• Journal of the Korean Electrochemical Society
• /
• v.10 no.4
• /
• pp.252-256
• /
• 2007

A series of spherical porous carbons were prepared via resorcinol-formaldehyde (RF) sol-gel polymerization in the presence of cationic surfactant (CTAB, cetyltrimethylammonium bromide), wherein the carbon sphere size was controlled by varying the CTAB introduction time after a pre-determined period of addition reaction (termed as "pre-curing"). The sphere size gradually decreases with an increase in the pre-curing time within the range of 30-150 nm. The carbons possess two types of pores; one inside carbon spheres (intra-particle pores) and the other at the interstitial sites made by carbon spheres (inter-particle pores). Of the two, the surface exposed on the former was dominant to determine the electric double-layer capacitor (EDLC) performance of porous carbons. As the intra-particle pores were generated inside RF gel spheres by gasification, the pore diameter was similar for all these carbons, thereby the pore length turned out to be a decisive factor controlling the EDLC performance. The charge-discharge voltage profiles and complex capacitance analysis consistently illustrate that the smaller-sized RF carbons deliver a better rate capability, which must be the direct result of facilitated ion penetration into shorter pores.

• Journal of the Korean Wood Science and Technology
• /
• v.30 no.3
• /
• pp.34-41
• /
• 2002

This study investigated the thermogravimetric analysis of two types of cured tannin-based adhesives from wattle and pine, with three hardeners of paraformaldehyde, hexamethylenetetramine and TN (tris(hydroxyl)nitromethan), at a temperature of 170℃ and a heating rate of 5, 10, 20 and 40℃/min for 10 minutes. The 5 minutes cured wattle tannin-based adhesive with each hardener at 170℃ was also tested to compare the degree of curing. It was found that thermogravimetric analysis could be used to measure the degree of curing of a thermosetting adhesive. The TG-DTG curves of all the adhesive systems were similar and showed three steps in a similar way to a phenolic resin. This means that each adhesive system is well cross-linked. However, a high thermal decomposition rate was shown at 150 to 400℃ in the case of the pine tannin sample with TN (tris(hydroxyl)nitromethan). The Flynn & Wall expression was used to evaluate the activation energy for thermal decomposition. As the level of conversion (𝛼) increased, the activation energy of each system increased. The activation energy of the wattle tannin-based adhesive with paraformaldehyde was higher than the others.

• Current Research on Agriculture and Life Sciences
• /
• v.18
• /
• pp.61-69
• /
• 2000

This study was conducted to investigate most effective the optimum lime content for lime-clay modification. To achieve the aim, characteristics of compaction and compressive strength were tested by adding of 0, 5, 10, 15 and 20% lime (Hydrated lime) of dry weight of the clay. Distilled water was added 10, 15, 20 and 25% of dry weight of lime-clay mixture. In this test, the compressive strength of the specimens was measured according to the following curing period : 7, 21, 28, 35 and 49 days. The results are as follows. (1) As lime additive increased, the optimum moisture content of lime-clay mixture was increased and the maximum dry density was decreased. (2) The soil mixture of 20% of the moisture content and 10% of lime additive was shown the maximum compressive strength. (3) As curing period longer, the compressive strength was increased but after 21 curing days, the increasing rate of compressive strength was low as compared with earlier its value. (4) In the range of 20% of the moisture content, compressive strength of mixture of 10% lime additive increased twice compared with that of mixture of 0% lime additive. (5) All of the lime-clay are possible to use for an sub-base material and 20% of moisture content of lime-clay mixture is possible to use for a base material.

• Journal of the Korea Concrete Institute
• /
• v.19 no.1
• /
• pp.27-37
• /
• 2007

The purpose of this study is to propose a method to predict the minimum curing time of early age concrete required to prevent frost damage. Tests were performed to examine major factors, which affect the compressive strength of concrete frozen at early ages and investigate the source of frost damage at early age concrete. The results from the tests showed that the loss rate of compressive strength decreases as the beginning time of frost damage was delayed and water-cement ratio was lower. In addition, the test results also showed that concrete made with type III cement was less susceptible to frost damage than concrete made with ordinary Portland cement and frost damage occurred through the formation of ice lenses. When early age concrete is being damaged by frozen, a phase transition into ice of free water presented at the capillary pores of the concrete gives a reason for the decrease of compressive strength. Accordingly, the frost resistance of fresh concrete can be determined based on the saturation degree of the capillary pores. The method to predict the minimum curing time was suggested using the concept of critical saturation degree of the capillary pores.

• Journal of Welding and Joining
• /
• v.33 no.5
• /
• pp.41-46
• /
• 2015

The snap cure NCP(non-conducive paste) adhesive material is essentially required for the high productivity flip chip bonding process. In this study, the accessibility of DEA(dielectric analysis) method for the evaluation of snap cure behavior was investigated with comparison to the isothermal DSC(differential scanning calorimetry) method. NCP adhesive was mainly formulated with epoxy resin and imidazole curing agent. Even though there were some noise in the dielectric loss factor curve measured by DEA, the cure start and completion points could be specified clearly through the data processing of cumulation and deviation method. Degree of cure by DEA method which was measured from the variation of the dielectric loss factor of adhesive material was corresponded to about 80% of the degree of cure by DSC method which was measured from the heat of curing reaction. Because the adhesive joint cured to the degree of 80% in the view point of chemical reaction reveals the sufficient mechanical strength, DEA method is expected to be used effectively in the estimation of the high speed curing behavior of snap cure type NCP adhesive material for flip chip bonding.

• Polymer(Korea)
• /
• v.27 no.3
• /
• pp.176-182
• /
• 2003

The fluorine-containing epoxy resin, 2-trifluorotoluene diglycidylether (FER) was prepared by reaction of 2-chloro-${\alpha}$,${\alpha}$,${\alpha}$-trifluorotoluene with glycerol diglycidylether in the presence of pyridine catalyst. Curing behavior of FER/DDM system was investigated using dynamic and isothermal DSC. Cure activation energy (Ea) was determined by Flynn-Wall-Ozawa's equation. The rheological properties of FER/DDM system were studied under isothermal condition using a rheometer. Cross-linking activation energy (Ec) was determined from the Arrhenius equation based on gel time and curing temperature. As a result, the chemical structure of FER was confirmed by FT-IR, $\^$13/C NMR, and $\^$19/F NMR spectroscopy. The cure activation energy of FER/DDM system was 55.4 kJ/mol and conversion and conversion rate were increased with the curing temperature. The cross-linking activation energy of FER/DDM system was 41.6 kJ/mol and gel time was decreased with the curing temperature.

• Journal of the Korean Vacuum Society
• /
• v.7 no.3
• /
• pp.229-236
• /
• 1998

In this paper, thin films of Polyimide (PI) were fabricated by vapor deposition polymerization method (VDPM) of dry processes. The film's properties with curing temperature and electrical properties were studies. The synthesis of hexafluoroisopropyliden-2,2-bis[phthalic anhydride](6FDA) and 4, 4'-diamino diphenyl ether (DDE) was carried out by vapor deposition polymerization(VDP) with the same deposition rate. The evaporation temperature of 6FDA and DDE were $214^{\circ}C$ and $137^{\circ}C$, respectively, so as to preserve balance of stoichiometry. The polymic acid (PAA) made by VDPM were changed to PI by thermal curing. The uniformity and density of PI thin films were increased according to increasing curing temperature. The relative permittivity and dissipation loss factor were 3.7 and 0.008 at the frequency of 100Hz~200KHz, respectively, for the fabricated in the curing temperature of $300^{\circ}C$. Also, the resistivity was about 1.05$\times$$ 10^{15}$$\Omega$cm at $30^{\circ}C$.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.31 no.4
• /
• pp.420-425
• /
• 1986

This study was conducted to investigate the influence of air temperature and relative humidity on excessive drying rate of burley tobacco. In experiment I, 4 temperatures and I humidity by day and air curing by night were treated from initial curing stage. In experiment II, 15 combinations of 3 temperatures and 5 humidities were applied from the yellow stage of cure. Yellowish cured leaves resulted from overdrying at high temperature and especially, at low humidity. How- ever, these were not produced at 75-80% RH and under 35$^{\circ}C$ by day with air curing b y night. The proper range of temperature and humidity for desirable color of cured leaf were the combinations of 30$^{\circ}C$, 75-80% RH or 35$^{\circ}C$, 80-85% RH. As excessive drying leaves increased, physical properties of cured leaves were poorer and chemical contents were less decomposed.

• Polymer(Korea)
• /
• v.26 no.1
• /
• pp.88-97
• /
• 2002

The effect of aminosiloxane modifier on the chemorheological properties of ortho-cresol novolac epoxy/phenol novelac/triphnylphosphine resin system was investigated aat different isothermal curing temperatures. By adding the aminosiloxane to the resin system, not only conversion rate and conversion were increased but also glass transition temperature was promoted. Critical conversion and gelation time obtained at the crossover point between storage and loss moduli were reduced and thus the viscosity was increased by the aminosiloxane. $C_1$ and $C_2$ in the WLF equation calculated from the glass transition temperature as a function of conversion and measured viscosity were found to vary with the curing temperature. By applying the change of glass transition temperature with conversion, $C_1$ and $C_2$ to WLF equation, it was possible to predict accurately the viscosity change with isothermal curing reaction.

• Elastomers and Composites
• /
• v.22 no.3
• /
• pp.195-203
• /
• 1987

In this study, as one of the developing ways of the functional elastomer, improvement of the functionality of CB-BR was attempted through moisture curing reaction. The curing reaction of CB-BR was determined with an use of 3-aminopropyltriethoxysilane(APS) as a crosslinking agent, also a solution reaction with an active chlorine of CB-BR was elucidated by using a reaction kinetics theory and a study of physical property was made through moisture curing on the compound of 3-aminopropyltriethoxysilane and CB-BR The results of this study obtained are as follows : 1) CB-BR reacted easily with APS in the liquid state and the reaction rate coefficient and activation energy were as follows : 2) Optimum pressure condition of moisture cured elastomer(CB-BR+APS) was 20 minutes at $150^{\circ}C$, and the crosslinked elastomer was close to the theoretical value (q=1) for Flory's equation($\frac{\alpha}{\alpha-1}=q{\nu}RT$)