• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.816-819
• /
• 1995

(Ba$_{1-x}$ , Sr$_{x}$)TiO/$_3$thin films on Pt/Ti/SiO$_2$/Si substrates were prepared by LP MOCVD(Low Pressure Metal-Organic Chemical Vapor Deposition). The crystalinity of BST deposit had a (100) preferred orientation with increasing deposition temperature due to surface diffusion. BST films deposited at 90$0^{\circ}C$ showed a dielectric constant of 365 and a dissipation factor of 0.052 at a frequency of 100kHz. The chance of capacitance of the films with applied voltage was small, showing paraelectric properties. BST film deposited at 90$0^{\circ}C$ had a charge storage density of 60 fc/${\mu}{\textrm}{m}$$^2$at a field of 0.2MV/cm and the leakage current density of 20 nA/$\textrm{cm}^2$ at a field of 0.15 MV/cm.cm.

• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.603-608
• /
• 2019

In this study, the multilayered thin films of (Ba,Sr)TiO3/K(Ta,Nb)O3 were fabricated by the sol-gel and spin coating methods, and their structural and electrical properties were investigated. The specimen showed polycrystalline X-ray diffraction (XRD) characteristics with a tetragonal structure. The average grain size and film thickness for one coating were about 30~40nm and 60nm, respectively. The phase transition temperature of specimen was lower than 10 ℃. The dielectric constant and loss at 20 ℃ of the specimen coated six times were 1,231 and 0.69, respectively. The rate of change in dielectric constant at an applied direct current (DC) voltage of the six times coated thin films was 17.3%/V. The electrocaloric effect was the highest around the temperature at which the remanent polarization rapidly changed. When an electric field of 660kV/cm was applied to the triply coated thin films, the highest electrocaloric property of 4.41 ℃ was observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.157-160
• /
• 2004

Ferroelectric $(Ba_xSr_{1-x})TiO_3$ (BST) thin films have been deposited on (001) MgO single crystals by a pulsed laser deposition (PLD) method. The structure of deposited BST thin films were investigated by an x-ray diffractometer. Calculated c-axis lattice parameters of the BST films exhibit a strong lattice distortion, which was not observed in ceramic BST at room temperature. This lattice distortion of BST has been attributed to strains caused by lattice constant difference between film and substrate, oxygen vacancies in BST film, and thermal expansion difference between film and substrate. Ferroelectric properties at 10 GHz have been measured using a HP 8510C vector network analyzer. Dielectric properties, capacitance tunability and quality factor, of the interdigitaed capacitors fabricated on BST films were calculated from the measured s-parameters. Two distinct behaviors in structural, opitical, and microwave properties of BST films were observed; below and above 200 mTorr of oxygen pressure in the deposition chmber.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.258-261
• /
• 2000

Highly (h00)-oriented (Ba, Sr)TiO$_3$(BST) thin films were grown by pulsed laser deposition on the perovskite LaNiO$_3$(LNO) metallic oxide layer as a bottom electrode. The LNO films were deposited on SiO$_2$/Si substrates by rf-magnetron sputtering method. The crystalline phases of the BST film were characterized by x-ray $\theta$-2$\theta$, $\omega$-rocking curve and $\psi$-scan diffraction measurements. The surface microsturcture observed by scanning electron microscopy was very dense and smooth. The low-frequency dielectric responses of the BST films grown at various substrate temperatures were measured as a function of frequency in the frequency range from 0.1 Hz to 10 MHz. The BST films have the dielectric constant of 265 at 1 kHz and showed multiple dielectric relaxation at the low frequency region. The origin of these low-frequency dielectric relaxation are attributed to the ionized space charge carriers such as the oxygen vacancies and defects in BST film, the interfacial polarization in the grain boundary region and the electrode polarization. We studied also on the capacitance-voltage characteristics of BST films.

• Journal of the Korean Vacuum Society
• /
• v.11 no.3
• /
• pp.135-140
• /
• 2002

In this paper, We deposited the BST thin-film on p-type (100)Si, (100)MgO and MgO/Si substrates respectively using RF magnetron sputtering method. After the BST thin-fil m was deposited, we performed RTA(rapid thermal anneal) at $600^{\circ}C$, oxygen atmosphere and 1 min. In the XRD measurement, we observed the (110) $Ba_{0.5}Sr_{0.5}TiO_3$ main peak in all samples and the peak intensity increased after post annealing. Then we manufactured a capacitor using Al Electrode and measured I-V, C-V. In C-V measurement result values for each substrate, dielectric constant was calculated 120 (bare Si), 305(MgO/Si), 310(MgO) respectively. A leakage current density was present less than 1 $\mu\textrm{A/cm}^2$ at applied fields below 0.3 MV/cm. In conclusion we confirmed that MgO/Si substrates give good results for BST thin-film deposition.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.5
• /
• pp.33-39
• /
• 1998

The BST (Ba$_{1-x}$ Sr$_{x}$TiO$_{3}$)(50/50) thin film has been grown by RF magnetron reactive sputtering and its characteristics such as crystallization, surface roughness, and electrical properties have been investigated with varying the film thickness. The crystallization and surface roughness of BST thin film are investigated by using XRD and AFM, respectively The BST thin film anealed at 800.deg. C for 2 min has pure perovskite structure and good surface roughness of 16.1.angs.. We estimate that the thickness and dielectric constant of interface layer between BST film and electrode are 3nm and 18.9, respectively, by measuring the capacitance with various film thickness. As the film thickness increases form 80nm to 240nm, the dielectric constant at 10kHz increases from 199 to 265 and the leakage current density at 200kV/cm decreases from 0.682.mu.A/cm$^{2}$ to 0.181 .mu.A/cm$^{2}$. In the case of 240nm-thick BST thin film, the charge storage density and leakage current density at 5V are 50.5fC/.mu.m$^{2}$ and 0.182.mu.A/cm$^{2}$, respectively. The values indicate that the BST thin film is a very useful dielectric material for the DRAM capacitor.or.

• Journal of the Korean Ceramic Society
• /
• v.43 no.11 s.294
• /
• pp.715-723
• /
• 2006

Perovskite oxide materials are very important for the electronics industry, because they exhibit promising properties. With an interest in the obvious applications, significant effort has been invested in the growth of highly crystalline epitaxial perovskite oxide thin films in our laboratory. And the desired structure of films was formed to achieve excellent properties. $Y_1Ba_2Cu_3O_{7-x}$ (YBCO) superconducting thin films were simultaneously deposited on both sides of 3 inch wafer by inverted cylindrical sputtering. Values of microwave surface resistance R$_2$ (75 K, 145 GHz, 0 T) smaller than 100 m$\Omega$ were reached over the whole area of YBCO thin films by pre-seeded a self-template layer. For implementation of voltage tunable high-quality varactor, A tri-layer structured SrTiO$_3$ (STO) thin films with different tetragonal distortion degree was prepared in order to simultaneously achieve a large relative capacitance change and a small dielectric loss. Highly a-axis textured $Ba_{0.65}Sr_{0.35}TiO_3$ (BST65/35) thin films was grown on Pt/Ti/SiO$_2$/Si substrate for monolithic bolometers by introducing $Ba_{0.65}Sr_{0.35}RuO_3$ (BSR65/35) thin films as buffer layer. With the buffer layer, the leakage current density of BST65/35 thin films were greatly reduced, and the pyroelectric coefficient of $7.6\times10_{-7}$ C $cm^{-2}$ $K^{-1}$ was achieved at 6 V/$\mu$m bias and room temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.196-196
• /
• 2008

We have investigated that the effect of post annealing on the structural and electrical properties of $Ba_{0.5}Sr_{0.5}TiO_3$ thin films. The BST thin films were deposited on n-type 4H-silicon carbide(SiC) using pulsed laser deposition (PLD). The deposition was carried out in oxygen ambient 100mTorr for 5 minutes, which results in about 300nm-thick BST films. For the BST/4H-SiC, 200nm thick silver was deposited on the BST films bye-beam evaporation. The X-ray diffraction patterns of the BST films revealed that the crystalline structure of BST thin films has been improved after post-annealing at $850^{\circ}C$ for 1 hour. The root mean square (RMS) surface roughness of the BST film measured by using a AFM was increased after post-annealing from 5.69nm to 11.49nm. The electrical properties of BST thin film were investigated by measuring the capacitance-voltage characteristics of a silver/BST/4H-SiC structure. After the post-annealing, dielectric constant of the film was increased from 159.67 to 355.33, which can be ascribed to the enhancement of the crystallinity of BST thin films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.45-48
• /
• 2000

High dielectric (Ba,Sr)TiO$_3$thin films were etched in an inductively coupled plasma (ICP) as a function of C1$_2$/Ar gas mixing ratio. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400$\AA$/min and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. We investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The surface roughness decreased as Cl$_2$increases in C1$_2$/Ar plasma because of non-volatile etching products. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystallinity of etched BST film maintained as similar to as-deposited BST under Ar only and Cl$_2$(20)/Ar(80). However, (100) orientation intensity of etched BST film abruptly decreased at Cl$_2$only plasma. It was caused that Cl compounds were redeposited on the etched BST surface and damaged to crystallinity of BST film during the etch process.