• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.51-51
• /
• 1998

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.2
• /
• pp.170-176
• /
• 2002

Nonlinear acoustic effect has been considered as an effective tool for the evaluation of material degradation. In this paper, the applicability of nonlinear acoustic effect to the evaluation of degraded 2.25Cr-1Mo steel is investigated. Firstly, artificial aging was performed to simulate the microstructural degradation in 2.25Cr-1Mo steel arising from long time exposure at $540^{\circ}C$. Secondly, ultrasonic nonlinear parameter was quantitatively measured by bi-spectrum and power spectrum. Nonlinear acoustic parameter from bi-spectrum was found to be clearly sensitive to the aging time.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.445-450
• /
• 2000

The integrity of the turbine rotors can be assessed by measuring reversible permeability and Vickers hardness of the aged rotors at service temperature. The measurement system of reversible permeability, which measured by applied alternating perturbing magnetic field, was constructed in order to evaluate material degradation, nondestructively. The test specimen was 1Cr-1Mo-0.25V steel used widely for turbine rotor material, and the specimens were prepared by the isothermal heat treatment at $630\;^{\circ}C$. The reversible permeability of the test materials were measured at room temperature. The peak interval of reversible permeability and Vickers hardness decreased with the increase of degradation. The degradation of test material may be determined nondestructively by the lineality of Vickers hardness and the peak interval of reversible permeability.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.2
• /
• pp.168-176
• /
• 2004

Interrupted creep tests were carried out on the Mod.9Cr-1Mo steel in order to investigate the structural degradation during creep. The ranges of creep stress and temperature were from 71 to 167MPa and 873 to 923k, respectively. The change of hardness and tempered martensitic lath width were measured in the grip and gauge parts of interrupted specimens. The lath structure was thermally stable in static conditions, but was not stable during creep, and the structural evolution was enhanced by creep strain. The relation between the change in lath width and strain was described in the from, $\delta$W= a ($W_s-W_o$)$cdot;varepsilon$, where $\varepsilon$ is the strain, $W_o$is the initial lath width, $W_s$ is the final lath width depending solely on stress, and a is the constant of the magnitude of 0.67 $\mu$m /strain. The change in Victors hardness was expressed by a one-valued function of creep life consumption ratio. Based on the empirical relation between strain and lath width, a model was proposed to explain the relation between change in hardness and creep life consumption ratio. The model revealed that about 65$%$ of dislocations in lath structures were eliminated by the migration of subboundaries.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.322-327
• /
• 2000

This paper investigates the time-dependent crack growth in X20CrMoV 12 1 steel weld joints. Crack growth test are carried out $545^{\circ}C$ on side-grooved 1/2T CT specimens under static loads. A simulated material is produced for the intercritical HAZ, where fracture normally occurs. Constitutive properties are obtained for the simulated HAZ material as well as for the base metal and weld metal. Finite element analyses of crack growth are performed on the models with and without a HAZ layer, using the experimental crack length-time history. The inclusion of HAZ layer increase the load line velocities significantly. The crack growth rates are correlated reasonably well with $C^*$. The smallest crack size for the validity of $C^*$ is found much smaller than the ASTM crack initiation size for 1T CT specimen of creep ductile materials.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2003.05a
• /
• pp.274-278
• /
• 2003

In recent, an application of high energy density beam we/ding is increasing to obtain the high quality in weldments. Laser welding, especially, has been recognized as an useful method and its beam power has also increased according to the development of relevant technology. However, welding method in the fields of power plant is conservative because their structures have required to endure high temperature and pressure. So, authors conduct the numerical simulation in order to consider the possibility of laser welding on the material of the pressure vessels ($2\frac{1}{4}Cr-1Mo$ steel). As a result of this study, we can confirm the advantages of laser welding and obtain useful information for the experiments of weldability.

• Journal of the Korean Magnetics Society
• /
• v.21 no.4
• /
• pp.136-140
• /
• 2011

Mechanical properties of degraded materials must be measured for evaluating the integrity of the facilities operating at high temperature. In fact it is complicated to obtain the different degraded specimens from an operating facility. Specimens of 1Cr-0.5Mo steel prepared by the isothermal heat treatment at $700^{\circ}C$ were tested, which has been widely used as tubes for heat exchangers and as plates for pressure vessels. The magnetic properties and Rockwell hardness (HRB) were measured at room temperature. The peak interval of Barkhausen noise envelope (PIBNE), coercivity, and hardness decreased with the increase of degradation. The magnetic and mechanical softening of matrix is likely to govern the properties of the specimen more than the hardening of grain boundary by carbide precipitations. The degradation of test material may be determined by the linear correlation of PIBNE and HRB. Degradation of 1Cr-0.5Mo steel could well be nondestructively evaluated by PIBNE measured with surface type probe.

• Journal of Energy Engineering
• /
• v.26 no.4
• /
• pp.1-6
• /
• 2017

This study evaluated hydrogen effect of metal and non-metallic materials used in the hydrogen blended natural gas vehicle. Hydrogen penetrated concentration of 34Cr-Mo steel(850MPa tensile strength) for winter driving conditions was measured 0.0018ppm and summer driving conditions was 5.3ppm. The critical hydrogen concentration of high strength metal used in this study was measured 1.03ppm by CLT. Therefore, 34CrMo steel cas cause problems in the 30% HCNG(25MPa) environment. In case of the test for non-metallic materials, all materials met the criteria of the gas resistance test, but Fluorocarbon Rubber material had a significant change in the volume. So if it is used, extra care is needed.

• Journal of Welding and Joining
• /
• v.26 no.3
• /
• pp.37-44
• /
• 2008

Charpy V-Notch test is commonly used to evaluate fracture toughness. However, since the region to be evaluated is limited to bulk material due to the specimen size required, individual evaluation of micro-structures on weldment is very difficult. In this study, ASP(Advanced Small Punch) test was carried out to evaluate material degradation and fracture toughness on the B.M, W.M and each micro-structures of HAZ for X20CrMoV121 and 2.25Cr1Mo steels with artificial aging time. In addition, to evaluate fracture toughness and material degradation of B.M and W.M of X20CrMoV121 steels with aging times, CVN (Charpy V-notch) test was performed. And then the correlation between ASP and CVN test on X20CrMoV121 steels was obtained. Furthermore, through this correlation, material degradation property of each micro-region of the HAZ in weldment, which was impossible to be evaluated by the CVN test, can be estimated and determined.

• Korean Journal of Materials Research
• /
• v.8 no.1
• /
• pp.64-70
• /
• 1998

자동차의 엔진밸브 스프링으로 사용되는 Si-Cr 스프링강의 영구 변형 저항성과 내피로성이 우수한 고강도강을 개발하기 위하여 탄소함량을 증대시키고 Mo, V, W와 같은 합금원소를 기존의 SAE 9254 스프링강에 첨가하여 개발강을 제조했다. SEM및 EDX가 부착된 TEM을 이용하여 미세조직을 관찰했고, 크립시험 및 피로시험기를 이용하여 스프림의 영구 변형 저항성 및 스프링의 내피로성을 조사했다. 실험결과, 개발강은 피로 특성치는 기존강과 동등 수준이면서 인장강도가 기존강의 것보다 10%가 더높은 2100MPa 급의 고강도를 나타내었으며 또한 영구 변형 저항성도 현저하게 개선되었는데 이는 W, Mo의 첨가로 인해 템퍼링시에 세멘타이트의 성장이 억제되어서 세멘타이트의 석출물이 미세하게 되었기 때문이다.