• Journal of Ocean Engineering and Technology
• /
• v.8 no.1
• /
• pp.41-49
• /
• 1994

The leak-before-break(LBB) design on the large structures such as ship's hull, tank structure, pressure vessels etc. is one of the most inportant subjects for the evaluation and the assurance of safety. In these structures, various loads are acting. In some structural members, therefore, out-of-plane stress due to bending often may become with in-plane stress due to stretching. In the present report, the characteristics of fatigue life and peneration behaviour from a surface cracked plate under combined tension and bending have been studied experimentally and analytically by using eccentricity. Estimation of fatigue crack growth was done with the Newman-Raju formula before penetration, and with the stress intensity factor after penetration proposed by the author. Calculated aspect ratio showed the good agreement with the experimental result. It was also found that particular crack growth behaviour and crack shape after penetration can be satisfactorily evaluated using the K solution proposed.

• KSTLE International Journal
• /
• v.2 no.1
• /
• pp.12-16
• /
• 2001

A finite element analysis of crack propagation in a half-space due to sliding contact was performed. The sliding contact was simulated by a rigid asperity moving across the surface of an elastic half-surface containing single and multiple cracks. Single, coplanar, and parallel cracks were modeled to investigate the interaction effects on the crack growth in contact fatigue. The analysis was based on linear elastic fracture mechanics and the stress intensity factor concept. The crack propagation direction was predicted based on the maximum range of the shear and tensile stress intensity factors.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.228-229
• /
• 2005

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.04a
• /
• pp.802-806
• /
• 2001

Chrome-molybden steel or chrome steel for machine structural use been shown to excellent hardenability adding boron of a small amount at low carbon steel. In the country boron steel has been used widely high strength volt and wear resistant components of construction equipment. SEM results showed classical fatigue fractures, consistent with surface crack initiation. The speciments were cycled using under load controlled rotary bending fatigue tests. In this study, the fatigue crack initiation as well as the fatigue crack growth behavior and the fracture mechanism were investigated through observations of fracture surface boron steel(AISI 51B20).

• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.1
• /
• pp.43-50
• /
• 1998

The purpose of the paper is to protect the damage of plastic IC package with searching the cause of the fracture due to the delamination and crack when the encapsulant of plastic IC package is on viscoelastic behavior with the effect of creep on high temperature, The model for analysis is the plastic SOJ package with dimpled diepad in the IR soldering process of surface mounting technology. The risk of delamination with calculating the distribution of viscoelastic thermal stress in the package without the crack in the surface mounting process is checked. The package model with the perfect delamination between chip and diepad is chosen to estimate the resistance against fracture in thermal loading with calculating C (t)-integrals according to the change of the design. The optimum design to depress the delamination and crack is presented.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.6
• /
• pp.665-670
• /
• 2011

In this paper, a new approach to detect surface cracks from a noisy thermal image in the infrared thermography is presented using an holomorphic characteristic of temperature field in a thin plate under steady-state thermal condition. The holomorphic function for 2-D heat flow field in the plate was derived from Cauchy Riemann conditions to define a contour integral that varies according to the existence and strength of a singularity in the domain of integration. The contour integral at each point of thermal image eliminated the temperature variation due to heat conduction and suppressed the noise, so that its image emphasized and highlighted the singularity such as crack. This feature of holomorphic function was also investigated numerically using a simple thermal field in the thin plate satisfying the Laplace equation. The simulation results showed that the integral image selected and detected the crack embedded artificially in the plate very well in a noisy environment.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1257-1265
• /
• 1998

Hertzian contact tests were used to investigate the evolution of fracturedamage in the coating layer as functions of contact load and coating thickness by studying crack patterns in porcelain on glass-infiltrated alumina bilayer system conceived to simulate the crown structure of a tooth. Cone cracks initiated at the coating top surface without delamination at interface and crack propagation to substrate. Preferentially the cracks made multi-cracks at the coating top surface rather than proceeding to interface. The cracks were highly stabilized with wide ranges between the loads to initiate first cracking and to cause final failure im-plying damage-tolerant capability. Finite element modelling was used to evaluate the stress distribution. Maximum tensile stress were responsible for the cracking at the coating layer and had a profound influence on the crack pattern and fracture damage in the layered structure materials.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.239-245
• /
• 2004

Resistance spot weldability of coated steels for automobile applications was investigated. Test samples were prepared from commercial products of 0.8 mm in thickness. Based on the tensile-shear test, surface quality examination and cracking behavior, it was clear that aluminized steels showed good weldability. Microstructural inspection revealed that the coated materials was piled up at the split zone in the welding of aluminized steels. It was also demonstrated that no weld crack was found in the aluminized steel weld metal even the welding was carried out with higher current. However, through thickness cracks were detected at the weld metal of zinc coated steel. Small particles were found on the crack surface of zinc coated steel weld metal. It was thought that zinc vapor played key role to form the weld crack.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.8
• /
• pp.1269-1276
• /
• 2001

In case of contact fatigue, the accurate calculation of surface tractions and subsurface stress is essential to the predication of crack initiation life. Surface tractions influencing shear stress amplitude have been obtained by contact analysis based on influence function. Subsurface stress has been obtained by using rectangular patch solutions. In this study, to simulate asperity contact under sliding condition, the tip of asperity was simulated by sphere and to calculate crack initiation life in the substrate, dislocation pileup theory was used.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.94-98
• /
• 2001

fatigue life and nondestructive evaluation were examined experimentally using surface crack specimen and compact tension specimen of 5083 aluminium alloy. Acoustic emission signals emanated during failure of aluminum alloys has been the subject of numerous investigations. Possible sources of AE during deformation have been suggested as the dislocations, fracture of brittle particles and debonding of these particles from the alloy matrix. Fatigue life and penetration behavior of long surface crack can be evaluated quantitatively using K values proposed by authors. The influence of stress ratio on the frequency characteristics of AE signals were investigated.