• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.30-35
• /
• 2003

In this study, sand cast AZ91E and zirconium grain refined MEZ are representative of two typical groups of magnesium alloys: those containing aluminium and those containing no aluminium but with zirconium as a grain refiner. The corrosion performance of these two alloys was evaluated and compared in 5%wt NaCI solution through measurements of weight loss and polarisation curves and examination of microstructure. Corrosion damage of AZ91E was deeper and more localised than that of MEZ, while MEZ had a lower rate of cathodic hydrogen evolution and a higher rate of anodic dissolution than AZ91E. These differences in behaviour can be related to the differences in microstructure and chemical composition between the two alloys.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.263-268
• /
• 1997

One of the principal causes of the deterioation of coastal concrete structures is the corrosion of reinforcing steel induced by the attack of chloride ions. An experimental study was performed to investigate the distribution of concentration of chloride ions in a coastal concrete structure and to measure the half-cell potential of embedded steel by using the copper-copper sulfate reference electrode. Quantitative analysis showed that the concentration of chloride ion in the aqueous phase near the surface of embedded steel exceeded a threshold value for corrosion, 0.05% by weight in concrete. The absolute value of half-cell potential at some members of embedded steel was measured to be higher than 350mV, indicating that the probability of corrosion is more than 90%. The prediction on corrosion based on the experimental measurements was confirmed by the observation of corrosion on the surface of steel bars in the concrete core taken out of the concrete structure.

• Journal of Welding and Joining
• /
• v.19 no.3
• /
• pp.334-341
• /
• 2001

The chemical and geometric effects of weld on flow-accelerated corrosion (FAC) of SA106 Gr.C low alloy steel pipe in 3.5wt% NaCl and simulated feedwater of nuclear power plant have been investigated by using rotating cylinder electrode. Polarization test and weight loss test were conducted and compared at rotating speed of 2000rpm (3.14m/s) with the variables of chemical and geometric parameters. The results showed that the chemical effects were relatively larger than the geometric effects, and the welded parts were the local anode and preferentially corroded, which could be explained by the differences between microstructural and compositional parameters. On the other hand, under active corrosion conditions, the heat affected zone were severely corroded and microstructural effects became the important role in the whole process.

• Journal of Ocean Engineering and Technology
• /
• v.17 no.3 s.52
• /
• pp.39-45
• /
• 2003

Shot peening is an effective method of improving the fatigue strength of components and structures. The compressive residual stress produced by surface plastic deformation with shot peening is usually regarded as the major factor in increasing fatigue strength. In this study, the influence of shot peening on corrosion was investigated. Spring steel immersed in $3.5\%$ NaCl prior was used to evaluate the effect of shot peening on fatigue properties. The immersion test was performed on the five kinds of specimens with shot peened and unpeened. The distributions of residual stresses of shot peened spring steels were measured in an X-ray diffraction apparatus, using the two-point method. Corrosion potential, polarization curve, residual stress, etc. were investigated, based on the experimental results. From test results, the effect of shot peening on the corrosion was evaluated.

• Advances in materials Research
• /
• v.7 no.2
• /
• pp.105-118
• /
• 2018

Magnesium and its alloys are attracted towards all engineering applications like automotive, marine, aerospace etc. due to its inherent high strength to weight ratio. But, extensive use of Mg alloys is limited to the current scenario because of low wear and corrosion resistance behavior. However, equal channel angular press is one of the severe plastic deformation technique which has been effective method to improve the wear and corrosion resistance by achieving fine grain structure. In this study, the effect of grain refinement on wear and corrosion resistance of AZ80 Mg alloys were investigated. The wear behavior of the coarse and fine-grained Mg alloys was examined through $L_9$ orthogonal array experiments in order to comprehend the wear behavior under varies control parameters. It was shown that ECAPed alloy increased the wear and corrosion resistance of the Mg alloy through the formation of fine grain and uniform distribution of secondary ${\beta}-phase$. Also, the performance of AZ80 Mg alloy for these changeswas discussed through SEM morphology.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.109-110
• /
• 2021

An attempt has been made on a constructive approach to evaluate the performance of snail shell ash (SSA) for its corrosion performance under marine environments. Corrosion performance of steel rebar in chloride contaminated SSA with (0% to 50%) replacement levels of cement extract medium was examined through electrochemical and weight loss techniques. Initially, snail shell powder (SSP) is made by pulverizing and subsequently SSA is by thermal decomposition methods. A critical level of 20 % SSA improved both corrosion resistance properties of cement extracts. SSA is a suitable replacement material for natural limestone in cement productions.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.147-153
• /
• 2007

This study sought to investigate the reaction of Co-binder containing tungsten with molten zinc. Four kinds of Co-W alloys (pure, 10%W, 20%W, 30%W) were prepared using the powder metallurgy method. The specimens were immersion-tested in molten pure zinc baths at $460^{\circ}C$. To evaluate the corrosion property in molten zinc, the weight loss of the specimen was measured after the immersion tests at different immersion times (10~300 min.). Co-10%W alloys, compared with pure cobalt, showed no effect of tungsten addition on the reaction rate in molten zinc. The relationship between the weight loss and the square root of immersion period represents a straight line in both pure cobalt and Co-10%W alloy. The Co-Zn reaction layer in Co- 1O%W alloy consists of $\gamma2$, $\gamma1$, $\gamma$ and ($\beta1$ phases. The rate of weight loss significantly increases and the weight loss behavior is not well accord with the linear relationship as the tungsten content in the Co-W alloy increases. The $\beta1$ layer was not formed on the Co-20%W alloy and neither was a stable Co-Zn intermetallic compound layer found on the Co-30%W alloy. The main cause of increase in reaction rate with increasing tungsten content is related with the instability of the Co-Zn reaction phases as seen on micro-structural analysis.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.38 no.1
• /
• pp.79-88
• /
• 2002

13%Cr martensitic stainless steel has been used mainly with a material for fish pre-processing machinery. However, it has not very nice cutting section because of little of the carbon content. Therefore, SUS420J2 steel that contents 0.3%C with high-strength in spite of the rust is used with a material for fish pre-processing machinery. However, studies on the corrosion characteristics of SUS420J2 steel are relatively rare. Especially, the corrosion phenomenon may cause serious degradation because the fish pre-processing machinery is exposed always to seawater environment. In this paper, the immersion corrosion test was carried out at seawater environment (pH=7.52) on SUS420J2 steel specimens that have various post-treatment conditions and its corrosion characteristics were evaluated. From test results, the specimens such as base metal, vacuum heat treatment, electrolytic polishing and tempering after quenching tend somewhat sensitive from the corrosion. In the case of vacuum heat treatment specimen of continuous immersion during 360 days, the weight loss ratio was high about seven times when compared with the different specimens. On the contrary, SUS420J2 steel specimen that has the heat treatment of tempering after quenching and the electrolytic polishing was less sensitive from the corrosion, and the weight loss ratio was very low.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.5
• /
• pp.58-68
• /
• 2000

When SS400 steel was welded with low hydrogen type and ilmennite type welding, the effect of post-weld heat treatment(PWHT) was investigated with parameters such as micro vickers hardness, corrosion potential, polarization behaviors, galvanic current, Al anode generating current and Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM) by PWHT in case of low hydrogen type and ilmennite type welding was lower than that of each parts by As-welded However hardness of WM area in case of low hydrogen type and ilmennite type welding was the highest among those three parts regardless of PWHT, Whereas in case of ilmennite type welding, WM area was the highest potential among these three parts on galvanic potential series with As-welded while BM area was the highest potential among these three parts by PWHT on the contrary. And in case of low hydrogen type welding, galvanic corrosion and micro cell corrosion of welding parts was decreased with PWHT. However, It was increased with PWHT in case of ilmennite type welding. Moreover Al anode generating current and anode weight loss in case of low hydrogen type was decreased by PWHT compared to As-wedled but, which was increased than that of As-welded in case of ilmennite type welding. Therefore, it is suggested that Corrosion resistance property in case of low hydrogen type welding is increased by PWHT. However its property was devreased with PWHT in case of ilmennite type welding.

• Journal of the Korean Chemical Society
• /
• v.56 no.4
• /
• pp.401-405
• /
• 2012

Corrosion inhibition efficiencies of holy basil on Al in HCl solution were studied by weight loss and thermometric methods in presence and in absence of stem extract of three different varieties of holy basil viz. ocimum basilicum ($E_B$), ocimum canum ($E_C$) and ocimum sanctum ($E_S$). Inhibition efficiency increases with the increasing concentration of stem extract and decreases with increases in acid strength. Results show that all varieties under study are good corrosion inhibitors, among which, $E_B$ is most effective. Maximum inhibition efficiency was found 97.09% in 0.5N HCl solution with 0.6% stem extract. The Langmuir adsorption isotherm indicates that surface coverage also increases with increasing in the concentration of extract of stem in HCl solution.