• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.241-242
• /
• 2021

In this study, we develop the damage depth diagnostic technology of fire damage concrete and propose an method of impaired depth due to fire by drying impaired concrete after immersing. Test results indicated that when assesing impared depth due to fire with the dry method after water immersing, impaired depth was clearly found and furthermore, compared with that by Phenolphthalein method 10 mm of damage depth was additionally identified, which is imposible to asses when Phenolphthalein is applied.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.245-246
• /
• 2021

In this study, we develop the damage depth diagnostic technology of fire damage concrete and propose an method of impaired depth due to fire by drying impaired concrete after immersing. Test results indicated that when assesing impared depth due to fire with the dry method after water immersing, impaired depth was clearly found and furthermore, compared with that by Phenolphthalein method 15 mm of damage depth was additionally identified, which is imposible to asses when Phenolphthalein is applied.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.243-244
• /
• 2021

In this study, we develop diagnostic technology for damage depth of fire-damaged concrete and propose methods for damage caused by fire by drying damaged concrete after immersion. As a result of the test, the damaged depth was clearly found when evaluating the depth of impurities caused by fire in a drying method after water had permeated, and it could be verified using thermogravimetric analysis.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 추계 학술논문 발표대회
• /
• pp.65-66
• /
• 2017

Early-frost damages easily take place in smaller and thinner walls and slabs. In case of slabs, it is difficult to visually determine the depth of early-frost damage. As such, the current study aims to determine the depth of early-frost damage caused to concrete structures due to bad curing in the winter. As a result, the study found that the depth of early-frost damages increased from the top as the atmospheric temperature on the concrete surface decreased. The changes in the color allowed the observer to easily identify the depth of early-frost damage with the naked eye. In particular, the color difference between potentially damaged parts and undamaged parts were the greatest around thirty minutes of drying after wetting.

• 한국건축시공학회지
• /
• 제3권3호
• /
• pp.73-81
• /
• 2003

In this paper, salt damage resistance of high durable concrete was tested. High durable concrete was made by using low water cement ratio, chemical admixture called super-durable admixture and mineral admixtures such as fly-ash, ground granulated blast-furnace slag, silica fume. Two kinds of salt damage resistance test were carried out. One method is chloride ion penetration test(ASTM C1202), and the other one is depth of chloride penetration test in saline solution. Test results were as followers: 1) The depth of chloride ion penetration increased exponentially as water cement ratio was increased and time passed. 2) Super-durable admixture had little effect on the improvement of salt damage resistance of concrete. 3) Silica fume and ground granulated blast-furnace slag were effective on salt damage resistance because of pozzolanic reaction, but fly-ash had a little effect.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 추계 학술논문 발표대회
• /
• pp.207-208
• /
• 2017

The current study assumed a condition in which concrete curing was not completed correctly in the winter, in order to analyze the effect of changes in early low-temperatures in early-frost damage depth. As a result, lower external temperature early on after depositing the concrete greatly reduced the temperature in the upper parts of the concrete, and it delayed the time during which the concrete temperature restored. In addition, for early-frost damages, lower early temperature increased the expansion of frozen water, which in turn relaxes the concrete structures and increases the absorption rate, ultimately extending the depth of early-frost damage.

• 한국건축시공학회지
• /
• 제24권3호
• /
• pp.297-308
• /
• 2024

본 연구에서는 화재로 손상된 콘크리트의 손상 깊이 판정방법을 제안하고자 하였다. 고온에 노출된 콘크리트의 경우 내부 조직이 팽창하여 건전한 부위보다 손상부위의 공극이 다량 발생하고 미세균열이 발생됨에 따라 흡수율이 더 높아져 수중 침치후 건조를 하는과정에서 건전부위보다 손상부위의 늦은 건조속도와 이에 따른 명도차이에 의한 색상차이를 이용하여 손상 깊이를 측정하는 것이다. 수중 침지방법의 경우 배합별로 각각 38.7 및 37.5mm로 나타났는데, 기존 페놀프탈레인에 의한 중성화 측정 방법보다 손상깊이를 깊게 추정하는 것을 알 수 있었다. 이는 Portlandite(Ca(OH)₂)의 존재여부에 따라 발색이 되는 페놀프탈레인법에 비해 조직이완에 따른 흡수율 원리를 이용한 손상 깊이를 측정하는 방법이 더 민감도가 높아 얻어진 결과로 사료된다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.167-168
• /
• 2020

In this study, we attempted to present a method for diagnosing the depth of the early frost damage concrete using organic pigments under the cold weather. As a result, it is considered that the organic pigment did not penetrate into the voids of the concrete that had been damaged by the early frost damage and only the surface was adhered. Therefore, when fine particles that can be melted in water and pass through voids are used, it is analyzed that it can penetrate damaged part of the concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2018년도 춘계 학술논문 발표대회
• /
• pp.145-146
• /
• 2018

In this study, the purpose of the study is to determine the depth of damage caused by early frost damage in concrete slab structures under the conditions of external temperature during winter. In other words, we intend to analyze the depth variation of the early frost damage as the thickness of the normal strength concrete slab members changes. As a result, the thinner the component was, the deeper the early frost damage was found to be, and the resulting increase in brightness of the concrete was delayed. and It is analyzed that under this test condition, an early frost damage was created with a thickness of 50 mm for the member and a thickness of 39 mm for the member of 300 mm.

• 한국지반신소재학회논문집
• /
• 제22권1호
• /
• pp.97-107
• /
• 2023

본 연구에서는 국내 동상피해 발생지역 중 동결지수가 높은 강원산간지역의 콘크리트도상 현장에 대하여 동상피해 원인과 동결심도를 분석하고 동결심도 자료를 바탕으로 콘크리트도상의 동결심도 산정식 및 강원지역의 동결심도 산정식을 고찰하였다. 강원산간지역의 콘크리트도상 동결심도와 강원지역의 동결심도 경향성을 비교한 결과 콘크리트도상은 동결지수 400(℃×일)이하에서는 동결심도가 강원지역의 동결심도보다 높게 나타났으며, 동결지수400(℃×일)이상의 구간에서는 강원 지역의 동결심도가 콘크리트도상의 동결심도보다 높게 나타났다. 본 연구를 통해 강원지역의 동결심도 산정식을 제시하여 강원지역의 철도 및 도로 건설사업 시 동상 방지대책 수립에 활용될 수 있도록 기초자료를 제공하였다.