AN EXPERIMENTAL STUDY ON THE TENSILE STRENGTH OF COMPOSITE RESIN TO ETCHED DENTIN SURFACE

상아질면(象牙質面)에 대(對)한 복합(複合)resin 인장강도(引張強度)에 관(關)한 실험적(實驗的) 연구(硏究)

The purpose of this study was to observe the tensile strength of composite resins to etched dentin surface with the various methods of placing bonding agent before composite resin or placing composite resin alone. Recently extracted 60 maxillary incisors were chosen. These were divided into 6 groups: Group I : Immediate Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds without bonding agent. Group II : Immediate Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds with bonding agent. Group III : Silar adaptation to the etched dentin surface with 37% phosphoric acid for 60 seconds after 5 minutes of bonding agent. Group IV : Immediate Enamelite adaptation to the etched dentin surfaces with 50% phosphoric acid for 120 seconds without bonding agent. Group V : Immediate Enamelite adaptation to the etched dentin surface with 50% phosphoric acid for 120 second s with bonding again. Group VI : Enamelite adaptation to the etched dentin surface with 50% phosphoric acid for 120 seconds after 5 minutes of bonding agent. All specimens were immersed in water at $37^{\circ}C$ for 24 hours before testing. The results were as follows: 1. The tensile strength of powder/liquid composite resin system was higher than that of pastel paste composite resin system. 2. The tensile strength of the composite resin group II, III, V, & VI with bonding agent was higher than that of the composite resin group I & IV without bonding agent. 3. The tensile strength of the composite resin group III & VI after 5 minutes added to bonding agent was higher than that of the composite resin group II & V immediately added to bonding agent.