• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.3
• /
• pp.324-330
• /
• 2006

In this study, carbothermal reduction method was employed to synthesis Sn-Sb alloy powders from chief metal oxides with ultrafine sizes. The Sn-Sb powders consisting of ultrafine particles were formed at $800{\sim}900^{\circ}C$ by reduction of oxides. Those powders have high initial discharge capacities ($570{\sim}637\;mAh/g$) and discharge capacities of those powders maintain initial capacity after 20 cycle due to existence of ultrafine particles in powders and alloying effect of Sn-Sb.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.4
• /
• pp.504-511
• /
• 2011

Nano-sized Sn powder was prepared by pulsed wire evaporation method. The Sn powder and carbon black were charged in jar and ball milled. The milling time was varied with 10 min., 1h, 2h, and 4h, respectively. The milled powders were dried and the shape and size were observed by FE-SEM. Nano-sized Sn powders were plastic-deformed and agglomerated by impact force of balls and heat generated during the SPEX milling. The agglomerated Sn powder also consisted of many nano-sized particles. Initial discharge capacities of milled Sn electrode powders with carbon powder were milled for 10 min., 1h, 2h, and 4h were 787, 829, 827, and 816 mAh/g, respectively. After 5 cycle, discharge capacities of Sn electrode powders with carbon powder milled for 10 min., 1h, 2h, and 4h decreased as 271, 331, 351, and 287 mAh/g, respectively. Because Sn electrode powders milled for 2h constist of uniform and fine size, the cyclability of coin cell made of this powders is better than others.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.8
• /
• pp.1144-1148
• /
• 2002

We prepared the polyaniline (Pani) film and powder by chemical polymerization and doping with different dopants and also investigated the capability of Li//polyaniline cells after assembling. The oxidation/reduction potentials and electrochemical reaction of Li//polyaniline cells were tested by cyclic voltammetry technique. The Li//Pani-HCl cells with 10% and 20% conductors show a little larger specific discharge capacities than that without conductor. The highest discharge capacity of almost 50 mAh/g at 100th cycle is also achieved. However, Li//Pani-LiPF6 with 20% conductor shows a remarkable performance of ~90 mAh/g at 100th cycle. This is feasible value for using as the positive electrode material of lithium ion secondary batteries. It is also proved that the powder type electrode of Pani is better to use than the film type one to improve the specific discharge capacity and its stability with cycle.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.88-90
• /
• 2003

The purpose of this study is to research and develop tin oxide-flash composite for lithium Ion polymer battery. Tin oxide is one of the promising material as a electrode active material for lithium Ion polymer battery (LIPB). Tin-based oxides have theoretical volumetric and gravimetric capacities that are four and two times that of carbon, respectively. We investigated cyclic voltammetry and charge/discharge cycling of SnO-flyash/SPE/Li cells. The first discharge capacity of SnO-flyash composite anode was 720 mAh/g. The discharge capacity of SnO-flyash composite anode 412 and 314 mAh/g at cycle 2 and 10 at room temperature, respectively. The SnO-flyash composite anode with PVDF-PMMA-PC-EC-$LiClO_4$ electrolyte showed good capacity with cycling.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.7
• /
• pp.636-643
• /
• 2006

Si-C materials were synthesized by the heating the mixture of silicon and polyvinylidene fluoride (PVDF). The electrochemical properties of the Si-C materials as the high capacitive anode materials of lithium secondary batteries were evaluated by the galvanostatic charge-discharge test through 2032 type $Si-C{\mid}Li$ coin cells. Charge-discharge tests were performed at C/10 hour rate(C = 372 mAh/g). Initial discharge and charge capacities of $Si-C{\mid}Li$ cell using a Si-C material derived from PVDF(20wt.%) were found to be 1,830 and 526 mAh/g respectively. The initial discharge-charge characteristics of the developed Si-C electrode were analyzed by the electrochemical galvanostatic test adopting the capacity limited charge cut-off condition(GISOC). The range of reversible specific capacity IIE(intercalation efficiency at initial discharge-charge) and IICs(surface irreversible specific capacity) were 216 mAh/g, 68 % and 31 mAh/g, respectively.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.1
• /
• pp.30-38
• /
• 2002

Disordered carbon and boron-substituted disordered carbons $C_{l-x}B_x(x=0.05,\;0.10,\;0.20)$ were synthesized by Pyrolysis of LPG(liquid Propane gas)and $BCl_3$. Their electrochemical properties as anode materials for Li-ion secondary batteries were then investigated. When PVDF is added to the sample in a weight ratio 5 : 95, the disordered carbon with x=0.00 had the first discharge capacity 374 mAh/g. Its cycling performance was relatively good from the second cycle and it had the discharge capacity 258 mAh/g at the 10th cycle. When PVDF is added to the sample in a weight ratio 5 : 95, the sample with x=0.05 among the samples $C_{l-x}B_x(x=0.05,\;0.10,\;0.20)$ exhibited the largest first discharge capacity 860 mAh/g and discharge capacity 181 mAh/g at the 10th cycle. All the samples had similar cycling performances from the second cycle. The sample $C_{0.90}B_{0.10}$ showed the best electrochemical properties as a anode materials fur Li-ion secondary battery from the view points of the first discharge capacity(853 mAh/g when $10w1.\%$ PVDF is used), cycling performance, discharge capacity(400mAh/g at the 10th cycle when $10wt.\%$ PVDF is used). All the samples showed generally larger charge and discharge capacities when $10wt.\%$ PVDF ratter than $5wt.\%$ PVDF is used. The plateau region in the range of voltage lower than 1.25V becomes larger probably since the structure becomes less disordered by the addition of boron. When boron is added, the charge and discharge capacities decreased suddenly at the second cycle. This may be become only a part of Li are reversibly deintercalated and intercalated and a part of Li which are strongly combined with B are not deintercalated. The increases in charge and discharge capacities are considered to be resulted from the increase in the potential of Li in the boron-added carbons, caused by the strengthening of the chemical bond between the intercalated Li and the boron-carbon host since the boron acts as electron acceptor.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.4
• /
• pp.297-303
• /
• 2008

$LiNiO_2$ cathode powders with fine size have been synthesized by spray pyrolysis from the spray solution with citric acid and ethylene glycol. The as-prepared powders with spherical shape, porous structure and micron size turned into $LiNiO_2$ powders with micron size and regular morphology after post-treatment at $800^{\circ}C$. The initial discharge capacities of the $LiNiO_2$ powders changed from 199 to 171mAh/g when the concentrations of the citric acid and ethylene glycol added to the spray solutions were changed from 0 to 1 M. The maximum initial discharge capacity of the $LiNiO_2$ powders obtained from the spray solution with citric acid and ethylene glycol was 198 mAh/g when the lithium component added to the spray solution was 6 mol% excess of the stoichiometric amount. The discharge capacities of the fine-sized $LiNiO_2$ powders dropped from 198 to 163 mAh/g by the 30 th cycle at a current density of 0.1 C.

• The Proceedings of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.9 no.3
• /
• pp.67-72
• /
• 1995

In this paper, we investigate the numbers and electrical capacities of general and industrial Korean lighting apparatus. The results show that the number of lighting apparatus are 68,211,000 in general and 53,836,000 in industrial building and the capacities of lighting apparatus are 3,261,609 kW in general and 4,278,683 kW in industrial building. The ratio of Lighting apparatus is that fluorescent lamps are 56.9%, high intensity discharge lamps are 29.7%, and incandescent lamps are 12.1%.

• Journal of the Korean Geosynthetics Society
• /
• v.7 no.2
• /
• pp.15-21
• /
• 2008

The advantages of prefabricated vertical drains over conventional sand drains include their relatively low costs, less disturbance to the soil mass, the easinees of installation, and their flexibility which ensures the integrity of the drains during installation. This study tested the change of discharge capacities with respect to the hydraulic gradients for each lateral pressure. From the test results, as increases the overburden pressure, the clay soil is being consolidated, and also lateral pressure to the PVD specimen is increased. Therefore, the discharge capacity is decreased. The size of opening space in the core of PVDs is proportionally related to the discharge capacity. The numerical analysis was performed with utilizing computer simulation with considering field conditions. The results of numerical analysis are compared well with the field measurements.

• Transactions of the Korean hydrogen and new energy society
• /
• v.10 no.1
• /
• pp.49-57
• /
• 1999

In order to study the effect of high energy ball milling on the $Mg_2Ni+Ni$, $Mg_2Ni+0.5Ni+0.5Al$ powders, we have investigated on the discharge properties, microstructures. The powder size of samples decreased as ball milling time. From the XRD results, the crystal structure of $Mg_2Ni+Ni$ mixed powders were changed to amorphous or nano-structure after 60hr ball milling. The discharge capacities of both $Mg_2Ni+Ni$ and $Mg_2Ni+0.5Ni+0.5Al$ powders increased, with increasing ballmilling time, the maximum capacity(342mAh/g) was shown for the 60 hrs ballmilled $Mg_2Ni+Ni$ sample. The capacity decreased drastically after a few charge-discharge cycles.