• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.269-277
• /
• 1998

This in vitro study compared the microleakage of 4 lining conditions when used with Gallium alloy GF II and Valiant PhD. Class V cavity was prepared on both buccal and lingual surface of 80 extracted human premolar & molar teeth with one margin in enamel and another in dentin. Before restoration, prepared cavities were applied to no-liner, cavity varnish, Scotchbond multipurpose, and Superbond D-liner II plus according to manufacture's instructions. The restored teeth were stored in saline for 1 week, then thermocycled for 100 times, stained with 0.5% basic fuchsin dye for 1 day, sectioned, and observed using a light microscope. Following results were obtained. 1. The leakage value of Superbond-lined group showed significantly lower than that of nolined group on both margins of Valiant PhD(p<0.05). 2; There was no significant difference between the 4 lining conditions in Gallium alloy GF II (p>0.05). 3. When We make a comparison between Gallium alloy GF II and Valiant PhD under same lining conditions, the microleakage value of Gallium alloy GF II showed lower than that of Valiant PhD on occlusal & gingival margin(p<0.05) except for Superbond-lined group(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.15 no.1
• /
• pp.107-119
• /
• 1990

The purpose of this study was to evaluate the marginal adaptability of the amalgam restorations in applying the cavity varnish (Copalite$^{(R)}$) and dentin bonding agent (Scotchbond 2$^{(R)}$) under the scanning electron microscope. For this study, eighteen sound extracted human molars were selected. Class I cavities in 12 teeth and class V cavities in 6 teeth were prepared using an air turbine with No. 701 tungsten carbide bur and finished using a low speed handpiece with No. 557 fissure bur. The prepared specimens were then divided into three groups including 4 class I cavities and 2 class V cavities in each group and restored as follows ; Group I. All the prepared cavities were restored with amalgam only (Control). Group II. Two layers of Copalite$^{(R)}$ cavity varnish were applied to the cavities with a gentle stream of air after each application and cavities were restored with amalgam. Group III. The enamel cavity margins were etched with 37% phosphoric acid gel for 60 sec., rinsed for 30 sec. and dried. One layer of visible lightcured Scotchbond Dental Adhesive$^{(R)}$ was applied and immediately cured for 20 seconds with visible light-cure unit and cavities were restored with amalgam. All the specimens were cut at the neck of the teeth and the occlusal halves of specimens were sectioned buccolingually in the longitudinal axis centering the amalgam restorations, using the disk. The cut specimens were ground with sandpapers (400, 600, 800, 1000 grit), and cleaned for 5 minutes in the ultrasonic cleaner (Brason Co. U.S.A.). In the cut surfaces, the amalgam - tooth interfaces were examined under the scanning electron microscope (JSM, 35C type, JEOL). The obtained results were as follows ; 1. The amalgam-tooth interfaces were reduced more significantly in the Copalite$^{(R)}$ and Scotchbond 2$^{(R)}$ application group than in the control group. 2. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed the findings similar to the Copalite$^{(R)}$ application group in the cavity floor, and the marginal adaptability was better in the side wall than in the cavity floor. 3. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed better marginal adaptability in the occlusal margin than in the gingival margin. 4. The marginal adaptability was in the order of the Scothbond 2$^{(R)}$ application group, the Copalite$^{(R)}$ application group and the control group.

• Restorative Dentistry and Endodontics
• /
• v.21 no.2
• /
• pp.559-568
• /
• 1996

The purpose of this study was to evaluate the micro leakage of composite resin when various phosphoric acid agents were used to etch the enamel and dentin. In this study, class V cavities were prepared on the buccal surfaces of fourty extracted human molar teeth, and they were randomly assigned into 4 groups with 10 teeth. The cavities of each groups were etched with 10%, 32%, 35% and 37% phosphoric acids for 15 seconds, washed and dried and the cavities were restored with composite resin after application of the adhesive. The specimens were immersed in 2% methylene blue solution for 3 days. And then, the specimens were sectioned buccoligually. Degree of dye penetration at tooth-restoration interfaces was examined by Inverted Metallurgical Microscope at the occlusal and gingival margins. The result were as follows : 1. The degree of microleakage at occlusal and gingival margin in all group was statistically difference among 10% and 35% (P<0.01), 10% and 37% (P<0.01), 32% and 35% (P<0.05) and 32% and 37% (P<0.05) acid concentrations, but was not statistically difference between 10% and 32%, 35% and 37% acid concentrations (P>0.05). The degree of microleakage was showed to dimish with increase of acid concentration. 2. The degree of microleakage at the occlusal margin was statistically significant difference among 10% and 32%,10% and 35%, 10% and 37% acid concentrations(P<0.05). The degree of microleakage among 32% and 35%, 32% and 37% and 32% and 37% acid concentrations was not statistically significant difference. 3. In comparison of microleakage at the gingival margin, the degree of microleakage above 32% acid concentration was not showed less than 10% acid concentration (P>0.05). In comparison of 32%, 35%, 37% acid concentrations, the degree of microleakage at 35% and 37% acid concentrations was showed less than 32% acid concentration(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.32 no.5
• /
• pp.469-475
• /
• 2007

The purpose of this study was to evaluate the effect of a new resin monomer on the microleakage of composite resin restorations. By adding new methoxylated Bis-GMA (Bis-M-GMA, 2,2-bis[4-(2-methoxy-3-methacryloyloxy propoxy) phenyl] propane) having low viscosity, the content of TEGDMA which has adverse effects on polymerization shrinkage might be decreased. As a result, microleakage might be improved. $2\;mm\;{\times}\;2\;mm\;{\times}\;2\;mm$ cavities with occlusal margins in enamel and gingival margins in dentin were prepared on buccal and lingual surfaces of 40 extracted human premolars. Prepared teeth were randomly divided into four groups and restored with Clearfil SE bond (Kuraray, Japan) and one of experimental composite resins; EX1, Experimental composite resin1 (Bis-M-GMA/TEGDMA = 95/5 wt%, 40 mm nanofillers); EX2, Experimental composite resin2 (Bis-M-GMA/TEGDMA = 95/5 wt%, 20 mm nanofillers); EX3, Experimental composite resin3 (Bis-GMA/TEGDMA = 70/30 wt%, 40 nm nanofillers); and Filtek Z250 (3M ESPE, USA) was filed as a control group. The restored teeth were thermocycled, and immersed in 2% methylene blue solution for 24 hours. The teeth were sectioned buccolingually with a low speed diamond saw and evaluated for microleakage under stereomicroscope. The data were statistically analyzed by Pearson Chi-Square test and Fisher Exact test (p = 0.05). The microleakage scores seen at the enamel margin were significantly lower than those of dentin margin (p = 0.007). There were no significant differences among the composite resins in the microleakage scores within each margin (p > 0.05). Bis-M-GMA, a new resin monomer having low viscosity, might in part replace high viscous Bis-CMA and might improve the quality of composite resin.

• Restorative Dentistry and Endodontics
• /
• v.27 no.2
• /
• pp.158-174
• /
• 2002

The aim of this study was to investigate the effect of light irradiation modes on polymerization shrinkage, degree of cure and microleakage of a composite resin. VIP$^{TM}$ (Bisco Dental Products, Schaumburg, IL, USA) and Optilux 501$^{TM}$ (Demetron/Kerr, Danbury, CT, USA) were used for curing Filtek$^{TM}$ Z-250 (3M Dental Products, St. Paul., MN, USA) composite resin using following irradiation modes: VIP$^{TM}$ (Bisco) 200mW/$\textrm{cm}^2$ (V2), 400mW/$\textrm{cm}^2$ (V4), 600mW/$\textrm{cm}^2$ (V6), Pulse-delay (200 mW/$\textrm{cm}^2$ 3 seconds, 5 minutes wait, 600mW/$\textrm{cm}^2$ 30seconds, VPD) and Optilux 501$^{TM}$ (Demetron/Kerr) C-mode (OC), R-mode (OR). Linear polymerization shrinkage of the composite specimens were measured using Linometer (R&B, Daejeon, Korea) for 90 seconds for V2, V4, V6, OC, OR groups and for up to 363 seconds for VPD group (n=10, each). Degree of conversion was measured using FTIR spectrometer (IFS 120 HR, Bruker Karlsruhe, Germany) at the bottom surface of 2 mm thick composite specimens V2, Y4, V6, OC groups were measured separately at five irradiation times (5, 10, 20, 40, 60 seconds) and OR, VPD groups were measured in the above mentioned irradiation modes (n=5 each). Microhardness was measured using Digital microhardness tester (FM7, Future-Tech Co., Tokyo, Japan) at the top and bottom surfaces of 2mm thick composite specimens after exposure to the same irradiation modes as the test of degree of conversion(n=3, each). For the microleakage test, class V cavities were prepared on the distal surface of the ninety extracted human third molars. The cavities were restored with one of the following irradiation modes : V2/60 seconds, V4/40 seconds, V6/30 seconds, VPD , OC and OR. Microleakage was assessed by dye penetration along enamel and dentin margins of cavities. Mean polymerization shrinkage, mean degree of conversion and mean microhardness values for all groups at each time were analyzed using one-way ANOVA and Duncan's multiple range test, and using chi-square test far microleakage values. The results were as follows : . Polymerization shrinkage was increased with higher light intensity in groups using VIP$^{TM}$ (Bisco) : the highest with 600mW/$\textrm{cm}^2$, followed by Pulse-delay, 400mW/$\textrm{cm}^2$ and 200mW/$\textrm{cm}^2$ groups, The degree of polymerization shrinkage was higher with Continuous mode than with Ramp mode in groups using Optilux 501$^{TM}$ (Demetron/Kerr). . Degree of conversion and microhardness values were higher with higher light intensity. The final degree of conversion was in the range of 44.7 to 54.98% and the final microhardness value in the range of 34.10 to 56.30. . Microleakage was greater in dentin margin than in enamel margin. Higher light intensity showed more microleakage in dentin margin in groups using VIP$^{TM}$ (Bisco). The microleakage was the lowest with Continuous mode in enamel margin and with Ramp mode in dentin margin when Optilux 501$^{TM}$ (Demetron/Kerr) was used.

• Restorative Dentistry and Endodontics
• /
• v.27 no.4
• /
• pp.403-410
• /
• 2002

Several ways of curing are being tried to improve material's properties and reduce marginal gap. However, all are considering about the pattern of light intensity. It was noted from the preliminary study the change of light wavelength from filter changing may give an impact on material's property and microleakage. The object of this study was to verify the effect of filters with various wavelength width on the microhardness and microleakage of composite resin ; hybrid type of DenFil and submicron hybrid type of Esthet X. Composite resins were cured using 3 kinds of filter; narrow-banded(465-475 nm), mid-banded(430-470 nm), wide-banded(400-500 nm). After the estimation of microhardness. degree of dye penetration and the maximum gap from SEM evaluation were done between 4 groups that showed no difference in microhardness value of the lower surface . The results were as follows : 1 Adequate microhardness could not be gained with a narrow-banded filter irrespective of curing time. At the upper surface, DenFil should be polymerized with middle or wide-banded filter for 20 seconds at least, while Esthet X be col$.$ed with middle or wide-banded filter for 30 seconds at least to get simitar hardness value to control group. 2. There was little dye penetration in enamel margin, but all dentin margins skewed much more dye penetration irrespective of curing conditions. Although there was no statistical difference, groups cured with mid-banded filter for 40 seconds and with wide-width filter for 20 seconds showed relatively less dye penetration. 3. It was revealed from the SEM examination that group cured with wide-banded filter had the smallest gap without statistical significance. Spearman's rho test showed that the correlation between the results of dye penetration and SEM examination was very low. From these results, it could be concluded that curing with wide-width filter would be better than the other techniques, even though the curing technique using mid-width filter seems to have its own unique advantage.

• Restorative Dentistry and Endodontics
• /
• v.32 no.5
• /
• pp.437-444
• /
• 2007

The purpose of this study was to compare the marginal microleakage of different 2-step adhesive systems in Class V cavities prepared with different diamond points. Forty Class V cavities were prepared with two different (coarse or fine) diamond points on cervical third of extracted molars. The occlusal and gingival margin of cavities was located in enamel and dentin, respectively. They were divided into one of four equal groups (n = 10) and ; Group 1-prepared with coarse diamond point (EX-41), restored with Single Bond and Z 250, Group 2-prepared with fine diamond piont (TF-21F), restored with Sing)e Bond and Z 250, Group 3-prepared with coarse diamond point (EX-41), restored with Clearfil SE Bond and Clearfil AP-X, Group 4-prepared with fine diamond point (TF-21F), restored with Clearfil SE Bond and Clearfil AP-X. Specimens were thermocycled, immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed leakages at enamel and dentinal margins. Data were analyzed using Mann-Whitney and Wilcoxon signed ranked test. In this study, marginal microleakage or Single Bond was not affected by type of diamond points. But Clearfil SE Bond showed higher marginal microleakage at both enamel and dentinal margin when Class V cavity was prepared with coarse diamond point.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.4
• /
• pp.558-563
• /
• 2000

The lasers have been used in dentistry for more than 30 years and the application of lasers for drilling dental hard tissue has been investigated since the early developement of lasers. Recently, the Er:YAG laser was invented for hard tissue ablation. The Er:YAG laser, having a wavelength of 2.94um, is highly absorbed in both water and hydroxiapatite, leading to a very effective material for hard tissue removal by bursting off the solid tissue component that is, enamel and dentin are removed by the Er :YAG laser by water vaporization and microexplosion, without any melting of inorganic tissues. Therefore, the Er:YAG laser produced round craters with well defined margins and the surrounding tissues had no cracks and no charring. When used for cavity preparation, pulpal damage should not occur if hear buildup is minimized by careful selection of exposure parameters and by use of a water spray. The present study demonstrated that the Er:YAG laser cut the tooth substance adequately for composite resin restoration, without having undesirable side effects such as harmful effects on the pulp, discoloration or cracking etc. Also, the child patients were well cooperative during laser treatment mainly because of little noise, lesser vibration and minimal pain compared to conventional means of cavity preparation.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.327-334
• /
• 2007

The purpose of this study was to evaluate the effect of burs on microleakage of Class V resin restorations when a self-etching primer adhesive was used. Forty Class V cavities were prepared with four different cutting burs on extracted third molars, and divided into one of four equal groups (n = 10); Group 1-plain cut carbide bur (no. 245), Group 2-cross cut carbide bur (no. 557), Group 3-fine diamond bur (TF-21F), Group 4-standard diamond bur (EX-41). The occlusal and gingival margin of cavities was located in enamel and dentin, respectively. Cavities were treated with Clearfil SE Bond and restored with Clearfil AP-X. Specimens were thermocycled, immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed leakages at enamel and dentinal margins. Data were analyzed using Mann-Whitney and Wilcoxon signed ranked test. The results of this study were as follows; 1. At enamel margin, microleakage of group 4 was statistically higher than those of group 1, 2 and 3 (p < 0.01). 2. At dentinal margin, microleakage of group 4 was statistically higher than group 3 (p < 0.01), but group 1 and 2 were not statistically different with group 3 and 4. 3. Enamel microleakage was statistically higher than dentinal microleakage in group 1, 2 and 3 (p < 0.05), but statistical difference between the microleakage of enamel and dentinal margin was not in Group 4. In conclusion, the use of coarse diamond bur showed high microleakage at both enamel and dentinal margin when Clearfil SE Bond was used in class V cavity.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.2
• /
• pp.222-233
• /
• 2007

One of the most important and basic test of dental restorative materials is the evaluation of microleakage into the tooth-restorative interface. There are many techniques to test microleakage, but most of them have several disadvantages. Recently developed microtomography(micro-CT) can provide the three dimensional image and information about the internal component in non-destructive way, therefore using micro-CT, it is possible to evaluate microleakage exactly in quantitative manner. The purpose of this study is to find a new method for quantitative and non-destructive evaluation of microleakage in composite resin restorations using micro-CT and to compare the new method with conventional dye penetration method. Thus, microleakages of two kinds of dentin bonding systems were evaluated with above two methods. 40 extracted sound human premolars were randomly divided into two groups consisting of 20 samples and restored accordingly. Group 1 : Class V resin restorations with $Adper^{TM}$ Singe Bond Group, 2 : Class V resin restorations with $Adper^{TM}\;Promp^{TM}$ L-pop. The $Filtek^{TM}$ Supreme was applied to the Class V cavities of all teeth. After that, 10 teeth from each group were applied to evaluation of microleakage using micro-CT, and other 10 teeth from each group were using conventional dye penetration method. The conclusions of this study were as follow : 1 Using micro-CT, Group 1 showed significantly less microleakage than Group 2 and there was statistically significant difference(p<0.01) between two groups. 2. Using conventional dye penetration method, Group 1 leaked less than Group 2 and there was statistically significant difference(p<0.01) between two groups 3. The difference between two groups is more evident in the method using micro-CT. 4. In all two methods, microleakage appeared more into the cavities to dentinal margins than enamel margins.