• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.418-419
• /
• 2006

We investigate the influence of the ambient gas during thermal annealing on the photoluminescence (PL) properties of europium-silicate thin films. The films were fabricated on substrates by using a radio-frequency magnetron sputtering method and subsequent rapid thermal annealing (RTA). The mechanism for the formation of the europium silicates during the annealing process was investigated by using X-ray diffraction (XRD) spectroscopy, Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). A series of narrow PL spectra from $Eu^{3+}$ ions was observed from the film annealed in $O_2$ ambient. Broad PL spectra associated with $Eu^{2+}$ ions, with a maximum intensity at 600 nm and a FWHM of 110 nm, were observed from the thin film annealed at $1000^{\circ}C$ in $N_2$ ambient.

• 한국전기전자재료학회논문지
• /
• 제20권3호
• /
• pp.263-267
• /
• 2007

We investigate the influence of the ambient gas during thermal annealing on the photoluminescence (PL) properties of europium-silicate thin films. The films were fabricated on substrates by using a radio-frequency magnetron sputtering method and subsequent rapid thermal annealing (RTA). The mechanism for the formation of the europium silicates during the annealing process was investigated by using X-ray diffraction (XRD) spectroscopy, Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). A series of narrow PL spectra from $Eu^{3+}$ ions was observed from the film annealed in $O_2$ ambient. Broad PL spectra associated with $Eu^{2+}$ ions, with a maximum intensity at 600 nm and a FWHM of 110 nm, were observed from the thin film annealed at $1000^{\circ}C$ in $N_2$ ambient.

• 한국전기전자재료학회논문지
• /
• 제19권11호
• /
• pp.1020-1024
• /
• 2006

Europium$(Eu^{2+}\;or\;Eu^{3+})$-activated calcium aluminium silicate phosphors were synthesized for the first time and the structures and luminescence characteristics of these phosphors were investigated. The phosphors in this study emitted blue, green, and even red light depending on the starting milterials and annealing conditions for synthesis. In addition, the structure was also changed when the different starting materials were used. When $CaCO_3$ was used as a starting material, tetragonal $Ca_2Al_2SiO_7$ was formed. However, pure green light was emitted when the annealing was conducted in reduced atmosphere and red one was emitted by annealing in air. In the case of $CaSiO_3$ as a starting material, triclinic $CaAl_2Si_2O_8$ was formed and only pure blue emission was observed. Moreover, this blue phosphor exhibited higher intensity than that of commercial YAG:Ce phosphor, which showed the possibility of application on the phosphor for new light source such as a UV-LED.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.430-431
• /
• 2009

In this study, europium doped strontium silicate ($Sr_2SiO_4:Eu^{2+}$) phosphor has been synthesized by conventional solid-state method and investigated luminescent characteristic. $SrCO_3$ and $SiO_2$ were mixed together by 2:1 mole ratio. Also $NH_4Cl$ was added as a flux. The mixture were sintered at $800^{\circ}C$, $1000^{\circ}C$ for 3h under the atmosphere (5% $H_2$/95% $N_2$). This phosphor can be applicated to the yellow phosphor for white LED because it has yellow emission band (540nm), which emits efficiently under the 370nm excitaion energy.

• 대한화학회지
• /
• 제50권2호
• /
• pp.137-140
• /
• 2006

Eu2+를 활성제로 한(Sr,Ba)2Ga2SiO7 녹색 형광체를 일반적인 고상 반응으로 합성하였고, 그 합성된 형광체의 광발광 특성을 연구하였다. 형광체 제조 시, 마노유발에서 보다 효과적인 혼합을 위하여 아세톤을 사용하여 혼합하였다. 또한 25%H2/75%N2의 혼합기체를 이용한 환원조건에서 단순한 공정으로 형광체를 합성하였다. 이 형광체는 405 nm의 여기 파장하에서 효율적으로 발광되는 녹색 밴드(513 nm)를 갖고 있기 때문에 백색 LED(Light Emitting Diode)램프에 응용할 수 있다.

• 공업화학
• /
• 제25권5호
• /
• pp.455-462
• /
• 2014

유러퓸-활성화 스트론튬 오쏘실리케이트($Sr_2SiO_4:Eu^{2+}$) 황색 형광체 분말의 소수성 코팅을 위하여 상압 유전체배리어 방전 플라즈마가 사용되었다. 전구물질은 헥사메틸다이실록세인(HMDSO), 톨루엔 및 n-헥세인이었으며, 운반기체는 아르곤이었다. 엑스선 회절분석 결과 플라즈마 코팅 처리 후에도 오쏘실리케이트의 격자구조는 변화가 없는 것으로 나타났다. 플라즈마 코팅된 형광체 분말의 특성은 주사전자현미경, 형광분광광도계, 접촉각 분석을 통해 조사되었다. HMDSO를 사용한 형광체 분말의 소수성 코팅시 물 접촉각은 $21.3^{\circ}$ (코팅 전)에서 $139.5^{\circ}$ (최대 $148.7^{\circ}$)로 증가되었고, 글리세롤 접촉각은 $55^{\circ}$ (코팅 전)에서 $143.5^{\circ}$ (최대 $145.3^{\circ}$)로 증가되었는데, 이 결과는 형광체 분말 표면에 소수성 박막 층이 잘 형성되었음을 나타낸다. 퓨리에변환적외선분광기 및 엑스선광전자분광기를 이용한 표면분석을 통해서도 형광체 분말에 소수성 박막 층이 잘 형성되어 있음을 알 수 있었다. HMDSO를 사용한 소수성 코팅 후 형광체의 광발광 효율이 증가하는 것으로 나타났으나, 톨루엔과 n-헥세인을 전구물질로 사용했을 때는 광발광 효율이 다소 저하되었다. 본 연구의 결과는 유전체배리어방전 플라즈마가 분말 형태인 형광체의 코팅에 이용될 수 있는 실용적인 방법임을 나타낸다.