• 한국전기전자재료학회논문지
• /
• 제19권5호
• /
• pp.467-476
• /
• 2006

We fabricated the YBCO films on LAO substrate using the TFA-MOD method and evaluated the effects of heat treatment temperature and film thickness on the microstructure, degree of texture, and critical properties. The calcining and firing were peformed at the temperature range of $370^{\circ}C-460^{\circ}C\;and\;750^{\circ}C-800^{\circ}C$, respectively. For the films fired at $775^{\circ}C$ after calcining at $400^{\circ}C-430^{\circ}C$showed highest critical temperature (Tc-onset) of 89.5 K and critical current (Ic) of 40A/cm-width which corresponds to critical current density (Jc) of $1.8MA/cm^2$. The highest critical properties are probably attributed to the formation of purer YBCO phase, stronger biaxial texture, and higher oxygen content, according to the XRD, pole-figure, SEM, Raman analysis. From the multi-coated films, the Ic increased from 39 to 169 A/cm-width as the coating repeated to four times, while the corresponding Jc was measured from once to be in the range of $0.8-1.2MA/cm^2$. Both Ic and Jc degraded as the coating repeated further, indicating that the optimum thickness is in the range of $1.0{\mu}m-1.7{\mu}m$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.91-92
• /
• 2006

The important merit of Bi-2212/Ag wire is to apply cable as round wire state. Bi-2212 high Tc superconducting wires were fabricated in order to apply Rutherford cable near the future. Various Ag ratio from 0.22 to 0.42 of Ag tubes for PID (powder-In-Tube) process were used to investigate the workability and to prevent breakage of filaments during drawing. In order to find proper heat treatment condition, we investigated micro-structure of Bi-2212/Ag wires by using differential thermal analysis, XRD and SEM. The effect of atmosphere on the peritectic decomposition temperature of precursor was investigated. The shape of grain was observed by SEM to investigate Bi-2212 phase formation in filaments. The higher of Ag ratio of mono filament had the higher critical current density, Jc. The wire with 0.42 of Ag ratio showed 7,886 A/cm2 of Jc at 77K.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권6호
• /
• pp.578-583
• /
• 1996

The magnetic properties have been investigated for the system of $Y_{1-x}$Yb$_{x}$Ba$_{2}$Cu$_{3}$F$_{y}$O$_{y}$ with x=0.0, 0.1, 0.2, 0.3, 0.4 and 0.5. In the magnetic hysteresis measurements, the values of the magnetic critical current densities are in the range of 10$^{4}$-10$^{5}$ A/cm$^{2}$ at the maximum external field 1.4 T. The upper critical field is over 100 T. The critical current density is estimated by the magnetization width .DELTA.M through the Bean critical state model. As the field strength is increased, the .DELTA.M diminishes slowly. The .DELTA.M for the fluorinated sample also decreases slowly with increasing field. It is considered that the large J, value results from this type is due to enhanced pinning center in grain boundary.y.ary.y.

• Progress in Superconductivity
• /
• 제4권1호
• /
• pp.90-93
• /
• 2002

The sintering process of BSCCO 2223 tapes is a complex process that is very sensitive to parameters, such as temperature, oxygen partial pressure, heating and cooling rate and holding time. During the first heat treatment, 2212 phase of precursor powder is partially transformed into 2223 phase and some residual secondary phases, such as $(Bi,Pb)_2$$Sr_2$CuO／sub y／(2201), $(Ca,Sr)_2$CuO／sub y／(2/1AEC), (Ca,Sr)／sub 14／Cu／sub 24／O／sub 41／(14／24 AEC) etc. The secondary phases are difficult to be removed from the BSCCO 2223 matrix on the heat treatment. These secondary phases degrade the critical current density. In order to minimize the amount and size of alkaline earth cuprate(AEC) particles step heat treatment is applied during the first heat treatment under the varying atmosphere. Experimental results showed that by adapting the step heat treatment process, the amount and particle size of the secondary phases in the final tapes are decreased. Consequently, the BSCCO 2223grain texture and Jc properties are improved.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1996년도 하계학술대회 논문집 C
• /
• pp.1489-1491
• /
• 1996

The effect of Ag alloy sheath have been investigated in terns of critical current density and mechanical property. Nevertheless the continuous improvement of critical current density($J_c$) of Ag sheathed Bi2223 oxide superconducting wire processed with powder in tube(PIT) method, poor mechanical strength is still considered to be demerits for power application. In this study, we prepared two kinds of Ag- x wt% Cu alloy and pure Ag sheathed Bi2223 superconducting tapes. The hardness and tensile strength of prepared tapes has been measured. Their mechanical propertes were improved by Ag alloying.

• 전기학회논문지
• /
• 제61권2호
• /
• pp.339-341
• /
• 2012

The high Tc superconductor of YBCO system with the nominal composition of precursor was prepared from mixed powders of $Y_2O_3$, $BaCO_3$, CuO and $TiO_2$ by the thermal pyrolysis method. The effect of $TiO_2$ doping to Y based ceramics superconductors fabricated by the thermal pyrolysis reaction, to investigate the effect of the dopant on the superconductivity. The voltage appearing across the field-cooled HTS sample increased with external magnetic field. The improvement of critical current property as well as the mechanical property is important for the application. The improvement of the critical current can be achieved by forming the nano size defect working as a flux pining center inside the superconductor. We simply added $TiO_2$ to starting materials to dope $TiO_2$ and observed an increase in the trapped field and the critical current density up to at least 5 wt % $TiO_2$. The $TiO_2$ was converted to fine $BaTiO_3$ particles which were trapped in YBCO matrix during the sintering process. We observed a peak effect of Jc that can be attributed to $TiO_2$ doping and results suggest that introducing a proper amount of pinning centers can significantly enhance current density.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.496-499
• /
• 2000

In order to investigate the effect of Ge addition to the Cu Matrix on the microstructure and the critical current density, four kinds of internal tin processed Nb$_3$Sn strands with pure Cu and Cu 0.2, 0.4, 0.6 wt％ Ge alloy were drawn to 0.8 mm diameter. The microstructure and critical current of internal tin processed Nb$_3$Sn wires that were heat treated at temperatures ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$ for 240 h were investigated. The Ge addition to the matrix did not make workability worse. A Ge rich layer in the Cu-Ge matrix suppressed the growth of the Nb$_3$Sn layer and promoted grain coarsening. The greater the Ge content in the matrix, the lower the net Jc result after Nb$_3$Sn reaction heat treatment. There was no significant variation in Jc observed with heat treatment temperature ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2002년도 학술대회 논문집
• /
• pp.101-104
• /
• 2002

The influences of the powder packing density on the Bi-2223/Ag tape have been investigated. For packing powder, both method of uniaxial press and packed rod form made by cold isostatic press(CIP) have been applied. As the pressure of cold isostatic press(CIP) is increased, fill factor and critical current (Ic) of Bi-2223/Ag tape is increased. At a pressure of 2000kgf/cm$^2$, fill factor reach ∼3l% and this sample has the engineering current density(Je) value of ∼8.5kA/cm$^2$(Ic ∼77A, Jc ∼ 30kA/cm$^2$). The tape sample packed by uniaxial press method shows more sawsaging effect than the sample processed by cold isostatic press(CIP), resulting from inhomogity of powder distribution produced by the process of uniaxial press.

• Progress in Superconductivity
• /
• 제10권1호
• /
• pp.17-22
• /
• 2008

We have examined the effect of ball-milling on the superconducting properties of $MgB_2$ doped with C. The ball-milling of pre-reacted $MgB_2$ powder was carried out in dry or wet state using C or diethylenetriamine ($C_{4}H_{13}N_3$) as additives. The diethylenetriamine, whose chemical formula contains no oxygen, was chosen to avoid an excess oxidation during doping. The superconducting transition temperature (Tc) of the ball-milled or doped $MgB_2$ powders was only slightly smaller than that of undoped $MgB_2$. The critical current density (Jc) of the highly ball-milled $MgB_2$ was higher than that of C-doped $MgB_2$. The addition of diethylenetriamine was detrimental to Jc, although Tc was almost unchanged.

• 한국표면공학회지
• /
• 제24권2호
• /
• pp.67-72
• /
• 1991

The feasibility of preparing superconducting $Y_1Ba_2Cu_3O_y$ films on metallic substrate was exmined in an attempt to fabricate a tape conductor. Deposition methods employed were sputtering, laser ablation, and plasma flash evaporation. Although zero resistance temperature (Tc) is achieved above 90 K, critical current density values (Jc) obtained so far is still low as compared with those reported in the films grown on single crystal substrates. This may be caused by the misalignment of the crystal structure of the films on metal substrates. A further improvement if Jc for highly-oriented polycrystalling films is being investigated at the present time.