• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.79-86
• /
• 2009

We successfully fabricated C-doped ex-situ $MgB_2$ wires using two different methods such as mechanical alloying(MA) and combined process(CP) of in-situ and ex-situ. In the MA, the precursor powder was prepared with a mixture of $MgB_2$ and 1 at% C powders by planetary ball milling for 0-100 h. In the CP, on the other hand, C-doped $MgB_2$ powder was prepared with Mg, B, and C powders by in-situ process via compaction, sintering, and crushing. The powders prepared by two methods were loaded into Fe tube and then the assemblages were drawn by a conventional powder-in-tube technique. The MA treatment of C-added $MgB_2$ decreased the particles/grains size and resulted in C-doping into $MgB_2$ after sintering, improving the critical current density($J_c$) in high external magnetic field. For the C-doped $MgB_2$ wire by MA for 25 h, the $J_c$ was $4.1{\times}10^3A/cm^2$ at 5 K and 6.4 T, which was 5.9 times higher than that of pure and untreated $MgB_2$ wire. The CP also provided C-doping into $MgB_2$ and improved the $J_c$ in high magnetic field; the C-doped $MgB_2$ wire fabricated by CP exhibited a $J_c$ being 2.3 times higher than that of the ex-situ wire used commercial $MgB_2$ powder at 5 K and 6.0 T($2.7{\times}10^3A/cm^2\;vs.\;1.2{\times}10^3A/cm^2$).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.371-372
• /
• 2012

We have studied lead-based gapless semiconductors, $PbPdO_2$, which is very sensitive to external parameters such as temperature, pressure, electric field, etc[1]. We have fabricated pure $PbPdO_2$, Co- and Mn-doped $PbPdO_2$ thin films using the pulsed laser deposition. Because of the volatile element of Pb, it is very difficult to grow the films. Note that in case of $MgB_2$, Mg is also volatile element. So in order to enhance the quality of $MgB_2$, some experiments are carried out in annealing with Mg-rich atmosphere [2]. This annealing process with volatile element plays an important role in making smooth surface. Thus, we applied such process to our studies of $PbPdO_2$ thin films. As a result, we found the optimal condition of ex-situ annealing temperature ${\sim}650^{\circ}C$ and time ~12 hrs. The ex-situ annealing brought the extreme change of surface morphology of thin films. After ex-situ annealing with PbO-rich atmosphere, the grain size of thin film was almost 100 times enlarged for all the thin films and also the PbO impurity phase was smeared out. And from X-ray diffraction measurements, we determined highly crystallized phases after annealing. So, we measured electrical and magnetic properties. Because of reduced grain boundary, the resistivity of ex-situ annealed samples changed smaller than no ex-situ sample. And the carrier densities of thin films were decreased with ex-situ annealing time. In this case, oxygen vacancies were removed by ex-situ annealing. Furthermore, we will discuss the transport and magnetic properties in pure $PbPdO_2$, Co- and Mn-doped $PbPdO_2$ thin films in detail.

• 한국초전도학회:학술대회논문집
• /
• 2009.07a
• /
• pp.55-55
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 2009.07a
• /
• pp.92-92
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 2009.07a
• /
• pp.93-93
• /
• 2009

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.4
• /
• pp.12-15
• /
• 2012

$MgB_2$ superconductor is highly sensitive to the Mg content. Even if the samples are synthesized with the appropriate looking stoichiometric ratio, the heat treatment leads to the loss of Mg either to ambiance or to MgO. To avoid it, either excess Mg is added in the starting powder or sealed ampoule annealing is employed. In this paper the effect of open Mg sintering ambiance on the ex-situ $MgB_2$ was studied to enhance its superconducting properties. The open Mg ambiance was created to avoid any overpressure of Mg by providing a hole in Fe tube used as sample holder. The decrease in resistivity of the synthesized sample was observed through the increased temperature dependence of electron-phonon interactions. A clear enhancement in the superconducting cross-sectional area and hence the in-field critical current density is obtained.

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.81-81
• /
• 2008

• 한국초전도학회:학술대회논문집
• /
• 2009.07a
• /
• pp.103-103
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.87-87
• /
• 2007

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.77-77
• /
• 2008