• Restorative Dentistry and Endodontics
• /
• v.40 no.2
• /
• pp.136-142
• /
• 2015

Objectives: The aim of this study was to evaluate the effects of tri-antibiotic paste (TAP) on microtensile bond strengths (MTBS) of dental adhesives to dentin. Materials and Methods: Sixty extracted molars had their occlusal surfaces flattened to expose dentin. They were divided into two groups, i.e., control group with no dentin treatment and experimental group with dentin treatment with TAP. After 10 days, specimens were bonded using self-etch (Filtek P90 adhesive) or etch-and-rinse (Adper Single Bond Plus) adhesives and restored with composite resin. Teeth were sectioned into beams, and the specimens were subjected to MTBS test. Data were analyzed using two-way ANOVA and post hoc Tukey tests. Results: There was a statistically significant interaction between dentin treatment and adhesive on MTBS to coronal dentin (p = 0.003). Despite a trend towards worse MTBS being noticed in the experimental groups, TAP application showed no significant effect on MTBS (p = 0.064). Conclusions: The etch-and-rinse adhesive Adper Single Bond Plus presented higher mean bond strengths than the self-etch adhesive Filtek P90, irrespective of the group. The superior bond performance for Adper Single Bond when compared to Filtek P90 adhesive was confirmed by a fewer number of adhesive failures. The influence of TAP in bond strength is insignificant.

• Restorative Dentistry and Endodontics
• /
• v.40 no.1
• /
• pp.30-36
• /
• 2015

Objectives: This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. Materials and Methods: 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resins with extracted human molars stored in saline for 24 hr. Testing was performed using the wire-loop method and a universal testing machine. Bond strength data was statistically analyzed using two way analysis of variance (ANOVA) and Tukey's post hoc test. Results: Two way ANOVA revealed significant differences for the factors of dentin adhesives and composite resins, and significant interaction effect (p < 0.001). All combinations with Xeno V (Dentsply De Trey) and Clearfil $S^3$ Bond (Kuraray Dental) adhesives showed no significant differences in micro-shear bond strength, but other adhesives showed significant differences depending on the composite resin (p < 0.05). Contrary to the other adhesives, Xeno V and BondForce (Tokuyama Dental) had higher bond strengths with the same manufacturer's composite resin than other manufacturer's composite resin. Conclusions: Not all combinations of adhesive and composite resin by same manufacturers failed to show significantly higher bond strengths than mixed manufacturer combinations.

• Restorative Dentistry and Endodontics
• /
• v.40 no.3
• /
• pp.202-208
• /
• 2015

Objectives: This study determined the effect of the air-stream application time and the bonding technique on the dentin bond strength of adhesives with different solvents. Furthermore, the content and volatilization rate of the solvents contained in the adhesives were also evaluated. Materials and Methods:Three adhesive systems with different solvents (Stae, SDI, acetone; XP Bond, Dentsply De Trey, butanol; Ambar, FGM, ethanol) were evaluated. The concentrations and evaporation rates of each adhesive were measured using an analytical balance. After acid-etching and rinsing, medium occlusal dentin surfaces of human molars were kept moist (conventional) or were treated with 10% sodium hypochlorite for deproteinization. After applying adhesives over the dentin, slight air-stream was applied for 10, 30 or 60 sec. Composite cylinders were built up and submitted to shear testing. The data were submitted to ANOVA and Tukey's test (${\alpha}=0.05$). Results: Stae showed the highest solvent content and Ambar the lowest. Acetone presented the highest evaporation rate, followed by butanol. Shear bond strengths were significantly affected only by the factors of 'adhesive' and 'bonding technique' (p < 0.05), while the factor 'duration of air-stream' was not significant. Deproteinization of dentin increased the bond strength (p < 0.05). Stae showed the lowest bond strength values (p < 0.05), while no significant difference was observed between XP Bond and Ambar. Conclusions: Despite the differences in content and evaporation rate of the solvents, the duration of air-stream application did not affect the bond strength to dentin irrespective of the bonding technique.

• Restorative Dentistry and Endodontics
• /
• v.26 no.1
• /
• pp.51-63
• /
• 2001

In order to know the effect of dentin bonding agents on the restoration of cervical abrasion, Scotchbond Multipurpose Single Bond and Clearfil Liner Bond 2 were used in 51 teeth with abrasion lesion and normal teeth. The surface structure and dentinal tubules of acid etched dentin and resin replica were examined using scanning electron microscopy. The interfacial morphology between dentin and adhesives was investigated by confocal laser scanning microscopy. Following results were obtained. 1. The hybrid layer and resin tag of the dentin showing cross-sectional surface of dentinal tubules are thicker and longer than those of dentin showing oblique surface of dentinal tubules. 2. The sclerotic cast was frequently observed in dentinal tubule, and the cast looked like cuboidal or rhomboidal-shaped crystals clumped from outer side to inner side. 3. The formation of hybrid layer and resin tag was the most prominent in Scotchbond Multipurpose group, whereas Clearfil Liner Bond 2 group showed very poor formation. The formation of hybrid layer and resin tag in Single Bond group was less than Scotchbond Multipurpose group.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.313-326
• /
• 2007

The purpose of this study was to prove that an intermediate resin layer (IRL) oan increase the bond strength to dentin by reducing the permeability of single-step adhesives. Flat dentin surfaces were created on buccal and lingual side of freshly extracted third molar using a low-speed diamond saw under copious water flow. Approximately 2.0 mm thick axially sectioned dentin slice was abraded with wet #600 SiC paper. Three single-step self-etch adhesives; Adper Prompt L-Pop (3M ESPE, St Paul, MN, USA), One-Up Bond F (Tokuyama Corp, Tokyo, Japan) and Xeno III (Dentsply, Konstanz, Germany) were used in this study. Each adhesive groups were again subdivided into ten groups by; whether IRL was used or not; whether adhesives were cured with light before application or IRL or not; the mode of composite application. The results of this study were as follows; 1. Bond strength of single-step adhesives increased by an additional coating of intermediate resin layer, and this increasement was statistically signigicant when self-cured composite was used (p < 0.001). 2. When using IRL, there were no difference on bond strengths regardless the curing procedure of single-step adhesives. 3. There were no significant difference on bond strengths between usage of AB2 or SM as an IRL. 4. The thickness of Hybrid layer was correlated with the acidity of adhesive used, and the nanoleakage represented by silver deposits and grains was examined within hybrid and adhesive layer in most of single-step adhesives. 5. Neither thickness of hybrid layer nor nanoleakage were related to bond strength.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.321-338
• /
• 1996

The purpose of this study was to evaluate the effect of moistening and air-drying of acid conditioned dentin and enamel on the marginal microleakage. In this study, Class V cavity were prepared on both buccal and lingual surface of sixty extracted human premolars with cementum margin. These specimens were randomly devided into three groups and three dentin adhesives(Scotchbond Multi-Purpose, All bond 2, Prisma Universal Bond 3) were applied to each group. The specimens in each group were subdevided into four groups (Wet/primed, Dry/primed, Wet/not primed, Dry/not primed) and the etched dentin and enamel surface were treated these four surface treatments prior to the placement of a bonding agent or adhesive. Wet/primed group was simply blot-dried with a damp facial tissue before primer placement ; Dry/primed group was air dried for 30 seconds before the placement of a primer ; Wet/not primed group and Dry/not primed group were not primed after blot dried and air dried for 30 seconds each group. The bonding agent and composite resin were applied for each group. All specimens were exposed to 500 cycle of thermal stress. Specimens were placed in a silver nitrate solution and then sectioned buccolingually through the center of the restoration. The dye penetrations of the specimens were observed with a stereo microscope. The statistical test were applied to the results using a one way analysis variance (ANOVA) and Duncan's multiple range test. The aspects of silver ion penetration into the resin/dentin interface were examined under scanning electron microscopy. The results were as follows. 1. In all groups, the enamel margin showed significantly lower leakage value than the cementum margin (p<0.05). 2. Regardless of various surface treatment and dentin adhesives, there was no significant difference at the enamel margins (p>0.05). 3. At the dentin margins, the leakage values of Dry/not primed group showed significantly higher than that of the other groups (p<0.05). The leakage values of Wet/primed group showed significantly lower than that of the other groups, but, there was no significant difference between Wet group and Dry group. 4. There was no significantly difference between the dentin adhesives regarding the surface treatments in all groups(p>0.05). 5. On the backscatterd scanning electron microscopy observation, the penetration of the silver ion occured at the bonding resin/dentin interface. In the Wet/primed group, resindentin hybrid zone and resin penetration into the dentin was observed. The resin tags were compactively formed to a thickness of $3\sim4{\mu}m$ at the upper part of dentinal tubules. In the Dry/primed group, the thickness of the hybrid zone and the diameter, depth of the resin tags diminished. In the Non-primed groups, the hybrid zone was not identified and few resin tag was observed. There was the gap formation in the resin/dentin interface.

• Restorative Dentistry and Endodontics
• /
• v.28 no.1
• /
• pp.1-10
• /
• 2003

This study investigated the influence of IRM on marginal microleakage of 5th generation adhesives. Class V cavities with gingival margins in dentin were prepared on both buccal and lingual surfaces of 60 extract-ed human molar teeth. Prepared teeth were randomly divided into six groups. Group 1 and 4 received no temporary restoration with IRM. Group 2 and 5 were covered with IRM mixed at P/L ratio(10g/1g). Group 3 and 6 were covered with IRM mixed at P/L ratio(10g/2g). The temporary restorations were removed mechanically with an ultrasonic scaler after one-week storage in distilled water. The cavities were restored using one of two adhesives and composites ; Single Bond/Filtek Z 250(Croup 1, 2 and 3), UniFil Bond/UniFil F(Group 4, 5 and 6). Following one day storage in distilled water, the restored teeth were thermocycled for 500 cycles(between $5^{\circ}C{\;}and{\;}55^{\circ}C$) and immersed in 2 % methylene blue for dye penetration testing. The results were analysed using Kruskal-Wallis Test, Mann-Whitney and Wilcoxon signed ranked test at a significance level of 0.05. The results of this study were as follows 1. Ranking of mean microleakage scores at the enamel margins was Group 10.05) 4. At the dentin margins, the microleakage of the group not pretreated with IRM was lower than that of the group pretreated with IRM. And the microleakage of UniFil Bond was lower than that of Single Bond. 5. Compared with microleakages between the enamel and dentin margins of each groups, Group 1, 2, 3, 4, 5 and 6 at dentin margin were higher microleakage than those at enamel margin. There were significant difference between enamel and dentin microleakage of Group 2 and 3(p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.18 no.2
• /
• pp.483-496
• /
• 1993

Dentin hypersensitivity medicaments such as Gluma, Scotchbond 2, All-Bond 2, which are resin adhesives, were used to compare the sealing effects of dentinal tubule under mechanical stress. Topical application of above medicaments on the dentin surfaces of extracted teeth followed by artificial tooth brushing for 6 weeks was performed for the comparison. The following conclusions on the degree of dentinal tubule exposure versus time by were reached by using polyvinyl siloxane impression material for taking the impression, epoxy resin for the duplication and SEM for observing the surface. 1. SEM was used to compare the accuracy of the duplicated surface, but no differences were found when teeth samples and the duplicated surfaces were observed. 2. After comparing the degree of dentinal tubules exposure with varnish applied contrast group, resin adhesive materials showed much less exposure as time went by. 3. The results indicated that AU-Bond 2 adhesive, under mechanical stress, showed lesser exposure of dentinal tubules comparing with Gluma and Scotchbond 2 adhesives After the results were put together, it was demonstrated that resin replica method is an useful way to evaluate the treatment effects of the dentinal tubule hypersensitivity medicaments. Also, it was noticed that under mechanical stress, All-Bond 2, classified as fourth generation, illustrated the best dentinal tubules sealing effects.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.365-376
• /
• 2007

The purpose of this study was to evaluate the effect of different etching times on microtensile bond strength (${\mu}TBS$) to dentin both initial and after thermocycling with 3 different types of total-etching adhesives. Fifty four teeth were divided into 18 groups by etching times (5, 15, 25 sec), adhesives types (Scotchbond Multipurpose (SM), Single Bond (SB), One-Step (OS)) and number of thermocycling (0, 2,000 cycles). Flat dentin surfaces were prepared on mid-coronal dentin of extracted third molars. After exposed fresh dentin surfaces were polished with 600-grit SiC papers, each specimen was acid-etched with 35% phosphoric acid (5, 15, 25 sec) and bonded with 3 different types of total etching adhesives respectively. Then, hybrid composite Z-250 was built up. Half of them were not thermocycled (control group) and the ethers were subjected to 2,000 thermocycle (experimental group). They were sectioned occluso-gingivally into $1.0\;{\times}\;1.0\;mm^2$ composite-dentin beams and tested with universal testing machine at a crosshead speed of 1.0 mm/min. Within limited data of this study, the results were as follows 1. There was no statistically significant difference in ${\mu}TBS$ between the thermocycled and non-thermocycled groups, except for both SM and SB etched for 25 sec. 2. In thermocycled SM and SB groups, bond strength decreased by extended etching time. In total etching systems, adhesive durability for dentin could be affected by type of solvents in adhesive and etching time. Especially, extended etching time may cause deteriorate effects on bond strength when ethanol-based adhesive was used.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.585.2-585
• /
• 2001

The purpose of this study was to evaluate the microtensile bond strength of sixth-generation adhesives according to various dentin surface treatments and to observe the interface between resin(Z-100TM) and dentin by SEM. This study employed forty-five non-caries extracted human molars and three adhesive systems were used; All-Bond 2(AB), One-Up Bond F(OU), AQ-Bond(AQ).; group 1, 2, 3 were used AB and were respectively treated by smearing(S), ultrasonic cleansing(US), etching(E).(omitted)