• 한국해양공학회지
• /
• 제18권6호
• /
• pp.96-100
• /
• 2004

Inconel 625 is useful in a variety of industrial applications because of the resistance to attack in various corrosive media at temperatures from $200^{\circ}C$ to over $1090^{\circ}C$, in combination with good low and high temperature mechanical strength. Rencently this material has also been widely used in offshore processing piping in order to extend the maintenance term and improve the quality of anti-corrosion. In general, high quality weldings for this material are readily produced by commonly used processes. How, not all processes are applicable to this material group of Ni-alloys. Metallurgical or the unavailability of matching, position or suitable welding processes produce a lower quality. Nowadays, the flux cored wire is developed and applied for increased productivity in several welding positions, including the vertical position. In this study, the weldability and weldment characteristics(mechanical properties) of inconel 625 are considered in FCAW(Flux Core Arc Welding) associated with the several shielding gases$(80\%Ar+20\%CO2,\;50\%Ar+50CO2,\;100CO2)$ in view of welding productivity.

• 한국해양공학회지
• /
• 제36권4호
• /
• pp.243-250
• /
• 2022

Subsea power cables are subjected to various external loads induced by environmental and mechanical factors during manufacturing, shipping, and installation. Therefore, the prediction of the structural strength is essential. In this study, experimental and theoretical analyses were performed to investigate the axial stiffness of subsea power cables. A uniaxial tensile test of a 6.5 m three-core AC inter-array subsea power cable was carried out using a 10 MN hydraulic actuator. In addition, the resultant force was measured as a function of displacement. The theoretical model proposed by Witz and Tan (1992) was used to numerically predict the axial stiffness of the specimen. The Newton-Raphson method was employed to solve the governing equation in the theoretical analysis. A comparison of the experimental and theoretical results for axial stiffness revealed satisfactory agreement. In addition, the predicted axial stiffness was linear notwithstanding the nonlinear geometry of the subsea power cable or the nonlinearity of the governing equation. The feasibility of both experimental and theoretical framework for predicting the axial stiffness of subsea power cables was validated. Nevertheless, the need for further numerical study using the finite element method to validate the framework is acknowledged.

• 콘크리트학회논문집
• /
• 제24권2호
• /
• pp.195-204
• /
• 2012

신구 콘크리트 접합부에서는 굽힌 후 편 철근을 이용한 이음이 발생한다. 철근의 굽힘과 펴는 과정에는 필연적으로 소성 변형이 발생하며, 이 과정에서 가공 경화, 바우싱거 효과, 시효 경화 현상이 발생된다. 이 연구에서는 강종, 지름, 굽힘 내면 반지름, 굽힌 후 펴기까지의 존치기간을 변수로 굽힌 후 편 철근의 인장에 대한 기계적 성질을 조사하였다. 연구 결과, 굽힌 후 편 철근은 비례한계점이 낮아지는 비선형성이 직선 철근에 비해 일찍 발생되었으며, 항복마루 없이 바로 변형경화가 발생하였다. 이것은 굽힘 가공에서 압축을 받은 부분의 바우싱거 효과에 의해 항복점이 낮아졌고, 굽힘 가공에서 인장을 받은 부분의 가공 경화에 의해 항복마루가 없어졌기 때문이다. 높은 강종일수록 항복강도의 저하가 크게 발생되었으며, SD400 철근의 항복강도는 설계기준강도보다 낮았다. 철근은 표면부의 강도가 내부보다 높기 때문에, 높은 강종일수록 굽힌 후 펴면 바우싱거 효과가 크게 발생된다. 굽힌 후 펴기까지의 존치기간이 길면 시효 경화에 의해 항복강도의 상승과 연성의 저하가 발생되었다. Ramberg-Osgood 모델을 기본 형태로 실험 자료를 회귀분석하여 항복강도와 존치기간을 고려한 굽힌 후 편 철근의 응력-변형률 관계를 구성하였다. 이 모델은 굽힌 후 편 철근이 사용된 접합부의 강성 평가에 활용될 수 있다.

• 접착 및 계면
• /
• 제2권4호
• /
• pp.24-31
• /
• 2001

용융 흐름성이 다른 폴리프로필렌(Polypropylene, PP)을 에틸렌-프로필렌 고무(EPR) 또는 에틸렌-프로필렌-디엔 단량체 고무(EPDM) 및 카르복실산 그룹을 갖고 있는 에틸렌 공중합체와 이축 압출기로 용융 혼합한 후 사출성형으로 고분자 블렌드 시편을 제조하였다. 제조된 블렌드의 기계적 특성과 시편의 두께 방향에 따른 모폴로지 변화를 조사하였으며 적외선 분광법(ATR-IR)을 이용하여 표면에서의 카르복실산 그룹의 상대적 피크 크기를 비교하였다. 단면의 모폴로지 조사에서 중앙부에는 PP 연속상에 고무 도메인이 골고루 혼합되어 있지만 표면쪽은 PP가 층을 이루고 있는 경사구조가 관찰되었다. PP의 흐름성이 클수록 블렌드의 인장강도 및 충격강도가 작아졌으며 EPR보다 EPDM을 고무성분으로 사용한 PP계 블렌드가 PP의 흐름성에 대한 영향을 적게 받았다. 또한 PP의 흐름성이 클수록 카르복실산 그룹이 표면에 많이 존재하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제14권3호
• /
• pp.83-90
• /
• 2010

구조물의 해석, 설계, 시공, 품질관리 등을 수립할 때 토목기술자는 경제적이며 효율적인 복합재료를 사용할 수 있다. 거더, 가로보, 콘크리트 상판으로 이루어진 교량시스템은 특별직교이방성 판으로 거동한다. 이러한 경계조건을 갖는 단면을 Navier 해 형태의 해석적 해를 구하기가 매우 어렵다. 복합재료로 이루어진 교량을 설계하기위하여, 단면은 가장 경제적이면서 응력에 유리한 폼코어 형태를 채택하였고, 응력을 산출함에 있어서는 유한차분법 프로그램을 사용하였다. 응력영역은 Tasi-Wu 파괴영역 기준을 이용하였다. 본 논문에서는 치수가 증가됨에 따른 인장강도 감소율을 고려하였다. 또한 이러한 경우에 대한 수치해석을 수행하였다.

• Steel and Composite Structures
• /
• 제29권5호
• /
• pp.603-622
• /
• 2018

Precast concrete structures are erected from individual prefabricated components, which are assembled on-site using different types of connections. In the present design of these structures, beam-to-column connections are assumed pin jointed. Bolted billet beam to-column connections have been used in the precast concrete industry for many years. They have many advantages over other jointing methods in component production, quality control, transportation and assembly. However, there is currently limited information concerning their detailed structural behaviour under vertical loadings. The experimental work has involved the determination of moment-relative rotation relationships for semi-rigid precast concrete connections in full-scale connection tests. The study reported in this paper was undertaken to clarify the behaviour of such connections under symmetrical vertical loadings. A series of full-scale tests was performed on sample column for which the column geometry and bolt arrangements conformed to successful commercial practice. Proprietary hollow core floor slabs were tied to the beams by 2T25 tensile reinforcing bars, which also provide the in-plane continuity across the connections. The contribution of the floor strength and stiffness to the flexural capacity of the joint is currently neglected in the design process for precast concrete frames. The flexural strength of the connections in the double-sided tests was at least 0.93 times the predicted moment of resistance of the composite beam and slab. The secant stiffness of the connections ranged from 0.94 to 1.94 times the flexural stiffness of the attached beam. In general, the double-sided connections were found to be more suited to a semi-rigid design approach than the single sided ones. The behaviour of double sided bolted billet connection test results are presented in this paper. The behaviour of single sided bolted billet connection test results is the subject of another paper.

• 융합정보논문지
• /
• 제9권7호
• /
• pp.94-99
• /
• 2019

마찰교반용접법(Friction Stir Welding, FSW)은 1991년에 영국 용접연구소 TWI(The Welding Institute)에서 최초 개발된 후 여러 산업분야에 걸쳐 적용연구가 활발히 진행되고 있다. 본 연구에서는 철도차량 차체의 주요 구성 소재인 알루미늄 합금 (Al-6005-T6) 평판 압출재에 대한 마찰교반접합 적용 기초연구를 수행하였다. 접합속도를 500 mm/min으로 고정한 채 회전공구의 회전속도를 600-1600 rpm으로 변화될 때 미세구조와 기계적 물성 변화에 미치는 영향에 대해 평가하였다. 경도 측정 결과 nugget부는 모재의 70% 수준의 경도값을 가지며 설정된 범위 내의 공구 회전속도와 연관성은 관찰되지 않았으며 용접계면에서 약 5 mm 벗어나게 되면 모재의 경도값을 가지는 것으로 확인되었다. 인장시험 결과 회전속도가 올라갈수록 항복강도와 인장강도가 소폭 하락하는 경향을 보였으며 연신률의 변화는 관찰되지 않았다.

• 열처리공학회지
• /
• 제36권1호
• /
• pp.1-6
• /
• 2023

In order to process plastic with similar mechanical performance to metal materials, it is necessary to improve the strength and hardness of core parts of the injection equipment in extrusion system. The tempering process is a heat treatment performed to reduce brittleness and improve elongation along with improvement of dimensional defects of martensite formed after quenching. In this study, changes in microstructure and mechanical properties according to temperature were evaluated after quenching and tempering of SM30C material. As a result, the strength and hardness were gradually decreased by tempering at 250~400℃, and the decrease was greatly increased under the tempering condition at 450℃. Under the tempering condition of 200~400℃, the main structure was lath martensite, and the precipitation amount and size of needle-shaped cementite increased along the lath with the increase of the tempering temperature. Most of the shape of cementite has a needle-like structure, and the formation of some spherical cementite is observed. Under the tempering condition of 450℃, a mixed structure of ferrite and martensite was formed according to the decomposition of martensite.

• 대한치과교정학회지
• /
• 제19권2호
• /
• pp.7-24
• /
• 1989

The physical properties of seven sizes of control groups and experimental group in stainless steel orthodontic wires were studied in tension, hardness, bending, torsion and observation of microstructure. The wires (0.40-0.90mm dia.) of round type were tested in the as-received condition. The wires of control groups were TRU-CHROME and REMANIUM, and experimental group was SK wire which was developed by ourselves and made in Korea. The results were as follows; 1. The chemical compositions of control groups and experimental group were austenite stainless steel wires of SOS 304. 2. Higher values of tensile and yield strength in tension were control group I, experimental group, control group II. Maximum tensile and yield strength of experimental group were $203.63{\pm}1.41kg/mm^2$ in 0.70mm diameter and $148.96{\pm}4.88kg/mm^2$ in 0.60mm diameter, and maximum elongation was $5.20{\pm}0.57%$ in 0.45mm diameter. 3. Hardness values of experimental group were similar to control groups. Maximum hardness values were $596.2{\pm}13.66Hv$ in 0.45mm diameter wire of control group I, $590.5{\pm}20.08Hv$ in 0.50mm diameter wire of control group II, and $563.6{\pm}5.35Hv$ in 0.70mm diameter wire of experimental group. 4. Torsion properties of experimental group were similar to control group I and more than control group II. Maximum torsion cycles were $31.8{\pm}2.48$ in 0.45mm diameter of control group I, $17.4{\pm}4.84$ in 0.60mm diameter of control group II, and $24.6{\pm}3.04$ in 0.45mm diameter of experimental group. 5. Maximum bending cycles of experimental group were smaller than control groups. Maximum bending cycles were $9.00{\pm}0.00$ in 0.50mm diameter wire of control group I, $10.0{\pm}0.82$ in 0.40mm diameter wire of control group II, and $8.0{\pm}1.26$ in 0.50mm diameter wire of experimental group. 6. Microstructures of experimental and control groups co-existed with martensited austenite structure and elongated austenite structure. 7. The direction of wire fracture was propagated parallel to torsion direction typically and there was no probability showing wire fracture at inclusions and surface scratches. 8. The type of wire fracture was brittle fracture at initiation site and ductile fracture at core.

• 한국산학기술학회논문지
• /
• 제15권10호
• /
• pp.5933-5938
• /
• 2014

본 연구에서는 Atos 60의 시험편에 혼합가스의 변화에 따른 FCA용접을 하였고, 용접특성 분석 위하여 용접공정상의 실시간 모니터링 시스템과 용접 후 기계적 성질을 평가 하였다. Ar 80%+$CO_2$ 20% 혼합하고 낮은 속도로 용접한 경우 가장 미려한 비드와 스패터 발생이 적게 나타났으며, 반면 $CO_2$ 100%인 경우 스패터가 많이 발생하는 것을 확인하였다. 정상단락이 발생하는 저전류 영역으로 혼합가스의 사용에 대한 스패터 발생을 확인 할수 있는 조건이며, $CO_2$ 100%인 경우 각층의 단락율은 약 2배 이상 높았고, Peak의 분포가 많은 아크의 불안정 상태로 나타났다. 인장시험결과 Ar 80%+$CO_2$ 20%, Ar 90%+$CO_2$ 10%, $CO_2$ 100%의 항복강도는 각각 511MPa, 507MPa, 469MPa 이었으며, $CO_2$ 100%의 항복강도 보다 각각 약 8.9% 8.1% 향상되었다. 인장강도는 각각 622MPa, 609MPa, 581MPa로 $CO_2$ 100%의 인장강도 보다 각각 약 7.0%, 4.8% 향상되었다.