측정하였는데, 3*(Al/Al-Si-N) 구조의 다층 박막의 경우 방사율은 0.27로 측정되었다.

• Tribology and Lubricants
• /
• 제32권5호
• /
• pp.141-146
• /
• 2016

The diketopyrrolopyrrole (DPP) pigment is a bicyclic 8-π-electron system containing two lactam units. Typical DPP derivative pigments have melting points of over 350°C and very low solubility in most solvents, and show absorption in the visible region with a molar extinction coefficient of 33,000 dm²mol⁻¹ and strong photoluminescence with maxima in the range 500–600 nm. X-ray structure analyses of DPP show that the whole molecule is almost in one plane. The phenyl rings are twisted out of the heterocyclic plane and the intermolecular hydrogen bonding between neighboring lactam NH and carbonyl units influences the structure of the DPP pigment in the solid state. In this study, mono-N-alkylation and mono-N-arylation were undertaken for Pigment Red 264 or Pigment Orange 73 with alkyl halide and aryl halide, respectively, in the presence of sodium tert-butoxide as a base catalyst to improve the solubility of DPP pigments and their application as CO₂ indicators. The synthetic yield was in the range 11–88%. The indicator dyes are highly soluble in organic solvents and shows pH-dependent absorption (λ_max 501 and 572 nm for the protonated and deprotonated forms, respectively) and emission (λ_max 524 and 605 nm for the protonated and deprotonated forms, respectively) spectra. The mono-N-alkylated and mono-N-arylated DPP pigment was identified by ¹H-NMR (¹H-Nuclear Magnetic Resonance Spectrometer), FT-IR (Fourier Transform Infrared Spectroscopy), and MS (Mass Spectrometry). According to the results of color and hue properties obtained by a color matching analyzer, the synthesized DPP pigment material can be used as a CO₂ indicator.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2001년도 춘계학술발표논문집
• /
• pp.79-79
• /
• 2001

백판지는 포장용기로 사용되기 때문에 인쇄적성 이외에 다양한 후가공적성이 요구 된다. V Varnish Coating도 이러한 후가공적성 중의 하나로서 국내 인쇄소에서는 기계 코팅으로 불리 우며, 목적은 표면에 고분자수지 피막을 입힘으로써 인쇄물의 광택을 높여서 상품가치를 높이고 수운침투와 같은 외부환경의 변화로부터 상품을 안전하게 보관하기 위함이다. arnish C Coating은 인쇄기의 마지막 Unit에서 인쇄와 동일한 방식으로 진행되는데, 코팅액의 배합은 인쇄소와 인쇄물에 따라 상이하다. 본 연구는 Varnish Coating(OI하 기계코팅) 광택향상을 통 한 품질개선 목적으로 수행되었다. 기계 코팅의 특 성 을 파 악 하 기 위 해 서 Gas Chromatography / Mass Spectrometer와 FT -IR Sp e ectrometer를 사용하여 성문운석을 실시해본 결과 코팅액으로 사용되는 광택바니스는 아크 랄과 페놀수지를 툴루엔 계열의 용매에 녹인 용액이고, 흐$\mid$석제로 쓰이는 인쇄바니스는 스티 렌수지를 동일한 용매에 녹인 용액으로 조사되었다. 기계코팅광택 저하현상의 원인파악을 위해서 도공층의 공극구조를 Mercury Porosimeter를 이용하여 파악한 결과 기공의 부피가 상 대적으로 크게 나타났다. 위의 결과를 토대로 기계코팅광택 저하는 코팅액이 과도한 기공부피를 갖는 도공층 내부 로 대부분 홉수되고 표면에 적은 양만이 잔류하기 때문으로 판단하고 해결방안은 도공층의 기공부피를 줄이는 쪽으로 정하였다. Mayor Coater와 QC를 이용하여 Coating Color Formula t tion 번경실힘을 진행하여 도공지 물성을 분석하였다. 그 결과 Double Coating의 Top Color에 서 강력한 상호작용을 하는 Protein과 콜레이를 감량 하고 경질탄산칼숨을 배제하여 기공의 부피를 줄인 경우 기계코팅광택 향상효과가 두드러지게 나타났다. 이러한 Lab 실험을 바탕으로 결정된 Color Formulation에 대한 현장실험을 진행하였고 Lab 평가 및 실인쇄 평가 결과 원하는 수준의 기계코팅광택 향상을 얻을 수 있었다. 몇 차례의 현장실험과 Long-Run Test한 제품들에 대한 물성을 문석한 결과 기계코팅굉택은 인쇄 광택과 같은 경향을 나타냈으며 실협실적으로 간단하게 측정되는 물성 중에서 Air Permeability와 강한 음의 상관관계롤 보였다.

• 공업화학
• /
• 제24권1호
• /
• pp.87-92
• /
• 2013

광촉매 혼성 저온 플라즈마는 폐수에 함유된 유기물을 분해시키는 효과적인 기술이다. 본 연구에서는 광촉매가 결합된 특별히 설계된 유전체 방전 시스템을 골프장이나 감귤농가에서 흔히 살포되는 디크로보스, 카보퓨란 및 메치다치온 살충제의 분해에 적용하였다. 단독 및 병합 시스템에서 살충제의 분해를 평가하였다. 단독 시스템은 UV의 차폐 유무 및 산소기체와 공기에 의한 오존(각종 반응 활성종들 포함) 플라즈마를 이용하였다. 혼성 시스템은 UV로 활성화된 산화아연, 이산화티타늄과 그래파이트 옥사이드와 결합하여 공기에 의한 플라즈마 반응에 적용하였다. 그래파이트 옥사이드는 모사 허머스 법으로 제조하여 FT-IR 분광기로 성능을 측정하였다. 반응시간 60 min에서 UV를 차폐하고 공기를 이용한 플라즈마 반응에 의한 분해성능과 비교하였으며, UV로 활성화된 그래파이트 옥사이드(0.01 g/L)와 결합된 플라즈마 반응은 디크로보스와 카보퓨란의 각각 100% 분해도를 보였다. UV를 활용한 광촉매 혼성 플라즈마는 살충제를 분해시키는 효과적인 대안으로 입증되었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 추계총회 및 학술대회 논문집
• /
• pp.186-186
• /
• 2012

최근 Flexible organic electronics 분야에 대한 관심과 더불어 소자의 산소 및 수분의 침투를 방지하기 위한 투습방지막 연구가 활발히 진행되고 있다. 이에 본 연구에서는 Closed Drift Linear Source(CDLPS) 플라즈마 공정을 이용하여 저온 고속의 $SiO_xC_yH_z$ barrier flims 형성 연구를 진행하였다. HMDSO(hexamethyldisiloxane), TMS(trimethylsilane)와 산소를 기반으로 HMDSO/HMDSO+산소의 비율에 따라 $Si(-O_x)$ 변화에 따른 특성 평가를 진행하였다. X-ray photoelectrom spectroscopy(XPS) 및 Ft-IR spectrometer 측정 시 3.7% 비율에서 실리콘 원소가 산소 라디칼과 효율적인 반응을 함으로써 단일한 $SiO_2$ 박막이 형성됨을 확인 하였다. 그와 반면에 비율의 증가로 인해 다량의 HMDSO 물질이 주입 되었을 시 산소 라디칼과 충분히 반응 되지 못하여 $SiO_2$에 비해 $Si(CH)_x$ 가 많이 함량 된 Polymer like한 $SiO_x$가 많이 형성되었다. 박막의 증착율의 경우에는 3.7%에서 18%로 증가함에 따라 35 nm/min에서 180 nm/min의 증착율을 가지는 것을 확인 하였다. 3.7% 비율의 단일 $SiO_2$ 공정 조건으로 유기태양전지에 형성 하였을 시 소자의 에너지 변환 효율(PCE)이 변화 없는 것을 확인하였다. 이는 기존 공정에 비해 CDLPS 플라즈마 공정의 경우 유기소자에 플라즈마로 인한 열에너지나 이온 충격 에너지로 인한 영향 없는 것을 확인 할 수 있다. 이런 장점을 통해 CDSPS를 이용한 공정 기술은 다양한 유기 소자의 barrier 형성 연구에 큰 도움이 될 것이다.

• 한국응용과학기술학회지
• /
• 제21권4호
• /
• pp.345-351
• /
• 2004

Highly ordered pure-silica MCM-41 materials possessing well-defined morphology have been successfully prepared with surfactant used as a template. The fabrication of mesoporous silica has received considerable attention due to the need to develop more efficient materials' for catalysis, separations, and chemical sensing. The surface modified MCM-41 was used as anadsorbent for biomolecules. Silica-supported organic groups and DNA adsorption on surface modified MCM-41 were investigated by FT-IR and UV-Vis spectrometer, respectively. The use of MCM-41 as the modification of electrode surfaces were investigated electrochemical properties of metal mediators with biomolecules. The modified ITO electrodes increased peak currents for a redox process of $[Ru(bpy)_3]^{2+}$ relative to the bare electrode. The electrochemical detection of DNA by cyclic voltammetry when the current is saturated in the presence of the mediator appeared more sensitive due to a higher catalytic current on the MCM-41 supported electrodes modified by carboxylic acid functional groups. The carboxyl or amine groups on the surface of MCM-41 interact and react with the $-NH_2$ groups of guanine and backbone, respectively. Highly ordered mesoporous materials with organic groups could find applications as DNA sensors.