• Progress in Superconductivity and Cryogenics
• /
• v.17 no.1
• /
• pp.48-52
• /
• 2015

The electrical insulation design for a superconducting coil system is important for developing high voltage superconducting apparatuses. Also, the degraded characteristics of superconducting tapes due to an electrical breakdown should be considered for superconducting coils design. In this study, the degradation characteristics of 2G high temperature superconducting (HTS) tapes were studied with respect to electrical breakdown tests. The degradation tests of 2G HTS tapes were performed with various stabilizer materials. The degradation characteristics of 2G HTS tapes such as critical current(Ic) and index number were observed by performing electrical breakdown tests. It was found that the characteristics such as Ic and index number can be degraded by an electrical breakdown. Moreover, it was concluded that the degradation characteristics of 2G HTS tapes were affected by a stabilizer material and applied breakdown voltage. The cross sectional view of 2G HTS tapes was observed by using a scanning electron microscope (SEM). As results, it is found that the degradation characteristics of 2G HTS tapes are concerned with hardness and electrical resistivity of stabilizer layers.

• Progress in Superconductivity and Cryogenics
• /
• v.3 no.1
• /
• pp.6-10
• /
• 2001

Stress/stram dependencies of the critical current $I_c$ in AgMgNi sheathed multifilamentary Bi(2212) superconducting tapes were evaluated at 77K, 0T. The external reinforcement was accomplished by soldering Ag-Mg tapes to sin91e side or both sides of the sample. With the external reinforcement. the strength of tapes increased but $I_c$, decreased The $I_c$, degradation characteristic according to the external reinforcement was improved markedly in terms of the stress although it appeared less rectal.table on the basis of the strain. Effects of external reinforcement were discussed in a viewpoint of monitoring sensitivity of cracking in superconducting filaments by considering n-value representing the transport behavior of the current. It is closely associated with the location of them relative to the voltage-monitoring region in the tape.

• Progress in Superconductivity and Cryogenics
• /
• v.20 no.4
• /
• pp.20-25
• /
• 2018

Niobium nitride (NbN) superconducting thin films with the thickness of 100 and 400 nm have been deposited on the surfaces of silicon oxide/silicon substrates using a sputtering method. Their superconducting properties have been evaluated in terms of the transition temperature, critical magnetic field, and critical current density. In addition, the NbN films were patterned in a line with a width of $10{\mu}m$ by a reactive ion etching (RIE) process for their characterization. This study proves the applicability of the standard complementary metal-oxide-semiconductor (CMOS) process in the fabrication of superconducting thin films without considerable degradation of superconducting properties.

• Proceedings of the KIEE Conference
• /
• 2003.07b
• /
• pp.900-902
• /
• 2003

Critical current($I_c$) degradation of HTS tapes after bending is one of the holiest issues in HTS development and application studies. Many people are measuring $I_c$ degradations for effect of tending radius. However even if the bending radius is larger than the breaking radius a HTS tapes can be damaged by repetitive bending, which is unavoidable in the winding processes. Therefore, We studied the $I_c$ degradation after repetitive bending, at 77K with self-field, of Bi-2223 tapes processed by "Powder-in-Tube" technique, which was made by America Superconductor Corporation(AMSC), Innova Superconductor Technology(InnoST) and Korea Electro-technology Research Institute(KERI). For each specimen $I_c$ degradation was measured various bending radius as function of repetitive bending number.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.257-258
• /
• 2006

The $I_c$ degradation behaviors of externally-reinforced Bi-2223 superconducting tapes under pressurized liquid nitrogen were investigated. Tapes with different thickness of reinforcement layers were compared and the results showed that when the bending strain was calculated at the outer surface, the tape with the thicker reinforcement showed a better bending strain tolerance of $I_c$, but when the bending strain was calculated at the outermost filament, the $I_c$ degradation behavior became identical for all tapes. $I_{c0}$ decreased with the increase of applied pressure. After depressurization to atmospheric pressure from 1 MPa, the $I_c$ was completely recovered to its initial values. Ballooning occurred after a thermal cycle.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.4
• /
• pp.12-15
• /
• 2009

The $I_c$ degradation behavior of critical current in differently processed YBCO and SmBCO CC tapes with IBAD template has been investigated. It has been known that the residual strain in the CC tape will influence the shape of the $I_c$-strain window; $I_c$ may show a peak value if there exist a residual strain induced in the tape during manufacturing. The difference of residual strain may be resulted from the adopted different deposition techniques. In this study, bending test of CC tapes has been done using the Goldacker bending test rig which can produce both compressive and tensile bending strain continuously or alternately to the sample. For SmBCO CC tapes, in continuous compressive bending test, $I_c$ showed a minimal increase and did not degrade up to the largest strain that can be applied using the bending rig equivalent to 1.15% based on the sample thickness. However, in the case of alternate application of compressive and tensile bending strain, $I_c$ showed a larger degradation and a lower reversible limit when compared with the case of continuous application of the bending strain. When $I_c$ started to degrade significantly at the tension side, the reversibility ended, also at the compression side which is resulted from the permanent deformation like delamination or cracks that was induced due to tensile bending strain.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.761-768
• /
• 2000

In order to investigate how the fatigue damage effects on the critical properties of superconductor, a fatigue test at room temperature and an Ic measurement test at 4.2K were carried out in this study, respectively, using a 9 strand Cu-Ni/NbTi/Cu composite cable. Through the fatigue test of a 9 strand Cu-NUNbTi/Cu composite cable, a conventional S-N curve was plotted even though there was a possibility of fretting among strands. It was found that the maximum stress corresponding to the inflection point on the S-N curve obtained was nearly the same value as the yielding strength of cable obtained from the static tensile test. However, the effect of cabling in multi-strands superconducting cable on the fatigue strength was not noticeable. The critical current(Ic) measurement was carried out at 4.2K in a NbTi strand out of the fatigued cable. It showed a degradation of lc at high stress amplitude regions over 380NTa, and the degradation became significant as the applied stress amplitude increased.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2000.02a
• /
• pp.112-114
• /
• 2000

We fabricated BSCCO multifilaments superconductor tape and evaluated the effect of twisting on the microstructural evolution and critical current. Twist pitches of the tapes are in the range of 70 - 8 mm and uniformly deformed. It was observed that grain size and the degree of texture decreased as decreasing pith, probably due to the formation of the irregular interface between Ag and filaments. In addition, critical current of the tapes decreased to 6.5A with decreasing pitch to 8 mm, showing 48% of degradation compared to the untwisted tape(12.5 A). These reduction of critical current may be related to the interface irregularity, smaller grain size, worse texture and the presence of cracks due to the induced strain during twisting processing.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.10a
• /
• pp.142-145
• /
• 2003

In order to investigate the effect of cryogenic rolling on the critical current density (Jc), 54 and 55-multi-filament Bi-2223/hg tapes have been fabricated using a PIT process including two different types of cooling methods. The densification of oxide filament was found to occur due to the cryogenic rolling, and this enhanced the critical current density. However, when the wire was fully immersed in liquid nitrogen used as the coolant in cryogenic rolling, Jc degradation appeared caused by the nitrogen penetration into the filament. The cryogenically rolled tape with an improved type of cooling showed approximately 10％ Jc's increase.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.3
• /
• pp.23-26
• /
• 2008

Constructions of coated conductor which is differently from Bi-2223 is comprised multiple coatings on a base material or substrate and designed to achieve the highest degree of alignment possibility of the atoms in the superconductor material. In this study, we are measured and analyzed degradations of critical current according to diameter. In addition to study the effects of bending strain, we observed the AC loss of coated conductor and carried out analytical study for relation between Ic degradation and AC loss as well. The measurement of AC loss and numerical calculation was carried out based on Norris theory to compare with experimental results. The relationship between critical current and AC loss of HTS tapes with partial deformation by mechanical stress was studied. These results will amount the most important basis data in the of HTS cable, magnet, etc that winding work is required.