• Journal of the Korean Society for Railway
• /
• v.11 no.3
• /
• pp.311-316
• /
• 2008

Ratcheting is a cyclic accumulation of strain under a cyclic loading. It is a kind of mechanisms which generate cracks in rail steels. Though some experimental and numerical study has been performed, modeling of ratcheting is still a challenging problem. In this study, an elastic-plastic constitutive equation with non-linear kinematic hardening equation was applied. Contact stresses in wheel-rail were analyzed. Under the tangential stress of the contact stresses, a cyclic stress-strain relation was obtained by using the model. A constant ratcheting strain per cycle was accumulated.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.6
• /
• pp.226-231
• /
• 2012

Characteristics of carburized surface layers in 0.18C-3.5Ni-1.5Cr-0.2Mo steels for main shaft bearings of wind turbines have been analyzed and evaluated before and after rolling contact fatigue tests. Mixed microstructure consisting of retained austenite and tempered martensite has been formed with compressive residual stresses in the surface hardened layers of the specimens showing uniform hardness distribution with value about Hv700 after vacuum carburizing and tempering. It has been found on the raceway of the layers of the specimens after rolling contact fatigue tests that the amount of retained austenite decreased and compressive residual stresses increased, resulting from cyclic contact stresses applied during the tests. It has been also revealed that higher durability of the bearings can be obtained through controlling the amount of the retained austenite in the surface of the bearing steels to be lower in this study.

• Proceedings of the KSR Conference
• /
• 2009.05a
• /
• pp.1592-1597
• /
• 2009

Ratcheting is a cyclic accumulation of strain under a cyclic loading. It is a kind of mechanisms which generate cracks in rail steels. Though some experimental and numerical study has been performed, modeling of ratcheting is still a challenging problem. In this study, an elastic-plastic constitutive equation considering non-linear kinematic hardening and isotropic hardening was applied. Under the tangential stress of the contact stresses, a cyclic stress-strain relation was obtained by using the model. Strain under repeated cycles was accumulated.

• Proceedings of the KSR Conference
• /
• 2004.06a
• /
• pp.632-637
• /
• 2004

In the shrink or press fitted shaft such as railway axle, fretting can occur by cyclic stress and micro-slippage due to local movement between the shaft and the hub. When the fretting occurs in the press fitted shaft, the fatigue strength remarkably decreases compared with that of without fretting. In this paper, the analysis of contact stresses in a press fitted shaft in contact with a hub was conducted by finite element method and the micro-slip according to the bending load was analyzed. It is found that the largest stress concentration and maximum slip amplitude of shrink fitted shaft are found at the edge of the interface and the distribution of contact stresses at the contact edge has largely influenced and coefficient of friction.

• Journal of the Korean Society for Railway
• /
• v.16 no.2
• /
• pp.93-98
• /
• 2013

Railway system is today the most efficient way for transportation in many cases in several forms of application. Yet, wear phenomenon, profile evolution, fatigue, fracture, derailment are the major worries (financial and safety) in this system which force significant direct and indirect maintenance costs. To improve the cyclic maintenance procedures and the safety issues, it can be very satisfactory to be informed of the state of wheel/rail interaction with mileage. In present paper, an investigation of the behavior of the shear stresses by logged distance is approached, by implementing the field measurement procedure, in order to determine the real conduct of the most important cause of defects in wheel/rail contact, shear stress. The results coming from a simulation procedure indicate that the amounts of shear stresses are still in high-magnitudes when the wheel and rail are completely worn; even though in simulation based on the laboratory measurements of profile evolutions, the stresses become significantly reduced by logged distance.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.7 s.178
• /
• pp.1740-1747
• /
• 2000

Under repeated rolling, initial plastic deformation introduces residual stresses which render the steady cyclic state purely elastic. This is called the process of shakedown. Many studies have been done about the shakedown in semi-infinite half space using calculated Hertizian pressure. In this paper shakedown processes in a shaft are studied by finite element analyses of a two dimensional(plane strain) model with elastic-linear-kinematic-hardening-plastic material subjected to repeated, frictionless rolling contact. Symmetric and non-symmetric pressure distributions are obtained using a simplified model of the bearing-shaft assembly. The rolling contact is simulated by repeatedly translating both pressure distributions along the surface of the shaft. By the influence of the non-symmetric pressure, larger residual radial tensile stress is generated in the immediate subsurface layer, which may make a crack propagate and, the subsurface undergoes a zigzag plastic deformation during the shakedown process, which may lead to a crack initiation.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.966-970
• /
• 2011

The thermo-mechanical interaction between brake block and wheel tread during braking has been found to cause thermal crack on the wheel tread. Due to thermal expansion of the rim material, the thermal cracks will protrude from the wheel tread and be more exposed to wear during the wheel/block contact than the rest of the tread surface. The wheel rim is in residual compression stress when is new. After service running, the region in the tread has reversed to tension. This condition can lead to the formation and growth of thermal cracks in the rim which can ultimately lead to premature failure of wheel. In the present paper, the thermal cracks of railway wheel, one of severe damages on the wheel tread, were evaluated to understand the safety of railway wheel in running condition. The residual stresses for damaged wheel which are applied to tread brake are investigated. Mainly X-ray diffusion method is used. Under the condition of concurrent loading of continuous rolling contact with rails and cyclic frictional heat from brake blocks, the reduction of residual stress is found to correlate well with the thermal crack initiation.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.4
• /
• pp.409-416
• /
• 2012

Recently, surface modification technology is of importance to improve the wear resistance and the corrosive resistance for high accurate mechanical parts such as LM guide, Ball Screw and Roller Bearing etc., Those has generally featured on rolling contact mechanism to improve not only the wear and the friction, but also the accuracy and the corrosion performances. For surface modifications of high accurate mechanical parts, normally thermal spray, PVD, CVD and E.P. processes have been used with many materials such as DLC, raydent, W, Ni, Ti etc. Diamondlike carbon (DLC) films possess a combination of attractive properties and have been largely employed to modify the tribological behaviors such as friction, wear, corrosion, fretting fatigue, biocompatibility, etc. However, for rolling contact mechanism mechanical parts DLC films are needed to study for commercial benefit. Rolling contact mechanism has features on effects of cyclic motions and stresses, and also not simply sliding motions. The papers focused on the performance test of wear and corrosive resistance according to Me-DLC film thickness. And also, its thickness effect of wear analysis was carried out through the simulation of the maximum shear stress under the rolling contact surface. As the results, Me-DLC films have more potential to improve the wear resistance for high precision mechanical parts than raydent films.

• Journal of the Korean Society for Precision Engineering
• /
• v.28 no.5
• /
• pp.537-542
• /
• 2011

The thermo-mechanical interaction between brake block and wheel tread during braking has been found to cause thermal crack on the wheel tread. Due to thermal expansion of the rim material, the thermal cracks will protrude from the wheel tread and be more exposed to wear during the wheel/block contact than the rest of the tread surface. The wheel rim is in residual compression stress when is new. After service running, the region in the tread has reversed to tension. This condition can lead to the formation and growth of thermal cracks in the rim which can ultimately lead to premature failure of wheel. In the present paper, the thermal cracks of railway wheel, one of severe damages on the wheel tread, were evaluated to understand the safety of railway wheel in running condition. The residual stresses for damaged wheel which are applied to tread brake are investigated. Mainly X-ray diffusion method is used. Under the condition of concurrent loading of continuous rolling contact with rails and cyclic frictional heat from brake blocks, the reduction of residual stress is found to correlate well with the thermal crack initiation.

• Journal of the Society of Naval Architects of Korea
• /
• v.43 no.2 s.146
• /
• pp.213-219
• /
• 2006

Low cycle fatigue cracks are mainly detected at discontinuous welded locations with high stresses under repeated cyclic static loads due to cargo leading and unloading. Theoretical and analytical methods have been used for evaluation of local stress and strain which have an effect on a prediction of fatigue life, but those have difficulties of considering stress concentration at notched location and complicated material behavior of welded joint or heat affected zone. Electronic speckle pattern interferometry(ESPI) system is nondestructive and non-contact measurement system which can get the relatively accurate full field strain at critical positions such as welded zone and structural discontinuous location. In this study, local strain was measured on welded cruciform joint by ESPI system and then low cycle fatigue test was performed. Effect of local strain on low cycle fatigue life was examined by measured values using ESPI system. Moreover, experimental fatigue life was compared with established S-N curves using theoretical local strain and stress calculated by Neuber's rule.