• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.4
• /
• pp.297-302
• /
• 2011

Recently, low temperature co-fired ceramic (LTCC) technology is widely used in sensors, actuators and microsystems fields because of its very good electrical and mechanical properties, high reliability and stability as well as possibility of making 3D micro structures. In this study, we investigated the effects of sputtering gas ratio and annealing temperature on the crystal structure of $Pb(ZrTi)O_3$ (PZT) thin films deposited on LTCC substrate. The LTCC substrate with thickness of $400\;{\mu}m$ were fabricated by laminating 4 green tapes which consist of alumina and glass particle in an organic binder. The PZT thin films were deposited on Pt / Ti / LTCC substrates by RF magnetron sputtering method. The results showed that the crystallization of the films were enhanced as increasing $O_2$ mixing ratio. At about 25% $O_2$ mixing ratio, was well crystallized in the perovskite structure. PZT thin films was annealed at various temperatures. When the annealing temperature is lower, the PZT thin films become a phyrochlore phase. However, when the annealing temperature is higher than $600^{\circ}C$, the PZT thin films become a perovskite phase. At the annealing temperature of $700^{\circ}C$, perovskite PZT thin films with good quality structure was obtained.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.381-386
• /
• 2010

Some basic properties of inorganic coatings hardened by the room temperature reaction with alkalies were examined. The coating paste was prepared from the powders in the system $Al_2O_3-SiO_2$-CaO using blast furnace slag, fly ash and amorphous ceramic fiber after mixing with a solution of sodium hydroxide and water glass. The mineralogical and morphological examinations were performed for the coatings prepared at room temperature and after heating to $1200^{\circ}C$ respectively. The binding force of the coating hardened at room temperature was caused by the formation of fairly dense matrix mainly composed of oyelite-containing amorphous phase formed by the reaction between blast furnace slag and alkali solution. At the temperature, fly ash and ceramic fiber was not reacted but imbedded in the binding phase, giving the fluidity to the paste and reinforcing the coating respectively. During heating up to $1200^{\circ}C$, instead of a break in the coating, anorthite and gehlenite was crystallized out by the reaction among the binding phase and unreacted components in ternary system. The crystallization of these minerals revealed to be a reason that the coating maintains dense morphology after heating. The maintenance of binding force after heat treatment is seemed to be also caused by the formation of welldispersed fiber-like mineral phase which is originated from the shape of the amorphous ceramic fiber used as a raw materials.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.231-236
• /
• 2018

We report p-type electrical characteristics of the amorphous $La_2NiO_{4+{\delta}}$ thin films which were sputtered on the glass substrates using an RF sputtering system. As-deposited thin films at room temperature and $300^{\circ}C$ were amorphous in nature. Post-annealing of the thin film samples over $400^{\circ}C$ resulted in the nano-crystallization of the $La_2NiO_{4+{\delta}}$. The electrical properties of the films were much dependent on the oxygen partial pressure, temperature of the post-annealing and sputtering ambient. The as-deposited samples at room temperature show a hole concentration of $7.82{\times}10^{13}cm^{-3}$, and it could be increased as high as $3.51{\times}10^{22}cm^{-3}$ when the films were post-annealed in an oxygen atmosphere at $500^{\circ}C$. Such p-type conductivity behavior of the $La_2NiO_{4+{\delta}}$ films suggests that the amorphous and nano-crystallized $La_2NiO_{4+{\delta}}$ films have potential for the application as p-type semiconductive or conductive materials at low temperatures where material diffusion is limited.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.75.2-75.2
• /
• 2010

We studied the fabrication of polycrystalline silicon (pc-Si) films as seed layers for application of pc-Si thin film solar cells, in which amorphous silicon (a-Si) films in a structure of glass/Al/$Al_2O_3$/a-Si are crystallized by the aluminum-induced layer exchange (ALILE) process. The properties of pc-Si films formed by the ALILE process are strongly determined by the oxide layer as well as the various process parameters like annealing temperature, time, etc. In this study, the effects of the oxide film thickness on the crystallization of a-Si in the ALILE process, where the thickness of $Al_2O_3$ layer was varied from 4 to 50 nm. For preparation of the experimental film structure, aluminum (~300 nm thickness) and a-Si (~300 nm thickness) layers were deposited using DC sputtering and PECVD method, respectively, and $Al_2O_3$ layer with the various thicknesses by RF sputtering. The crystallization of a-Si was then carried out by the thermal annealing process using a furnace with the in-situ microscope. The characteristics of the produced pc-Si films were analyzed by optical microscope (OM), scanning electron microscope (SEM), Raman spectrometer, and X-ray diffractometer (XRD). As results, the crystallinity was exponentially decayed with the increase of $Al_2O_3$ thickness and the grain size showed the similar tendency. The maximum pc-Si grain size fabricated by ALILE process was about $45{\mu}m$ at the $Al_2O_3$ layer thickness of 4 nm. The preferential crystal orientation was <111> and more dominant with the thinner $Al_2O_3$ layer. In summary, we obtained a pc-Si film not only with ${\sim}45{\mu}m$ grain size but also with the crystallinity of about 75% at 4 nm $Al_2O_3$ layer thickness by ALILE process with the structure of a glass/Al/$Al_2O_3$/a-Si.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.6
• /
• pp.254-261
• /
• 2010

Polycrystalline silicon (pc-Si) films are fabricated and characterized for application to pc-Si thin film solar cells as a seed layer. The amorphous silicon films are crystallized by the aluminum-induced layer exchange (ALILE) process with a structure of glass/Al/$Al_2O_3$/a-Si using various thicknesses of $Al_2O_3$ layers. In order to investigate the effects of the oxide layer on the crystallization of the amorphous silicon films, such as the crystalline film detects and the crystal grain size, the $Al_2O_3$ layer thickness arc varied from native oxide to 50 nm. As the results, the defects of the poly crystalline films are increased with the increase of $Al_2O_3$ layer thickness, whereas the grain size and crystallinity are decreased. In this experiments, obtained the average pc-Si sub-grain size was about $10\;{\mu}m$ at relatively thin $Al_2O_3$ layer thickness (${\leq}$ 16 nm). The preferential orientation of pc-Si sub-grain was <111>.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.353-359
• /
• 2000

$(Bi_{0.15}Sb_{0.85})_2Te_3$ and $(Bi_{1-x}Sb_x)_2Te_3$ thermoelectric thin films were prepared by magnetron sputtering process, and their thermoelectric characteristics were investigated with variation of the sputtering condition and the $Sb_2Te_3$ content. The $(Bi_{0.15}Sb_{0.85})_2Te_3$ film, deposited by DC sputtering at $300^{\circ}C$ with rotating the Corning glass substrate at 10 rpm, was fully crystallized to $(Bi,Sb)_2Te_3$ phase with c-axis preferred orientation. This $(Bi_{0.15}Sb_{0.85})_2Te_3$ film exhibited the Seebeck coefficient of 185 $\mu$V/K which was higher than the values of other $(Bi_{0.15}Sb_{0.85})_2Te_3$ films fabricated with different sputtering conditions. With increasing the $Sb_2Te_3$ content, the Seebeck coefficient and electrical resistivity of p-type $(Bi_{1-x}Sb_x)_2Te_3$ (0.77$\leq$x$\leq$1.0) film were lowered. Among p-type $(Bi_{1-x}Sb_x)_2Te_3$ films, a maximum power factor of $0.79{\times}10^{-3}W/K^2-m$ was obtained at (Bi_{0.05}Sb_{0.95})_2Te_3$ composition..

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.884-889
• /
• 1998

Amorphous silicon films of large area have been crystallized by a line shape excimer laser beam of one dimensional scanning with a gaussian profile in the scanning direction. In order to characterize the crystalline phase transition of thickness variables in excimer laser annealing(ELA), angle wrapping method was used. And also to characterize the residual stresses of crystalline phase transition in the case of angle wrapped-crystalline silicon on corning 7059 glass, polarized raman spectroscopies were measured at various laser energy density and substrate temperature. The residual stress varies from $9.0{\times}10^9$ to $9.9{\times}10^9$, and from $9.9{\times}10^9$ to $1.2{\times}10^10$dyne/${cm}^2$ of the substrate temperature at room temperature and varies from $8.1{\times}10^9$ to $9.0{\times}10^9$, and from $9.0{\times}10^9$ to $9.9{\times}10^9$dyne/${cm}^2$ of the substrate temperature at $400^{\circ}C$ as a function of direction from surface to substrate. According to the direction from the surface in liquid phase to the interface and from the interface to near the substrate in solid phase of recrystallized Si thin film, respectively. Thus, the stress is increased from(Liquid phase to solid phase) with phase transition.

• Resources Recycling
• /
• v.31 no.4
• /
• pp.49-55
• /
• 2022

In this study, the heavy metal ions (of Pb, Cd, Cr, and Hg) in wastewater were removed using a spent Li₂O-Al₂O₃-SiO₂-based crystallized glass previously used as an induction top plate material. Changes in the removal efficiency of heavy metals according to different reaction parameters, such as the amount of zeolite used as a heavy-metal adsorbent, adsorption time, initial concentration of the heavy metals, and pH of the initial solution, were investigated. As the amount of zeolite added increased, the heavy-metal removal efficiency also increased. Adsorption time had a considerable influence on adsorption characteristics, and the removal efficiency of all heavy metals increased with increasing adsorption time. In the case of Cd, the removal efficiency was greatly improved depending on the adsorption time. The initial concentration of the heavy-metal solution did not affect the removal efficiency; however, the initial pH of the heavy-metal solution affected the removal efficiency. More specifically, the removal efficiency of Cd increased while that of Pb and Cr decreased with increasing pH. The adsorption characteristics of Hg were not significantly affected by pH.

• Korean Journal of Mineralogy and Petrology
• /
• v.34 no.4
• /
• pp.277-291
• /
• 2021

A mineral phase contained in a rock sample can be categorized into several crystal populations with distinct origins and crystal growth histories. A detailed textural and mineralogical investigation on a clinopyroxene megacryst-bearing porphyritic dike with glassy chilled margins (tachylyte) in the southeastern Ulleung Island was conducted to decipher its crystal populations. During this study, we have measured glass and mineral major element compositions using electron microprobe analyzer. Tachylyte has a homogeneous trachyandesitic composition without any significant alteration characteristics, suggesting that its composition may represent the original melt composition of the dike. Clinopyroxene and plagioclase larger than 0.5 mm are antecrysts equilibrated with a more primitive melt composition than trachyandesitic tachylyte. Meanwhile, clinopyroxene and plagioclase microlites (<0.5mm) are regarded as primocrysts crystallized in-situ. According to our results, all clinopyroxenes in the Stage I Dodong Basalt are sectored into basal and prismatic parts, whose compositional ranges systematically vary: [Mg+Si+Fe]_basal ↔ [Al+Ti+Na]_prism. Therefore, we suggest that the effect of the elemental partitioning caused by the clinopyroxene sector zonation in Stage I volcanism should be considered in the future works.

• Applied Chemistry for Engineering
• /
• v.34 no.3
• /
• pp.285-290
• /
• 2023

Poly-lactic acid (PLA) is the most promising polymer in additive manufacturing as an alternative to acrylonitrile butadiene styrene (ABS). Since it is produced from renewable resources such as corn starch and sugar beets, it is also biocompatible and biodegradable. However, PLA has a couple of issues that limit its use. First, it has a comparatively low glass transition temperature of around 60 ℃, such that it exhibits low thermal resistance. Second, PLA has low impact strength because it is brittle. Due to these problems, scientists have found methods to improve the crystallinity and ductility of PLA. Polyethylene glycol (PEG) is one of the most studied plasticizers for PLA to give it chain mobility. However, the blend of PLA and PEG becomes unstable, and phase separation occurs even at room temperature as PEG is self-crystallized. Thus, it is necessary to investigate the optimal mixing ratio of PLA-PEG at the molecular scale. In this study, molecular dynamics will be conducted with various ratios of L-type PLA (PLLA) or DL-type PLA-PEG (PDLA-PEG) systems by using BIOVIA Materials Studio.