• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2000년도 International Symposium on Magnetics The 2000 Fall Conference
• /
• pp.473-479
• /
• 2000

The nanocrystalline Fe$_{84}$Zr$_{7}$B$_{6}$Cu$_{1}$ $Al_{2}$ alloy was annealed at 450 $^{\circ}C$ and 550 $^{\circ}C$ for l hour to achieve the ultra-soft magnetic properties such as large magnetoimpedence ratio(MIR), the incremental permeability ratio(PR), nearly zero coercivity, zero magnetostriction, etc. The PR and MIR of the sample were measured from 100 kHz to 10 MHz at a cryogenic chamber where the temperature can be varie from 10 K to 300 K. The increment of MIR value is proportional to increasing temperature. The maximum PR values measured at high frequency above 1 MHz remain almost same despite of the temperature variation from 10 K to 300 K except the sharpness in PR curves. However, the maximum PR values measured below 1 MHz show drastic increment at above 150K due to thermal activation of magnetic domains.s.s.

• 대한금속재료학회지
• /
• 제56권11호
• /
• pp.805-812
• /
• 2018

High pressure die casting is one of the precision casting methods. It is highly productivity and suitable for manufacturing components with complex shapes and accurate dimensions. Recently, there has been increasing demand for efficient heat dissipation components, to control the heat generated by devices, which directly affects the efficiency and life of the product. Die cast aluminum alloys with high thermal conductivity are especially needed for this application. In this study, the influence of elements added to the die cast aluminum alloy on its thermal conductivity was evaluated. The results showed that Mn remarkably deteriorated the thermal conductivity of the aluminum alloy. When Cu content was increased, the tensile strength of cast aluminum alloy increased, showing 1 wt% of Cu ensured the minimum mechanical properties of the cast aluminum. As Si content increased, the flow length of the alloy proportionally increased. The flow length of aluminum alloy containing 2 wt% Si was about 85% of that of the ALDC12 alloy. A heat dissipation component was successfully fabricated using an optimized composition of Al-1 wt%Cu-0.6 wt%Fe-2 wt%Si die casting alloy without surface cracks, which were turned out as intergranular cracking originated from the solidification contraction of the alloy with Si composition lower than 2 wt%.

• 열처리공학회지
• /
• 제25권6호
• /
• pp.292-298
• /
• 2012

In this study, Cu-2.5at.%Ni-1at.%Si alloys were fabricated by horizontal continuous casting system to improve the electrical conductivity and mechanical properties of Cu-Ni-Si alloy. Withdrawing speed was changed with 50, 100, 150 and 200 mm/min for the optimum manufacturing condition. Microstructure was observed using OM, FE-SEM and TEM. Electrical conductivity was measured by 4-point probe method and mechanical properties were tested. A horizontal continuous cast thin slab had sound macro and micro structures with partly crystallized structures. Electrical resistivity decreased with increasing annealing temperature from 250 to $850^{\circ}C$, with increasing annealing temperature The maximum hardness and tensile strength were Hv 130, 610 MPa at $550^{\circ}C$, respectively. With changing withdrawing speed from 50 to 150 mm/min, hardness, tensile strength, yield strength and elongation were Hv 60-65, 210-230 MPa, 65-75 MPa and 40-50%, respectively.

• 한국표면공학회지
• /
• 제43권2호
• /
• pp.64-72
• /
• 2010

CuSnZn electroplating was investigated as alternative to Ni plating. Evaluation of electrolyte and plating process was performed to control physical characteristics of the film, and to collect practical data for application. Hull-cell test was conducted for basic comparison of two commercialized products and developed product. Based on hull-cell test results, long term test of three electrolytes was performed. Various analysis on long term tested electrolyte and samples have been done. Reliable and practical data was collected using FE-SEM (FEI, Sirion), EDX (ThermoNoran SIX-200E), ICP Spectrometer (GBC Scientifi c, Integra XL), FIB (FEI, Nova600) for anlysis. Physical analysis and reliability test of the long term tested film were also carried out. Through this investigation plating time, plating speed, electrolyte composition, electrolyte metal consumption, hardness and corrosion resistance has been compared. This set of data is used to predict and control the chemical composition of the film and modify the physical characteristics of the CuSnZn alloy.

• 소성∙가공
• /
• 제30권1호
• /
• pp.5-15
• /
• 2021

The effects of heat treatments (T6 and T73) on the microstructure, mechanical properties, and high cycle fatigue behavior of modified AA7075 alloys were investigated. A modified 7075 alloy was manufactured using modified-Mg (Mg-Al2Ca) instead of the conventional element Mg. Based on the microstructure, the average grain size was 4.5 ㎛ (T6) and 5.2 ㎛ (T73). Regardless of heat treatment, the modified AA7075 alloys consisted of Al matrix containing homogeneously distributed Al2CuMg and MgZn2 phases with reduced Fe-intermetallic compound. Room temperature tensile tests showed that the properties of modified 7075-T6 (Y.S.: 622MPa, T.S: 675MPa, elongation: 15.4%) were superior to those of T73 alloy (Y.S.: 492MPa, T.S: 548MPa, elongation: 12.8%). Experimental data show that the fatigue life of T6 was 400 MPa, about 64% of its yield strength. However, the fatigue life of T73 alloy was 330 MPa and 67%. Irrespective of the stress level, all crack initiation points were located on the specimen surface, and no inclusions acting as stress concentrators were seen. Superior mechanical properties and high cycle fatigue behavior of modified AA7075-T6 alloy are attributed to the fine grains and homogeneous distribution of small second phases such as MgZn2 and Al2CuMg, in addition to reduced Fe-intermetallic compounds.

• 한국재료학회지
• /
• 제10권6호
• /
• pp.422-429
• /
• 2000

Zr 합금의 재결정 거동 및 미세조직 변화에 미치는 열처리 온도 및 시간의 영향의 조사하기위하여 순수 Zr과 Zircaloy-4, Zr-0.88n-0.4Nb-0.4Fe-0.2Cu, Zr-1Nb 합금을 냉간가공한 후 $400^{\circ}C$~$900^{\circ}C$에서 각각 30분~5000분 동안 열처리하였다. 열처리 온도에 따른 Zr합금의 경도, 미세조직 및 석출물 특성을 미소경도기, 광학 현미경 및 투과 전자 현미경을 이용하여 조사하였다. 냉간 가공채는 $400^{\circ}C$에서 $600^{\circ}C$ 범위에서 재결정이 일어났는 데 합금원소가 증가함에 따라 재결정온도가 상승했고 결정립 성장이 억제되었다. 그리고 합금원소 증가에 따른 경도증가 영향이 재결정 이후에도 지속되었다. 열처리 온도 및 시간에 비례하여 재결정 이후 결정립 크기는 증가한 반면 경도변화는 상대적으로 미미하였다. Fe나 Cu가 Zr에 첨가될 경우 회복중 경도증가가 수반되는데, 이는 회복중 생성과 관련이 있는 것으로 사료된다.

• 한국자기학회지
• /
• 제2권3호
• /
• pp.216-221
• /
• 1992

액체급냉법으로 제작한 단일박대형 $Fe_{73.5}Cu_1Nb_3Si_{16}B_{6.5}$ 합금의 투자율 여효에 대한 열처리 효과를 펄스측정법으로 조사하였다. 미열처리 시료의 자화율 X와 인가자기장이 10 Oe 때의 자속밀도 $B_{10}$은 약 800과 0.8 T 였으며, 교류소자후 1초에서 64초 사이의 X의 변화율 D는 약 16%였다. $300^{\circ}C$에서 $600^{\circ}C$ 사이의 1시간의 등온 열처리에 의하여 연자기특성은 향상하였으며 최적 열처리온도 $570^{\circ}C$에서 X, $B_{10},$ D는 각각 15000, 1.2 T, 1.1 % 이였다. 열처리에 의한 특성의 변화의 원인을 미세결정립의 크기와 자기변형등에 연관하여 고찰하였다.

• 소성∙가공
• /
• 제26권5호
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• 한국자기학회지
• /
• 제17권5호
• /
• pp.194-197
• /
• 2007

극초진공 하에서 제작한 다양한 전이자성합금 박막에 대해 (Co-Fe, Co-Mn) 그 자기적 특성과 함께 Meservey-Tedrow 방식으로 측정한 스핀 편극치를 비교 분석 하였다. 약 20 nm 두께의 제작된 시료들은 표면 효과가 우세하리라는 기대와는 반대로 거의 벌크와 유사한 자기적 특성을 보였다. CoFe 또는 NiFe의 경우와는 달리 CoMn 경우 즉 강자성과 반자성 금속의 합금의 경우, 그 스핀 편극치가 그 자기모멘트에 의존하는 경향을 관찰 하였다. 이는 페르미 에너지 준위에서 터널링 현상에 대해 중요한 역할을 하는 sp-편력전자들과 고립되어 있는 d-전자 간의 교환상호작용(exchange interaction)에 의한 영향으로 이해할 수 있다.

• Applied Microscopy
• /
• 제47권1호
• /
• pp.50-54
• /
• 2017

The microstructure, the crystallization behavior, and magnetic properties of FeSi-based soft magnetic alloys (FINEMET) were investigated using transmission electron microscopy, X-ray diffraction, and coercive force measurements. The amorphous $Fe_{73.28}Si_{13.43}B_{8.72}Cu_{0.94}Nb_{3.63}$ alloys particles, prepared in $10^{-4}$ torr by gas atomization process, were heat treated at $530^{\circ}C$, $600^{\circ}C$, and $670^{\circ}C$ for 1 hour in a vacuum of $10^{-2}$ torr. Nanocrystalline Fe precipitation was first formed followed by the grain growth. Phase formation and crystallite sizes was compared linked to its magnetic behavior, which showed that excellent soft magnetic property can directly be correlated with its microstructure.