• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.134-134
• /
• 2008

아연도금강판은 유-무기 코팅 처리를 통해 도금층 표면의 방청성 향상과 추가적인 고기능성을 부여한다. 최근 POSCO 에서는 가전, 건재 및 자동차용으로 사용하기 위해 다양한 Cr-free 코팅강판을 개발하였다. 본 발표에서는 기존의 크로메이트 처리 강판을 대체하기 위해 유-무기 복합코팅 강판 개발과 품질특성을 소개하고자 한다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.112.1-112.1
• /
• 2007

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.393-399
• /
• 1998

The composition and the properred orientation of Co-Fe-Cr alloy electrodeposits were invesigated according to the electrolysis conditions using sulface bath. The current efficiency and the cathode overpotential decrased noticeably with the increase of Cr content in the bath. As the D.C. current density increased increased, the Cr content in the alloy increasd, while Co content decreased and Fe content remained constant, In the pulse current electrolysis, the Cr content of the alloy increased with the mean current density and off-time and then its content increased mord more noticeably with the peak current density than that of D.C. electrolysis. The preferred orientation of the alloy changed from (220)+(111) to (220) with decreasing cathode overpotential.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.3
• /
• pp.149-157
• /
• 1993

In the study of TAB(Tape Automated Bonding)technologies, Cu-Cr sputtered seed layer has been used to improve the adhesion between Polyimide and Cu film and electrical properties. But the Cu electrodeposit on Cu-Cr film had poor adhesion or powder-like form due to the surface Cr oxides on the Cu-Cr film. By means of activating the Cu-Cr film with the oxalic acid and phosphoric acid, the Cu film with the improved adhesion could be coated on the Cu-Cr sputtered film in CuSO4 solution. The etching rate was compared with increasing the Cr content of the sputtered Cu-Cr film, and anodic polarization curve in FeCl3 solution was investigated. With increasing the Cr content, the etching rate was reduced. The clean etching cross section could be obtained with increasing the concentration of FeCl3 solution. But above the 13 w/o Cr content, Cu-Cr sputtered film could not bed etched cleanly only with FeCl3 solution and additives were needed.

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.66-74
• /
• 1996

In this study, friction and wear properties of flame sprayed specimens and hard Cr plating specimens were tested, and their properties were compared each other in dry and lubrication condition. Ni-Cr powder and steel powder were used as the spray powder and sprayed on the steel(S45C) substrate by flame sprayed method. Each wear surface was observed with SEM after friction and wear test. The friction coefficient of the as-forged steel specimens was the highest among surface treatment specimens, and the other specimens appeared in order as follows ; hard Cr-plating specimens, Ni-Cr powder sprayed specimens, steel powder sprayed specimens. Comparing the wear volumes in dry condition, as forged steel specimens appeared the greatest wear volume, and the other specimens appeared wear volume in order as follows ; Ni-Cr powder sprayed specimens, steel powder sprayed specimens, hard Cr plating specimens. In friction and wear test, the hard Cr plating specimens were worn by the abrasive phenomenon, involving the cracks. The wear volume of steel powder sprayed specimens was lower than that of Ni-Cr powder sprayed specimens. Comparing the tensile strength of both sprayed coating layers, the steel powder sprayed coating layer was better than Ni-Cr powder sprayed coating layer.

• Corrosion Science and Technology
• /
• v.12 no.1
• /
• pp.56-64
• /
• 2013

An Eectrolytic Corrosion(EC) test method was evaluated by the comparison with Copper Accelerated Acetic Salt Spray(CASS) and Neutral Salt Spray(SS) tests. Those methods were applied in order to evaluate corrosion resistance of Ni-Cr plated and Zn-plated Fe substrates. The correlations between results obtained by different test methods were investigated. Results showed that the electrochemical method such as the EC test method was superior to the conventional methods such as CASS and SS, in terms of the quantitative accuracy and the test-time span. Furthermore, the EC test method provided the useful means to estimate the initiation of corrosion of each layer by monitoring the rest potentials of the coated layers such as Ni, Cr, and Zn on Fe substrate. With regard to test time spans, the EC test provided the 78 times and 182 times faster results than the CASS test in cases of $Fe+5{\mu}m$ $Ni+0.5{\mu}m$ Cr and $Fe+20{\mu}m$ $Ni+0.5{\mu}m$ Cr respectively, while the EC test was 85 times faster results than the Salt Spray test in the case of $Fe+20g/m^2$ Zn. Therefore, the EC test can be the better method to evaluate the resistance to corrosion of coated layers than the conventional methods such as the SS test and the CASS.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.8 no.2
• /
• pp.89-98
• /
• 1988

This research evaluated factors on cement-based solidification process designed for hazardous sludge produced from electroplating industry. Four factors of sand/cement ratio, water/cement ratio, amount of wet sludge and amount of a precipitator, were investigated in terms of leachability and compressive strength of the solidified materials. Results of triplicate tests and statistical analysis indicated that sand/cement ratio(S/C) had the greatest effect on leaching of Cr(VI) from the solidified materials while water/cement ratio(W/C) on Zn and compressive strength. Cr(VI) was fixed better than Zn by portland cement. An experimental modeing was developed to estimate leached metal concentration and compressive strength at a given condition. Proper mixing criteria were also suggested for the use of the solidified mixture as construction materials. In solidification of 30g dry sludge, optimal condition was studied for S/C ratio, W/C ratio and the weight of precipitator which were 1, 1.5 and 1.075g respectively.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.722-727
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.56mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.1
• /
• pp.5-12
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.5mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability.

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.2
• /
• pp.89-97
• /
• 1993

An improvement in corrosion resistance of various types of Zn-coated steel sheets is thought to be possible with the addition of fine oxide powder to the coating. In this study the corrosion resistance of the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheet has been investigated and the results were as follows : The corrosion resistance of $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheets was improved by increasing the contents of Co and Cr ions, and also $Al_2O_3$ powders in the bath because of the increased amount of Co, Cr and $Al_2O_3$ in deposits. In the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steels sheet, the structure of deposits was changed from fine microstructure as observed in high Co containing deposits to coarse microstructure as in high Cr and $Al_2O_3$ containing deposits. By cold rolling of the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheets to about 2 percent, thr corrosion resistance was improved further.