• Transactions of the Korean Society of Automotive Engineers
• /
• v.21 no.1
• /
• pp.145-153
• /
• 2013

In this study, shear punch-creep (SP-Creep) at Sn-4Ag/Cu pad the joint was tested by using environment-friendly Pb-free solder alloy Sn-4Ag of electronic components. Pb eutectic alloy (Sn-37Pb) joints limited to environmental issues with reflow time (10sec, 30sec, 100sec, 300sec) according to two types of solder alloy joints are compared and evaluated by creep strain rate, rupture time and IMC (Intermetallic Compound) behavior. As the results, reflow time increases with increasing thickness of IMC can be seen at overall 100sec later in case of two solder joints on the IMC thickness of Sn-4Ag solder joints thicker than Sn-37Pb solder joints. In addition, when considering creep evaluation factors, lead-free solder alloy Sn-4Ag has excellent creep resistance more than Pb eutectic alloy. For this reason, the two solder joints, such as in the IMC (Cu6Sn5) was formed. However, the creep resistance of Sn-4Ag solder joints was largely increased in the precipitation strengthening effect of dispersed Ag3Sn with interface more than Sn-37Pb solder joints.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.11a
• /
• pp.63-64
• /
• 2008

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.11a
• /
• pp.85-86
• /
• 2007

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.199-200
• /
• 2009

• Journal of Power System Engineering
• /
• v.19 no.5
• /
• pp.45-51
• /
• 2015

Grade 91 steel is used for the major structural components of Generation-IV reactor systems such as a very high temperature reactor (VHTR) and sodium-cooled fast reactor (SFR). Since these structures are designed for up to 60 years at elevated temperatures, the prediction of long-term creep life is very important to determine an allowable design stress of elevated temperature structural component. In this study, a large body of creep rupture data was collected through world-wide literature surveys, and using these data, the long-term creep life was predicted in terms of three methods: Larson-Miller (L-M), Manson-Haferd (M-H) and Wilshire methods. The results for each method was compared using the standard deviation of error. The L-M method was overestimated in the longer time of a low stress. The Wilshire method was superior agreement in the long-term life prediction to the L-M and M-H methods.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.352-357
• /
• 2003

Creep tests for Titan were carned out using constant-load at $600^{\circ}C$, $650^{\circ}C$ and $700^{\circ}C$. Material constants necessary to predict creep life were acquired from the experimental creep data. And the applicability of Monkman-Grant(M-G) and modified M-G relationships was discussed. It was discovered the log-log plot of M-G relationships between the rupure time(tr) and he minimum creep rate(${\varepsilon}_m$) was conditional on test temperatures. The slop of m was 2.75 at $600^{\circ}C$ and m was 1.92 at $700^{\circ}C$. However; the log-log plot of modified M-G relationships between $t_r/\varepsilon_r$ and $\varepsilon_m$ was indpendent on stresses and temperatures. That is the slop of m' was almost 3.90 in all the data. Thus, change M-G relationships to creep life prediction could be vtilized more reasonably than that of M-G relationships for type Titan. It was divided that the constant slopes never theless of temperatures of practical stresses in the modified relationship were due to an intergranular break grown by wedge-type cauities.

• Korean Journal of Materials Research
• /
• v.2 no.6
• /
• pp.468-476
• /
• 1992

Stress rupture properties and fracture behavior of Ni microalloyed W were studied using direct load creep tester at 100$0^{\circ}C$, 110$0^{\circ}C$ and 120$0^{\circ}C$ in $H_2$. At the same grain size, 15${\mu}$m, the 100hr. stress rupture strength of W-0.4wt% Ni was 23% higher than that of W-0.2wt%Ni due to the grain growth during test. The minimum creep rate of W-0.2wt%Ni was decreased with an increase in initial grain size. By increasing the Ni content of Ni microalloyed W, rupture time was increased owing to the smaller number and size of cavity. All the specimens showed intergranular fracture by grain boundary sliding and nucleation, growth and coalescence of cavities at grain boundary.

• Korean Journal of Metals and Materials
• /
• v.49 no.7
• /
• pp.515-521
• /
• 2011

Small punch creep testing has received attention due to the convenience of using smaller specimens than those of conventional uniaxial creep tests, which enables creep testing on developing or currently operational components. However, precedent studies have shown that it is necessary to consider friction between the punch and specimen when computing uniaxial equivalent stress from a finite element model. In this study, small punch creep behaviors of AISI 316L stainless steel, which is widely used in high temperature-high pressure machineries, have been compared for the two different ceramic balls such as $Si_3N_4$ and $Al_2O_3$. The optimal range of the friction coefficient is 0.4~0.5 at $650^{\circ}C$ for the best fit between experimental and simulation data of AISI 316 L stainless steel. The higher the friction coefficient, the longer the creep rupture time is. Therefore, the type of ceramic ball used must be specified for standardization of small punch creep testing.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.2 s.28
• /
• pp.65-70
• /
• 1998

In this report, the creep properties and creep life estimation by Larson-Miller Parameter(LMP) Method for 2.25Cr1Mo steel to be used as power plant tubes or other components were presented at the high temperatures of 500, 550, and $600^{\circ}C$. It was confirmed experimentally and quantitatively that a creep life estimation equation at such various high temperatures was well derived by LMP and could be used very effectively within the creep life of 10$^3$ hours, but very unreliable and even dangerous for design in a long term of creep life such as 10$^4$ or $10^5$ hours.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.43-48
• /
• 2000

In this study, a small punch creep(SP-Creep) test using miniaturized specimen$(10{\times}10{\times}0.5mm)$ has been described for the development of the newly semi-destructive creep test method for high temperature structural components such as headers and tubes of boiler turbine casino and rotor and reactor vessel. The SP-Creep testing technique has been applied to 2.25Cr-1Mo(STBA24) steel used widely as boiler tube material and the creep test temperature are varied at $550^{\circ}C{\sim}600^{\circ}C$. The overall deformations of SP-Creep curves are definitely depended with applied load and creep test temperature and show the creep behaviors of three steps like conventional uniaxial creep curves. The steady state creep rate${\delta}_{ss}$ of SP-Creep curve for miniaturized specimen increases with increasing creep temperature, but the exponential value with creep loading is decreased. The activation energy$(Q_{spc})$ during SP-Creep deformation with various test temperatures shows 605.7kJ/mol that is g.eater than 467.4kJ/mol reported in uniaxial creep test. This may be caused by the difference of stress states during creep deformation In two creep test. But from the experimental results, e.g. SP-Creep curve behaviors, the steady state creep rate${\delta}_{ss}$ with creep temperature, and the exponential value(n) with creep loading, it can be summarized that the SP-Creep test may be a useful test method to evaluate the creep properties of the heat resisting material.