• 한국재료학회지
• /
• 제24권5호
• /
• pp.271-276
• /
• 2014

Silica nano-powder (SNP) is an inorganic material able to provide high-performance in various fields because of its multiple functions. Methods used to synthesize high purity SNP, include crushing silica minerals, vapor reaction of silica chloride, and a sol-gel process using TEOS and sodium silicate solution. The sol-gel process is the cheapest method for synthesis of SNP, and was used in this study. First, we investigated the shape and the size of the silica-powder particles in relation to the variation of HCl and sodium silicate concentrations. After drying, the shape of nano-silica powder differed in relation to variations in the HCl concentration. As the pH of the solution increased, so did the density of crosslinking. Initially, there was NaCl in the SNP. To increase its purity, we adopted a washing process that included centrifugation and filtration. After washing, the last of the NaCl was removed using DI water, leaving only amorphous silica powder. The purity of nano-silica powder synthesized using sodium silicate was over 99.6%.

• Membrane and Water Treatment
• /
• 제13권2호
• /
• pp.105-110
• /
• 2022

Al₂O₃ positively charged nanofiltration composite membrane was successfully prepared with aluminate coupling agent (ACA) as modifier, sodium bisulfite (NaHSO₃) and potassium persulfate (K₂S₂O₈) as initiator and methacryloyloxyethyl trimethylammonium chloride (DMC) as crosslinking monomer. The surface of the membrane before grafting and after polymerization were characterized by SEM and FT-IR. Three factor and three-level orthogonal experiments were designed to explore the optimal conditions for membrane preparation, and the optimal group was successfully prepared. The filtration experiments of different salt solutions were carried out, and the retention molecular weight was determined by polyethylene glycol (PEG). The results showed that the polymerization temperature had the greatest effect on the rejection rate, followed by the reaction time, and the concentration of DMC had the least effect on the rejection rate. The rejection rates of CaCl₂, MgSO₄, NaCl and Na₂SO₄ in the optimal group were 83.8%, 81.3%, 28.1% and 23.6% (average value), respectively. The molecule weight cut-off of 90% (MWCO) of the optimal group was about 460, which belongs to nanofiltration membrane.

• 폴리머
• /
• 제32권4호
• /
• pp.390-396
• /
• 2008

조직공학용 생체재료로 사용하고자 가교제 1,3-butadiene diepoxide(BD)를 사용하여 락타이드(LA)와 가교시킨 히아루론산(HA) 고분자를 제조하였다. 가교된 고분자의 락타이드 및 BD 반응도는 핵자기 공명 분광법으로 결정하였다. 반응도와 팽윤도는 LA/HA 몰비 혹은 가교제 농도를 증가시킴에 따라 증가하였다. 탄성률은 가교제 농도가 증가하거나 HA/LA 몰비가 감소함에 따라 감소하였다. 생분해는 2단계로 진행되었으며 BD 농도가 증가할수록 서서히 진행되었다. 첫 단계 분해는 주로 가교구조에 존재하는 에스테르기의 분해에 기인한 것으로 나타났다. 세포 성장 저해는 BD 농도가 증가함에 따라 증가하였다. 세포 독성은 BD 농도가 클 경우 약간 나타났으나 그 값은 6% 미만으로 세포 성장에 큰 문제는 없는 것으로 나타났다.

• 공업화학
• /
• 제21권6호
• /
• pp.621-626
• /
• 2010

음이온 교환막은 전기투석뿐만 아니라 역전기투석에 의한 전기생산과 축전 탈이온에 의한 정수 분야에 이용될 수 있다. 본 연구에서는 폴리비닐알콜 수용액 상에서 (vinylbenzyl)trimethylammonium chloride와 2-hydroxyethyl methacrylate를 중합한 후 글루타르산과의 에스테르화 반응, 그리고 글루타르알데히드와 가교반응을 통해서 음이온 교환막을 제조하였다. 실험 변수에 따라 음이온 교환막을 제조하고 이온교환막의 전기화학적 물성을 조사하였다. 중합반응에서 음이온 교환성 단량체 비율에 따라 이온교환량과 저항 값이 변하였으며, 에스테르화 반응에서는 글루타르산의 함량의 증가에 따라 함수율과 전도도가 감소하였다. 형성된 필름과 알데히드의 가교반응 시간 변화는 함수율, 전기저항, 이동수 값들에 영향을 미쳤다. 끝으로 제조된 이온 교환막의 chronopotentiometry와 한계전류밀도도 측정하였다.

• 한국염색가공학회지
• /
• 제30권2호
• /
• pp.107-116
• /
• 2018

Simplification of the manufacturing process in shoe making is essential to improve productivity and reduce production costs. To improve the adhesion of EVA foam used as a midsole, EVA/itaconated EPDM(EPDM-g-IA)(80/20wt%) blend was prepared using Torque Rheometer-Plasti-Corder, and 1,6-hexamethylenediamine/crosslinking agent/foaming agent/additive were mixed, followed by amidation reaction and foaming to prepare EVA/EPDM-g-IA foam for shoe midsole. In this study, we investigate the effect of the content of 1,6-hexamethylenediamine(0, 0.5, 1.0, 2.0, 3.0) on the mechanical properties, water-contact angle and adhesion of EVA/itaconated EPDM foam. As the content of 1,6-hexamethylenediamine increased, mechanical properties such as tensile strength, tear strength, tensile elastic modulus, hardness, and water-contact angle were lowered, but elongation at break and compression set(%) were increased. Both normal type and non-UV type adhesive strength increased with increasing diamine content. In particular, it was found that the adhesion strength of the non-UV type adhesion increased sharply with increasing diamine content. As a result, an adherend rupture occurs in a foam sample having a content of 1,6-hexamethylenediamine of 3phr. From this, it can be seen that the EVA/itaconated EPDM foam for shoe midsoles, which can be used for non-UV adhesion without primer and UV treatments, have been developed.

• Elastomers and Composites
• /
• 제36권4호
• /
• pp.268-277
• /
• 2001

PPG, PEG, trimethylolpropane(TMP) 등의 폴리올에 MDI(4,4'-diphenyl methane diisocyanate)를 각각 혼합하고 경화시켜 여러가지 물성을 측정하였다. 경화시간은 PEG와 TMP의 함량이 늘어날수록 짧게 나타났고 분자량의 효과보다는 관능기의 수에 더 큰 영향을 받았다. NCO-OH 반응은 NCO-NCO반응보다 활성적이고 빠르게 일어났다. 경도는 가교밀도와 분자구조의 영향을 받았으며 NCO-NCO 반응으로 생긴 도막은 취약하였고 NCO-OH간의 반응으로 생긴 도막은 유연하였다. 부착력은 결정화도와 수축율이 클수록 낮은 값을 나타내었으며 TMP 함량이 증량될수록 높은 값을 나타내었다. 난연성은 난연제의 종류와 함량에 영향을 받았으며 난연효과는 IXOL B-251이 가장 우수하였고 TCCP는 수지와의 상용성이 좋지 않아 부분적으로 분리되었다.

• Macromolecular Research
• /
• 제15권4호
• /
• pp.363-369
• /
• 2007

Novel biodegradable elastic hydrogels, based on hydrophilic and hydrophobic polymer blocks, were synthesized via the radical crosslinking reaction of diacrylates of poly(ethylene glycol) (PEG) and poly(${\varepsilon}-caprolactone$) (PCL). PEG and PCL diols were diacrylated with acryloyl chloride in the presence of triethylamine, with the reaction confirmed by FT-IR and $^1H-NMR$ measurements. The diacrylate polymers were used as building-blocks for the syntheses of a series of hydro gels, with different block compositions, by simply varying the feed ratios and molecular weights of the block components. The swelling ratio of the hydrogels was controlled by the balance between the hydrophilic and hydrophobic polymer blocks. Usually, the swelling ratio increases with increasing PEG content and decreasing block length within the network structure. The hydrogels exhibited negative thermo-sensitive swelling behavior due to the coexistence of hydrophilic and hydrophobic polymer components in their network structure, and such thermo-responsive swelling/deswelling behavior could be repeated using a temperature cycle, without any significant change in the swelling ratio. In vitro degradation tests showed that degradation occurred over a 3 to 8 month period. Due to their biodegradability, biocompatibility, elasticity and functionality, these hydrogels could be utilized in various biomedical applications, such as tissue engineering and drug delivery systems.

• 폴리머
• /
• 제34권5호
• /
• pp.485-489
• /
• 2010

본 연구에서는 폴리락트산(PLA)의 용융강도를 높이기 위하여 PLA에 글리시딜 메타크릴레이트(GMA)를 PLA에 첨가한 후 전자선을 조사하여 PLA를 개질하였다. GMA는 5 phr(parts per hundred parts of resin)로 고정하고 전자선 조사량을 변화시키며 개질 PLA을 제조하였으며, 이후 열적, 유변학적 특성 및 젤화도를 조사하였다. 주파수 0.1 rad/s에서 조사량 300 kGy로 개질된 PLA와 순수 PLA의 유변학적 물성을 서로 비교해보면 복합점도는 약 210배, 탄성률은 약 14500배 상승하는 예외적으로 아주 큰 변화를 보였다. 젤화도의 결과로 조사량 200 kGy 이하로 조사된 시료에서 일어난 분자반응은 가교화 반응보다는 가지화 반응이 우세하다는 것을 알 수 있었다.

• 폴리머
• /
• 제39권2호
• /
• pp.240-246
• /
• 2015

양기능성 실란 커플링제인 bis(triethoxysilylpropyl)tetrasulfide(TESPT)가 실리카/천연고무 복합소재 내에서 실리카의 hydroxy기와 고무 계면간에 화학적 결합반응을 하여 실리카-실란-고무간의 3차원 사슬구조를 형성한 것을 열분해 가스 크로마토그래피 질량분석기(Py-GC/MS)와 주사전자현미경(SEM)을 통해 관찰하였다. TESPT의 첨가로 배합물 내의 황 함유율이 증가하여 스코치 시간($t_{10}$)은 감소하고, TESPT 내 sulfur donor 역할을 하는 황이 활성화제 및 촉진제와의 복합반응으로 가교반응이 지속적으로 이루어짐에 따라서 가교속도지수(CRI)의 값이 감소하였다. 또한 TESPT가 첨가된 컴파운드는 첨가되지 않은 컴파운드에 비해 가공성 및 기계적 물성이 향상되었다. 결과적으로, 실리카로 충전된 천연고무 복합소재에 실란 커플링제(TESPT)가 첨가되어 화학반응으로 실리카-실란-고무간의 3차원 사슬구조가 형성됨을 관찰하였고 이에 따라 가교밀도가 증가하여 복합소재의 물성 증가에 기여함을 보여주었다.

• 한국응용과학기술학회지
• /
• 제33권4호
• /
• pp.615-626
• /
• 2016

약용매에 용해가 가능한 알킬기 변성 에폭시수지를 합성하기 위하여, 1단계에서 당량비 기준 dodecyl phenol (DP)/formaldehyde = 1.25~1.333/1.0로 하여, 합성된 도데실 페놀 노볼락 화합물의 벤젠 고리수가 3.0~5.0가 되도록 합성하였고, 2단계에서는 당량비 기준으로 1단계에서 합성된 도데실 페놀 노볼락 화합물/비스페놀A형 에폭시수지 (YD-128) = 1/2로 합성하였고, 3단계는 지방산을 투입하여 지방산 변성 도데실 페놀 노볼락 에폭시수지를 합성하였다. 합성된 수지의 반응성도, 점성도와 분자량 변화, 약용매 가용성 등을 측정한 결과, 1단계에서 합성된 도데실 페놀 노볼락 화합물의 벤젠고리수가 늘어남에 따라 지방산 변성 도데실 페놀 노볼락 에폭시수지의 점도가 상승하였고, 약용매 가용성이 우수하였다. 도료 제조 후 물성을 측정한 결과, 개환촉매로 triphenylphosphine(TPP)을 사용한 DPFAC-5는 건조속도, 접착성, 도막경도, 내충격성, 내산성 및 저장안정성이 양호하였다.