• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.2
• /
• pp.99-107
• /
• 2009

This study produced a design curve and fatigue limit for a variation in volume ratio and reduction ratio of TiNi/Al composites. In many cases, stress-life curve does not indicate fatigue limit, so it was presented by probabilistic-stress-life curve. Goodman diagram was used to analyze the fatigue strength of materials with a finite life determined by repeated load and the fatigue strength of endurance limit with an infinite life. The fatigue experiment was conducted using the scenk-type plane bending specimen in same shape. The result of the fatigue test, which had been conducted under consistent stress amplitude, was examined. (i) The optimal condition for TiNi/Al in accordance with hot pressing (ii) Impacts of fatigue limit caused by a variation in reduction ratio and volume ratio of TiNi/Al composites (iii) Probability distribution for fatigue limit of TiNi/Al2024 and TiNi/Al6061.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.4
• /
• pp.207-212
• /
• 2004

Full-beads of multi-layer steel engine head gaskets that are used to seal the combustion gas between the head and the block are subject to cyclic bending stresses due to the variation of the head/block gap during engine operation. The S-N curve for the fatigue durability assessment of the full-bead formed on NBR-coated SUS301 thin plate is deduced from the axial fatigue test results because of the difficulty in conducting the bending fatigue test of thin plate. The experimental verification of the deduced S-N curve is presented. It is shown that the NBR coating increases the endurance limit of the plate significantly. Mechanism of crack nucleation and propagation in the full-bead is discussed with photographs of the fatigue cracks.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.440-440
• /
• 2011

We report on the non-volatile memory characteristics of a bistable organic memory (BOM) device with Au nanoparticles (NPs) embedded in a conducting poly N-vinylcarbazole (PVK) colloids hybrid layer deposited on flexible polyethylene terephthalate (PET) substrates. Transmission electron microscopy (TEM) images show the Au nanoparticles distributed isotropically around the surface of a PVK colloid. The average induced charge on Au nanoparticles, estimated using the C-V hysteresis curve, was large, as much as 5 holes/NP at a sweeping voltage of ${\pm}3$ V. The maximum ON/OFF ratio of the current bistability in the BOM devices was as large as $1{\times}105$. The cycling endurance tests of the ON/OFF switching exhibited a high endurance of above $1.5{\times}105$ cycles and a high ON/OFF ratio of ~105 could be achieved consistently even after quite a long retention time of more than $1{\times}106$ s.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.22 no.3
• /
• pp.414-420
• /
• 2013

Research on decreasing the weight of composite sandwich panels is in progress. This paper reports the experimental results for the mechanical behavior of a composite sandwich panel. The skins of sandwich panels were made of glass fiber sheets and plywood matrix composites. Their interior layers consisted of glass fiber pultrusion pipes and gold foam. Experimental tests were performed to obtain the mechanical properties and complex mechanical behavior. Before fatigue tests, tensile tests and 3-point bending tests were carried out to obtain the optimal design and determine their strength and failure mechanisms in the flat-wise position. After the static test, a fatigue test were conducted at a load frequency of 5 Hz, stress ratio (R) of 0.1, and endurance limit for the S-N curve. It showed that the failure modes were related to both the core design and skin failure.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.23 no.2
• /
• pp.145-151
• /
• 2014

Recently, the growing demand for weight reduction and improved structure durabilityfor commercial vehicles has led to active research into the development and application of suitablecomposite materials. This studysuggests abimaterial composite frame produced by apultrusion process to replace steel frames. We focused on the development of a composite frameconsisting of two types of materialsby mixing anorthotropic material with anisotropic material. The inside layer consisted of an aluminum pipe, and the outside layer was composed of a glass fiber pipe. To determine the strength and failure mechanisms of the composite material, tensile tests, shear tests, and three-point bending tests were conducted, followed by fatigue tests. After static testing, the fatigue tests were conducted at a load frequency of 5 Hz, a stress ratio (R) of 0.1, and an endurance limit of $10^6$ for the S-N curve. The resultsshowed that the failure modes were related to both the core design and the laminating conditions.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1992.04a
• /
• pp.120-125
• /
• 1992

The fatigue tests were performed on the high strength concrete beams with single edged notch which was reinforced steel fiber. The steel fibers were used 1.0 percent by volume fraction. These were tested consists of constant amplitude tests for different levels of loading. The test program included endurance limit with repect to flexural fatigue and relation of load-CMOD(crack mouth opening displacement). The results of test, it is found from S-N curve that the fatigue strength for a life of 2 million cycles of load was approximately 70percent with respect to the static ultimate strength .

• Proceedings of the KSR Conference
• /
• 2002.05a
• /
• pp.399-403
• /
• 2002

The transmission system of high speed train serve in the severe condition compared with those of other trains, namely, they have to transmit high power to run with high speed and they have to make maximum use of the limited space. To clarify the strength of gear for Korea High-Speed Train, a bending fatigue test of gear specimen is performed and compare with actual gear's. From this result, specimen test is useful to infer S-N curve and endurance limit of actual gear that much time and expense are consumed.

• Journal of the Korea Safety Management & Science
• /
• v.13 no.2
• /
• pp.61-66
• /
• 2011

Fire disasters have frequently happened in concrete structures, which resulted in severe structural damages and unsafety. In this case, the method which had evaluated the safety of damaged structures was often unaccepted from most of stakeholders and engineers. The objective of this study is to develope the procedure and method to be able to determine the safety. Numerical simulation was applied to produce the maximum temperature and temperature distribution. Nextly, temperature propagation analysis was performed to plot temperature gradients at each depth and location. The material strength curve versus temperature was applied to determine the safety of concrete structures damaged by fire. The maximum temperature should be calibrated considering real fire records ; magnitude, intensity, situation etc. The results shows that the selected procedure and method was applicable and practical.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.1243-1251
• /
• 2013

The purpose of this study is to investigate the influence of initial clamping force of tension clamp on the performance of an elastic rail fastening system used in sharp curve track. In this study, the initial clamping force and the increasing lateral wheel loads were conducted in the analytical and experimental study, i.e., finite element analysis, laboratory and field test. Using the analytical and experimental results, the performance of the tension clamp was investigated. It was found that the stress of tension clamp depends on the initial clamping force. Therefore the initial clamping force appeared to directly affect the compression stress of the tension clamp. It was found that the compression stress of tension clamp was transferred to the tensile stress by applied the lateral wheel load in service sharp curve track. Further, it was concluded that the initial clamping force was applied on the strengthening force for the tension clamp and then the appropriate initial clamping force was important to ensure a stable performance and long term endurance of tension clamp.

• Transactions of the Korean hydrogen and new energy society
• /
• v.31 no.1
• /
• pp.89-95
• /
• 2020

The main scope of this paper is to see if the conventional pump can be properly used for a specific fuel, Di-methyl Ether (DME) despite of its low lubricity and high reactivity in the experimental conditions. A wobble plate type fuel pump was connected to the common rail to verify that the pump could deliver the fuel at the required pressure and resultantly DME could be used as fuel without modifying the original pump. At each required pressure (30 Mpa, 35 Mpa, 40 Mpa, 45 Mpa, and 50 Mpa), the pump met the pressure required by the common rail. In addition, pump performance experiments tended to follow the usual performance curve while the flow rate decreased as the pressure increased. The maximum flow rate of the pump was 470 kg/h at 30 Mpa and all measurements were taken with keeping DME temperature below 60℃.