• 열처리공학회지
• /
• 제27권6호
• /
• pp.288-294
• /
• 2014

The study on the migration of carbon in T23/T91 dissimilar metal welds for the boiler was conducted at $600^{\circ}C$ with an increase of aging time from 1 to 100 hrs. Following results were obtained. The heavily etched dark band tended to increase from a molten boundary owing to an increase of aging time, which leads to form hard (T91) and soft (T23) zones with different hardness. It was found that carbon was migrated from T23 area to T91 area due to different carbon activities. In addition, soft and hard zones were formed in regional area mainly resulted from carbide dissolutions and precipitates.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.1120-1125
• /
• 2004

Welding characteristics of STS304 stainless steel and Inconel 600 using a continuous wave Nd:YAG laser are experimentally investigated. Alloy 600 being used in steam generator tubing of pressurized water reactor(PWR) exposed to some corrosion environment, stress corrosion cracking can occur on this material. Presented here are the results from a series of experiments in which dissimilar metal welds were made using the gas tungsten arc welding process with pure argon shielding gas. But It is well known that solidification cracking susceptibility of austenitic alloys depends on the solidification temperature range and amount/distribution of solute rich liquid that exists at the terminal stages of solidification. An experimental study was conducted to determine effects of welding parameters and to optimize those parameters that have the most influence on eliminating or reducing the extent welding zone formation at dissimilar metal welds.

• 한국정밀공학회지
• /
• 제21권11호
• /
• pp.53-60
• /
• 2004

Laser welding techniques have been characterised for various materials. In this paper, the laser weldability of STS304 stainless steel and Inconel 600 at dissimilar metal welds using a continuous wave Nd:YAG laser are experimentally investigated. Inconel 600 is being used in a steam generator tubing of pressurized water reactor(PWR) exposed to some corrosion. Stress corrosion cracking can occur on this material. An experimental study was conducted to determine effects of welding parameters, on eliminating or reducing the extent welding zone formation at dissimilar metal welds and to optimize those parameters that have the most influence parameters such as focus length, power, beam speed, shielding gas, and wave length of laser were tested.

• 비파괴검사학회지
• /
• 제35권1호
• /
• pp.52-60
• /
• 2015

원자력발전소에는 탄소강과 스테인리스강 용접을 위해 alloy600 용접재를 적용한 이종금속용접부가 다수 존재하며, 전 세계적으로 이종금속용접부에서 결함 발생 보고가 지속되고 있다. 주기적인 건전성 평가를 위해 이종금속용접부 초음파검사 일반절차서 (KPD-UT-10)를 적용하여 검사를 수행하고 있으며, 검사절차서에서는 탐촉자와 검사체 표면 사이의 간격을 최대 1/32"(0.8mm) 이내로 제한하고 있다. 국내의 일부 이종금속용접부는 테이퍼진 형상과 불규칙한 표면 형상을 가지고 있어, 가변형 위상배열초음파기술을 적용하여 검사 신뢰성을 높이고자 본 연구를 수행하였다. 연구 결과, 검사체 표면이 불규칙한 시편 내부의 인공결함에 대한 검출이 양호하였고, 이를 통해, 가변형 위상배열초음파기술의 현장 적용 가능성을 확인하였다.

• 한국압력기기공학회 논문집
• /
• 제7권4호
• /
• pp.1-11
• /
• 2011

This paper presents the effects of preventive maintenance schemes on the residual stress distributions in dissimilar metal welds. Dissimilar metal weld is known susceptible to PWSCC and thus, effective maintenance schemes to prevent PWSCC are needed. Three preventive maintenances schemes, i.e. weld overlay, MSIP and inlay weld which are widely used in nuclear power plants, are selected and their effects on welding residual stresses are investigated via finite element analyses. As results, weld overlay and MSIP were proved effective method to mitigate residual stresses and inlay weld, on the other hand, produces strong tensile residual stresses in the inner surface. Although Alloy 690 known to be resistant to PWSCC are used in inlay weld, continuous careful observation are needed since tensile welding residual stresses are key parameter for PWSCC.

• 대한기계학회논문집A
• /
• 제37권5호
• /
• pp.649-655
• /
• 2013

이종금속용접부에 대한 실제 용접 공정 중 용접부에서 결함이 발견되면 이를 제거하고 보수용접이 수행된다. 일반적으로 보수용접을 수행하면 용접부에서 인장 잔류응력이 크게 증가될 수 있는 것으로 알려져 있다. 따라서 Alloy 82/182를 사용하여 보수용접이 수행된 이종금속용접부의 일차수 응력부식 균열 현상을 평가하기 위해서는 보수용접에 의한 용접부의 응력 변화를 정확하게 평가해야 한다. 본 논문에서는 비선형 유한요소해석을 수행하여 보수용접에 의한 원자력 이종금속 맞대기 용접부의 응력 분포를 평가하였다. 특히 보수용접 공정 모사를 위한 여러 유한요소 해석방법이 이종금속용접부의 응력분포에 미치는 영향을 평가하였다.

• Nuclear Engineering and Technology
• /
• 제48권1호
• /
• pp.228-235
• /
• 2016

Flaws at dissimilar metal welds (DMWs), such as reactor coolant systems components, Control Rod Drive Mechanism (CRDM), Bottom Mounted Instrumentation (BMI) etc., in nuclear power plants have been found. Notably, primary water stress corrosion cracking (PWSCC) in the DMWs could cause significant reliability problems at nuclear power plants. Therefore, phased array ultrasound is widely used for inspecting surface break cracks and stress corrosion cracks in DMWs. However, inspection of DMWs using phased array ultrasound has a relatively low probability of detection of cracks, because the crystalline structure of welds causes distortion and splitting of the ultrasonic beams which propagates anisotropic medium. Therefore, advanced evaluation techniques of phased array ultrasound are needed for improvement in the probability of detection of flaws in DMWs. Thus, in this study, an investigation of focusing and steering phased array ultrasound in DMWs was carried out using a time reversal technique, and an adaptive focusing technique based on finite element method (FEM) simulation. Also, evaluation of focusing performance of three different focusing techniques was performed by comparing amplitude of phased array ultrasonic signals scattered from the targeted flaw with three different time delays.

• Journal of Welding and Joining
• /
• 제29권2호
• /
• pp.56-63
• /
• 2011

his paper aimed to understand the residual stress in the dissimilar metal welds of nuclear power plant. Two kinds of residual stress were considered, which caused by welding and machining. Residual stress due to mechanical machining was measured by hole-drilling technique and x-ray diffraction method for the SA508 and F316L. Weld residual stress at dissimilar metal weld between SA508 and F316L was evaluated by FEA. Residual stress profiles were obtained for the inside surface and through thickness of welds. Machining effect was also analyzed by FEA. According to the residual stress measurement, it was observed that mechanical machining can generate tensile stress on the surface of the test material. However, FEA results showed that mechanical machining did not increase the tensile stress on the surface of weld region. Further study with more elaborate measurement and numerical analysis is required to identify the effect of machining on residual stress in the dissimilar metal weld region.

• Journal of Welding and Joining
• /
• 제34권3호
• /
• pp.61-68
• /
• 2016

Characteristics of dissimilar metal welds between alloy steel ASTM A387 Gr. 91 and carbon steel ASTM A516 Gr.70 made with Flux cored arc welding(FCAW) have been evaluated in terms of microstructure, mechanical strength, chemical analysis by EDS as well as corrosion test. Three heat inputs of 15.0, 22.5, 30.0kJ/cm were employed to make joints of dissimilar metals with E91T1-B9C wire. Post-weld heat treatment was carried out at $750^{\circ}C$ for 2.5 h. Based on microstructural examination, tempered martensite and lower bainite were formed in first layer of weld metal. The amount of tempered martensite was decreased and the amount of lower bainite was increased with increasing heat input and layer. Heat affected zone of alloy steel showed the highest hardness due to the formation of tempered Martensite and lower Bainite. Tensile strengths of dissimilar welds decreased with increasing heat inputs. Dissimilar welds seemed to have a good hot cracking resistance due to the low HCS index below 4. The salt spray test of dissimilar metals showed that the corrosion rate increased with increasing heat inputs due to the increase of the amount of lower Bainite.

• Journal of Welding and Joining
• /
• 제4권3호
• /
• pp.32-42
• /
• 1986

In this study, the influence of carbon equivalents on friction welds of dissimilar steels was investigated. Four types of carbon steels with 10mm diameter were welded to a high-speed tool steel SKH 9. Main experimental results could be summarized as follows (1) Under constant friction pressure, the friction time increased almost linearly with the increasing burn-off length, while the forge length decreased almost linearly. (2) The maximum hardness in carbon steels increased almost linearly with the increasing carbon equivalent, but was much lower than that in the high speed steel. (3) After quenching and tempering of dissimilar steel friction welds, the hardness in carbon steel weldments became similar as that in the base metal, while the hardness in SKH 9 weld was still higher that of the base metal. (4) Relative movement in the friction phae occurred not at the interface of the weldments, but in the high speed steed steel near the interface. (5) For considered material combinations and welding parameters, most of fractures in tension and twisting tests occurred in the base metal. And welds with so high strength could produced in a wide range of welding parameters.