• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.71-74
• /
• 2006

High $J_c$ over 1 $MA/cm^2$ YBCO film has been successfully prepared using nitrate precursors by spray pyrolysis method. Aerosol drolpets generated using a concentric spray nozzle were directly sprayed on a $LaAlO_3$(100) single crystal substrate. The cation ratio of precursor solution was Y:Ba:Cu=1:2.65:1.35. The distance between nozzle and substrate was 15 cm. Deposition temperature was ranging from $750^{\circ}C\;to\;800^{\circ}C$. Deposition pressure was 100 Torr, and oxygen partial pressure was varied from 10 Torr to 50 Torr. The microstructure, phase formation, texture development and superconducting properties of deposited films were largely changed with oxygen partial pressure. Deposited films showed a texture with(001) planes parallel to substrate plane. High quality film was obtained when film was deposited at $760^{\circ}C$ with an oxygen partial pressure of 30 Torr. The critical current density($J_c$) of the YBCO film was 1.75 $MA/cm^2$ at 77 K and self-field.

• Korean Journal of Crystallography
• /
• v.14 no.2
• /
• pp.51-55
• /
• 2003

SrTiO₃ (STO) thin fims were deposited on the biaxially textured Ni-3 wt%W alloy substrates to be used as a single buffer layer for YBa₂CU₃O/sub 7-8/(YBCO) coated conductor. Thin films of YBCO and STO were deposited using pulsed laser. The deposition condition for epitaxial growth of STO on the textured metal was identified, and YBCO coated conductor with a single STO buffer layer with critical current density of 1.2 MA㎠ at 77 K under zero magnetic field and critical temperature of 86 K, was fabricated.

• Steel and Composite Structures
• /
• v.46 no.4
• /
• pp.471-483
• /
• 2023

This paper presents an analytical hyperbolic theory based on the refined shear deformation theory for mechanical stability analysis of the simply supported advanced composites plates (exponentially, sigmoidal and power-law graded) under triangular, trapezoidal and uniform uniaxial and biaxial loading. The developed model ensures the boundary condition of the zero transverse stresses at the top and bottom surfaces without using the correction factor as first order shear deformation theory. The mathematical formulation of displacement contains only four unknowns in which the transverse deflection is divided to shear and bending components. The current study includes the effect of the geometric imperfection of the material. The modeling of the micro-void presence in the structure is based on the both true and apparent density formulas in which the porosity will be dense in the mid-plane and zero in the upper and lower surfaces (free surface) according to a logarithmic function. The analytical solutions of the uniaxial and biaxial critical buckling load are determined by solving the differential equilibrium equations of the system with the help of the Navier's method. The correctness and the effectiveness of the proposed HyRPT is confirmed by comparing the results with those found in the open literature which shows the high performance of this model to predict the stability characteristics of the FG structures employed in various fields. Several parametric analyses are performed to extract the most influenced parameters on the mechanical stability of this type of advanced composites plates.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.45 no.9
• /
• pp.79-84
• /
• 2008

Switching speeds increase in both frequency and the transition rate of edges. Inadequate forecast for simultaneous switching signals may cause designing the power planes without sufficient current capability. The delay of critical signals in a chip can be therefore inadvertently increased and the situation makes it hard to debug issues. It is important to find the degree of increased switching during the debugging or chip characterization phases. This paper proposes the interpolation method to predict the switching density in a design. The interpolation was achieved by utilizing the dependencies between switching frequency and the delay appeared in a ring oscillator. The ring oscillator was primarily used to accumulate the effects of the ground bounce by higher switching. The result of interpolation was demonstrated using DongBu Hitec 0.18um CMOS technology.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.108-112
• /
• 2006

We fabricated Bi-2212/$SrSO_4$ bulk superconductors by the casting process and evaluated the effects of the powder mixing method and annealing temperature on the texture, microstructure, and critical current. In the process, the Bi-2212 powders were mixed with $SrSO_4$ by hand-mixing(HM) and planetary ball milling(PBM) method and then the powder mixtures were melted at $1100^{\circ}C{\sim}1200^{\circ}C$, solidified, and annealed. We observed that the rod made by the PBM had a more homogeneous microstructure and smaller $SrSO_4$ and second phases than that of the rod made by the HM, resulting in increased $I_c$. The $I_c$ of the rod also depended on the annealing temperature and the highest $I_c$ was obtained to be 200 A when prepared by HM at $1200^{\circ}C$ and annealed at $810^{\circ}C$ which is probably due to the moderate density and 2212 texture and the smaller and less second phase compared to that at higher temperature. The possible causes of the variations of $I_c$ with the powder mixing method and annealing temperature were related to the microstructural evolution based on the SEM, EPMA, and DTA analyses.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.59-64
• /
• 2006

High $J_c\;YBa_2Cu_3O_x$ superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. Coating solutions were prepared by dissolving Y-, Ba- and Cu-acetates in DCA solvent followed by drying in rota vapor to obtain the blue gel that is diluted in methanol and 2-methoxyethanol for adjusting the cation concentration. DCA-MOD precursor solution was coated on a single crystal(001) $LaAlO_3(LAO)$ substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ in flowing oxygen atmosphere with a 7.2% humidity. Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. X-ray diffraction analysis showed that YBCO grains grew with a (001) preferred orientation. A High critical current density($J_c$) of 1.28 $MA/cm^2$(@77 K and self-field) was obtained id. the YBCO film prepared using 2-methoxyethanol as a solvent.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.623-626
• /
• 2005

Toward the practical applications, on operation of conduction-cooled HTS SMES at temperatures well below 77 K should be investigated, in order to take advantage of a greater critical current density of HTS and considerably reduce the size and weight of the system. Recently, research and development concerning application of the conduction-cooled HTS SMES that is easily movement are actively progressing in Korea. Electrical insulation under cryogenic temperature is a key and an important element in the application of this apparatus. Using multi wrapped copper by polyimide film for HIS SMES, the breakdown characteristics of models for turn-to-turn, that is surface contact model, were investigated under ac and impulse voltage at 77 K. A material that is Polyimide film (Kapton) 0.025 mm thickness is used for multi wrapping of the electrode. Statistical analysis of the results using Weibull distribution to examine the wrapping number effects on breakdown voltage under ac and impulse voltage in $LN_2$ was carried.

• Journal of Electrochemical Science and Technology
• /
• v.15 no.1
• /
• pp.67-95
• /
• 2024

Direct alcohol fuel cells (DAFCs) have gained much attention as promising energy conversion devices due to their ability to utilize alcohol as a fuel source. In this regard, Molybdenum-based electrocatalysts (Mo-ECs) have emerged as a substitution for expensive Pt and Ru-based co-catalyst electrode materials in DAFCs, owing to their unique electrochemical properties useful for alcohol oxidation. The catalytic activity of Mo-ECs displays an increase in alcohol oxidation current density by several folds to 1000-2000 mA mg_Pt^-1, compared to commercial Pt and PtRu catalysts of 10-100 mA mg_Pt^-1. In addition, the methanol oxidation peak and onset potential have been significantly reduced by 100-200 mV and 0.5-0.6 V, respectively. The performance of Mo-ECs in both acidic and alkaline media has shown the potential to significantly reduce the Pt loading. This review aims to provide a comprehensive overview of the bifunctional mechanism involved in the oxidation of alcohols and factors affecting the electrocatalytic oxidation of alcohol, such as synthesis method, structural properties, and catalytic support materials. Furthermore, the challenges and prospects of Mo-ECs for DAFCs anode materials are discussed. This in-depth review serves as valuable insight toward enhancing the performance and efficiency of DAFC by employing Mo-ECs.

• Journal of Powder Materials
• /
• v.18 no.2
• /
• pp.149-158
• /
• 2011

Electro-Discharge Sintering (EDS) employs a high-voltage/high-current-density pulse of electrical energy, discharged from a capacitor bank, to instantaneously consolidate powders. In the present study, a single pulse of 0.57-1.1 kJ/0.45 g-atomized spherical $Ti_{52}Zr_{28}Ni_{20}$ powders in size range of 10~30 and $30\sim50{\mu}m$ consisting of ${\beta}$-(Ti, Zr) and icosahedral phases were applied to examine the structural evolution of icosahedral phase during EDS. Structural investigation reveals that high electrical input energy facilitates complete decomposition of icosahedral phase into C14 laves and ${\beta}$-(Ti, Zr) phases. Moreover, critical input energy inducing decomposition of the icosahedral phase during EDS depends on the size of the powder. Porous Ti and W compacts have been fabricated by EDS using rectangular and spherical powders upon various input energy at a constant capacitance of $450{\mu}F$ in order to verify influence of powder shape on microstructure of porous compacts. Besides, generated heat (${\Delta}H$) during EDS, which is measured by an oscilloscope, is closely correlated with powder size.

• Applied Chemistry for Engineering
• /
• v.22 no.5
• /
• pp.518-521
• /
• 2011

A PEMFC single cell with the active area of $25cm^2$ was used to verify the effect of water management in the anode. Water management is one of the most critical operating variables. In this paper the effect of operating condition change, such as anode humidification and temperature, was investigated under constant current density of $200mA/cm^2$ where possible anode flooding operating area. Also experiments to observe the effect of the anode and cathode stoichiometry change and flow field design on the water management were performed. The water management was effected by the stoichimetry change. The temperature and humidification change also affected the fuel cell performance.