• Restorative Dentistry and Endodontics
• /
• 제42권3호
• /
• pp.206-215
• /
• 2017

Objectives: To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide ($Al_2O_3$) particles at different pressures. Materials and Methods: Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abrasion pressures (1, 2, and 2.8 bar), and each group was further divided into 2 groups depending on aging parameters (n = 12). Panavia F 2.0 was placed on pre-conditioned zirconia surfaces, and SBS testing was performed either after 24 hours or 10,000 fatigue cycles (cyclic loading) and 5,000 thermocycles. Non-contact profilometry was used to measure surface roughness. Failure modes were evaluated under optical and scanning electron microscopy. The data were analyzed using 2-way analysis of variance and ${\chi}^2$ tests (${\alpha}=0.05$). Results: The 2.8 bar group showed significantly higher surface roughness compared to the 1 bar group (p < 0.05). The interaction between pressure and time/cycling was not significant on SBS, and pressure did not have a significant effect either. SBS was significantly higher (p = 0.006) for 24 hours storage compared to CLTC. The 2 bar-CLTC group presented significantly higher percentage of pre-test failure during fatigue compared to the other groups. Mixed-failure mode was more frequent than adhesive failure. Conclusions: CLTC significantly decreased the SBS values regardless of the air-abrasion pressure used.

• 대한치과의사협회지
• /
• 제57권5호
• /
• pp.264-268
• /
• 2019

Objectives: This study aimed to measure the water sorption / solubility of Biodentine, composite resin and glass ionomer cement. Materials and Methods: The materials used in this study were Biodentine(BD), Filtek Z250(FZ) and Ketac Molar(KM). Twenty disc-shaped specimens of each material were prepared of 6mm diameter and 1mm thickness. All specimens were desiccated for 24 hours and weighed(m1). After then, They were immersed in distilled water and stored at $37^{\circ}C$. 1 week later, They were washed with running water, wiped with absorbent paper and weighed(m2). Finally, They were dried for 24 hours and weighed(m3). Water sorption and solubility, net water uptake were calculated. Results: KM and BD showed high water sorption than FZ(P<0.05). KM and BD exhibited similar water sorption(P<0.05). BD exhibited high solubility than KM(P=0.012). BD exhibited high net water uptake than FZ(P=0.008). Conclusion: Biodentine showed higher water sorption, solubility and net water uptake than Filtek Z250 and Ketac Molar. Within limitation of this study, it is not recommended to use Biodentine for permanent restoration.

• 디지털융복합연구
• /
• 제19권3호
• /
• pp.245-251
• /
• 2021

본 연구에서는 지르코니아의 새로운 표면처리 방법이 레진 시멘트와의 전단결합강도에 미치는 영향을 알아보고자 하였다. 지르코니아 표면처리 방법 따라 5개의 그룹으로 분류하였다: 표면처리 미시행한 군(CON군), 100℃에서 9% 불산에 10분간 노출시킨 군(HF군), 15% 지르코니아 슬러리를 적용한 군(ZS15군), 30% 지르코니아 슬러리를 적용한 군(ZS30군), 50% 지르코니아 슬러리를 적용한 군(ZS50군). 표면처리한 지르코니아 위에 레진 시멘트를 적용하였고, 열 순환 처리 후 지르코니아와 레진 시멘트 간의 전단결합강도를 측정하였다. 전단결합강도에 대한 통계 방법으로 Kruskal-Wallis test와 Mann-Whitney U test 및 Boneferroni correction를 사용하였다(α=.05/10=.005). 지르코니아 슬러리를 적용한 군은 CON군과 HF군에 비해 높은 전단결합강도를 보였다(p<.05/10=.005). 지르코니아 슬러리를 이용한 표면처리 방법은 레진 시멘트와 지르코니아 간의 전단결합강도를 증대시킴을 확인하였다. 본 연구 결과, 새로운 표면처리 방법은 지르코니아가 지닌 접착의 한계점을 보완하고 개선함으로써 지르코니아의 보다 다양한 임상적 적용 가능성을 기대할 수 있을 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제30권6호
• /
• pp.493-504
• /
• 2005

본 연구는 상아질 접착제와 레진 시멘트의 적합성 여부를 알아보고자 시행하였다. 발거한 제3대구치의 상아질 표면을 노출시킨 후 Tescera ATL 복합레진 시편을 상아질 접착제 [All Bond 2 (Bisco), Clearfil SE Bond (Kuraray), Adper Prompt L-POP (3M), One-Up Bond F (Tokuyama)]와 레진시멘트 [Choice (Bisco), Panavia F (Kuraray), RelyX ARC (3M), Bistite II DC (Tokuyama)]로 접착하고 미세인장 결합강도 및 주사전자 현미경 관찰을 시행한 결론은 다음과 같다. 1. Clearfil SE Bond와 All-Bond 2가 Prompt L-Pop과 One-Up Bond F 보다 높은 미세인장 결합강도를 보였다(p<0.05). 2. Clearfil SE Bond와 All-Bond 2 사용시 1-step 상아질 접착제보다 혼성층이 두껍고 레진 tag가 길었다.

• Restorative Dentistry and Endodontics
• /
• 제13권1호
• /
• pp.69-78
• /
• 1988

The study was designed to establish a more nearly quantitative method for assessing the marginal leakage of dental restorations. 27 Class V cavities with $45^{\circ}$ bevel joint were prepared and classified into 2 groups. One group was filled with Scotchbond and silux. The other group was filled with glass ionomer cement, Scotchbond and silux. After finishing, all specimens were subjected manually to 100 thermal cycles at $0^{\circ}C$ and $100^{\circ}C$ water-bath. They were soaked in a samarium nitrate solution for 3 hours, irradiated with flux of $6{\times}10^{12}$ neutrons/$cm^2$/sec for 11 hours, cooled for 200 hours, counted with the HPGE detector and the tracer uptake was determined by comparison with a standard of samarium (10 ${\mu}g$). The following results were obtained. 1. Both of the two groups showed a considerable amounts of marginal leakage. 2. The group filled without glass ionomer cement base showed more marginal leakage than the group filled with glass ionomer cement base. 3. Neutron Activation Analysis produced a good quantitative method to measure the marginal leakage and samarium was appropriate to measure the marginal leakage of resin restorations using neutron activation analysis.

• Restorative Dentistry and Endodontics
• /
• 제46권1호
• /
• pp.3.1-3.14
• /
• 2021

Objectives: This study aimed to evaluate the interface between a calcium silicate cement (CSC), Biodentine and dental adhesives in terms of sealing ability. Materials and Methods: Microleakage test: 160 standardized class II cavities were prepared on 80 extracted human molars. The cavities were filled with Biodentine and then divided into 2 experimental groups according to the time of restoration: composite resin obturation 15 minutes after Biodentine handling (D0); restoration after 7 days (D7). Each group was then divided into 8 subgroups (n = 5) according to the adhesive system used: etch-and-rinse adhesive (Prime & Bond); self-etch adhesive 2 steps (Optibond XTR and Clearfil SE Bond); self-etch adhesive 1 step (Xeno III, G-aenial Bond, and Clearfil Tri-S Bond); and universal used as etch-and-rinse or self-etch (ScotchBond Universal ER or SE). After thermocycling, the teeth were immersed in a silver nitrate solution, stained, longitudinally sectioned, and the Biodentine/adhesive percolation was quantified. Scanning electron microscopic observations: Biodentine/adhesive interfaces were observed. Results: A tendency towards less microleakage was observed when Biodentine was etched (2.47%) and when restorations were done without delay (D0: 4.31%, D7: 6.78%), but this was not significant. The adhesives containing 10-methacryloyloxydecyl dihydrogen phosphate monomer showed the most stable results at both times studied. All Biodentine/adhesive interfaces were homogeneous and regular. Conclusions: The good sealing of the CSC/adhesive interface is not a function of the system adhesive family used or the cement maturation before restoration. Biodentine can be used as a dentine substitute.

• 구강회복응용과학지
• /
• 제31권1호
• /
• pp.1-9
• /
• 2015

목적: 중합방법 및 측정시기에 따른 여러 이중중합 레진 시멘트의 기계적 성질인 압축강도와 간접인장강도를 비교 평가하는 것이다. 연구 재료 및 방법: 1개의 레진강화형 글래스아이오노머 시멘트인 FujiCEM 2, 2개의 전통적인 이중중합 레진 시멘트인 RelyX ARC와 Multilink N, 2개의 이중중합 자가접착 레진 시멘트인 RelyX U200과 G-CEM LinkAce를 사용하였다. 제조사의 지시에 따라 시멘트를 혼합하여 압축강도와 간접인장강도 측정을 위한 시편을 제작하였다. 중합방법 및 측정시기의 영향을 평가하기 위해 시멘트에 따라 4가지 실험 조건으로 나눴고, 만능시험기로 압축강도와 간접인장강도 측정하였다. 각각의 강도 값을 계산 후 통계처리 하였다. 결과: 압축강도에서는 RelyX ARC의 광중합과 Multilink N의 광중합, 간접인장강도에서는 RelyX ARC의 광중합을 제외하고 모든 중합방법에서 24시간 뒤 측정된 강도가 즉시 측정한 강도보다 더 높은 값을 보여주었다. FujiCEM 2는 시멘트간 비교에서 가장 낮은 강도 값을 보였다(P < 0.05). 결론: 치과용 시멘트 중에서 최근 출시된 이중중합 자가접착 레진 시멘트는 기존의 레진 시멘트와 비교시 제품별로 차이가 있었으나, 압축강도와 간접인장강도에서는 유의한 차이를 보이지 않았다.

• 대한치과의사협회지
• /
• 제49권1호
• /
• pp.22-32
• /
• 2011

This paper reviewed the following subheadings and a few selected references in each section were discussed: ${\cdot}$ Sealant placed over caries; is it possible? Initial caries which is not sticky during proving is possible to be placed with sealants. ${\cdot}$ Prophylaxis of fissure; which method is most effective? Mechanical preparation with fissurotomy or resin polishing bur is one of the most effective method to clean the pit and fissure. ${\cdot}$ Glassionomer cement as a sealant; GIC, wheather it released fluoride or not, cannot be as cost-effective as resin-based sealants. ${\cdot}$ Sealant products; Color(white vs opaque), fluoride(containing vs not), filler component(filled vs non-filled) do not influenced the quality and retention of sealants. ${\cdot}$ Use of intermediate bonding agent to improve retention; Intermediate bonding may increase the retention rate of sealants ${\cdot}$ Penetration method of sealants; Several methods including waiting before light curing are recommended.

• 대한치과보철학회지
• /
• 제51권2호
• /
• pp.99-106
• /
• 2013

연구 목적: 본 연구의 목적은 다이의 수렴각과 치관길이의 차이와 시멘트 종류의 차이가 전부주조관의 유지력에 미치는 영향을 비교한 것이다. 연구 재료 및 방법: 치관 길이 5 mm와 10 mm의 금속다이를 각각 5, 10, 15, 25도의 수렴각을 갖도록 제작한 후 전부주조관을 치과용 시멘트 중, 인산아연 시멘트(Fleck's Zinc Phosphate Cement, Mizzy Co., Cherry Hill, NJ, USA), 레진-변형 글래스 아이오노머 시멘트(Vitremer, 3M Dental Products, St, Paul, MN, USA), 레진 시멘트(Panavia 21, Kuraray Co., Osaka, Japan)로 합착하고 500회 thermocycling을 시도한 후, Instron Universal Testing Machine (Instron Corp., Canton, MA, USA)에 장착시켜, 인장력을 가하여 전부주조금관이 분리될 때 까지 인장력을 측정하여 분리되는 순간의 최대하중값(N)을 측정, 비교하였다. 통계분석은 측정된 각 군간 유지력의 상호관계를 알아보기 위하여 one-way 및 two-way ANOVA를 시행하였고 동일 길이를 가진 시멘트 군 사이에서의 수렴각 차이에 따른 영향, 다이 길이 증가에 따른 영향 및 유지력 차이를 검정하기 위해 t-test를, 수렴각 증가 에 따른 유의성을 살펴 보기 위해서는 Tukey's HSD test를 시행하였다(${\alpha}$=0.05). 결과: 동일 수렴각에서 평균 유지력은 레진 시멘트, 인산아연 시멘트, 레진-변형 글래스 아이오노머 시멘트 순으로 높게 나타났으며 모든 시멘트에서 수렴각의 증가에 따 라서 평균 유지력은 유의차를 보이면서 감소하였다(P<.05). 동일 수렴각에서 10 mm 실험군은 다이 길이 5 mm 실험군과 비교해보았을 때 길이 증가에 따른 유지력의 증가가 통계학적으로 유의차를 나타내면서 증가된 결과를 보였다. 5 mm 실험군에서 유지력은 수렴각의 변화와 시멘트의 종류, 수렴각과 시멘트의 상호영향(interaction)에서 모두 유의성 있는 차이를 보였다(P=.001). 각 시멘트 군에서의 유지력은 10 mm 길이 금속 다이의 수렴각이 증가할수록 유의한 차이를 보이면서 감소한 것으로 나타났다 (P=.0001). 결론: 임상에서 사용되고 있는 특정 치과용 시멘트의 적용시 유지력은 지대치의 기하학적 형태에 영향을 받고 있으며 서로 다른 치관 길이와 수렴각을 가지는 경우 유지 력 증가를 위해 시멘트 선택에 있어 주의가 요망된다.

• 대한치과보철학회지
• /
• 제52권2호
• /
• pp.82-89
• /
• 2014

연구 목적: 본 연구의 목적은 중합 과정 중 치과용 레진 시멘트의 점탄성 성질의 변화를 관찰하기 위한 것이다. 연구 재료 및 방법: 6 종류의 레진시멘트(Clearfil SA luting, Panavia F 2.0, Zirconite, Variolink N, RelyX Unicem clicker, RelyX U200)가 이번 실험에 사용되었다. AR1500 stress controlled rheometer를 이용해 $32^{\circ}C$에서 동적 시간 경과 시험(dynamic oscillation time sweep test)이 시행되었다. 각각의 레진시멘트의 전단 저장 계수(G'), 전단 손실 계수(G"), 손실 탄젠트(tan ${\delta}$), 변위량을 20분 동안 3번씩 반복 측정하였다. 측정 결과는 일원배치분석 및 Tukey's hoc test로 사후 검정을 시행하였다(${\alpha}$=0.05). 결과: 모든 레진 시멘트는 혼합 후 시간에 따라 G' 값이 증가하였고, 최종적으로 안정상태에 도달하였다. 실험 종료 시점에서 RelyX U200은 가장 높은 G'값을 나타냈고, RelyX Unicem (clicker type)과 Variolink N이 가장 낮은 G'값을 나타냈다. Tan ${\delta}$와 변위량은 일정 수준의 값을 유지하다가 G'이 증가하기 시작하는 시점에서 0에 도달하였다. 이는 변위량이 0에 도달하는 지점과 거의 일치하였으며, 그 시간은 6분 내외였다. 결론: 본 연구에서 RelyX U200은 다른 레진 시멘트와 비교하여 가장 오랜 시간 동안 소성을 유지하고, 경화 완료 후 가장 높은 강도(rigidity)를 보였다. 따라서 여러 개의 보철물을 동시에 합착해야 하는 경우에 RelyX U200이 유용할 것으로 사료된다.