• Restorative Dentistry and Endodontics
• /
• v.8 no.1
• /
• pp.107-113
• /
• 1982

The purpose of this study was to observe the tensile strength of composite resins to etched dentin surface with the various methods of placing bonding agent before composite resin or placing composite resin alone. Recently extracted 60 maxillary incisors were chosen. These were divided into 6 groups: Group I : Immediate Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds without bonding agent. Group II : Immediate Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds with bonding agent. Group III : Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds after 5 minutes of bonding agent. Group IV : Immediate Enamelite adaptation to the etched dentin surfaces with 50% phosphoric acid for 120 seconds without bonding agent. Group V : Immediate Enamelite adaptation to the etched dentin surface with 50% phosphoric acid for 120 second s with bonding again. Group VI : Enamelite adaptation to the etched dentin surface with 50% phosphoric acid for 120 seconds after 5 minutes of bonding agent. All specimens were immersed in water at $37^{\circ}C$ for 24 hours before testing. The results were as follows: 1. The tensile strength of powder/liquid composite resin system was higher than that of pastel paste composite resin system. 2. The tensile strength of the composite resin group II, III, V, & VI with bonding agent was higher than that of the composite resin group I & IV without bonding agent. 3. The tensile strength of the composite resin group III & VI after 5 minutes added to bonding agent was higher than that of the composite resin group II & V immediately added to bonding agent.

• Restorative Dentistry and Endodontics
• /
• v.15 no.1
• /
• pp.165-173
• /
• 1990

The purpose of this study was to measure the effect of two commercially available composite resin systems and GC dentin cement on the shear bond strength of the etched porcelain to enamel and dentin. The specimens were divided into six groups, and each group was as follows. Group I : etched enamel-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group II : etched enamel-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain. Group III : dentin-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group IV : dentin-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain Group V : dentin-GC dentin cement-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group VI : dentin-GC dentin cement-Scotchbond 2-Silux- unfilled resin-silane-etched porcelain Following polymerization. the specimens were stored in 100% humidity for 24 hours before testing. Shear bond strength was measured with Instron universal testing machine. The results obtained were as follows; 1. The shear bond strength of the etched porcelain to enamel was greater than that of the etched porcelain to dentin. 2. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of CHOICE-dentin/enamel bonding agent. 3. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement. 4. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of the groups lined with GC dentin cement. 5. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement and the group directly bonded with CHOICE-dentin/enamel bonding agent.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.1
• /
• pp.26-33
• /
• 2004

Self-etching priming bonding system was recently developed in order to simplify the clinical skills & save chair time after continuous improvements on dentin bonding agents. To test the magnitude of microleakage of a new "self-etching priming bonding agent" using sound premolar 4th, 5th, 6th generation dentin bonding agent was applied. Measure the magnitude of infiltration to the gap of enamel-restoration interface and dentin-restoration interface. After bonding of composite resin to sample surfaces according to the manufactures direction and 500 times thermocycling on dwell time 30 second, and microleakage was measured by the ratio of the depth to the axial wall and the magnitude of infiltration. Afterward analyzed by ANOVA test. The result were as follows ; 1. Enamel groups showed lesser microleakage (Group I, II, III, IV) than dentin groups(Group V, VI, VII, VIII). (p<0.05) 2. There are no statical differences among the dentin groups, in enamel groups, group IV showed more microleakage than group I, II, III. (p<0.05). For a clinical acceptance, better enamel marginal adaptation is required.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.442-449
• /
• 2009

The aim of this study was to examine that thick dentin bonding agent application or low modulus composite restoration could reduce stresses on dentin bonding agent layer. A mandibular first premolar with abfraction lesion was modeled by finite element method. The lesion was restored by different composite resins with variable dentin bonding agent thickness ($50{\mu}m$, $100{\mu}m$, $150{\mu}m$). 170N of occlusal loading was applied buccally or lingually. Von Mises stress on dentin bonding agent layer were measured. When thickness of dentin bonding agent was increased von Mises stresses at dentin bonding agent were decreased in both composites. Lower elastic modulus composite restoration showed decreased von Mises stresses. On root dentin margin more stresses were generated than enamel margin. For occlusal stress relief at dentin boning agent layer to applicate thick dentin bonding agent or to choose low elastic modulus composite is recommended.

• The Journal of Advanced Prosthodontics
• /
• v.2 no.2
• /
• pp.39-45
• /
• 2010

PURPOSE. The aim of this study was to determine differences in shear bond strength to human dentin using immediate dentin sealing (IDS) technique compared to delayed dentin sealing (DDS). MATERIALS AND METHODS. Forty extracted human molars were divided into 4 groups with 10 teeth each. The control group was light-cured after application of dentin bonding agent ($Excite^{(R)}$ DSC) and cemented with $Variolink^{(R)}$. II resin cement. IDS/SE (immediate dentin sealing, $Clearfil^{TM}$ SE Bond) and IDS/SB (immediate dentin sealing, $Adapter^{TM}$ Single Bond 2) were light-cured after application of dentin bonding agent ($Clearfil^{TM}$ SE Bond and $Adapter^{TM}$ Sing Bond 2, respectively), whereas DDS specimens were not treated with any dentin bonding agent. Specimens were cemented with $Variolink^{(R)}$. II resin cement. Dentin bonding agent ($Excite^{(R)}$. DSC) was left unpolymerized until the application of porcelain restoration. Shear strength was measured using a universal testing machine at a speed of 5 mm/min and evaluated of fracture using an optical microscope. RESULTS. The mean shear bond strengths of control group and IDS/SE group were not statistically different from another at 14.86 and 11.18 MPa. Bond strength of IDS/SE group had a significantly higher mean than DDS group (3.14 MPa) (P < .05). There were no significance in the mean shear bond strength between IDS/SB (4.11 MPa) and DDS group. Evaluation of failure patterns indicates that most failures in the control group and IDS/SE groups were mixed, whereas failures in the DDS were interfacial. CONCLUSION. When preparing teeth for indirect ceramic restoration, IDS with $Clearfil^{TM}$ SE Bond results in improved shear bond strength compared with DDS.

• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.470-478
• /
• 1997

The purpose of this study was to investigate the effects of moistening mechods of dentin on the morphologic states of hybrid layers and on the interfacial bond strength between dentin and composite. Specimens were divided into 6 groups based on the surface moistening methods and materials used. After the dentin surface was conditioned with 10 % phoporic acid and irrigated: 1. The dentin surface was dried. Then bonding agent and composite were applied. 2. The dentin surface was blot-dryed. Then primer, bonding atent and composite were applied. 3. The dentin surface was dryed first. Within 20 seconds, the surface was rewetted, then primer, bonding agent and composite were applied. 4. The dentin surface was dryed. Then primer, bonding agnent and composite were applied. 5. The dentin surface was dryed first. Atter 24hrs, the surface was rewetted, and then primer, bonding agent and composite were applied. 6. The surface was conditioned with NaOCl for 5min. Then primer, bonding agent and composite were applied. To reveal the hybrid layer, scanning electron microscopy was used after the samples were ion beam etched. The shear bond strength of each group was tom pared by ANOVA. In groups 2, 3 and 4, the hybrid layer was clearly visible, but the width was more limited in group 4. In group 1 and 5, the hybrid layer was not found, and a gap was formed between dentin and composite. In group 6, the hybrid layer was not found, but the interface between the dentin and composite was intimate. The shear bond strength of each group was as follows: Group 1 : 4MPa, Group 2 : 14MPa, Group 3 : 12MPa, Group 4 : 14MPa, Group 5 : 5MPa, Group 6 : 9MPa.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.425-435
• /
• 1996

The effect of application of dentin bonding agent to the exposed dentin on the intradental nerve activity (INA), dentinal fluid movement and sealing of the dentinal tubules, was investigated in this study. The INA was recorded from the single pulp nerve unit dissected from the inferior alveolar nerve. And specimen of dentin was observed by SEM. Dentinal fluid 'movement through exposed dentin surface was measured before and after the application of dentin bonding agent. 1. Eight Ao-fiber units (conduction velocity: $8.0{\pm}4.0m$/sec) were identified. 4M NaCl evoked an irregular burst of action potentials which ceased immediately after washing. 2. In 4 $A{\delta}$-fiber units, appliction of All Bond 2 completely abolished the INA induced by 4M NaCl. Also, application of Scotchbond Multipurpose(SBMP) totally abolished the INA induced by 4M NaCl in 4 $A{\delta}$-fiber units. 3. Before the application of dentin bonding agent, outward dentinal fluid movement of $10.2{\pm}5.7\;pl{\cdot}s^{-1}{\cdot}mm^{-2}$ was obsered. But after the application of dentin bonding agent the movement of dentinal fluid was stopped. 4. The gap width of 2-$3{\mu}m$ was formed between exposed dentin and adhesive resin in the specimens applied with dentin bonding agents of All Bone 2 and SBMP. But the formation of hybrid layer and the penetration of resin into were dentinal tubules were not clearly observed in interface between dentin and adhesive resin.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.468-476
• /
• 1998

The purpose of this study was to observe the morphologic change of dentinal surface, adhesion in interface between dentin and bonding agents, and penetration pattern of resin tags into dentinal tubles according to bonding procedure of ONE-STEP universal adhesive system. Ten extracted human molars were mounted in dental stone and sectioned to expose mid-coronal occlusal dentin and again sectioned tooth crown apically. Specimens were randomly assigned to three groups for dentin conditioning with 32% phoshoric acid, two coats of bonding agents after dentin conditioning, and bond of composite resin. The surfaces of dentin were treated with etch ant and applied bonding agent, and bonded composite resin according to the directions of manufacturer. Specimens which were boned composite were sectioned longitudinally for observing interfaces between resin and dentin. Two of specimens which were sectioned longitudinally were immersed in 6 N HCL for 30 seconds and 1% NaOCL for 12 hours to partially demineralize and deproteinize the dentin substrate. Each specimen was mounted on a brass stub, sputter-coated with gold and observed under SEM. The result were as follows : 1. On the dentinal surface which was conditioned with 32% phosphoric acid. the smear layer was completely removed. orifices of dentinal tubules were opened 3-$5{\mu}m$ wide. and dentinal surface was irregular. 2. On the dentinal surface which was applied ONE-STEP. bonding agent. resin particles were observed on the orifices of dentinal tubules and intertubular dentin. 3. There were close adaptation between dentin and resin and were the pattern which composite invaded into dentin. 4. 1-$3{\mu}m$-wide hybrid layer was visible in the interface between dentin and resin. 5. Long and funnel shaped resin tags were observed in demineralized specimens. and the surfaces of tags were rough.

• Restorative Dentistry and Endodontics
• /
• v.20 no.2
• /
• pp.699-720
• /
• 1995

This study was conducted to evaluate the effect of benzalkonium chloride solution as a wetting agent instead of water on dentin bonding with NTG-GMA/BPDM system (All-bond 2, Bisco.) and DSDM system (Aelitebond, Bisco.). Benzalkonium chloride solution is a chemical disinfectant widely used in medical and dental clinics for preoperative preparation of skin and mucosa due to its strong effect of cationic surface active detergent. Eighty freshly extracted bovine lower incisor were grinded labially to expose flat dentin surface, and then were acid-etched with 10 % phosphoric acid for 15 second, water-rinsed, and dried for 10 second with air syringe. The specimens were randomly divided into 8 groups of 10 teeth. The specimens of control group were remoistured with water and the specimens of experimental groups were remoistured with 0.1 %, 0.5 %, and 1.0 % benzalkonium chloride solution respectively. And then, the Aelitefil composite resin was bonded to the pretreated surface of the specimens by use of All-bond 2 dentin bonding system or Aelitebond dentin bonding system in equal number of the specimens. The bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, the mode of failure was observed, the fractured dentin surface were examined under scanning electron microscopy, and FT-IR spectroscopy was taken for the purpose of investigating the changes of the dentin surface pretreated with benzal konium chloride solution followed by each primer of the dentin bonding systems. The results were as follows : In the group of bonding with NTG-GMA/BPDM dentin bonding agent(All-bond 2), higher tensile bond strength was only seen in the experimental group remoistured with 0.1 % benzal konium chloride solution than that in water-remoistured control group(p<0.05). In the group of bonding with DSDM dentin bonding agent (Aelitebond), no significant differences were seen between the control and each one of the experimental group(p<0.05). Higher tensile bond strength were seen in NTG-GMAIBPDM dentin bonding agent group than in DSDM dentin bonding agent group regardless of remoistur ization with benzal konium chloride solution. On the examination of failure mode, cohesive and mixed failure were predominantly seen in the group of bonding with NTG-GMAIBPDM dentin bonding agent, while adhesive failure was predominantly seen in the group of bonding with DSDM dentin bonding agent. On SEM examination of fractured surfaces, no differences of findings of primed dentin surface between the groups with and without remoisturization with benzal konium chloride solution. FT-IR spectroscopy taken from the control and the experimental group reve::.led that some higher absorbance derived from the primers binding to dentin surface was seen at the group pretreated with 0.1 % benzal konium chloride solution than at the control group of remoisturizing with water.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.4
• /
• pp.372-380
• /
• 2008

Purpose: The purpose of this study was to evaluate the effect of various methods of dentin bonding agent application on microtensile bond strength between dentin and resin, using a 2-step etch-and-rinse dentin bonding agent. Material and methods: Twenty freshly extracted human molars were obtained and divided into 4 groups of 5 teeth. 2-step etch-and-rinse dentin bonding agent was used for all groups. The control specimens were prepared using a direct immediate bonding technique. The delayed dentin sealing (A, C) specimens were prepared using an indirect approach with delayed dentin sealing. For group A, resin was built-up on uncured dentin bonding agent, and for group C, resin was built-up on pre-cured dentin bonding agent. Preparation of the immediate dentin sealing (B) specimens also used an indirect approach with immediate dentin sealing immediately following preparation. All teeth were prepared for a microtensile bond strength test. Specimens were stored in water for 24 hours. Ten beams (1.0 ${\times}$ 1.0 ${\times}$ 11 mm) from each tooth were selected for testing. Bond strength data (MPa) were analyzed with a one-way ANOVA test, and post hoc comparison was done using the Scheffe's test. Results: The mean microtensile bond strengths of control group, B and C (DDS with pre-cure) were not statisticaaly different from each other at 32.7, 33.3, 34.2 MPa. the bond strength for group A (DDS without pre-cure), 19.5 MPa, was statistically different (P < .01) from the other 3 groups. Conclusion: When preparing teeth for indirect bonded restorations, DDS with pre-curing dentin bonding agent and IDS results in the same bond strength between dentin and resin. On the contrast, the bond strength was decreased when DDS without pre-curing dentin bonding agent was used.