THE EFFECTS OF VARIOUS ALL-ETCHING AGENTS AND VARIED ETCHING TIME ON ENAMEL MORPHOLOGY AND BOND STRENGTH

수종의 All-Etching Agent와 산부식시간에 따른 법랑질 산부식형태 및 전단 결합강도에 관한 연구

The effects of various All-Etching Agents (10% phosphoric acid, 10% maleic acid and 10 % citric acid) and 32 % phosphoric acid and varied etching time were evaluated by observing the morphology of the etched enamel surfaces using Scanning electron microscopy and by measuring the shear bond strength of a composite resin to human enamel. A total of 156 extracted premolar and molar teeth free of irregularities were employed in this study. Specimens for the observation of enamel morphology were divided into 12 groups of 3 teeth each, based on the type of etchant used and application time. After exposure to the etching agent specimens were washed air-dried and then glued to aluminum stubs and coated with a layer of gold for examination in the scanning electron microscope. Specimens for the evaluation of bond strength were divided into 12 groups of 10 teeth each also based on the type of etchant used and application time. After exposure to the etching agent the specimens were washed, air-dried and a thin layer of bonding agent was applied using a brush. Z 100 composite resin was light cured to the surface and stored at $37^{\circ}C$, 100% humidity for 7 days. An Instron Universal Testing Machine was used to apply a shearing force at $90^{\circ}$ angle from the enamel surface. It is concluded from this study that commercial All-etching agents can be used with a 15-second etching without adversely affecting retention of dental resin materials. At the same time, the acid concentration is probably a suitable compromise regarding the acid's function as a dentin demineralizing all-etch conditioning agent. The following results were obtained. 1. Specimens etched with 10 % citric acid showed a random superficial etching pattern which could not be related to prism morphology. 2. Specimens etched with 10 % and 32 % phosphoric acid and 10 % maleic acid showed a type I pattern in which core material was preferentially removed leaving the prism peripheries relatively intact or a type II pattern in which prism peripheries were preferentially removed. This delineation became more distinguished as etching time was increased. 3. All-Etching Agents and 32 % phosphoric acid showed a statistically significant higher shear bond strength at 15 seconds etching time.(p<0.05) 4. 10 % maleic acid and 32 % phosphoric acid exhibited a statistically significant higher shear bond strength than 10 % phosphoric and citric acid at 15 seconds etching time.(p<0.05).