• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.178.2-178.2
• /
• 2015

In and Ga doped ZnO (IGZO) films were deposited on 5 nm thick Cu film buffered Polycarbonate (PC) substrates with RF magnetron sputtering and then the effect of Cu buffer layer on the optical and electrical properties of the films was investigated. While IGZO single layer films show the electrical resistivity of $1.2{\times}10-1{\Omega}cm$, IGZO/Cu bi-layered films show a lower resistivity of $1.6{\times}10-3{\Omega}cm$. Although the optical transmittance of the films in a visible wave length range is deteriorated by Cu buffer layer, IGZO films with 5 nm thick Cu buffer layer show the higher figure of merit of $2.6{\times}10-4{\Omega}-1$ than that of the IGZO single layer films due to the enhanced opto-electrical performance of the IGZO/Cu bi-layered films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.8
• /
• pp.846-851
• /
• 2004

Transparent conducting indium tin oxide (TC-ITO) thin films on polymeric substrates have been deposited by a dc reactive magnetron sputtering without heat treatments. The polymeric substrates are acryl (AC), poly carbornate (PC), and polyethlene terephthalate (PET) as well as soda lime glass is also used to compare with the polymeric substrates. Sputtering parameters are an important factor for high quality of TC-ITO thin films prepared on polymeric substrates. Furthermore, the material, electrical and optical properties of as-deposited ITO films are dominated by the ratio of oxygen partial pressure. As the experimental results, the surface roughness of ITO films becomes rough as the oxygen partial pressure increases. The electrical resistivity of as-deposited ITO films decreases initially, and then increases with the increase of oxygen partial pressure. The optical transmittance at visible wavelength for all polymeric substrates is above 82 %.

• Applied Science and Convergence Technology
• /
• v.23 no.3
• /
• pp.145-150
• /
• 2014

MgO thin films were deposited by internal ICP-assisted reactive-magnetron sputtering with bipolar pulse bias on a substrate to suppress random arcs. Mg is reactively sputtered by a bipolar pulsed DC power of 100 kHz into ICP generated by a dielectrically shielded internal antenna. At a mass flow ratio of $Ar/O_2$ = 10 : 2 and an ICP/sputter power ratio of 1 : 1, optimal film properties were obtained (a powder-like crystal orientation distribution and a RMS surface roughness of approximately 0.42 nm). A bipolar pulse substrate bias at a proper frequency (~a few kHz) prevented random arc events. The crystalline preferred orientations varied between the (111), (200) and (220) orientations. By optimizing the plasma conditions, films having similar bulk crystallinity characteristics (JCPDS data) were successfully obtained.

• Journal of Surface Science and Engineering
• /
• v.50 no.2
• /
• pp.55-71
• /
• 2017

Transparent Conductive Oxide (TCO), especially Indium Tin Oxide (ITO) films are almost prepared by DC magnetron sputtering because of the advantage of obtaining homogeneous large area coatings with high reproducibility. The purpose of this report is describe a detailed investigation of key factors dominating electrical and structural properties of sputtered ITO films. It was confirmed that crystallinity and electrical properties of ITO films were strongly depend on the sputtering pressure and kinetic energy of sputtered particles which are expected to have a close relation with the transport processes between target and substrate. And also, nodule formation on the ITO target was suppressed by both $CaCO_3$ addition and decreasing micro-pore in the target. On the other hand, we focused on the characteristics of amorphous TCO film to use as transparent electrode for various applications. To realize high thermoelectric performance, it was tried to control both high electrical conductivity and low thermal conductivity for the amorphous IZO:Sn films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.8
• /
• pp.706-710
• /
• 2007

Ti-containing amorphous carbon (a-C:Ti) films shows attractive mechanical properties such as low friction coefficient, good adhesion to various substrate and high wear resistance. The incorporation of titanium in a-C films is able to improve the electrical conductivity, friction coefficient and adhesion to various substrates. In this study, a-C:Ti films were depositied on Si wafer by closed-field unbalanced magnetron (CFUBM) sputtering system composed two targets of carbon and titanium. The tribological properties of a-C:Ti films were investigated with the increase of DC bias voltage from 0 V to - 200 V. The hardness and elastic modulus of films increase with the increase of DC bias voltage and the maximum hardness shows 21 GPa. Also, the coefficient of friction exhibites as low as 0.07 in the ambient. In the result, the a-C:Ti film obtained by CFUBM sputtering method improved the tribological properties with the increase of DC bias volatage.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.303-304
• /
• 2008

Al, N-codoped ZnO(ZnO:N,Al) thin films were deposited on n-type Si(100) substrate at $450^{\circ}C$ with various conditions of ambient gas$(N_2:O_2)$ by DC magnetron sputtering method using ZnO:$Al_2O_3$(2wt%) as a target, and then were annealed at 500, 700, $800^{\circ}C$ in $N_2$ gas for one hour. XRD patterns showed that all of the ZnO:N,Al thin films annealed at $80^{\circ}C$ grew with two peaks, which means poor crystallinity of the thin films deposited. Hall effects in Van der Pauw configuration proved that after annealing the films deposited showed low resistivity and high carrier concentration. While the films annealed at $800^{\circ}C$ showed low resistivity of $\sim10^{-2}\Omega$ cm and high carrier concentration of $\sim10^{19}cm^{-3}$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.179-180
• /
• 2012

Aluminum alloys are widely known as non-ferrous metal with light weight and high strength. Consequently, these materials take center stage in the aircraft and automobile industry. The Al7075 aluminum alloy is based on the Al-Zn-Mg-Cu and one of the strongest wrought aluminum alloys. Aluminum nitride has ten times higher thermal conductivity($319W/m{\cdot}K$) than Al2O3 and also has outstanding electric insulation($1{\times}1014{\Omega}{\cdot}cm$). Furthermore, it has high mechanical property (430 MPa) even though its co-efficient of thermal expansion is less than alumina For these reasons, it has great possibilities to be used for not only the field which needs high strength lightweight but also electronic material field because of its suitability to be applied to the insulator film of PCB or wafer of ceramic with high heat conduction. This paper investigates the mechanical properties and corrosion behavior of aluminum alloy Al7075 deposited with aluminum nitride thin films To improve the surface properties of Al7075 with respect to hardness, and resistance to corrosion, aluminum nitride thin films have been deposited by pulsed DC reactive magnetron sputtering. The pulsed DC power provides arc-free deposition of insulating films.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1352-1354
• /
• 1997

Transparent conductive thin films have found many application in many active and passive electronic and opto-electronic devices as like flat Panel display electrode and window heat mirror, etc. Low resistivity and high transmittance of this films can be obtained by controlling deposition parameters, which are oxygen partial Pressure, substrate temperature and dopant concentration. In this study, We prepared non-stoichiometric and Sb-doped thin films of tin dioxide by reactive DC magnetron sputtering technology. The lowest resistivity of about $3.0{\times}10^{-3}\;{\Omega}cm$ and 80% transmittance in the visible light region have heed obtained at optimal deposition condition.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.327-327
• /
• 2013

본 연구에서는 $SiO_2$ Target과 $In_2O_3$ Target으로 co-sputtering방법을 이용해 증착한 Si-doped $In_2O_3$ (ISO) 박막의 Si 도핑 농도에 따른 전기적, 광학적, 구조적 특성에 대해 연구하였고, 이를 유기태양 전지(OPVs) 에 적용함으로써 그 가능성을 타진하였다. $In_2O_3$ target의 DC power를 100 W로 고정시킨 채 $SiO_2$ target의 RF power 크기를 20~60 W 변화시키면서 상온에서 실험을 진행한 결과 최적 조건은 박막의 두께가 200 nm일 때 Working pressure는 3 mTorr이고, RF power는 50 W이었다. 이 조건으로 제작된 ISO 박막은 550 nm에서 81.51%의 광투과율과 51.91 Ohm/sq.의 비교적 낮은 면저항이 나타남을 Hall measurement 및 UV/Vis spectroscopy 분석을 통해 알 수 있었다. 또한 X-ray diffraction 분석법과 Transmission Electron Microscope 분석법을 통해 $SiO_2$ 도핑 power가 50 W 이상으로 증가할 경우 ISO 박막의 결정성이 감소하여 완벽한 비정질상의 ISO 투명박막이 형성됨을 확인할 수 있었다. 비정질 특성을 갖는 ISO 투명 전극을 이용하여 유기 박막형 태양전지를 제작한 결과 Voc (0.576 V), Jsc (7.671 mA/$cm^2$), FF (62.96%), PCE (2.78%)의 특성을 나타냄으로서 co-sputtering 공정을 통해 최적화된 ISO 박막을 유기 박막형 태양전지에 적용함으로써 광전소자로의 적용 가능성을 확인할 수 있었다.

• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.328-333
• /
• 2004

Transparent ZnO:Al conductor films for the optoelectronic devices were deposited by using the capacitively coupled DC magnetron sputtering method. The effect of Al doping concentration and discharge power on the electrical and optical properties of the films was studied. The film resistivity of $8.5${\times}$10^{-4}$ $\Omega$-cm was obtained at the discharge power of 40 W with the ZnO target doped with 2 wt% $Al_2$$_O3$. The transmittance of the 840 nm thick film was 91.7% in the visible waves. Increasing doping concentration of 3 wt% $Al_2$$O_3$ in ZnO target results in significant decrease of film resistivity, which may be due to the formation of $Al_2$$O_3$ particles in the as-deposited ZnO:Al film and the reduced ZnO grain sizes. Increasing DC power from 40 to 60 W increases deposition rate by more than 50%, but can induce high defect density in the film, resulting in higher film resistivity.