Fabrication and Characteristics of Indium Tin Oxide Films on CR39 Substrate for OTFT

  • Kwon, Sung-Yeol
    • Transactions on Electrical and Electronic Materials
    • /
    • v.7 no.5
    • /
    • pp.267-270
    • /
    • 2006
  • The Indium tin oxide (ITO) films were deposited on CR39 substrate using DC magnetron sputtering. ITO thin films deposited at room temperature because CR39 substrates its glass-transition temperature of is $130^{\circ}C$. ITO thin films used bottom and top electrode and for organic thin film transparent transistor.(OTFT) ITO thin film electrodes electrical properties and optical transparency properties in the visible wavelength range (300 - 800 nm) strongly dependent on volume of oxygen percent. For the optimum resistivity and transparency of ITO thin film electrode achieved with a 75 W plasma power, 10 % volume of oxygen and a 27 nm/min deposition rate. Above 85 % transparency in the visible wavelength range (300 - 800 nm) measured without post annealing process and $9.83{times}10{-4}{\Omega}cm$ a low resistivity was measured thickness of 300 nm.

Fabrication and Characteristics of Indium Tin Oxide Films on Polycarbonates CR39 Substrate for OTFTs

  • Kwon, Sung-Yeol
    • Korean Journal of Materials Research
    • /
    • v.17 no.4
    • /
    • pp.232-235
    • /
    • 2007
  • Indium tin oxide (ITO) films were deposited on polycarbonate CR39 substrate using DC magnetron sputtering. ITO thin films were deposited at room temperature because glass-transition temperature of CR39 substrate is $130^{circ}C$ ITO thin films are used as bottom and top electrodes and for organic thin film transparent transistor (OTFT). The electrodes electrical properties of ITO thin films and their optical transparency properties in the visible wavelength range (300-800 nm) strongly depend on the volume of oxygen percent. The optimum resistivity and transparency of ITO thin film electrode was achieved with a 75 W plasma power, 10 % volume of oxygen and a 27 nm/min deposition rate. Above 85% transparency in the visible wavelength range (300-800 nm) was measured without post annealing process, and resistivity as low as $9.83{\times}^{TM}10^{-4}{\Omega}$ cm was measured at thickness of 300 nm.

Characteristics of CrOx Thin-films for High Precision Resistors (고정밀저항용 크롬산화박막의 특성)

  • Seo, Jeong-Hwan;Noh, Sang-Soo;Lee, Eung-Ahn;Kim, Kwang-ho
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.18 no.3
    • /
    • pp.253-258
    • /
    • 2005
  • This paper presents characteristics of CrOx thin-film, which were deposited on $Al_2$O$_3$ wafer by DC reactive magnetron sputtering in an argon-oxide atmosphere for high temperature applications. The present paper deals with a study of the technological characteristics of thin film resistors to provide a control in obtaining temperature coefficients of resistance of given value. The optimized condition of CrOx thin-film were thickness range of 2500 $\AA$ and annealing condition(350 $^{\circ}C$, 1 hr) in oxide partial pressure(3.5${\times}$10$^{-4}$ torr). Under optimum conditions, the CrOx thin-films is obtained a high resistivity, p=340 $\mu$Ωcm, a low temperature coefficient of resistance, TCR=-55 ppm/$^{\circ}C$. The CrOx thin films resistors which were fabricated in this paper had excellent characteristics as high precision resistors.

Fabrication and characteristics of ITO thin films on CR39 substrate for transparent OTFT

  • Kwon, Sung-Yeol
    • Journal of Sensor Science and Technology
    • /
    • v.16 no.3
    • /
    • pp.229-233
    • /
    • 2007
  • The indium tin oxide (ITO) films were deposited on CR39 substrate using DC magnetron sputtering. The ITO thin films deposited at room temperature because CR39 substrate its glass-transition temperature is $130^{\circ}C$. The ITO thin films used bottom and top electrode and for organic thin film transparent transistors (OTFTs). The ITO thin film electrodes electrical properties and optical transparency properties in the visible wavelength range (300-800 nm) strongly dependent on volume of oxygen percent. For the optimum resistivity and transparency of the ITO thin film electrode achieved with a 75 W plasma power, 10 % volume of oxygen and a 27 nm/min deposition rate. Above 85 % transparency in the visible wavelength range (300-800 nm) measured without post annealing process and a low resistivity value $9.83{\times}10^{-4}{\Omega}cm$ was measured thickness of 300 nm. All fabrication process of ITO thin films did not exceed $80^{\circ}C$.

Dependence of Gas Pressure on Cr Oxide Thin Film Growth Using a Plasma Focus Device (플라즈마 포커스를 이용한 크롬 산화물 박막 성장의 분위기 기체 압력 의존성 연구)

  • Jung, Kyoo-Ho;Lee, Jae-Kap;Im, Hyun-Sik;Karpinski, L.;Scholz, M.;Lee, Jeon-Kook
    • Korean Journal of Materials Research
    • /
    • v.17 no.6
    • /
    • pp.308-312
    • /
    • 2007
  • Chromium oxide thin films have been deposited on silicon substrates using a tabletop 9kJ mathertyped plasma focus (PF) device. Before deposition, pinch behavior with gas pressure was observed. Strength of pinches was increased with increasing working pressure. Deposition was performed at room temperature as a function of working pressure between 50 and 1000 mTorr. Composition and surface morphology of the films were analyzed by Auger Electron Spectroscopy and Scanning Electron Microscope, respectively. Growth rates of the films were decreased with pressure. The oxide films were polycrystalline containing some impurities, Cu, Fe, C and revealed finer grain structure at lower pressure.

Development of a High Temperature and Exactitude Pressure Sensors for Superior Environmental Characteristics (내환경성이 우수한 고온.고정밀용 압력센서의 개발)

  • 서정환;백명숙;임창섭
    • Proceedings of the Korean Society of Marine Engineers Conference
    • /
    • 2002.05a
    • /
    • pp.13-22
    • /
    • 2002
  • This paper presents characteristics of CrOx thin-film Strain gauge pressure sensors, which were deposited on SUS630 diaphragm by DC reactive magnetron sputtering in an argon-Oxide atmosphere(Ar-(10%)$O_2$). The optimized condition of CrOx thin-film strain gauges were thicknessrange of 2500$\AA$ and annealing condition ($350^{\circ}C$, 3 hr) in Ar-10 %$O_2$deposition atmosphere. Under optimum conditions, the CrOx thin-films for strain gauge is obtained a high resistivity, $\rho$=156.7$\mu$$\Omega$cm, a low temperature coefficiect of resistance, TCR=-86 ppm/$^{\circ}C$ and a high temporal stability with a good longitudinal, 15. The output sensitivity of pressure sensor obtained is 2.46㎷/V and the maximum non-linearity is 0.3%FS and hysteresis is less than 0.2%FS. The output characteristics of pressure transmitter obtained is 4~20㎃ and total accuracy is less than $\pm$0.5%FS. In those conclusions, CrOx thin film pressure sensors is quite satisfactory for many applications in industrial electronics.

  • PDF

Characteristics of chromium oxide thin-films for high temperature piezoresistive sensors (고온용 압저항센서용 크롬산화박막의 특성)

  • Seo, Jeong-Hwan;Noh, Sang-Soo;Lee, Eung-Ahn;Chung, Gwiy-Sang;Kim, Kwang-Ho
    • Journal of Sensor Science and Technology
    • /
    • v.14 no.1
    • /
    • pp.56-61
    • /
    • 2005
  • This paper present characteristics of chromium oxide thin-film as piezoresistive sensors, which were deposited on Si substrates by DC reactive magnetron sputtering in an argon-Oxide atmosphere for high temperature applications. The chemical composition, physical and electrical properties and thermal stability ranges of the $CrO_{x}$ sensing elements have studied. $CrO_{x}$ thin films with a linear gauge factor(GF${\fallingdotseq}$15), high electrical resistivity (${\rho}$ = $340{\mu}{\Omega}cm$) and TCR<-55 ppm/$^{\circ}C$ have been obtained. These $CrO_{x}$ thin films may allow high temperature pressure sensor miniaturization to be achieved.

The Formation Technique of Thin Film Heaters for Heat Transfer Components (열교환 부품용 발열체 형성기술)

  • 조남인;김민철
    • Journal of the Semiconductor & Display Technology
    • /
    • v.2 no.4
    • /
    • pp.31-35
    • /
    • 2003
  • We present a formation technique of thin film heater for heat transfer components. Thin film structures of Cr-Si have been prepared on top of alumina substrates by magnetron sputtering. More samples of Mo thin films were prepared on silicon oxide and silicon nitride substrates by electron beam evaporation technology. The electrical properties of the thin film structures were measured up to the temperature of $500^{\circ}C$. The thickness of the thin films was ranged to about 1 um, and a post annealing up to $900^{\circ}C$ was carried out to achieve more reliable film structures. In measurements of temperature coefficient of resistance (TCR), chrome-rich films show the metallic properties; whereas silicon-rich films do the semiconductor properties. Optimal composition between Cr and Si was obtained as 1 : 2, and there is 20% change or less of surface resistance from room temperature to $500^{\circ}C$. Scanning electron microscopy (SEM) and Auger electron spectroscopy (AES) were used for the material analysis of the thin films.

  • PDF

The Wet Etching Rate of Metal Thin Film by Sputtering Deposition Condition (스퍼터링 증착 조건에 따른 금속 박막의 습식 식각율)

  • Hur, Chang-Wu
    • Journal of the Korea Institute of Information and Communication Engineering
    • /
    • v.14 no.6
    • /
    • pp.1465-1468
    • /
    • 2010
  • The wet etching is a process using chemical solution and occurring chemical reaction on substrate surface. when we do wet etching process, we have to consider stoichiometry, etching time and temperature of etchant for good resolution. In this experiment, we used Cr, Al andIndium-tin-oxide (ITO) metal and we deposited them with DC sputtering machine. The Cr thin film metal thickness is about $1300{\AA}$, ITO films show a low electrical resistance and high transmittance in the visible range of an optical spectrum and Ai film is used for signal line. We measured and analysed wet etching properties on the metal thin films.

Oxidation of CrAlMgSiN thin films between 600 and 900℃ in air (CrAlMgSiN 박막의 600-900℃에서의 대기중 산화)

  • Won, Seong-Bin;Xu, Chunyu;Hwang, Yeon-Sang;Lee, Dong-Bok
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2013.05a
    • /
    • pp.112-113
    • /
    • 2013
  • Thin CrAlMgSiN films, whose composition were 30.6Cr-11.1Al-7.3Mg-1.2Si-49.8N (at.%), were deposited on steel substrates in a cathodic arc plasma deposition system. They consisted of alternating crystalline Cr-N and AlMgSiN nanolayers. After oxidation at $800^{\circ}C$ for 200 h in air, a thin oxide layer formed by outward diffusion of Cr, Mg, Al, Fe, and N, and inward diffusion of O ions. Silicon ions were relatively immobile at $800^{\circ}C$. After oxidation at $900^{\circ}C$ for 10 h in air, a thin $Cr_2O_3$ layer containing dissolved ions of Al, Mg, Si, and Fe formed. Silicon ions became mobile at $900^{\circ}C$. After oxidation at $900^{\circ}C$ for 50 h in air, a thin $SiO_2-rich$ layer formed underneath the thin $Cr_2O_3$ layer. The film displayed good oxidation resistance. The main factor that decreased the oxidation resistance of the film was the outward diffusion and subsequent oxidation of Fe at the sample surface, particularly along the coated sample edge.

  • PDF