• The Korean Journal of Ceramics
• /
• 제5권1호
• /
• pp.87-90
• /
• 1999

It was suggested that tape casting method can be used to fabricate high-temperature electrostatic chucks(HTESC) based on a metal substrate coated with a glass-ceramic insulating layer. The adhesion of the coating was excellent such that it was able to withstand temperature cycling to over $300^{\circ}C$ without spalling. The electrostatic clamping pressure reached a very high value of about 9 torr at 600V and generally followed the theoretical voltage-squared curve. Based on these results, we believe that we successfully developed a viable technique for manufacturing low cost HTESC.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.390-393
• /
• 2001

This study demonstrated the feasibility of tape casting method to fabricate soda borosilicate glass-coated stainless steel electrostatic chucks(ESC) for low temperature semiconductor processes. The glass coatings on the stainless steel substrates ranged from $100{\mu}m$ to $150{\mu}m$ thick. The adhesion of the glass coatings was found to be excellent such that it was able to withstand moderate impact tests and temperature cycling to over $300^{\circ}C$ without cracking and delamination. The electrostatic clamping pressure generally followed the theoretical voltage-squared curve except at elevated temperatures and higher applied voltages when deviations were observed to occur. The deviation is due to increased leakage current at higher temperature and applied voltage as the electrical resistivity drops.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.390-393
• /
• 2001

This study demonstrated the feasibility of tape casting method to fabricate soda borosilicate glass-coated stainless steel electrostatic chucks(ESC) for low temperature semiconductor processes. The glass coatings on the stainless steel substrates ranged from 100 $\mu\textrm{m}$ to 150 $\mu\textrm{m}$ thick. The adhesion of the glass coatings was found to be excellent such that it was able to withstand moderate impact tests and temperature cycling to over 300$^{\circ}C$ without cracking and delamination. The electrostatic clamping pressure generally followed the theoretical voltage-squared curve except at elevated temperatures and higher applied voltages when deviations were observed to occur. The deviation is due to increased leakage current at higher temperature and applied voltage as the electrical resistivity drops.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2002년도 춘계 기술심포지움 논문집
• /
• pp.169-172
• /
• 2002

This study demonstrated the feasibility of using tape-casting followed by sintering as a low-cost alternative for coating glass-ceramic or glass film on a metal substrate. The process has been successfully used to fabricate a glass-on-stainless steel and a glass-ceramic-on-molybdenum electrostatic chuck(ESC) with the insulating layer thickness about $150{\mu}{\textrm}{m}$. Electrical resistivity data of the coaling were obtained between room temperature and 55$0^{\circ}C$; although the resistivity values dropped rapidly with increasing temperature in both coatings, the glass-ceramic still retained a high value of $10^{10}$ ohm-cm at $500^{\circ}C$. Clamping pressure measurements were done using a mechanical apparatus equipped with a load-cell at temperatures up to $350^{\circ}C$ and applied voltages up to 600V; the clamping behavior of all ESCs generally followed the voltage-squared curve as predicted by theory. Based on these results, we believe that we have a viable technology for manufacturing ESCs for use in reactive-ion etch systems.

• 마이크로전자및패키징학회지
• /
• 제9권1호
• /
• pp.49-52
• /
• 2002

본 연구를 통하여 저온 반도체 공정용 정전퍽(ESC)을 테이프캐스팅 공정에 의하여 스테인레스스틸에 소다붕규산염유리가 도포된 형태로 제작할 수 있음을 입증하였다. 스테인레스스틸 기판위의 유리 도포층은 125 $\mu\textrm{m}$의 두께로 제작되었다. 유리 도포층의 접합력은 매우 우수하여 $300^{\circ}C$이상의 온도변화에서도 균열이나 층간갈라짐 현상이 발생하지 않았다. 정전 고착압력은 전반적으로 이론적 관계인 전압의 제곱에 비례하는 경향을 보였으나, 고온과 고인가전압에서는 이 관계에서 벗어나는 것으로 나타났다. 이러한 이탈현상은 고온과 고인가전압에서 전기비저항의 감소에 따른 누설전류의 증가에 기인한다.