• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.1
• /
• pp.30-34
• /
• 2016

In this paper, we report that selective etching on N-polar face by EC (electro-chemical)-etching effect on the reduction of bowing and strain of FS (free-standing)-GaN substrates. We applied the EC-etching to concave and convex type of FS-GaN substrates. After the EC-etching for FS-GaN, nano porous structure was formed on N-polar face of concave and convex type of FS-GaN. Consequently, the bowing in the convex type of FS-GaN substrate was decreased but the bowing in the concave type of FS-GaN substrate was increased. Furthermore, the FWHM (full width at half maximum) of (1 0 2) reflection for the convex type of FS-GaN was significantly decreased from 601 to 259 arcsec. In the case, we confirmed that the EC-etching method was very effective to reduce the bowing in the convex type of FS-GaN and the compressive stress in N-polar face of convex type of FS-GaN was fully released by Raman measurement.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.7
• /
• pp.594-598
• /
• 2008

The metal catalyst particles which there is as impurities on a tip part of carbon nanotube (CNT) are not good to apply it to a nano-electronic device. It was very important the opening of CNT-tip to fix a target bio material and a material to accept in CNT in a biosensor, so we performed $HNO_3$ wet etching to remove the metal catalyst particle which there was on a tip part of CNT grown up in the study and observed the opened CNT-tip with etching time. We synthesized the CNTs using a HF-PECVD method and choses the CNT length of 700 nm for the application of nano-electronic device such as a biosensor etc.. We observed the opened CNT-tip with wet etching times of $HNO_3$ (10, 30, 60 min). From the results, we observed that the CNT-tip was opened with the increase of wet etching time lively. In case of CNTs etched during 60 min, we confirmed that there was not the ratio of Ni included in CNTsI as catalyst. Conclusively, in the case of CNT etched for 60 minutes, it is completely good for application of a biosensor and, in addition, the metal-free CNTs will contribute to the application of other nanoelectronic devices.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.860-863
• /
• 2002

In this study, Ag thin films deposited on LCD-grade glass were etched using inductively coupled fluorine-based plasmas and the effect of various $CF_4$-based gas mixtures on the Ag etching characteristics were studied. When $CF_4$-based gas mixtures were used with $N_2$, due to the very low vapor pressure of etch products, etch products remained on the substrate after the etching. However, when $CF_4$ used with Ar, residue-free Ag etching could be obtained due to the removal of etch product by sputtering by $Ar^+$ ions.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.278-278
• /
• 2011

수소 중성입자빔을 이용한 silicon etching은 기존의 silicon etching 공정 가스(Fluorine이나 Chlorine 계열의 가스) 사용 시 배출되는 유해 가스로 인한 지구 온난화 방지 및 폐기물 처리에 추가적인 비용이 발생하지 않는 친환경 etching 공정이다. 본 연구에 사용된 수소 중성입자빔을 발생시키기 위한 플라즈마 소스는 낮은 압력에서 높은 플라즈마 밀도를 발생시킬 수 있는 ECR 플라즈마 소스를 사용하였으며 중성입자빔의 에너지를 조절할 수 있는 중성화판과 플라즈마로부터의 전하손상을 방지할 수 있어 charge free 공정을 가능하게 하는 Limiter로 구성되어 있다. 본 연구에서는 플라즈마 밀도, 공정 압력 그리고, 중성입자빔의 에너지를 조절하여 수소 중성입자빔을 이용한 poly-crystal silicon과 a-Si:H 간의 etch rate와 etching selectivity를 관찰하였다.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.813-818
• /
• 1998

A simple method to measure the elastic modulus E and Poisson's ratio v of diamod-like carbon (DLC) films deposited on Si wafer was suggested. Using the anisotropic etching technique of Si we could make the edge of DLC overhang free from constraint of Si substrate. DLC film is chemically so inert that we could not on-serve any surface damage after the etching process. The edge of DLC overhang free from constraint of Si substrate exhibited periodic sinusoidal shape. By measuring the amplitude and the wavelength of the sinu-soidal edge we could determine the stain of the film required to adhere to the substrate. Since the residual stress of film can be determine independently by measurement of the curvature of film-substrate com-posite we could calculated the biaxial elastic modulus E/(1-v) using stress-strain relation of thin films. By comparing the biaxial elastic modulus with the plane-strain modulus E/(1-{{{{ { v}^{2 } }}) measured by nano-in-dentation we could further determine the elastic modulus and Poisson's ratio independently. This method was employed to measure the mechanical properties of DLC films deposited by {{{{ { {C }_{6 }H }_{6 } }} rf glow discharge. The was elastic modulus E increased from 94 to 169 GPa as the {{{{ { V}_{ b} / SQRT { P} }} increased from 127 to 221 V/{{{{ {mTorr }^{1/2 } }} Poisson's ratio was estimated to be abou 0.16∼0.22 in this {{{{ { V}_{ b} / SQRT { P} }} range. For the {{{{ { V}_{ b} / SQRT { P} }} less than 127V/{{{{ {mTorr }^{1/2 } }} where the plastic deformation can occur by the substrate etching process however the present method could not be applied.

• Journal of the Semiconductor & Display Technology
• /
• v.21 no.3
• /
• pp.57-62
• /
• 2022

The plasma resistance of multi-component glasses containing La, Gd, Ti, Zn, Y, Zr, Nb, and Ta was analyzed in this study. The plasma etching was performed via inductively coupled plasma-reactive ion etching (ICP-RIE) using CF₄/O₂/Ar mixed gas. After the reaction, the glass with a low fluoride sublimation temperature and high content of P, Si, and Ti elements showed a high etching rate. On the other hand, the glass containing a high fluoride sublimation temperature component such as Ca, La, Gd, Y, and Zr exhibited high plasma resistance because the etch rate was lower than that of sapphire. Glass with low plasma resistance increased surface roughness after etching or nanoholes were formed on the surface, but glass with high plasma resistance showed little change in surface microstructure. Thus, the results of this study demonstrate the potential for the development of plasma-resistant glasses (PRGs) with other compositions besides alumino-silicate glasses, which are conventionally referred to as plasma-resistant glasses.

• The korean journal of orthodontics
• /
• v.37 no.4
• /
• pp.283-292
• /
• 2007

The purpose of this study was to evaluate the clinical usefulness of 4 self etching primers by measuring the shear bond strength of orthodontic brackets and examining the failure pattern of bracket-tooth interfaces. Methods: Seventy-five, defect-free, premolars were randomly assigned into five groups: control group (37% phosphoric acid + Transbond XT primer) and self etching primer treated groups (Transbond Plus self etching primer, Unifil bond, Clearfil SE bond, and Adhese). The shear bond strength was measured with a universal testing machine and the amount of residual adhesive remaining on the brackets after debonding was assessed by the adhesive remnant index (ARI). Results: The results showed that the groups conditioned with self etching primer had significantly lower shear bond strength than the control group (p < 0.05), although clinically acceptable. However, there were no significant differences in shear bond strength among the self etching primer groups (p > 0.05). Evaluation of the ARI scores indicated there was less resin remnant on the teeth in the groups conditioned with self etching primers, although not statistically significant. Conclusion: The results of this study suggest that all four of the self etching primers have shown acceptable bond strength for clinical use.

• Clean Technology
• /
• v.9 no.2
• /
• pp.57-61
• /
• 2003

A novel nitric acid-free desmut solution has been developed to remove smut, which is produced from a NaOH etching, on the surface of aluminum alloy metal in metal surface treatment processes. Comparing with the performance of 5% $HNO_3$ desmut solution, the mixed acid solution containing 2% $H_2O_2$, 0.5% HF, and 10% $H_2SO_4$ shows the same effect of smut removal for aluminum alloy samples of A16061 and A15052. To examine the surface alterations of the aluminum samples, in addition, the surface analysis is carried out with scanning electron microscopy (SEM) and electron probe microanalysis (EPMA).

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.136-149
• /
• 1996

The effects of various All-Etching Agents (10% phosphoric acid, 10% maleic acid and 10 % citric acid) and 32 % phosphoric acid and varied etching time were evaluated by observing the morphology of the etched enamel surfaces using Scanning electron microscopy and by measuring the shear bond strength of a composite resin to human enamel. A total of 156 extracted premolar and molar teeth free of irregularities were employed in this study. Specimens for the observation of enamel morphology were divided into 12 groups of 3 teeth each, based on the type of etchant used and application time. After exposure to the etching agent specimens were washed air-dried and then glued to aluminum stubs and coated with a layer of gold for examination in the scanning electron microscope. Specimens for the evaluation of bond strength were divided into 12 groups of 10 teeth each also based on the type of etchant used and application time. After exposure to the etching agent the specimens were washed, air-dried and a thin layer of bonding agent was applied using a brush. Z 100 composite resin was light cured to the surface and stored at $37^{\circ}C$, 100% humidity for 7 days. An Instron Universal Testing Machine was used to apply a shearing force at $90^{\circ}$ angle from the enamel surface. It is concluded from this study that commercial All-etching agents can be used with a 15-second etching without adversely affecting retention of dental resin materials. At the same time, the acid concentration is probably a suitable compromise regarding the acid's function as a dentin demineralizing all-etch conditioning agent. The following results were obtained. 1. Specimens etched with 10 % citric acid showed a random superficial etching pattern which could not be related to prism morphology. 2. Specimens etched with 10 % and 32 % phosphoric acid and 10 % maleic acid showed a type I pattern in which core material was preferentially removed leaving the prism peripheries relatively intact or a type II pattern in which prism peripheries were preferentially removed. This delineation became more distinguished as etching time was increased. 3. All-Etching Agents and 32 % phosphoric acid showed a statistically significant higher shear bond strength at 15 seconds etching time.(p<0.05) 4. 10 % maleic acid and 32 % phosphoric acid exhibited a statistically significant higher shear bond strength than 10 % phosphoric and citric acid at 15 seconds etching time.(p<0.05).

• 전기의세계
• /
• v.34 no.8
• /
• pp.470-475
• /
• 1985

우주물질의 대부분이 플라즈마 상태에 있지마는 지구상에서는 천둥이 칠 때 생기는 방전이나 극지방에서 볼 수 있는 오로라와 같이 극히 일부분이 자연상태의 프라즈마로 존재한다. 지금까지 플라즈마의 이용은 그것이 내는 밝은 빛을 이용한 조명이나, 높은 열을 이용한 용접이나 절단이 고작이었으나, 최근에 들어 초고온, 고밀도 플라즈마를 이용한 핵융합 에너지 연구나 Free Electron Laser나 Gyrotron과 같이 새로운 Radiation Source로써 종래의 Source가 만들지 못하던 주파수 영역이나 Glow Discharge에서 생기는 저온 Plasma를 이용한 Plasma Etching PECVD(Plasma Enhanced CHemical Vapor Deposition), Plasma Ashing, Sputtering등은 VLSI의 제조에 필요불가결한 공정의 일부분이 되고 있다. 앞으로 수회에 걸쳐 본 기술해설란을 통하여 이들 Plasma의 이용 기술을 소개하고자 하며 본회에서는 그중에서 Plasma Etching에 대해서 그 원리와 기술상의 특징을 살펴보고자 한다.