• Journal of Welding and Joining
• /
• 제19권6호
• /
• pp.652-657
• /
• 2001

To analyze and predict crack initiation position and propagation directions on the spot welded area are very important for strength design of the automobile body structure. It is necessary to test by method considering random loads with variable amplitude for strength design of vehicle body structure, because driving cars are actually subjected to random loads with variable amplitude in the road. Although this condition, nearly all tests haute been performed under constant load conditions in the laboratory because it is impossible to replay like an actual conditions. In this study, using in-plane bending type specimens, the overload factor affecting on the fatigue strength, crack initiation and propagation directions of spot-welded specimens have been studied.

• 산업기술연구
• /
• 제9권
• /
• pp.43-49
• /
• 1989

In this study, 3-point bending test for the mode I state and 4-point shear test for the mode II state were adopted to verify the crack initiation load level through comparing the test results of the acoustic emission and the ASTM testing criteria, using Jecheon granite, as the rock sample. The major result obtained in this study is that the crack initiation load levels obtained by using ASTM testing criteria and by measuring acoustic emissions showed analogous, roughly. However in case of demanding high safety, the crack initiation load level needs to be underestimated to the level that the crack begins to deform nonlinearly.

• 한국철도학회논문집
• /
• 제7권4호
• /
• pp.345-349
• /
• 2004

This study investigates the fatigue lives of SM490A material(base metal) specimens and fillet weld specimens, which are made same material and weld method for the railway vehicle. These fatigue lives have a difference, the fatigue lives of weld specimen are shorter than those of base metal. We measured the strains on the weld positions of the specimens during the fatigue test for investigation of crack initiation and crack growth. In these result, we could find the information of the crack initiation position on weld bead and the history of crack growth. Also we knew that the fatigue crack initiation cycles and the changes of the strain which were affected the fractured surface roughness and morphology.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.156-161
• /
• 2004

To predict the direction of the fatigue crack initiated from a hole under various types of biaxial fatigue loads with different phase difference and biaxiality, fatigue parameters were investigated. Axial and torsional biaxial fatigue loads were selected with the respective combination of five different phase differences of 0, 45, 90, 145 and 180 degrees and five biaxialities of 0, $1/{\sqrt{3}}$, 1, ${\sqrt{3}}$, ${\infty}$. Directions of the fatigue crack initiation around the hole were found to approach to the circumferential direction of the specimen with increment of the phase difference for fatigue tests with phase differences less than $90^{\circ}$. Whereas directions for tests with phase differences greater than $90^{\circ}$ went away from the circumferential direction and those were symmetric to the directions for tests with phase difference less than $90^{\circ}$. With increase of biaxilities, the fatigue crack initiated more apart from the circumferential direction of the specimen. These crack initiation direction were predicted using maximum tangential stress range and maximum shear stress range obtained at far-field and around the hole. Comparing these two stress parameters, The crack initiation direction can be successfully explained by using the direction of the maximum tangential stress range obtained around the hole and at far-field.

• 대한기계학회논문집A
• /
• 제34권1호
• /
• pp.103-110
• /
• 2010

본 연구에서는 프랑스의 RCC-MR A16 절차에 기초하여 Mod.9Cr-1Mo 강(ASME Grade 91) 구조의 크리프-피로 균열 개시 및 성장 평가법을 확장 개발하였다. 현재의 A16 지침은 오스테나이트 스테인리스강에 대해서만 크리프-피로 균열 개시 및 성장 평가법을 제시하고 있지만, 현재 초초임계(USC) 화력발전소는 물론 미래형 원자로 시스템의 구조재료로서 폭넓게 채택되고 있는 Mod.9Cr-1Mo 강에 대한 지침은 제시하지 않고 있다. 본 연구에서는 FMS(페리틱-마르텐사이트강)에 대한 크리프-피로 균열 개시 및 성장 평가법을 제시하고 있고, 구조물에 대한 크리프-피로 균열 거동 평가를 수행하였다. 평가결과는 구조시험을 수행한 결과 얻은 관찰 이미지와 비교하였다.

• 대한기계학회논문집A
• /
• 제26권3호
• /
• pp.528-536
• /
• 2002

As one step for the safety performance of LNG storage tank, the change in fracture toughness within the X-grooved weld heat-affected zone (HAZ) of newly developed 9% Ni steel, which was submerged arc (SA)-welded, was investigated. Both crack initiation fracture toughness and crack arrest fracture toughness were evaluated by the crack tip opening displacement (CTOD) tests and compact crack arrest (CCA) tests. As the evaluated region approached the fusion line, each test result shorted different tendency, that is, crack initiation toughness decreased while crack arrest toughness increased. The results were discussed through the observation of the microstructural change.

• 대한기계학회논문집A
• /
• 제31권3호
• /
• pp.344-354
• /
• 2007

The objective of this study is to investigate the effect of arbitrarily located defect around the circular hole in the aircraft structural material such as Al/GFRP laminates and monolithic Al alloy sheet under cyclic bending moment. The fatigue behavior of these materials may be different due to the defect location. Material flaws in the from of pre-existing defects can severely affect the fatigue crack initiation and propagation behavior. The aim of this study is to evaluate effects of relative location of defects around the circular hole in monolithic Al alloy and Al/GFRP laminates under cyclic bending moment. The fatigue behavior i.e., the stress concentration factor($K_t$), the crack initiation life($N_i$), the relationship between crack length(a) and cycles(N), the relationship between crack growth rate(da/dN) and stress intensity factor range(${\Dalta}K$) near a circular hole are considered. Especially, the defects location at ${\theta}_1=0^{\circ}\;and\;{\theta}_2=30^{\circ}$ was strongly effective in stress concentration factor($K_t$) and crack initiation life($N_i$). The test results indicated the features of different fatigue crack propagation behavior and the different growing delamination shape according to each location of defect around the circular hole in Al/GFRP laminates.

• 지질공학
• /
• 제20권1호
• /
• pp.89-100
• /
• 2010

암석의 손상상태를 평가하기위한 여러 방법들이 제안되어 있으나, 일부의 방법은 명확한 손상기준을 제시하기도 하지만 일부의 방법은 매우 모호하여 분석자의 주관에 따라 값이 달라지기도 한다. 그러므로 이 연구에서는 황등화강암을 대상으로 현재까지 제안된 모든 손상기준 결정방법을 적용하여, 각 방법의 적용성, 오차 및 최적의 손상기준결정 방법 등을 연구하였다. 또한 암석의 균열발달 및 파괴특성의 규명에 가장 중요한 손상기준인 균열개시응력과 균열손상응력을 FSR 및 장기 정하중 시험을 이용하여 검정하였다. 황등화강암의 균열닫힘응력과 균열개시응력은 각각 57.5 MPa, 77.6 MPa이며 균열체적변형률에서 측정하는 것이 가장 정확한 것으로 판단된다. 2차 균열개시응력은 90.6 MPa로 측정되었으며, 미소파괴음 계수 및 계수율이 균열개시응력의 측정에 가장 효과적인 것으로 판단된다. 균열결합응력 측정은 체적강성곡선, 미소파괴음 계수 및 미소파괴음 계수율이 가장 효과적인 방법으로 판단되며, 균열결합응력은 110.3 MPa이다. 균열손상응력은 체적강성곡선 및 미소파괴음 계수율에서 가장 명확히 측정되며, 약 127.5 MPa이다. 일축압축강도에 대한 비로서 나타낸 균열개시응력은 0.47로 FSR 값 0.46과 매우 유사하며, 균열손상응력은 0.77로 장기 정하중 시험을 통하여 측정된 장기 강도비 0.75~0.8과 거의 일치하여 균열개시응력 및 균열손상응력 값이 정확함을 검정하였다.

• Steel and Composite Structures
• /
• 제13권4호
• /
• pp.383-396
• /
• 2012

In order to develop a verification method for extremely low cycle fatigue (ELCF) of steel structures, the initiation mechanism of ductile cracks is investigated in the present study, which is the first step of brittle fracture, occurred in steel bridge piers with thick-walled sections. For this purpose, a total of six steel columns with small width-thickness ratios were tested under cyclic loading. It is found that ductile cracks occurred at the column base in all the specimens regardless of cyclic loading histories subjected. Moreover, strain history near the crack initiation location is illustrated and an index of energy dissipation amount is proposed to evaluate deformation capacity of structures.

• Corrosion Science and Technology
• /
• 제15권5호
• /
• pp.203-208
• /
• 2016

DC potential drop technique was employed during the slow strain rate tests to study the hot salt stress corrosion crack (HSSCC) initiation at 300 and $400^{\circ}C$. Threshold stresses for HSSCC initiation were found to about 88 % of the yield strength at both temperatures, but the time from crack initiation to final failure (${\Delta}t_{scc}$) decreased significantly with temperature, which reflects larger tendency for brittle fracture and secondary cracking. The brittle fracture features consisted of transgranular cracking through the primary ${\alpha}$ grain and discontinuous faceted cracking through the transformed ${\beta}$ grains.