• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.136-142
• /
• 1997

In this study, the amorphous foil filler, thickness of 20 - $20~30\mu\textrm{m}$ was made to develop Cu-7.5wt%Mn-7.5wt%Si insert alloy(melting point temperature : solidus line 1003K, liquidus line 1070K). Liquid phase diffusion bonding of 304 stainless steels (STS304), is carried out successfully by using developed Cu-7.5Mn-7.5Si insert alloy. Bonding conditions are taken from bonding pressure of 5MPa, bonding temperatures from 1073K to 1423K varied within 50K and brazing holding times of 0, 30, 60 and 240 minutes. As the results, the tensile strength in the liquid phase diffusion bonding is a little bit lower than that in the solid phase diffusion bonding. The authors find out that the liquid phase diffusion bonding needs lower bonding pressure than the others. Therefore, the liquid phase diffusion bonding had an excellent brazability in which the bonding process showed the typical mechanism of diffusion bonding. In corresponding, the new developed insert alloy of low melting pointed Cu-7.5Mn-7.5Si makes possible brazing between the STS304.

• Journal of Welding and Joining
• /
• v.9 no.3
• /
• pp.26-33
• /
• 1991

As it takes very long time for the Transient Liquid Phase(TLP) bonding, we tried to reduce the bonding time by changing insert material for the high diffusivity element. On this study boron powder was doped as a insert material on the bonding surface of Rene 80 superalloy, and diffusion treated at 1150.deg.C under vacuum. On this method differently from the TLP bonding the insert material was not melted during bonding but only the base metal reacted with the boron was inducedly melted. Therefore, as this bonding mechanism is different from the existing ones, it is suggested as a Melting Induced Diffusion Bonding. When this process was used for the diffusion bonding, the bonding time including homogenization decreased greatly compared to the conventional TLP bonding.

• Journal of Welding and Joining
• /
• v.13 no.2
• /
• pp.132-138
• /
• 1995

Rene80 superalloy was liquid phase diffusion bonded by using boron(B) as an insert material, where B has high diffusivity and higher melting point as an insert material. Bonding procedure and bonding mechanism of Rene80/B/Rene80 joint were investigated. As results, liquid metal was produced by solid state reaction between base metal and insert material on bonding zone. The liquid metal was produced preferentially at the grain boundary. Except for production of liquid metal, other bonding procedure was nearly same as TLP(Transient Liquid Phase) bonding. Bonding time, however, was reduced compared to prior result of TLP bonding. By bonding S.4ks at l453K, Ren80/B/Rene80 joint was isothermally solidified and homogenized where thickness of insert material was 7.5.mu.m.

• Transactions of Materials Processing
• /
• v.28 no.1
• /
• pp.15-20
• /
• 2019

The superplastic forming/diffusion bonding process has been developed to fabricate a core frame structure with joint nodes out of tubes, for the development of a titanium high performance bicycle. The hydroforming process has been applied for bulging of a tube in the superplastic condition before, and during the diffusion bonding process. In this experiment, a commercial Ti-3Al-2.5V tube was selected as raw material for the study. The forming experiment has been performed using a servo-hydraulic press with a capacity of 200 ton. Next, nitrogen gas was used to acquire necessary pressure for the bulging and bonding of the tubes to fabricate the joint nodes. The pertinent processing temperature was $870^{\circ}C$ for the superplastic hydroforming/diffusion bonding (SHF/DB) process, using the Ti-3Al-2.5V tube. The bonding quality and the progress of bulging and diffusion bonding have been observed by the investigation of the joining interfaces at the cross section of the joint structure. The control of the nitrogen pressure throughout the SHF/DB process, was an important factor to avoid any significant defects in the joint structure. The whole progress stage of the diffusion bonding could be observed at a joint interface. A core structure with 5 joint nodes to manufacture a titanium bicycle could be obtained in a SHF/DB process.

• Journal of Welding and Joining
• /
• v.15 no.6
• /
• pp.32-40
• /
• 1997

Solid state diffusion bonding is the joining process performed by creep and diffusion, which is accelerated by heating below melting temperature and proper pressing, in vacuum or shielding gas atmosphere. By this process we can obtain sufficient joint which can't be expected from the fusion welding. For Ti-6Al-4V alloy, the optimum solid state diffusion bonding condition and mechanical properties of the joint were found, and micro void morphology at bond interface was observed by SEM. The results of tensile test showed sufficient joint, whose mechanical properties are similar to that of base metal. 850$^{\circ}$C, 3MPa is considered as the optimum bonding condition. Void morphology at interface is long and flat at the initial stage. As the percentage of bonded area increases, however, small and round voids are found. Variation of void shape can be explained as follows. As for the void shrinkage mechanism, at the initial stage, power law creep is the dominant, but diffusion mechanism is dominant when the percentage of bonded area is increased.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.22 no.5
• /
• pp.812-817
• /
• 2013

This study demonstrates the diffusion bonding process between a tungsten carbide shank (K30) and tungsten carbide (DX5) for micro WC-PCD tool fabrication. A type of nickel alloy was used as the filler met alto improve the bond ability between K30 and DX5. The bonding pressure, time, and surrounding conditions were kept constant. In particular, the normal pressure was controlled precisely under buckling analysis. Diffusion bonding was performed at various operation temperatures (1170-1770 K) by using a specially designed jig. The microstructure on the localized bonded surface was analyzed using scanning electron microscopy and optical microscopy. In the case of diffusion bonding of WCat 1370-1770K, the filler metal melted completely and diffused between the two base metals, and they were bonded more tightly on both sides than at temperatures below 1370 K. Our results demonstrated the importance of sensitive temperature dependence of diffusion bonding.

• Journal of Welding and Joining
• /
• v.10 no.3
• /
• pp.63-72
• /
• 1992

The joining methods of ceramics to metals which can be expected to obtain high temperature strength are mainly classified into the solid-state diffusion bonding method and the active brazing method. Between these two, the solid-state diffusion bonding method is given attentions as substituting method for active brazing method due to being capable of obtaining higher bonding strength at high temperature and accurate bonding. In this paper, the solid-state diffusion bonding of $Al_{2}$O$_{3}$ ceramics to Ni-Cr-Mo alloy steel (SNCM21) using insert metal was carried out. The insert metal employed in this study was experimentally home-made, Ag-Cu-Ti alloy. Influence of several bonding parameters of $Al_{2}$O$_{3}$SNCM21 joint was quantitatively evaluated by bonding strength test, and microstructural analyses at the interlayer were performed by SEM/EDX. From above experiments, the optimum bonding condition of the solid-state diffusion bonding of $Al_{2}$O$_{3}$/SNCM21 using Ag-Cu-Ti insert metal was determined. Futhermore, high temperature strength and thermal-shock properties of $Al_{2}$O$_{3}$/SNCM21 joint were also examined. The results obtained are as follows. 1. The maximum bonding strength was obtained at the temperature of 95% melting point of insert metal. 2. The high temperature strength of $Al_{2}$O$_{3}$/SNCM21 joint appeared to bemaximum value at test temperature 500.deg.C and the bonding strength with increasingtemperature showed parabolic curve. 3. The strength of thermal-shocked specimens was far deteriorated than those of as-bonded specimens. Especially, water-quenched specimen after heated up to 600.deg. C was directly fractured in quenching.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.386-391
• /
• 2017

Using a customized diffusion bonder, we executed diffusion bonding for ring shaped white gold and red gold samples (inner, outer diameter, and thickness were 15.7, 18.7, and 3.0 mm, respectively) at a temperature of $780^{\circ}C$ and applied pressure of 2300 N in a vacuum of $5{\times}10^{-2}$ torr for 180 seconds. Optical microscopy, field emission scanning electron microscopy (FE-SEM), and energy-dispersive X-ray spectroscopy (EDS) were used to investigate the microstructure and compositional changes. The mechanical properties were confirmed by Vickers hardness and shear strength tests. Optical microscopy and FE-SEM confirmed the uniform bonding interface, which was without defects such as micro pores. EDS mapping analysis confirmed that each gold alloy was 14K with the intended composition; Ni and Cu was included as coloring metals in the white and red gold alloys, respectively. The effective diffusion coefficient was estimated based on EDS line scanning. Individual values of Ni and Cu were $5.0{\times}10^{-8}cm^2/s$ and $8.9{\times}10^{-8}cm^2/s$, respectively. These values were as large as those of the melting points due to the accelerated diffusion in this customized diffusion bonder. Vickers hardness results showed that the hardness values of white gold and red gold were 127.83 and 103.04, respectively, due to solid solution strengthening. In addition, the value at the interface indicated no formation of intermetallic compound around the bonding interface. From the shear strength test, the sample was found not to be destroyed at up to 100,000 gf due to the high bonding strength. Therefore, these results confirm the successful diffusion bonding of 14K white-red golds with a diffusion bonder at a low temperature of $780^{\circ}C$ and a short processing time of 180 seconds.

• Journal of the Korean Society of Safety
• /
• v.32 no.1
• /
• pp.9-14
• /
• 2017

Diffusion bonding is a technique that has the ability to join materials with minimum change in joint micro-structure and deformation of the component. The quality of the joints produced was examined by metallurgical characterization and the joint micro-structure developed across the diffusion bonding was related to changes in mechanical properties as a function of the bonding time. An increase in bonding time also resulted in an increase in the micro-hardness of the joint interface from 55 VHN to 180 VHN, The increase in hardness was attributed to the formation of intermetallic compounds which increased in concentration as bonding time increased.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.785-790
• /
• 2002

Distributions of residual stress in diffusion bonding of dissimilar materials intermetallics TiAl to steel 40Cr were simulated by FEM calculation. Results showed that destructive residual stresses presented in the minute area adjacent to bond-line of the base material with smaller coefficient of thermal expansion. Reducing bonding temperature and diminishing bonding time are in favor of the mollification of interface tresses.